• 한국초전도ㆍ저온공학회논문지
• /
• 제8권1호
• /
• pp.9-14
• /
• 2006

Sample preparation plays a critical role in microstructure analysis using TEM. Although TEM specimen has been usually prepared by jet-polishing or Ar-ion beam milling technique. these methods could not be applied to YBCO CC which is composed of IBAD or RABiTS substrates, several buffet layers, and YBCO superconducting layer because of big difference in mechanical strengths between the metallic phase and oxide phases. To obtain useful cross-sectional information such as interface between the phases or second phases in YBCO CC, it is prerequisite to secure the large area of thin section in the cross-sectional direction. The superconducting layer or the buffer layers are relatively weak and fragile compared to the metallic substrate such as Ni-5wt%W RABiTS of Hastelloy-based IBAD, and preferential removal of weak ceramic phases during polishing steps makes specimen preparation almost impossible. Tripod polisher and small jig were home-made and employed to sample preparation. The polishing angle was maintained <$1^{\circ}$ throughout the polishing steps using 2 micrometers attached to the tripod plate. TEM specimens with large and thin area could be secured and used for RABiTS/IBAD substrate analyses. In some cases, additional Ar-beam ion milling with low beam current and impinging angle was used for less than 30 sec. to remove debris or polishing media attacked to the specimens.

• 미생물학회지
• /
• 제51권4호
• /
• pp.374-381
• /
• 2015

국내의 경우 항만과 연안해역 준설로 인하여 연간 수 천만톤 이상 준설토사가 발생하며 매년 증가하고 있으나, 대부분 투기장에 장기간 방치되며, 더구나 2012년부터 런던협약에 의해 해양투기가 금지되고 있어 환경친화적인 준설토처리 및 재활용기술개발이 시급하다. 준설토 재활용기술에서는 중간처리과정후 발생하는 현탁수(유기물과 중금속 함유 $10{\mu}m$ 미만 미세오염퇴적물 포함)의 처리가 필요한데 현재 이 기술은 연구되어 있지 않다. 본 연구에서는 복합유용미생물제제(BM-S-1)을 이용하여 미세해양오염퇴적물($10{\mu}m$ 이하 입자)내 오염되어 있는 유기물질, 영양염류 및 중금속을 정화하여 배출함으로써 오염퇴적물 정화처리수 방류수질 기준을 충족하고자 하였다. BM-S-1 복합미생물제제를 이용한 해양준설토의 친환경정화시스템으로서 일일 50 L 처리용량의 Lab scale 실험장치를 HRT 6.5일, BOD 용적부하 $0.2-0.6kg/m^3{\cdot}day$의 조건으로 생물반응기를 100일 이상 운전하였다. SCOD, T-N 및 T-P의 제거효과는 각각 96.1%, 92.0% 및 79.0%로 나타나 오염미세퇴적토 내의 유기물의 처리효과가 매우 양호하였다. 또한 몇 가지의 중금속(Zn, Ni 및 Cr) 처리에도 효과적이었다. 아울러 물리적으로 분리하기 어려운 $10{\mu}m$ 이하의 미세토양의 고액분리가 가능함을 확인하였다. 미생물군집구조를 분석한 결과 Flavobacteria 및 Gammaproteobacteria 강이 매우 우점하였으며, 이들에 속한 미생물종들은 해양 내의 각종유기물(다당류, 단백질 및 기타 생물중합체)을 처리하는 것으로 알려졌다. 따라서 본 실험에서 사용된 BM-S-1 미생물제제와 처리시스템은 고농도의 염분이 함유되어있는 유기물 및 중금속 오염 해양퇴적물 정화에 효율적으로 적용가능한 것으로 판단되며, 정화, 분리된 미세해양퇴적물은 목적에 맞게 재사용 가능할 것으로 사료된다.

• Korean Chemical Engineering Research
• /
• 제43권2호
• /
• pp.206-214
• /
• 2005

$TiO_2$에 담지된 불균일 촉매상에서 ppm 수준으로 존재하는 수중 유기오염물질들을 제거하기 위한 모델반응으로 액상 trichloroethylene(TCE) 분해반응을 선정하였으며, 여러 반응변수의 동시제어가 가능하도록 디자인된 연속 흐름식 고정층 반응기 내에서 incipient wetness 기법으로 제조된 여러 전이금속 산화물 촉매들의 TCE 분해활성을 조사하였다. 선택된 반응조건에서 모델반응의 내부확산저항은 없었으며, $36^{\circ}C$의 반응온도에서 촉매표면에 흡착에 의한 액상 TCE 제거된 정도는 무시할 만하였고 촉매반응에 의해서만 제거될 수 있었다. TCE 제거반응에 대한 촉매들의 활성 및 반응시간에 따른 분해효율의 의존성은 사용된 금속 산화물 및 담지체의 종류에 따라 달라지는 것으로 나타났다. 5 wt.% $CoO_x$/$TiO_2$ 촉매는 본 대상반응에 대하여 가장 우수한 활성을 갖는 것으로 나타났으며, 반응시간의 경과 정도에 따라 TCE 분해효율이 점진적으로 증가하여 안정되는 전이구간의 존재를 확인할 수 있었다. 이와 같은 촉매활성의 반응시간 의존성은 반응 초기와 일정시간 경과 후의 $TiO_2$ 표면에 존재하는 $CoO_x$의 표면구조가 상이할 뿐만 아니라 반응시간 경과와 함께 활성이 더욱 높은 Co species의 표면노출을 암시하고 있다. $NiO_x$, $CrO_x$와 같은 금속 산화물 촉매들의 반응활성은 매우 낮은 수준이었다. $TiO_2$와 MFI를 담지체로 하여 각각 incipient wetness법과 이온교환법으로 제조된 $CuO_x/TiO_2$, Cu-MFI, $FeO_x/TiO_2$ 및 Fe-MFI의 TCE 제거효율을 반응시간의 함수로 살펴본 결과, Cu 촉매들에서 관찰되는 반응시간-분해효율 거동과는 다른 현상이 $FeO_x/TiO_2$와 Fe-MFI 촉매상에서 관찰되었다. $36^{\circ}C$의 반응온도에서 전반응시간 동안에 5 wt.% $FeO_x/TiO_2$ 촉매상에서 TCE 제거반응은 일어나지 않았으나, 1.2 wt.% Fe-MFI의 경우 반응 초기에 높은 제거율을 일정시간 동안 유지하다가 서서히 감소하는 비활성화 현상이 발생하였다. 이는 동일한 활성성분이 사용된다 할지라도 그 제조방법에 따라 촉매활성이 달라질 수 있음을 보여주고 있으며, 액상반응 중에 일어나는 활성성분의 redox cycle이 중요한 역할을 할 수 있음을 암시하고 있다. 가장 우수한 $CoO_x/TiO_2$ 촉매의 TCE 분해활성에 미치는 $CoO_x$ 담지량, 반응온도 등의 영향을 조사한 결과, 최적의 $CoO_x$ 담지량이 존재하였고 반응온도가 높을수록 TCE 제거효율은 높게 나타났다. 반응 중에 $CoO_x$ leaching에 의한 $CoO_x$의 손실이 확인되었으나 TCE 전환율에 영향을 미칠 정도는 아닌 것으로 판단되었다.

• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 1998년도 가을 학술발표회 프로그램
• /
• pp.2-4
• /
• 1998

Proliferation of Nocardia amarae cells in activated sludge has often been associated with the generation of nuisance foams. Despite intense research activities in recent years to examine the causes and control of Nocardia foaming in activated sludge, the foaming continued to persist throughout the activated sludge treatment plants in United States. In addition to causing various operational problems to treatment processes, the presence of Nocardia may have secondary effects on the fate of heavy metals that are not well known. For example, for treatment plants facing more stringent metal removal requirements, potential metal removal by Nocardia cells in foaming activated sludge would be a welcome secondary effect. In contrast, with new viosolid disposal regulations in place (Code o( Federal Regulation No. 503), higher concentration of metals in biosolids from foaming activated sludge could create management problems. The goal of this research was to investigate the metal sorption property of Nocardia amarae cells grown in batch reactors and in chemostat reactors. Specific surface area and metal sorption characteristics of N. amarae cells harvested at various growth stages were compared. Three metals examined in this study were copper, cadmium and nickel. Nocardia amarae strain (SRWTP isolate) used in this study was obtained from the University of California at Berkeley. The pure culture was grown in 4L batch reactor containing mineral salt medium with sodium acetate as the sole carbon source. In order to quantify the sorption of heavy metal ions to N amarae cell surfaces, cells from the batch reactor were harvested, washed, and suspended in 30mL centrifuge tubes. Metal sorption studies were conducted at pH 7.0 and ionlc strength of 10-2M. The sorption Isotherm showed that the cells harvested from the stationary and endogenous growth phase exhibited significantly higher metal sorption capacity than the cells from the exponential phase. The sequence of preferential uptake of metals by N. amarae cells was Cu>Cd>Ni. The specific surFace area of Nocardia cells was determined by a dye adsorption method. N.amarae cells growing at ewponential phase had significantly less specific surface area than that of stationary phase, indicating that the lower metal sorption capacity of Nocardia cells growing at exponential phase may be due to the lower specific surface area. The growth conditions of Nocardia cells in continuous culture affect their cell surface properties, thereby governing the adsorption capacity of heavy metal. The comparison of dye sorption isotherms for Nocardia cells growing at various growth rates revealed that the cell surface area increased with increasing sludge age, indicating that the cell surface area is highly dependent on the steady-state growth rate. The highest specific surface area of 199m21g was obtained from N.amarae cell harvested at 0.33 day-1 of growth rate. This result suggests that growth condition not only alters the structure of Nocardia cell wall but also affects the surface area, thus yielding more binding sites of metal removal. After reaching the steady-state condition at dilution rate, metal adsorption isotherms were used to determine the equilibrium distributions of metals between aqueous and Nocardia cell surfaces. The metal sorption capacity of Nocardia biomass harvested from 0.33 day-1 of growth rate was significantly higher than that of cells harvested from 0.5- and 1-day-1 operation, indicatng that N.amarae cells with a lower growth rate have higher sorpion capacity. This result was in close agreement with the trend observed from the batch study. To evaluate the effect of Nocardia cells on the metal binding capacity of activated sludge, specific surface area and metal sorption capacity of the mixture of Nocardia pure cultures and activated sludge biomass were determined by a series of batch experiments. The higher levels of Nocardia cells in the Nocardia-activated sludge samples resulted in the higher specific surface area, explaining the higher metal sorption sites by the mixed luquor samples containing greater amounts on Nocardia cells. The effect of Nocardia cells on the metal sorption capacity of activated sludge was evaluated by spiking an activated sludge sample with various amounts of pre culture Nocardia cells. The results of the Langmuir isotherm model fitted to the metal sorption by various mixtures of Nocardia and activated sludge indicated that the mixture containing higher Nocardia levels had higher metal adsorption capacity than the mixture containing lower Nocardia levels. At Nocardia levels above 100mg/g VSS, the metal sorption capacity of activate sludge increased proportionally with the amount of Noeardia cells present in the mixed liquor, indicating that the presence of Nocardia may increase the viosorption capacity of activated sludge.

• Applied Biological Chemistry
• /
• 제42권1호
• /
• pp.73-78
• /
• 1999

Pyrite의 산화과정에서 생성되는 황산 때문에 발생하는 산성 광산 유출수는 다량의 중금속들을 함유하므로 적절한 처리 과정을 거친 후 배출되어야 한다. 산성 광산 유출수의 중화과정에서 발생하는 침전물은 주로 철과 알루미늄의 수산화물인대, 이 두 침전물은 2단계 중화과정을 거치면 분리될 수 있다. 본 연구에서는 대구시 달성군 가창면에 위치한 폐중석광산의 유출수를 이용하여 철과 알루미늄의 침전물에 의한 중금속의 제거 현상을 조사하였다. 유출수의 pH는 3.2였으며 As, Cd, Cu, Mn, Pb, Zn 등의 함량이 하천수질기준이나 폐수배출허용기준을 상회하였다. 1단계 중화에서는 $Ca(OH)_2$를 이용하여 철이 먼저 침전되도록 하였으며, 철을 100% 침전시켰을 때 납은 상당부분 침전으로 제거되었으나 대부분의 중금속은 제거되지 않았다. 2단계 중화에서는 1단계 중화 후의 상등액을 pH 7.5까지 적정하였는데, 이 때 As, Cd, Cu, Mi, Mn, Zn 등의 중금속들이 하천으로 방류가 가능한 수준으로 제거되었다. 1단계 중화에서 발생한 철 침전물은 특별한 처리 없이 폐기될 수 있을 것이며, 2단계 중화에서 생성된 침전물은 중금속을 함유하므로 특정폐기물로 취급하여 처리하여야 할 것이다. 이러한 두 단계 중화과정을 거치면 효과적인 중금속의 제거와 함께 산성 광산 유출수의 처리 후 발생하는 중금속 함유 침전물의 처리에 따른 비용의 절감이 가능할 것이다.

• Restorative Dentistry and Endodontics
• /
• 제31권5호
• /
• pp.378-389
• /
• 2006

본 연구는 도말층 제거 여부에 따른 근관 밀폐효과를 평가하기 위해 단근관 치아를 3% NaOCl 하에서 Ni-Ti file을 이용하여 crown-down법으로 근관 형성 후 최종세정제로 NaOCl을 사용한 군과 EDTA를 사용한 군, 6개월 보관한 NaOCl-6군과 EDTA-6군으로 분류하였다. Continuous wave법으로 근관 충전 시행 후 색소 침투를 시행한 다음 해부학적 근첨에서 1.5 mm (Level 1), 3.0 mm (Level 2), 4.5 mn (Level 3)에서 수평절단 하여 누출률을 측정하였다. 1. 모든 실험군에서 평균 누출률은 치근단부에서 치경부로 갈수록 감소하였다. 2. NaOCl군의 누출률이 EDTA 군보다 level 1 2, 3에서 높게 나타났으나 level 1에서만 통계학적 유의차를 보였다 (p < 0.05). 3. NaOCl-6군의 누출률이 EDTA-6 군보다 Level 1, 2, 3에서 높게 나타났으나 level 1에서만 통계학적 유의차를 보였다 (p < 0.05). 4. NaOCl-6군의 누출률이 NaOCl군에 비해 Level 1, 2, 3에서 증가하였으나 level 1에서만 통계학적 유의차를 보였다 (p < 0.05). 5. EDTA-6군의 누출률이 EDTA 군에 비해 Level 1, 2, 3에서 증가하였으나 통계학적 유의차는 없었다. 6. 주사전자현미경 관찰 결과 NaOCl 군과 NaOCl-6 군은 도말층이 제거되지 않아 상아세관내로 sealer 및 근관충전재가 침투하지 못한 반면, EDTA 군과 EDTA-6 군에서는 도말층이 제거되고 상아세관내로의 sealer와 근관충전재의 침투가 관찰되었다. 이상의 연구결과 EDTA를 이용하여 도말층을 제거한 경우 근관충전 즉시와 6개월 후 치근단 1/3 부위의 근단부 미세누출을 감소시킬 수 있을 것으로 사료된다.