• Journal of the Korean Ceramic Society
• /
• v.30 no.7
• /
• pp.535-542
• /
• 1993

It was investigated in this study that a preparation method, activation energy, surface area, pore volume, pore size distribution and DTA analysis of the dry gel in process of producing monolithic porous gel in Li2O-Al2O3-TiO2-SiO2 system by the sol-gel technique using metal alkoxides. Activation energy for gellation according to the variation of water concentration and the kind of catalysts ranged from 10 to 20kcal/mole. Monolithic dry gels were prepared after drying at 9$0^{\circ}C$ when the amount of water for gellation was 4~8 times more than the stoichiometric amount, that was necessary for the full hydrolysis of the mixed metal alkoxide. The specific surface area, the pore volume, the average pore radius of the dried gel at 18$0^{\circ}C$ according to the various kinds of catalyst were about 348~734$m^2$/g, 0.35~0.70ml/g and 10~35$\AA$, respectively. It showed that the dry gels were porous body. As a result ofthe analysis of DTA, it was confirmed that the exothermaic peaks at 715$^{\circ}C$ and 77$0^{\circ}C$ was clue to the crystallization of dried gel.

• Journal of the Korean Ceramic Society
• /
• v.13 no.1
• /
• pp.30-34
• /
• 1976

In general the chemical composition of glass ceramics in Li2O-Al2O3-SiO2 system is similar to the composition of $\beta$-spodumene (Li2O-Al2O3-4SiO2). With the object to manufacture the glass ceramics which can be produced in the domestic pot the composition of glass was so settled at 1.0 Li2O.0.9Al2O3.6.0SiO2 in order to reduce the contents of Li2O, to prevent the corrosion of the pot and to decrease the cost of raw materials. 0.2 mole and 0.1 mole of the mixture of TiO2 and ZrO2 as nucleants were added to the basic composition of 1.0 Li2O-0.9Al2O3-6.0SiO2. Each sample was divided into two kinds with a TiO2/ZrO2 ratio of 2 to 1 and the other with a TiO2/ZrO2 ratio fo 1 to 1. Thermal expansion coefficient, the most important property of glass ceramics, was tested. The softening point and the melting point of the samples were observed by the use of a heating microscope. The results obtained were as follows. The manufacturing of glass ceramics seems to be possible in the industrial plant using the domestic pot. 1) The composition of the glass which can be melted in the domestic pot process was near 1.0 Li2O.0.9Al2O3.6.0SiO2. 2) The temperature range of crystal creation and crystal growth was between 850-94$0^{\circ}C$, and 5 hours holding the samples at the temperature range was enough to crystallize them. The major crystal was $\beta$-spdumene and there existed petalite partialy. 3) The thermal expansion coefficient fo the crystallized glass was negative. 4) The deforming point of the crystallized glass was 1435$^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.2
• /
• pp.127-135
• /
• 1992

It has been reported that natural petalite showed a low negative thermal coefficient and wide coefficient and wide coexisting region with liquid phase in Li2O-Al2O3-SiO2 system. Therefore, we investigated variation of microstructure and thermal and mechanical properties when the amount of SiO2 content in petalite compound and MgO addition to it compound were changed. As SiO2 content exceeded 80 wt%, crystal phases of $\beta$-cristobalite and $\beta$-spondumene solid solution were formed. Generally, the densification and bending strength were increased by the addition of MgO, but the positive thermal coefficient was found in the case of MgO 10 wt% addition because of second phase and glassy phase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.79-83
• /
• 2009

The glass-ceramic of the $Li_{2}O-Al_{2}O_{3}-SiO_{2}$ system was investigated to develop the low thermal expansion materials. The glass of this system was heat treated at $775^{\circ}C$ for 2 h for nucleation and subsequently at $825{\sim}900^{\circ}C$ for 2 h for crystallization. The crystal structure of the glass-ceramic of this system was a single phase of $\beta$-quartz solid solution($Li_{x}Al_{x}Si_{1-x}O_{2}$). The thermal expansion of the glass-ceramic showed $4.40{\times}10^{-7}{\sim}1.33{\times}10^{-6}K^{-1}$ between $25{\sim}300^{\circ}C$ and $1.56{\times}10^{-6}{\sim}2.53{\times}10^{-6}K^{-1}$ between $25{\sim}800^{\circ}C$, higher than lower temperature range. The mechanical strength remained almost same at around high 110 MPa with heating temperature changes.

• The Journal of Natural Sciences
• /
• v.8 no.2
• /
• pp.111-118
• /
• 1996

In order to improve the chemical durability of glass in the $Na_2O$-CaO-$SiO_2$ system, it was investigated in the effect of $B_2O_3$ and ZnO addition and changing amount of each composition, $Na_2O$, $Al_2O_3$, $Li_2O$. In this minimize the change of softening point of glass was as follow.(wt%)$B_2O_3$:3.36%, ZnO:2.88%, $Na_2O$:9.93%, $Al_2O_3$, $Li_2O$:0.19%, $SiO_2$:70.56%, CaO:11.22%, $K_2O$:0.14%

• Journal of the Korean Ceramic Society
• /
• v.52 no.3
• /
• pp.215-220
• /
• 2015

Phase evolution, microstructure, and microwave dielectric properties of $Li_2O$ and $Al_2O_3$ doped $Zn_{1.9}Si_{1.05}O_4$, i.e., $Zn_{1.9-2x}Li_xAl_x-Si_{1.05}O_4$, ceramics (x = 0.02 ~ 0.10) were investigated. The ceramics were densified by $SiO_2$-rich liquid phase composed of the Li-Al-Si-O system, indicating that doped Li and Al contributed to the formation of the liquid. As the secondary phase, ${\beta}$-spodumene solid solution with the composition of $LiAlSi_3O_8$ was precipitated from the liquid during the cooling process. The dense ceramics were obtained for the specimens of $$x{\geq_-}0.06$$ showing the rapid densification above $1000^{\circ}C$, implying that a certain amount of liquid is necessary to densify. The specimen of x = 0.06 sintered at $1050^{\circ}C$ exhibited good microwave dielectric properties; the dielectric constant and the quality factor ($Q{\times}f_0$) were 6.4 and 11,213 GHz, respectively.

• Journal of the Korean Ceramic Society
• /
• v.51 no.1
• /
• pp.25-31
• /
• 2014

New green phosphor is synthesized by reducing $LiAlO_2:xEu^{3+}$ phosphors in a low pressure $H_2$ atmosphere. The $LiAlO_2:xEu^{3+}$ prepared by a solid state reaction method is reported as red phosphor. The effect of the reduction treatment on the $LiAlO_2:xEu^{3+}$ on the crystalline phase change and photoluminescence (PL) property are characterized. The reduced phosphor had a broad green light spectrum centered at 524 nm. The PL intensity of the reduced phosphor increased to a maximum at the reduction temperature of $1100^{\circ}C$. The PL intensity decreased with a further increase in the reduction temperature. The crystalline phase constituting the reduced phosphor varied with the temperature. A new crystalline phase $Li_2Al_4O_7$ was observed at $1100^{\circ}C$. The origin of the green-light emission is discussed in relation to the crystalline phase change.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.572-580
• /
• 1994

With low thermal expansion coefficients, eucryptite (Li2O.Al2O3.2SiO2) and spodumene (Li2O.Al2O3.4SiO2) in LAS ceramic system show good thermal shock resistance. In this study, sillimanite or kaolin group silicate minerals and Li2CO3 were used as starting materials, and if necessary SiO2 or Al2O3 were added for making stoichiometrically formed specimens. By this process, eucryptite powders were synthesized and characterized. The powder mixtures of lithiumcabonate and silicate minerals calcined at 80$0^{\circ}C$ for 2 hrs were made into powder compacts. $\beta$-Eucryptite single phase was formed via intermediate phases of Li2SiO3 and LiAlO2 et al, by heating at 110$0^{\circ}C$ or 120$0^{\circ}C$ for 10 hrs from those powder compacts. When using the sillimanite group minerals, Virginia kyanite or andalusite was reacted to form eucryptite at 120$0^{\circ}C$and CMK International kyanite were completed at 110$0^{\circ}C$. When kaolin group minerals were used, it was found that the synthesizing temperature (100$0^{\circ}C$) of $\beta$-eucryptite from the mixture of New Zealand white kaolin was lower than that from Hadong pink kaolin (110$0^{\circ}C$). The Microstructure of systhesized powder showed the irregular lump shape such as densed crystallines.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.98-98
• /
• 2003

초내열성 결정화유리는 전기전자부품, 천체만원경의 반사경, 직화용 조리기기, 군사용 부품 등에 광범위하게 이용되고 있는데 이중 LAS 계가 가장 오랫동안 알려진 조성 계이다. 이 결정화유리는 주입성형후 열처리에 의하여 결정상을 생성하여 사용되는데 표면이 매우 낮은 조도를 갖는 것으로 알려져 있으나 실제로는 제조상에 조도가 높게 나타나는 문제점이 제기되고 있다. 따라서 본 연구에서는 미세조직적인 측면에서 이러한 점을 연구하고자 Li$_2$O-AL$_2$O$_3$-SiO$_2$를 주성분으로 하고 소량의 MgO와 핵생성제로서 TiO$_2$, ZrO$_2$를 사용하여 시편을 제조하였다. 제조된 결정화유리의 결정화도의 차이에 따라 AFM, $\alpha$-STEP등으로 표면의 조도를 정량화였다. 결정상의 종류, 크기, 결정화도, 결정상간의 간격 등이 표면의 조도에 어떻게 영향을 주는가 에 대하여 연구한 결과를 제시하였다.

• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.45-51
• /
• 2005

$K^+-{\beta}^{{\prime}{\prime}}-Al_2O_3$ in the $K_2O-Li_2O-Al_2O_3$ ternary system was synthesized using aluminum nitrate solution as a starting material. For the synthesis of pure $K^+-{\beta}^{{\prime}{\prime}}-Al_2O_3$, raw materials with chemical composition of $0.84K_2O{\cdot}0.082Li_2O{\cdot}5.2Al_2O_3$ were mixed in solution state. The effects of dispersant and solution-pH were investigated in minimizing the particle size and on the synthesis of pure $K^+-{\beta}^{{\prime}{\prime}}-Al_2O_3$. Ethanol was used for a dispersant, and $NH_4OH$ solution and nitric acid were added for pH adjustment. The solution pH was increased from 1.0 to 7.5 by 0.5 increments. Each sample was calcined at $1200^{\circ}C$ for 2 h and characterized with X-ray diffraction and particle size analyzer. The pH of solution significantly effected both particle size and phase formation, while the addition of ethanol only effected particle size. The synthesis of pure $K^+-{\beta}^{{\prime}{\prime}}-Al_2O_3$ was favored by addition of nitric acid (for pH control).