• Journal of the Korean Magnetics Society
• /
• v.10 no.3
• /
• pp.112-117
• /
• 2000

We inserted CoO layer in NiO spin-valves to improve on magnetoresistance and exchange coupling field. The magnetoresistance ratio was increased from 4.5 % to 5.5 % with the increase of CoO thickness. We can not find the dependence between (111) texture and exchange coupling by the measurement of XRD of CoO/NiO spin-valves. The surface roughness of CoO layer, 6.1 $\AA$ is twice more than that of NiO layer, 3.1 $\AA$. The increase of exchange coupling field and coercive field in the CoO/NiO spin-valves will be due to increasing roughness. We prepared the NiO/CoO/NiO/CoO/NiO spin-valves to reduce coercive field and the coercive field decreased from 110 Oe to 50 Oe, and the coupling field is not changed from 70 Oe.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.130-134
• /
• 2006

Buffer layers such as $CeO_2\;and\;Yb_2O_3$ films for YBCO coated conductors were deposited on (100) $SrTiO_3$ single crystals and (100) textured Ni substrates by a metal organic chemical vapor deposition (MOCVD) system of the hot-wall type. The substrates were moved with the velocity of 40 cm/hr. Source flow rate, $Ar/O_2$ flow rate and deposition temperature were main processing variables. The degree of film epitaxy and surface morphology were investigated using XRD and SEM, respectively. On a STO substrate, the $CeO_2$ film was well grown epitaxially above the deposition temperature of $450^{\circ}C$. However, on a Ni substrate, the XRD showed NiO (111) and (200) peaks due to Ni oxidation as well as (111) and (200) film growth. For the films deposited with $O_2$ gas as oxygen source, it was found that the NiO film was formed at the interface between the buffer layer and the Ni substrate. The NiO layer interrupts the epitaxial growth of the buffer layer. It seems that the epitaxial growth of the buffer layer on Ni metal substrates using $O_2$ gas is difficult. We are considering a new method avoiding Ni oxidation with $H_2O$ vapor instead of $O_2$ gas.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.126-135
• /
• 1997

$H_2/O_2$ 비에 따른 Hybrid HVOF 용사된 $Cr_3C_2$-7wt%(NiCr) 용사층의 특성 및 산화거동 This study was performed to investigate the influence of fuel/oxygen ratio (F/O=3.2, 3.0, 2.8) on the characteristics and the oxidation behavior of the hybrid-HVOF sprayed $Cr_3C_2$-7wt%NiCr coatings. Decomposition and the oxidation of the $Cr_3C_2$was occured during spraying. The degree of transformation from $Cr_3C_2$to $Cr_7C_3$ was increased with decreasing the F/O ratio. The microstructural differences of the as sprayed coating with F/O ratio can not be distinguished, However, large pores were diminished and then the coatings became dense by heat treatment. Microhardness of the as-sprayed specimen which sprayed with F/O=3.0 condition was hightest ($Hv_{300}$=1140) and the hardness was increased to 1500 after heat treatment at $600^{\circ}C$ for 50hrs in air. It was supposed that hardness was increased due to the formation of $Cr_2O_3$ within $Cr_3C_2$/$Cr_7C_3$matrix and the densification of coating layer during heat treatment. Apparent activation energy for oxidation was varied from 21.2 kcal$mol^{-1}K^{-1}$ to 23.8 kcal$mol^{-1}K^{-1}$ with respect to the F/O ratio. The surface morphology was changed to porous and oxide chusters were grown after oxidation $1000^{\circ}C$ for 50 hours by the aggressive evolution of gas phase ($CrO_3$ and$CO_2$). The oxide cluster was composed of Ni and Cr.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• v.y2005m4
• /
• pp.106-111
• /
• 2005

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2-8wt.\% Y_{2}O_3$ ceramic coating during cyclic oxidation. $Al_{2}O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_{2}O_4 and Ni(Al,Cr)_{2}O_4$ during cyclic oxidation It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr,Al)_{2}O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.340-344
• /
• 1998

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2$-8wt.% $Y_2O_3$ ceramic coating during cyclic oxidation. $Al_2O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_2O_4$ and $Ni(Al, Cr)_2O_4$ during cyclic oxidation. It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr, Al)_2O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• Journal of the Korean Magnetics Society
• /
• v.8 no.2
• /
• pp.62-66
• /
• 1998

We have studied on the magnetic properties of the specimen with additives Bi$_2$O$_3$and$V_2O_5$ that sintered at 900 $^{\circ}C$ for 4 hours for sybthesizing optimal Ni-Zn-Cu ferrite. Curie temperature rises from 240 $^{\circ}C$ to 270 $^{\circ}C$ as Ni contents increase. Magentic maximum induction$(B_m)$ increases from 2650 G to 3300 G, 3500 G in the specimens with $V_2O_5$ and Bi$_2$O$_3$resectively. On the contrary coercive force $(H_c)$ lowers to 2.05 Oe~1.05 Oe. Permeability all increase in the specimen with additives. In the specimen with additive Bi$_2$O$_3$, we have obtained the low relative loss factor of $6.3{\times}10^{-5}~7.84{\times}10^{-5}$ in the range of 1MHz due to increase of resistivity in grain boundary. In the specimen with additive $V_2O_5$ in spite of increase permeability relative loss factor increase of due to decrease of Q-value.

• Applied Microscopy
• /
• v.42 no.4
• /
• pp.207-211
• /
• 2012

We examined the electrical properties and microstructure of NiO produced using a sol-gel method and Ni nitrate hexahydrate ($Ni[NO_3]_2{\cdot}6H_2O$) to investigate if this NiO thin film can be used as an insulator layer for resistance random access memory (ReRAM) devices. It was found that as-prepared NiO film was polycrystalline and presented as the nonstoichiometric compound $Ni_{1+x}O$ with Ni interstitials (oxygen vacancies). Resistances-witching behavior was observed in the range of 0~2 V, and the low-resistance state and high-resistance state were clearly distinguishable (${\sim}10^3$ orders). It was also demonstrated that NiO could be patterned directly by KrF eximer laser irradiation using a shadow mask. NiO thin film fabricated by the sol-gel method does not require any photoresist or vacuum processes, and therefore has potential for application as an insulating layer in low-cost ReRAM devices.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.11a
• /
• pp.667-672
• /
• 2005

In order to effectively utilize visible light in the photocatalytic reaction, nanaocomposite of Ni doped $TiO_2$ and $NiTiO_3$ powders were synthesized by mechanical alloying and heat treatment. About 5.4 wt% of $NiTiO_3$ with particle size less than 15nm was uniformly formed in the Ni-doped rutile $TiO_2$ matrix. The UV/VIS-DRS and PL investigation showed that the nanocompasite $TiO_2$ powders had a longer absorpt ion wavelength (600$\sim$650nm, 2.0$\sim$1.9eV) than that of Ni-doped $TiO_2$ or rutile $TiO_2$ powder. The carbon decomposition of 4-CP by the nanocompasite $TiO_2$ powders were higher than other $TiO_2$ (P-25).

• Journal of Surface Science and Engineering
• /
• v.44 no.5
• /
• pp.196-200
• /
• 2011

The Ni-based superalloy, Inconel 713, was oxidized at $800{\sim}1100^{\circ}C$ for 50 and 100 hours in air. It displayed excellent oxidation resistance, forming a few micrometer-thick scales. The major scale was ${\alpha}-Al_2O_3$. Other scales formed were $TiO_2$, $NiAl_2O_4$ and $Cr_2O_3$. Generally, uniform oxidation occurred over the alloy surface, resulting in the formation of ${\alpha}-Al_2O_3$ with and without $Cr_2O_3$. Other oxides such as $TiO_2$ and $NiAl_2O_4$ sometimes also formed. Locally, nodular oxidation occurred at the nodules that consisted of diverse alloying elements. The scales were adherent at $800^{\circ}C$. However, they spalled a little at $900{\sim}1100^{\circ}C$.

• Ceramist
• /
• v.10 no.3
• /
• pp.28-33
• /
• 2007

The structural and optical properties of Ni-doped transparent glass-ceramics are reviewed. The quantum efficiencies of ceramics were examined to explore suitable crystalline phase for Ni-doping in glass-ceramics. Inverse spinel $LiGa_5O_8$ have the quantum efficiency of almost 100 % at room temperature. Transparent glass ceramics containing $LiGa_5O_8$ was successfully synthesized by heat treatment of $Li_2O-Ga_2-O_3-SiO_2-NiO$ glass. Most of $Ni^{2+}$ ions in glass-ceramic were incorporated into $LiGa_5O_8$ nanocrystals. The near-infrared emission covering from the O-band to L-band (1260-1625 nm) was observed from the Ni-doped $Li_2O-Ga_2O_3-SiO_2$ glass-ceramic though it was not observed from the as-cast glass. The lifetime of the emission was about $580\;{\mu}sec$ even at 300K. The emission quantum efficiency was evaluated as about 10 % that is enough high for practical usage as gain media of optical fiber amplifiers. The figure of merit (the product of the stimulated emission cross section and lifetime) was as high as that of rare-earth-doped glasses. The broad bandwidth, high quantum efficiency and high figure of merit show that transparent glass-ceramics containing $Ni^{2+}:LiGa_5O_8$ nanocrystals are promising candidates as novel ultra-broadband gain media.