• 한국환경과학회지
• /
• 제4권5호
• /
• pp.103-103
• /
• 1995

In the Chinhae Bay, Korea, sedimentation rates and sedimentary record of anthropogenic metal loads were determined by $^{210}Pb$ dating and heavy metal analysis of four sediment cores . The sedimentation rates varied from 0.16g/$cm^2$/yr(3.1mm/yr) at Sta. Ct, located within narrow waterway to 0.24g/$cm^2$/yr(4.8mm/yr) at Sta. Cl, located in Haengam Bay. Maximum contents of Mn, Zn, Cu and Cr were observed at Sta. C2 located near the mouth of Masan Bay, while minimum contents were observed at Sta. CB. Mn/Fe ratios at Sta. C2 and Sta. C4 showed gradually increasing and decreasing downward, respectively, in the upper layer of sediment cores. This suggests that Mn may be diagenetically redistributed in highly reduced environment. At Sta. C2, the concentrations of Zn and Cu began to increase from 1920s by anthropogenic input and have been remarkablely increasing since mid 1960s. At Sta. C3, located near Sungpo, anthropogenic input of these two elements has also slightly increased after 1970s. However, pollution of these two elements was not significant in Haengam Bay(Sta. Cl) and Chiljun watenway(Sta. C4). The pollution of Co, Ni and Cr was not remarkable in all core samples except surface sediment of Sta. C2. The total input of anthropogenic Zn and Cu since 1920s was estimated to be 28∼792 ㎍/cm2 and 0∼168㎍/cm2, respectively. Sta. C2 showed remarkablely higher values relative to other stations: anthropogenic loads of Zn and Cu constituted 27% and 29% of the total sedimentary inventories at the present day, respectively. Fe, Ni, Cr and Co contents showed good correlation(r>0.8) with each other. Anthropogenic Zn and Cu also showed a very good positive correlation(>0.9). However, correlation between these two group of element was quite scattered, indicating different sources and geochemical behaviors.

• 한국전기전자재료학회논문지
• /
• 제21권7호
• /
• pp.645-651
• /
• 2008

To reduce noise in high frequency and distortion of signal, the composition of $(Ca_{0.7}Sr_{0.3})(Zr_{0.97}Ti_{0.03})O_3$ and $(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ was developed. The composition was not solid solution, but mixtures of various phases composed of Ca, Sr, Zr, Ti and Ba oxides. The dielectric constant increased, the quality factor and the insulation resistance decreased with $(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ content. The composition of $0.4(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ satisfied the electric characteristics and the temperature coefficient of dielectric constant (TCC). In addition, the glass frit and $MnO_2$ also affected the electric characteristics. From the result of the best fit simulation, $MnO_2$ 0.3 mol%, the glass frit 0.6 wt% showed the insulation resistance $906{\Omega}{\cdot}F$, the quality factor 821, and the dielectric constant 92. With the selected composition, MLCC capacitors sized $4.5{\times}3.2{\times}2.5mm$ were manufactured with 105 layered of the dielectric thickness $16{\mu}m$ using Ni inner electrode, They represented the capacitance $98{\sim}102$ nF, the quality factor 1,200 and the insulation resistance $1,500{\Omega}{\cdot}F$. Also, they had high break-down voltage with $107{\sim}115V/{\mu}m$, and satisfied the SL TCC characteristics.

• 한국전기전자재료학회논문지
• /
• 제26권1호
• /
• pp.22-26
• /
• 2013

PTCR ceramics of $(Ba_{0.998}Sm_{0.002})TiO_3+0.001MnCO_3+xSiO_2$ (x=1, 2, 3, 4, 5, 6 mol%) were fabricated by solid state method. Disk samples of diameter 5 mm and thickness about 1mm were sintered at $1,290^{\circ}C$ for 2 h in reduced atmosphere of $5%H_2-95%N_2$ followed by re-oxidation at $600^{\circ}C$ for 30 min. in $20%O_2-80%N_2$.and their microstructures and electrical properties were investigated with SEM and Multimeter. The color of sintered samples was strongly dependent on $SiO_2$ content showing that the color of samples with $SiO_2$ of 1~2 mol% was gray but that of samples with $SiO_2$ of 4~6 mol% was changed from gray to blue, which seems to be related with the reduction of samples due to the oxygen vacancies created during the sintering in reduced atmosphere. $SiO_2$ content had a great influence on the microstructure and the electrical properties. With increasing $SiO_2$ content, the grain size of samples increased and the resistivity as well as the resistivity jump ($R_{285}/R_{min}$) decreased, which is considered to be attributed to the resistivity change at grain interior and grain boundary due to the fast mass transfer through $SiO_2$ liquide phase during the sintering. Samples with 2 mol% $SiO_2$ has the resistivity of $202{\Omega}cm$ and the resistivity jump of 3.28. It is expected that $SiO_2$ doped $BaTiO_3$ based PTC ceramics can be used for multilayered PTC thermistor due to the resistance to the sintering in reduced atmosphere.

• 한국균학회지
• /
• 제25권4호통권83호
• /
• pp.369-376
• /
• 1997

본 실험은 노루궁뎅이버섯(Hericium erinaceus isolate KU-1)의 균사생장에 관한 영양원 실험으로 대량의 균사체 수확을 위한 배양기 조성을 밝히기 위한 기초를 확립하고자 실시하였다. 최적온도는 $25^{\circ}C$이며 pH4에서 160.5 mg으로 가장 건물중이 높았고 탄소원 중 glucose, sucrose, galactose, mannose 순으로 균사생장 및 균사밀도가 우수하였다. 무기태질소원으로는 ammonium acetate 30 mM에서 균사생장이 가장 양호하였다. 아미노산 중 arginine 15 mM에서 우수하였다. C/N율 200에서 35.9 mm로 균사생장의 최대치를 보였다. 상술한 실험의 결과를 토대로 Table 1과 같은 새로운 합성배지를 조제할 수 있었고, 이를 Ko배지라 명명하였다. 이 Ko배지와 기존배지간의 한천배지상에서 균사생장 비교한 결과, Ko배지에 가장 우수한 균사생장과 균사밀도를 나타냈다. Ko배지의 조성은 glucose 18.02g, arginine 3.613g, ammonium acetate 2.313g, $CaCl_2\;0.33g$, $KH_2-PO_4\;8.5g$, $MgSO_4{\cdot}7H_2O\;2.0g$, $FeSO_4{\cdot}7H_2O\;0.02g$, $ZnSO_4{cdot}7H_2O\;0.02g$, $MnSO_4{\cdot}7H_2O\;0.02g$, water 1 liter이다.

• 대한전기학회논문지
• /
• 제41권4호
• /
• pp.379-384
• /
• 1992

The Fe-base amorphous ribbons with 15mm width and about 20x10S0-6Tm thickness, (FeS179-xTCrS1xT)BS116TSiS15T and (FeS181-xTMnS1xT) BS112TSiS17T (x:0-6), were prepared melt spinner. The thickness of the ribbons followed by PFC (Planar Flow Casting). The initial permeability and total core losses were measured as a function of additive elements (Cr, Mn) and annealing conditions in high frequency for the purpose of using these materials as a core of magnetic amplifier and switched mode power supplies. The initial permeabilities were enhanced and core losses were decreased by non-magnetic field annealing in proper conditions. The lowest core loss in 0.2T/10kHz was measured at 3% Cr addition amorphous ribbon, and the loss was 5.6W/kg. The permeability of the ribbon at 10kHz was about 9000.

• 한국습지학회지
• /
• 제16권2호
• /
• pp.261-268
• /
• 2014

본 연구의 목적은 직렬연결 2단 수직 및 수평 모래 갈대 인공습지에 생활하수를 간헐적으로 주입하였을 때 각 수질항목별 처리효율을 평가하는 것이다. 하수는 수리학적 부하량 $314L/m^2{\cdot}day$(수직 흐름 인공습지 기준)를 하루 4(10분 동안 주입후 5시간 50분 동안 중단)회 균등하게 간헐적으로 주입하였다. 평가 결과 pH는 유입수(7.27)보다 수직 흐름 인공습지 유출수(5.81)에서 감소하였다가 수평 흐름 인공습지 유출수(6.40)에서 다시 증가하였다. DO의 농도는 유입수에 비하여 유출수에서 높았으며 겨울로 갈수록 증가하였다. 수직 흐름 인공습지의 산소 전달율 (oxygen transfer rate: OTR)은 $58.72gO_2/m^2{\cdot}day$ 그리고 수평 흐름 인공습지의 OTR은 $7.72gO_2/m^2{\cdot}day$이었다. 각 항목별 평균 처리효율은 SS 94.80%, BOD 90.77%, $COD_{Cr}$ 85.87%, $COD_{Mn}$ 87.72%, T-N 64.74%, $NH_4{^+}$-N 86.44%, T-P 87.70%이었다. 유출수중 T-N의 반 정도는 $NO_3{^-}$-N(7.21 mg/L)이었으며 $NO_2{^-}$-N은 평균 0.64 mg/L이었다.

• Journal of Electrical Engineering and Technology
• /
• 제13권4호
• /
• pp.1638-1643
• /
• 2018

Multi-layer ceramic capacitors as decoupling capacitor were fabricated by dielectric composition with a high dielectric constant. The fabricated decoupling capacitors were embedded in the PCB of the 10G RF transceiver module and evaluated for the characteristics of electrical noise by the level of AC input voltage. In order to further improve the electrical properties of the $BaTiO_3$ based composite, glass frit, MgO, $Y_2O_3$, $Mn_3O$, $V_2O_5$, $BaCO_3$, $SiO_2$, and $Al_2O_3$ were used as additives. The electrical properties of the composites were determined by various amounts of additives and optimum sintering temperature. As a result of the optimized composite, it was possible to obtain a density of $5.77g/cm^3$, a dielectric constant of 1994, and an insulation resistance of $2.91{\times}10^{12}{\Omega}$ at an additive content of 5wt% and a sintering temperature of $1250^{\circ}C$. After forming a $2.5{\mu}m$ green sheet using the doctor blade method, a total of 77 layers were laminated and sintered at $1180^{\circ}C$. A decoupling capacitor with a size of $0.6mm(W){\times}0.3mm(L){\times}0.3mm(T)$ (width, length and thickness, respectively) and a capacitance of 100 nF was embedded using a PCB process for the 10G RF Transceiver modules. In the range of AC input voltage 400mmV @ 500kHz to 2200mV @ 900kHz, the embedded 10G RF Transceiver modules evaluated that it has better electrical performance than the non-embedded modules.

• 한국환경농학회지
• /
• 제27권1호
• /
• pp.27-34
• /
• 2008

농어촌 등에서 소규모로 발생하는 하수를 자연정화공법 의한 인공습지에서 효과적으로 처리하기 위하여 소형 하수처리장치를 호기성조 및 혐기성조로 구분하여 시공한 다음, 최적 하수 부하량을 조사하기 위해 하수 부하량별 오염물질의 처리효율을 조사한 결과 호기-혐기 조합형 소형 하수처리장에서 전반적으로 하수 부하량이 증가함에 따라 오염물질의 처리효율이 점점 감소하는 경향으로 특히 하수부하량 300 $Lm^{-2}day^{-1}$ 이상에서 수처리효율의 감소폭이 약간 컸다. 따라서 본 소형 하수처리장에서 BOD, $COD_{Mn}$, 탁도, T-N 및 T-P를 안정적으로 처리하기 위한 최적 부하량은 300 $Lm^{-2}day^{-1}$ 이었고, 이 때의 방류수 중 BOD, $COD_{Mn}$, 탁도, T-N 및 T-P의 처리효율은 각각 99, 94, 99, 49 및 89%로 현행 방류수 수질기준을 만족하면서 안정적으로 처리되었다. 하지만 본 소형 하수처리장에서 방류수 중의 T-N 및 T-P 함량은 각각 $28.5{\sim}29.4$ 및 $0.9{\sim}2.1mgL^{-1}$ 정도로서 앞으로 질소와 인의 방류수 수질기준이 각각 20 및 2 $mgL^{-1}$로 강화됨에 따라 보다 안정적인 수처리를 위해서는 T-N 및 T-P 처리효율을 향상시켜야 할 것으로 판단된다. 이에 최적 하수 부하량하에서 질소와 인의 강화될 방류수 수질기준(질소 20 $mgL^{-1}$ 및 인 2 $mgL^{-1}$)을 만족시키면서 안정적인 하수처리를 위한 최적의 수처리 공정개선 방안을 조사하였다. 호기-혐기 조합형 소형 하수처리장에서 수처리 공정개선 중 질소 및 인의 처리효율 향상이 가능한 방안은 혐기성조의 깊이 및 여재 입경 변경과 여재에 굴패각을 혼합한 방법이었다. 혐기성조의 깊이 및 여재 입경 변경 조건 중 혐기성조 1.5 m 깊이에서 여재 A(유효입경 1.50 mm)를 사용한 경우 T-N 및 T-P의 처리효율을 각각 10 및 3% 향상시켰고, 여재에 굴패각 혼합한 경우 T-N 및 T-P의 처리효율을 각각 14 및 7% 향상시켰다. 또한 동일한 조의 체적하에서 혐기성조의 깊이를1.5 m로 깊게한 것은 혐기성조 깊이 1 m에 비해 부지면적을 약 33% 정도 감소시킬 수 있을 것으로 판단되며, 또한 굴패각을 사용한 것은 폐기물의 재활용면에서도 매우 효과적인 방안으로 사용될 수 있을 것으로 판단된다.

• Bulletin of the Korean Chemical Society
• /
• 제20권9호
• /
• pp.1035-1039
• /
• 1999

Manganese-activated zincgallate (Zn1-xMnxGa2O4) phosphor as a green phosphor was readily prepared by coprecipitation in aqueous basic solution of metal salts. The obtained product converted to amorphous zincgallate even at 300℃, followed by crystallization at 1000 ℃. The pyrolyzed phosphor showed fine particle, then reduction treatment at 900 ℃ changed into homogeneous shape with slight grain growth(particle size less than 0.5 mm). The photoluminescence characteristics of the zincgallates have been investigated as a function of dopant concentrations, reducing atmospheres and temperatures. Under UV excitation the phosphors displayed the highest green emission efficiency at 504 nm when the specimen oxidized at 1000 ℃ was reduced at 900 ℃ in a mild hydrogen atmosphere (97% N2, 3% H2) with a flow rate of 100 ml/min.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 추계학술대회 논문집 Vol.16
• /
• pp.348-351
• /
• 2003

산소 과전압이 낮은 $MnO_2$를 촉매로 사용하여 반도체 산화물계의 산소선택성 전극을 제조하고 산화물 coating층의 미세구조와 전기화학적 특성을 분석하였다. Ti 기판에 열분해 법을 이용하여 $MnO_2$ 피막을 형성하였고, 또한 PVDF : $MnO_2$의 함량비를 1 : 1에서 1 : 40까지 정량적으로 변화시키고 DMF의 함량을 각각의 고정된 PVDF : $MnO_2$의 함량비에서 변화시켜 Pb전극에 1.5 mm/sec의 속도로 5회 dipping하여 $MnO_2$ 피막층을 형성 하였다. $450^{\circ}C$에서 1시간 열분해하여 약 $1\;{\mu}m$의 $MnO_2$ 피막층이 형성되었으나 Ti 기판과의 접착력이 약하여 피막자체에 대한 전기화학적 특성을 관찰할 수 없었다. PVDF : DMF = 4 : 96인 경우 pb 전극의 피막층이 얇기 때문에 박리현상이 일어났으며 이는 산화물 용제의 낮은 점도 때문인 것으로 판단된다. 또한 PVDF : DMF = 10 : 90의 경우는 5회 dipping 하여 약 $150\;{\mu}m$의 피막층을 형성하였다. PVDF : $MnO_2$의 함량비가 1:1에서 1:6 까지는 DMF의 함량에 무관하게 전극 특성이 나타나지 않았지만 $MnO_2$의 양이 상대적으로 증가하면 cycle이 증가하더라도 거의 일정한 전류 값을 갖고 $MnO_2$와 PVDF의 비가 20:1 이상의 조성에서는 균일한 CV 특성을 나타냈다. 이는 $MnO_2$가 효과적으로 촉매 작용을 한 것으로 판단되며 anodic polarization에 의한 산소 발생 과전압도 약 1.4V 정도로 감소되었다.동등한 MSIL 코드를 생성하도록 시스템을 컴파일러 기법을 이용하여 모듈별로 구성하였다.적용하였다.n rate compared with conventional face recognition algorithms. 아니라 실내에서도 발생하고 있었다. 정량한 8개 화합물 각각과 총 휘발성 유기화합물의 스피어만 상관계수는 벤젠을 제외하고는 모두 유의하였다. 이중 톨루엔과 크실렌은 총 휘발성 유기화합물과 좋은 상관성 (톨루엔 0.76, 크실렌, 0.87)을 나타내었다. 이 연구는 톨루엔과 크실렌이 총 휘발성 유기화합물의 좋은 지표를 사용될 있고, 톨루엔, 에틸벤젠, 크실렌 등 많은 휘발성 유기화합물의 발생원은 실외뿐 아니라 실내에도 있음을 나타내고 있다.>10)의 $[^{18}F]F_2$를 얻었다. 결론: $^{18}O(p,n)^{18}F$ 핵반응을 이용하여 친전자성 방사성동위원소 $[^{18}F]F_2$를 생산하였다. 표적 챔버는 알루미늄으로 제작하였으며 본 연구에서 연구된 $[^{18}F]F_2$가스는 친핵성 치환반응으로 방사성동위원소를 도입하기 어려운 다양한 방사성의 약품개발에 유용하게 이용될 수 있을 것이다.었으나 움직임 보정 후 영상을 이용하여 비교한 경우, 결합능 변화가 선조체 영역에서 국한되어 나타나며 그 유의성이 움직임 보정 전에 비하여 낮음을 알 수 있었다. 결론: 뇌활성화 과제 수행시에 동반되는 피험자의 머리 움직임에 의하여 도파민 유리가 과대평가되었으며 이는 이 연구에서 제안한 영상정합을 이용한 움직임 보정기법에 의해서 개선되었다. 답이 없는 문제, 문제 만들기, 일반화가 가능한 문제 등으로 보고, 수학적 창의성 중 특히 확산적 사고에 초점을 맞추어 개방형 문제가 확산적 사고의 요소인 유창성, 독창성, 유연성 등에 각각 어떤 영향을 미치는지 20주의 프로그램을 개발, 진행하여 그 효과를 검증하고자