• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.67-67
• /
• 2008

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.1-4
• /
• 2007

The most common technique to fabricate $MgB_2$ superconducting wire is by powder-in-tube (PIT) technique. Therefore, the starting powder for the processing of $MgB_2$ superconductors is an important factor influencing the superconducting properties and performance of the conductors. In this study, the influence of magnesium precursor powders and annealing temperatures on the transition temperatures ($T_c$) and critical current densities ($J_c$) of $MgB_2/Fe$ wires was investigated. All the $MgB_2/Fe$ wires were fabricated by in situ PIT process. It was found that higher $J_c$ was obtained for $MgB_2$ wires with smaller particle size of magnesium precursor powders. The $J_c$ also increases with decreasing annealing temperatures.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.62-67
• /
• 2007

The effects of the heat-treatment temperature on the carbon (C) substitution amount, full width at half maximum (FWHM) value, critical temperature ($T_c$), critical current density ($J_c$) have been investigated for 10 wt % malic acid ($C_4H_6O_5$)-doped $MgB_2/Fe$ wires. All the samples were fabricated by the in-situ powder-in-tube (PIT) method and heat-treated within a temperature range of $650^{\circ}C$ to $1000^{\circ}C$. As the heat-treatment temperature increased, it seemed that the lattice distortion was increased by a more active C substitution into the boron sites from the malic acid addition. These increased electron scattering defects seemed to enhance the $J_c-H$ properties in spite of an improvement in the crystallinity, such as a decrease of the FWHM value and an increase of the $T_c$. Compared to the un-doped wire heat-treated at $650^{\circ}C$ for 30 min, the $J_c$ was enhanced by the C doping in a high-field regime. The wire heat-treated at $900^{\circ}C$ resulted in a higher magnetic $J_c$ of approximately $10^4\;A/cm^2$ at 5 K and 8 T.

• Korean Journal of Materials Research
• /
• v.27 no.11
• /
• pp.597-602
• /
• 2017

In this study, an Al-0.7wt%Fe-0.2wt%Mg-0.2wt%Cu-0.02wt%B alloy was designed to fabricate an aluminum alloy for electrical wire having both high strength and high conductivity. The designed Al alloy was processed by casting, extrusion and drawing processes. Especially, the drawing process was done by severe deformation of a rod with an initial diameter of 12 mm into a wire of 2 mm diameter; process was equivalent to an effective strain of 3.58, and the total reduction in area was 97 %. The drawn Al alloy wire was then annealed at various temperatures of 200 to $400^{\circ}C$ for 30 minutes. The mechanical properties, microstructural changes and electrical properties of the annealed specimens were investigated. As the annealing temperature increased, the tensile strength decreased and the elongation increased. Recovery or/and recrystallization occurred as annealing temperature increased, and complete recrystallization occurred at annealing temperatures over $300^{\circ}C$. Electric conductivity increased with increasing temperature up to $250^{\circ}C$, but no significant change was observed above $300^{\circ}C$. It is concluded that, from the viewpoint of the mechanical and electrical properties, the specimen annealed at $350^{\circ}C$ is the most suitable for the wire drawn Al alloy electrical wire.

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.67-67
• /
• 2007

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.79-79
• /
• 2008

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.79-86
• /
• 2009

We successfully fabricated C-doped ex-situ $MgB_2$ wires using two different methods such as mechanical alloying(MA) and combined process(CP) of in-situ and ex-situ. In the MA, the precursor powder was prepared with a mixture of $MgB_2$ and 1 at% C powders by planetary ball milling for 0-100 h. In the CP, on the other hand, C-doped $MgB_2$ powder was prepared with Mg, B, and C powders by in-situ process via compaction, sintering, and crushing. The powders prepared by two methods were loaded into Fe tube and then the assemblages were drawn by a conventional powder-in-tube technique. The MA treatment of C-added $MgB_2$ decreased the particles/grains size and resulted in C-doping into $MgB_2$ after sintering, improving the critical current density($J_c$) in high external magnetic field. For the C-doped $MgB_2$ wire by MA for 25 h, the $J_c$ was $4.1{\times}10^3A/cm^2$ at 5 K and 6.4 T, which was 5.9 times higher than that of pure and untreated $MgB_2$ wire. The CP also provided C-doping into $MgB_2$ and improved the $J_c$ in high magnetic field; the C-doped $MgB_2$ wire fabricated by CP exhibited a $J_c$ being 2.3 times higher than that of the ex-situ wire used commercial $MgB_2$ powder at 5 K and 6.0 T($2.7{\times}10^3A/cm^2\;vs.\;1.2{\times}10^3A/cm^2$).