• Journal of Korea Foundry Society
• /
• v.20 no.5
• /
• pp.323-329
• /
• 2000

The HSS consists of hard carbide and matrix of martensite, and so its characteristics of wear resistance, fracture resistance, and surface roughness are good. This study was undertaken to investigate the influence of Nb and V and manufacturing conditions on microstructural behaviors and characteristics in the HSS cylindrical specimens(90 $mm^{O.D.}$ ${\times}$ 60 $mm^{I.D.}$ ${\times}$ 50 $mm^H$) manufactured using VCC(Vertical Centrifugal Casting). In the specimen of Fe-2C-6Cr-1.5W-3Mo-4V alloy, the amount of MC carbide was increased and $M_7C_3$ carbide was decreased with the increase of V and Nb contents. The primary VC carbide was formed and followed by the rod-type eutectic MC carbide was formed in the cell boundary in 9%V added specimen. MC carbide was increased, and $M_7C_3$ carbide was decreased with the addition of Nb content. In the specimen containing more than 3%Nb, primary NbC carbide was formed within the cell of matrix. With increase in rpm, cell and carbides became fine, and amount of carbide $M_7C_3$ was decreased due to increase in cooling rate.

• Journal of Power System Engineering
• /
• v.5 no.3
• /
• pp.88-94
• /
• 2001

Stellite 12 alloy-powders were overlaid on 410 stainless steel valve seat using plasma transferred arc(PTA) process. Variation of the microstructure, hardness, wear and corrosion of overlaid deposit with current change was investigated. The deposit showed hypoeutectic microstructure, which was consisted of primary cobalt dendrite and networked $M_7C_3$ type eutectic carbides. As current increased, the amount of eutectic carbide decreased and its dendritic secondary arm spacing increased. Hardness of the deposit was decreased with increase of current. Stress relief heat treatment at $600^{\circ}C$ for two hours resulted in slight increase of hardness in the deposit and showed uniform hardness distribution in base metal without any hardened layer in HAZ. Specific wear decreased with increase of sliding distance. The deposit of high hardness with a lot of eutectic carbide showed relatively low specific wear. Initial corrosion current density of the deposit in 0.1N sulfuric acid was lower than those of 410 stainless steel, and showed a little variation with PTA current.

• Transactions of the Korean hydrogen and new energy society
• /
• v.30 no.1
• /
• pp.1-7
• /
• 2019

The preparation and catalytic activities of various transition metal carbide crystallites (VC, MoC, WC) were examined in this study. In particular, the effect of different kinds of transition metal crystallites were scrutinized on the ammonia decomposition reaction. The experimental results showed that BET surface areas ranged from $8.3m^2/g$ to $36.3m^2/g$ and oxygen uptake values varied from $9.1{\mu}mol/g$ to $25.4{\mu}mol/g$. Amongst prepared transition metal carbide crystallites, tungsten compounds (WC) were observed to be most active for ammonia decomposition reaction. The main reason for these results were considered to be related to the extent of electronegativity between these materials. Most of transition metal carbide crystallites were exceeded by Pt/C crystallite. However, the steady state reactivities for some of transition metal carbide crystallites (WC) were comparable to or even higher than that determined for the Pt/C crystallite.

• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.349-353
• /
• 2016

We prepared a number of reaction-bonded silicon carbides (RBSCs) made from various mixing ratios of raw SiC particles, and investigated their microstructure and etch characteristics by Reactive Ion Etch (RIE). Increasing the amount of $9.5{\mu}m$-SiC particles results in a microstructure with relatively coarser Si regions. On the other hand, increasing that of $2.6{\mu}m$-SiC particles produces much finer Si regions. The addition of more than 50 wt% of $2.6{\mu}m$-SiC particles, however, causes the microstructure to become partially coarse. We also evaluated their etching behaviors in terms of surface roughness (Ra), density and weight changes, and microstructure development by employing Confocal Laser Scanning Microscope (CLSM) and Scanning Electron Microscope (SEM) techniques. During the etching process of the prepared samples, we confirmed that the residual Si region was rapidly removed and formed pits isolating SiC particles as islands. This leads to more intensified ion field on the SiC islands, and causes physical corrosion on them. Increased addition of $2.6{\mu}m$-SiC particles produces finer residual Si region, and thus decreases the surface roughness (Ra.) as well as causing weight loss after etching process by following the above etching mechanism.

• Korean Journal of Materials Research
• /
• v.21 no.11
• /
• pp.592-595
• /
• 2011

It is well known that modified 9Cr-1Mo steel has a low thermal expansion and high thermal conductivity with excellent high temperature properties compared to austenitic stainless steel. For these advantages, the steel is very popular for the boiler tube of thermal power plants. Normalizing is commonly utilized to obtain martensite in this steel, which shows an unusual toughness for martensite. However, some accidents related to this steel have been reported recently, opening the necessity for further study. As a particular behavior of the steel, an abrupt drop of the impact value has been identified upon tempering at 750$^{\circ}C$ for about 1 hour. It is well known that $Fe_3C$ forms during autotempering and turns to $Cr_2C$ at an early stage and then transforms to $Cr_{23}C_6$. In this study, the cause of the abrupt drop of the impact value was investigated with an impact test, microstructural observation, nanodiffraction and phase analyses using instruments such as optical and transmission electron microscopes (TEM) with an extraction carbon replica of the carbides. The analyses revealed that the $M_2C$ that formed when retained for about 1 hour at 750$^{\circ}C$ causes a drastic decrease in the mechanical properties. The sharp drop in mechanical properties, however, disappeared as the $M_2C$ transformed into $M_{23}C_6$ with longer retention.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.5
• /
• pp.282-289
• /
• 2009

The effects of the high temperature gas nitriding (HTGN), tempering and subzero treatment of STD11 steel have been investigated. HTGN treatment was carried out at $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$ for 1 hr. in an atmosphere of $1\;kg/cm^2$ nitrogen gas. Tempering and double-tempering were performed at $550^{\circ}C$ for 1 hr. The surface layer of HTGN-treated steel appeared the precipitates of $M_2N$, $M_7C_3$ and $M_{23}C_6$ in the matrix of austenite. However, the interior region exhibited martensite with the precipitation of carbides. The nitrogen content of the surface layer appeared ~1.35 wt.%, ~0.83 wt.% and ~0.56 wt.% at the HTGN treatment temperature of $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$, respectively. The surface hardness of double-tempered and subzero-treated steel measured the maximum value of 828 Hv, 960 Hv, 750 HV after HTGN treatment at the $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$, respectively. These hardness value increased above 230~420 Hv compared with the HTGN-treated steel due to the decrease in retained austenite and existence of fine precipitates.

• Journal of Powder Materials
• /
• v.12 no.2 s.49
• /
• pp.112-116
• /
• 2005

In the present study, the focus is on the analysis of carbothermal reduction of oxide powder prepared from waste WC/Co hardmetal by solid carbon under a stream of argon for the recycling of the WC/Co hard-metal. The oxide powder was prepared by the combination of the oxidation and crushing processes using the waste $WC-8 wt.\%Co$ hardmetal as the raw material. This oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and gases discharge of the mixture during carbothermal reduction was analysed using XRD and gas analyzer. The oxide powder prepared from waste $WC-8wt.\%Co$ hardmetal has a mixture of $WO_{3} and CoWO_{4}$. This oxide powder reduced at about $850^{\circ}C$, formed tungsten carbides at about $950^{\circ}C$, and then fully transformed to a mixed state of tungsten carbide (WC) and cobalt at about $1100^{\circ}C$ by solid carbon under a stream of argon. The WC/Co composite powder synthesized at $1000^{\circ}C$ for 6 hours from oxide powder of waste $WC-8wt.\%Co$ hardmetal has an average particle size of $0.3 {\mu}m$.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.874-879
• /
• 1995

Magnetic properties of FeMoN, FeMoTaN, FeTaN and FeTaC films deposited by DC magnetron reactive sputter were investigated, and correlated with their microstructure. FeMoN films were not showen the soft magnetic prop¬erties, because of generated $Fe_{2}Mo$, $Fe_{3-2}N$ and $Fe_{4}N$ phases. Ta added films, however, effectivly retarded the $\alpha$-Fe grain growth and suppressed the generation of Fe nitrides or carbides during heat treatement. The soft magnetic properties of $B_{s}:15\;kG,\;H_{e}:0.25\;Oe,\;\mu':4000(at\;5\;MHz),\;and\;B_s:14.5\;kG,\;He:0.25\;Oe,\;\mu':2700(5MHz)$ were observed in $Fe_{78.8} Ta_{8.5}N_{12.7}\;and\;Fe{75.6}Ta_{8.1}C_{16.3}$ films, respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.6
• /
• pp.335-340
• /
• 2003

To improve properties of wear resistance and anti-corrosion of the trivalent chromium platings, oxinitrocarbunsing and steam oxidation were conducted. Armophous trivalent Cr platings could be transformed to chromium carbides of high hardness, that showed low friction and wear rate. Even though micro-cracks were within as platings, superior anti-corrosion property was obtained by these treatments due to healing of cracks at the interface between the trivalent chromium platings and substrate.

• Journal of the korean Society of Automotive Engineers
• /
• v.10 no.1
• /
• pp.33-41
• /
• 1988

A turning (facing) test on Glass Fiber Reinforced Plastics was performed with several tool materials, e.g., cemented carbides, cermet and ceramic, and the wear patterns and wear rate were analyzed to clarify the relation between physical(mechanical) properties and flank wear of cutting tool. The main results are obtained as follows: (1) When cutting speed is increased, the flank wear in every tool material grows the abnormal wear in the shape of triangle at a certain speed, i.e., a critical speed. (2) When cutting speed is increased, the wear rate in experimental tool material starts to increase remarkably at a critical speed. (3) The thermal conductivity among the properties of the tool material and the thermal crack coefficient of it are almost in proportion to the critical speed. (4) The order of performance in tool materials for cutting GFRP is K 10, M10, P20, TiC, CB.