• 한국세라믹학회지
• /
• 제33권3호
• /
• pp.307-312
• /
• 1996

In following addition of 0.3, -0.6, 0.8, 1.0 and 5 weight percent MgSiF66H2O studies have been made of the setting and hardening characteristics of ordinary portland cement. MgSiF66H2O retarded the setting time of ordinary portland cement and extended the induction pariod of the hydration. In ordinary portland cement the setting characteristics were drastically altered especially at high MgSiF66H2O contents. Evidence was also obtained by the formation of a KSiF6 which was very fine particle. The results wee as follows. 1. Slump was slightly decreased when MgSiF66H2O added. 2. Setting time was retarded depending on the amount of retarding agent 2 to 8 hours 3. Compressive strength was almost same or some increased in comparision with opc. 4. When MgSiF66H2O was added to cement paste K2SiF6 were formed It was fine-sized distributed uniformly in cement grain and caused retardation of cement setting.

• 한국결정성장학회지
• /
• 제19권4호
• /
• pp.190-195
• /
• 2009

스컬용융법에 의해 Na사규소운모를 합성하였다. $Mg_3(OH)_2Si_4O_{10}:Na_2SiF_6:SiO_2=8.3:24.8:66.9$ mol% 비율로 혼합한 출발원료를 ${\phi}13{\times}H14cm$의 냉각도가니에 채우고 2.84MHz 출력주파수의 고주파발진기를 이용하여 가열하였다. 원료는 융액상태에서 1시간 유지하였으며 도가니 내에서 냉각시켰다. 운모의 비저항은 추정하였으며, 원주모양과 판상으로 합성할 수 있었다.

• 한국표면공학회지
• /
• 제53권2호
• /
• pp.59-66
• /
• 2020

Effects of Na₂SiO₃ concentration added into 0.1 M NaOH + 0.05 M NaF solution on the formation behavior and properties of PEO films on AZ91 Mg alloy were investigated under 1200 Hz of alternating current (AC) by voltage-time curves, in-situ observation of arc generation behavior and measurements of film thickness, surface roughness and micro vickers hardness. In the absence of Na₂SiO₃ in the 0.1 M NaOH + 0.05 M NaF solution, about 4 ㎛ thick PEO film was formed within 1 min and then PEO film did not grow but white spots were formed by local burning. Addition of Na₂SiO₃ up to 0.2 M caused more increased formation voltage and growth of PEO film with uniform generation of arcs. Addition of Na₂SiO₃ from 0.2 M to 0.4 M showed nearly the same voltage-time behavior and uniform arc generation. Addition of Na₂SiO₃ more than 0.5 M resulted in a decrease of formation voltage and non-uniform arc generation due to local burning. PEO film growth rate increased with increasing added Na₂SiO₃ concentration but maximum PEO film thickness was limited by local burning if added Na₂SiO₃ concentration is higher than 0.5 M. Surface roughness of PEO film increased with increasing added Na₂SiO₃ concentration and appeared to be proportional to the PEO film thickness. PEO film hardness increased with increasing added Na₂SiO₃ concentration and reached a steady-state value of about 930 H_V at more than 0.5 M of added Na₂SiO₃ concentration.