The possibility of the existence of a field-induced micro-macrodomain switching was proposed and examined using 9 mol % PbZrO3-doped 0.6Pb(Ni1/3Nb2/3)O3-PbTiO3 (PNN-PT) systems having rhombohedral symmetry at room temperature. the thermally depoled (freshly prepard) specimens prepared from the rhombohedral side of the system exhibited a relaxor behavior for the whole range of temperature examined (for T

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.338-339
• /
• 2005

본 연구에서는 $Fe_2O_3$를 첨가한 $Pb(Ni_{1/3}Nb_{2/3})O_3-Pb(Zr_xTi_{1-x})O_3$ 세라믹스에서 Zr/Ti 비 변화에 따른 소결 및 압전, 유전특성을 조사하였다. $0.4Pb(Ni_{1/3}Nb_{2/3})O_3-0.6Pb(Zr_xTi_{1-x})O_3$+0.25Wt% $Fe_2O_3$ 계에서 Zr/(Ti+Zr)비(x)를 0.39에서 0.42까지 변화시킨 조성을 1100 - $1250^{\circ}C$ 온도에서 2시간 소결하여 이의 결정구조 및 미세조직을 분석하였고, 압전, 유전 특성 및 RAINBOW 액츄에이터로의 응용을 조사하였다. $1150^{\circ}C$에서 소결한 0.405 조성(x)에서 유전상수(${\varepsilon}r$) = 4669, 전기기계결합계수(kp) = 0.75, 압전상수($d_{33}$) = 810 pC/N의 우수한 특성 값을 나타내었으며, 닥터블레이드법에 의해 RAINBOW 액츄에이터를 제작하여 변위특성을 조사하였다.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1197-1201
• /
• 1994

The fracture strength and fracture modes were studied in 3Y-TZP/NiNi bonding which change their interfacial structure with bonding condition. Average 4-point bending strength of 200 MPa to 400 MPa were achieved. The formation of Ti-oxide phase at the interface critically influenced the bonding strength and fracture mode. The fracture surface of Ti-oxide free interface contained multiphase in some case including ZrO2. From the result it was confirmed that in order to maximize the bonding strength crack deflection from interface to ceramic was required.

• Journal of Korean Society of Environmental Engineers
• /
• v.36 no.6
• /
• pp.396-401
• /
• 2014

Nanomaterials have been widely used in many fields. This study investigates the effects of metal oxide nanoparticles (CuO, NiO, $TiO_2$, $Fe_2O_3$, $Co_3O_4$, ZnO) on germination and germination index (G.I.) of seeds, Lactuca and Raphanus. Under aqueous exposure, CuO on Lactuca shows the most significant impacts on activities compared to others, showing $EC_{50s}$ for germination and G.I. as 0.46 mg/L and 0.37%, respectively. The effects of nanoparticle phytotoxicity on seed Lactuca was much higher than that of Raphanus. In general, the toxicities on seed germination and germination index were as following orders : CuO > ZnO > NiO ${\gg}$ $TiO_2$, $Fe_2O_3$, $Co_3O_4$. No measurable inhibition was observed at 1,000 mg/L (maximum exposure concentration) of $TiO_2$, $Fe_2O_3$, $Co_3O_4$.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.10
• /
• pp.3213-3217
• /
• 2012

Reactive adsorption desulfurization (RADS) experiments were conducted over a series of commercial metal oxide supports ($Al_2O_{3-}$, $SiO_{2-}$, $TiO_{2-}$ and $ZrO_{2-}$) supported Ni/ZnO adsorbents. The adsorbents were characterized by X-ray diffraction (XRD), temperature programmed reduction (TPR), and Fourier transform infrared spectroscopy (FTIR) in order to find out the influence of specific types of surface chemistry and structural characteristics on the sulfur adsorptive capacity. The desulfurization performance of all the studied adsorbents decreased in the following order: Ni/ZnO-$TiO_2$ > Ni/ZnO-$ZrO_2$ > Ni/ZnO-$SiO_2$ > Ni/ZnO-$Al_2O_3$. Ni/ZnO-$TiO_2$ shows the best performance and the three hour sulfur capacity can achieve 12.34 mg S/g adsorbent with a WHSV of $4h^{-1}$. Various characterization techniques suggest that weak interaction between active component and support component, high dispersion of NiO and ZnO, high reducibility and large total Lewis acidity of the adsorbents are important factors in achieving better RADS performance.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.169-170
• /
• 2005

본 연구에서는 초음파 센서에 응용 가능한 $0.4Pb(Ni_{1/3}Nb_{2/3})O_3-0.6Pb(Zr_xTi_{1-x})O_3+0.5Wt%$ $MnO_2$ 세라믹스에 Zr/(Ti+Zr)비를 0.37에서 0.41로 변화시킨 조성을 1175 $\sim$ 1200$^{\circ}C$ 온도에서 소결하여 이의 결정구조 및 미세조직을 분석하였고, 압전, 유전 특성을 고찰하였다. 본조성에서 x=0.385 조성에서 최대 유전상수 값 3490 이 나타났으며, 그 이상의 첨가에서는 감소하였다. 상경계 영역인 x=0.385 조성에서 $\varepsilon$r, $K_p$, $d_{33}$ 값이 최대값을 나타내었다. $0.4Pb(Ni_{1/3}Nb_{2/3})O_3-0.6Pb(Zr_xTi_{1-x})O_3+0.5Wt%$ $MnO_2$, 세라믹스에서는 kp 와 $d_{33}$ 는 Zr/(Ti+Zr)비 0.385조성까지 증가하였다가 그 이상 조성에서 감소하였다. $1175^{\circ}C$에서 2시간 소결한 x=0.385조성에서 $\varepsilon$r=3490, kp=0.71, Qm=476의 우수한 압전 특성을 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.488-494
• /
• 1988

Effects of MnO2 addition on themicrostructure, dielectric and piezoelectric properties of Rhombohedral, Tetragonal and Morphotropic phase boundary(MPB) in Pb(Ni1/3Nb2/3)O3-PbTiO3-PbZrO3 system were investigated and respectively the amount of MnO2 addition was 0, 0.2, 0.5, 1.0, 3.0wt%. In the tetragonal region, compared with the Rhombohedral and Morpotropic phase boundary, Mechanical quality factor(Qm), Curie temperature(Tc) and Dissipation factor were promoted by addition of MnO2. According to the results of the microstructure, dielectric and piezoelectric properties, the solid solution range of MnO2 addition in this system was 0.2-0.5wt%.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.285-291
• /
• 2004

As a part of assessment of the structural material for the molten salt handling system, corrosion behavior of Inconel 718, X-750, Haynes 75 and Haynes 263 alloys in the molten salt of LiCl-Li$_2$O-O$_2$was investigated in the range of temperature; $650^{\circ}C$, time; 24~168h, $Li_2O$; 3wt%, mixed gas; Ar~10%$O_2$. In the molten salt of LiCl-$Li_2O-O_2$, the order corrosion rate was Haynes 263 ＜ Haynes 75 ＜ Inconel X-750 ＜ Inconel 718. Haynes 263 alloy showed the highest corrosion resistance among the examined alloys. Corrosion products of alloys were as fellows: Haynes 75: $Cr_2O_4$, $NiFe_2O_4$, $LiNiO_2$, $Li_2NiFe_2O_4$, Inconel 718; $Cr_2O_4$, $NiFe_2O_4$, Haynes 263; $Li(Ni,Co)O_2$, $NiCr_2O_4$, $LiTiO_2$, Inconel X-750; $Cr_2O_3$, $NiFe_2O_4$,$FeNi_3$, (Al,Nb,Ti)$O_2$. Haynes 263 showed local corrosion behavior and Haynes 75, Inconel 718 and Inconel X-750 showed uniform corrosion behavior.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.100-100
• /
• 2011

Nanomaterial architecture with highly ordered, vertically oriented $TiO_2$ nanotube arrays shows a good promise for diverse technological applications. As inspired from the literature reports that Nickel modification can improve the photocatalytic activity of $TiO_2$, it was planned to coat Ni into the $TiO_2$ matrix. In this study, first $TiO_2$ nanotubes(TiNTs) were prepared by anodization (60V,3min) in HF-free aqueous electrolyte on ultrasonically cleaned polished titanium sheet substrates ($1{\times}7cm^2$). The typical thickness of the sintered TiNT ($500^{\circ}C$for10min) was ~1 micronas confirmed from the FESEM study. In the next part, as-anodized and sintered TiNT/Ti photoanodes were used to coat Ni by AC electrodeposition from aqueous 0.1M nickel sulphate solution. During AC electrodeposition, conditions such as 1V DC offset voltage, 9V amplitude (peak-to-peak) and 750 Hz frequency were fixed constant and the deposition time was varied as 0.5 min, 1 min, 2 min and 10 min. The photoelectrochemical performance of pristine and Ni modified TiNT/Ti photoanodes was measured in 1N NaOH electrolyte under 1 SUN illumination in the potential range of -1V and 1.2V versus Ag/AgCl reference electrode. The photocurrent performance of TiNT/Ti photoanode decreased upon Ni modification and the results were confirmed after repeated experiments. This suggests us that Ni modification inhibits the photoelectrochemical performance of $TiO_2$ nanotubes.

• Journal of the Korean Magnetics Society
• /
• v.16 no.3
• /
• pp.168-172
• /
• 2006

We studied the magnetic and the related electronic properties of Ni-doped rutile $TiO_{2-{\delta}}$ films (including oxygen deficiency $\delta$) prepared using a sol-gel method. A room-temperature ferromagnetism was observed in the $TiO_{2-{\delta}}$ : Ni films with the saturation magnetization ($M_S$) decreasing with increasing Ni doping and remaining constant above 6 at% Ni doping. The observed ferromagnetism below 6 at% Ni doping is interpreted as due to magnetic polaron formed by a trapped electron in oxygen vacancy and magnetic impurity ions around it. For small Ni doping, $M_S$ up to $3.7{\mu}B/Ni$ was obtained. The ferromagnetism for Ni doping above 6 at% is interpreted as due to the existence of Ni clusters that can explain the p-n conductivity transition observed by Hall effect measurements.