• Journal of the Korean Vacuum Society
• /
• v.6 no.S1
• /
• pp.43-46
• /
• 1997

High resolution x-ray diffraction and two dimensional triple axis mapping were used to characterize a group of GaN layers of about 1.1$\mu$m grown by direct current plasma molecular beam epitaxy technique on 6H-SiC(0001). A FWHM of 11.9 arcmins for an $\omega$ scan and 1.2 arcmins for an $\omega$/2$\theta$ scan were observed. A careful study of the rocking curves showed there were some large mosaics in the GaN layer and a tilt of $0.029^{\circ}$ between the GaN layer and the SIC substrate was detected. The two dimensional triple axis mapping showed that the GaN mosaica were disoriented in the (0001) plane but rather uniformed in direction perpendicular to the plane. A mosaics were disoriented in the (0001) plane but rather uniformed in direction perpendicular to the plane. A mosaic model was deduced to explain the phenomenon and the dislocation density was estimated to be about~$10^9\;\textrm{cm}^{-2}$ acc ding to the model.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.165-165
• /
• 2003

The growth of GaN on Si is of great interest due to the several advantages low cost, large size and high-quality wafer availability as well as its matured technology. The crystal quality of GaN is known to be much influenced by the surface pretreatment of Si substrate [1]. In this work, the properties of GaN overlayer grown on ion implanted Si(111)and bare Si(111) have been investigated. Si(111) surface was treated ion implantation with 60KeV and dose 1${\times}$10$\^$16//$\textrm{cm}^2$ prior to film growth. GaN epilayers were grown at 1100$^{\circ}C$ for 1 hour after growing AlN buffer layers for 15-30 minutes at 1100$^{\circ}C$ with metal organic chemical vapor deposition (MOCVD). The properties of GaN epilayers were evaluated by X-Ray Diffraction (XRD), Scanning electron microscope (SEM) Photoluminescence (PL) at room temperature and Hall measurement The results showed that the GaN on ion implanted Si(111) markedly affected to the structural, optical and electrical characteristic of GaN layers.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.1012-1017
• /
• 1999

Low resistance ohmic contacts to the Si-doped $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$(~$\times10^{19}\textrm{cm}^{-3}$) were obtained using the W metallization schemes. Specific contact resistance decreased with increasing annealing temperature. The lowest resistance is obtained after a nitrogen ambient annealing at $950^{\circ}C$ for 90 s, which results in a specific contact resistance of $2.75\times10^{-8}\Omega\textrm{cm}^{-3}$. Interfacial reactions and surface are analyzed using x-ray diffraction and scanning electron microscopy (SEM). The X-ray diffraction results show that the reactions between the W film and the $\textrm{In}_{0.17}\textrm{Ga}_{0.83}\textrm{N}$ produce a $\beta$-$W_2N$ phase at the interface. The SEM result shows that the morphology of the contacts is stable up to a temperature as high as $850^{\circ}C$. Possible mechanisms are proposed to describe the annealing temperature dependence of the specific contact resistance.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.10 no.1
• /
• pp.7-13
• /
• 2010

We have investigated effects of the rapid thermal annealing of GaN epilayers by molecular beam epitaxy in nitrogen atmosphere. The improvement of structural properties of the samples was observed after rapid thermal annealing under optimum conditions. This improvement in crystal quality is due to a reduction of the spread in the lattice parameter in epilayers. The annealing has been performed in a rapid thermal annealing furnace at $950^{\circ}C$. The effect of rapid thermal annealing on the structural properties of GaN was studied by x-ray diffraction. The Bragg peak shifts toward larger angle as the annealing time increases. As the thermal treatment time increases, FWHM(full width at half maximum) of the peak slightly increase with its decreases followed and it increases again. Results demonstrate that rapid thermal annealing did not always promote qualities of GaN epilayers. However, rapid thermal annealing under optimum conditions improve structural properties of the samples, elevating their crystal quality with a reduction of inaccuracy in the lattice parameter of the epilayers.

• Proceedings of the KIEE Conference
• /
• 1988.11a
• /
• pp.372-375
• /
• 1988

The III-V ternary alloy semiconductor $In_{l-x}Ga_{x}As$ were grown by the temperature Gradient of $0.60{\leq}x{\leq}0.98$. The electrical properties were investigated by the Hall effect measurement with the Van der Pauw method in the temperature range of $90{\sim}300K$. $In_{l-x}Ga_{x}As$ were revealed n-type and the carrier concentration at 300K were in the range of $9.69{\times}10^{16}cm^{-3}{\sim}7.49{\times}10^{17}cm^{-3}$. The resistivity was increased and the carrier mobility was decreased with increasing the composition ratio. The optical energy gap determined by optical transmission were $20{\sim}30meV$ lower than theoretical valves on the basis of absorption in the conduction band tail and it was decreased with increasing the temperature by the Varshni rule. In the photoluminescence of undoped $In_{l-x}Ga_{x}As$ at 20K, the main emission was revealed by the radiative recombination of shallow donor(Si) to acceptor(Zn) and the peak energy was increased with increasing the composition, X. The diffusion depth of Zn increases proportionally with the square root of diffusion time, and the activation energy for the Zn diffusion into $In_{0.10}Ga_{0.90}As$ was 2.174eV and temperatures dependence of diffusion coefficient was D = 87.29 exp(-2.174/$K_{B}T$). The Zn diffusion p-n $In_{x}Ga_{x}As$ diode revealed the good rectfying characteristics and the diode factor $\beta{\approx}2$. The electroluminescence spectrum for the Zn-diffusion p-n $In_{0.10}Ga_{0.90}As$ diode was due to radiative recombation between the selectron trap level(${\sim}140meV$) and Zn acceptor level(${\sim}30meV$). The peak energy and FWHM of electroluminescence spectrum at 77K were 1.262eV and 81.0meV, respectively.

• 전기의세계
• /
• v.28 no.4
• /
• pp.53-63
• /
• 1979

Interface recombination velocity in $Al_{x}$G $a_{1-x}$ As-GaAs and $Al_{0.85}$, G $a_{0.15}$ As-GaA $s_{1-y}$S $b_{y}$ heterojunction systems is studied as a function of lattice mismatch. The results are applied to the design of highly efficient III-V heterojunction solar cells. A horizontal liquid-phase epitaxial growth system was used to prepare p-p-p and p-p-n $Al_{x}$G $a_{1-x}$ As-GaA $s_{1-y}$S $b_{y}$-A $l_{x}$G $a_{1-x}$ As double heterojunction test samples with specified values of x and y. Samples were grown at each composition, with different GaAs and GaAs Sb layer thicknesses. A method was developed to obtain the lattice mismatch and lattice constants in mixed single crystals grown on (100) and (111)B oriented GaAs substrates. In the AlGaAs system, elastic lattice deformation with effective Poisson ratios .mu.$_{eff}$ (100=0.312 and .mu.$_{eff}$ (111B) =0.190 was observed. The lattice constant $a_{0}$ (A $l_{x}$G $a_{1-x}$ As)=5.6532+0.0084x.angs. was obtained at 300K which is in good Agreement with Vegard's law. In the GaAsSb system, although elastic lattice deformation was observed in (111) B-oriented crystals, misfit dislocations reduced the Poisson ratio to zero in (100)-oriented samples. When $a_{0}$ (GaSb)=6.0959 .angs. was assumed at 300K, both (100) and (111)B oriented GaAsSb layers deviated only slightly from Vegard's law. Both (100) and (111)B zero-mismatch $Al_{0.85}$ G $a_{0.15}$As-GaA $s_{1-y}$S $b_{y}$ layers were grown from melts with a weight ratio of $W_{sb}$ / $W_{Ga}$ =0.13 and a growth temperature of 840 to 820 .deg.C. The corresponding Sb compositions were y=0.015 and 0.024 on (100) and (111)B orientations, respectively. This occurs because of a fortuitous in the Sb distribution coefficient with orientation. Interface recombination velocity was estimated from the dependence of the effective minority carrier lifetime on double-heterojunction spacing, using either optical phase-shift or electroluminescence timedecay techniques. The recombination velocity at a (100) interface was reduced from (2 to 3)*10$^{4}$ for y=0 to (6 to 7)*10$^{3}$ cm/sec for lattice-matched $Al_{0.85}$G $a_{0.15}$As-GaA $s_{0.985}$S $b_{0.015}$ Although this reduction is slightly less than that expected from the exponential relationship between interface recombination velocity and lattice mismatch as found in the AlGaAs-GaAs system, solar cells constructed from such a combination of materials should have an excellent spectral response to photons with energies over the full range from 1.4 to 2.6 eV. Similar measurements on a (111) B oriented lattice-matched heterojunction produced some-what larger interface recombination velocities.ities.ities.s.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.3
• /
• pp.66-74
• /
• 1999

InAlGaAs/InGaAs HBTs with the various emitter junction gradings(xf=0.0-1.0) and the modified collector structures (collector- I;n-p-n, collector-II;i-p-n) are simulated and analyzed by HMC (Hybrid Monte Carlo) method in order to find an optimum structure for the shortest transit time. A minimum base transit time($ au$b) of 0.21ps was obtainsed for HBT with the grading layer, which is parabolically graded from $x_f$=1.0 and xf=0.5 at the emitter-base interface. The minimum collector transit time($\tau$c) of 0.31ps was found when the collector was modified by inserting p-p-n layers, because p layer makes it possible to relax the electric field in the i-type collector layer, confining the electrons in the $\Gamma$-valley during transporting across the collector. Thus InAlGaAs/InGaAs HBT in combination with the emitter grading($x_f$=0.5) and the modified collector-III showed the transit times of 0.87 psec and the cut-off frequency (f$\tau$) of 183 GHz.

• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.348-352
• /
• 2005

Gallium oxyhydroxide (GaOOH) powders were heat-treated in a flowing ammonia gas to form GaN, and the reaction kinetics of the oxide to nitride was quantitatively determined by X-ray diffraction analysis. GaOOH turned into intermediate mixed phases of $\alpha-\;and\;\beta-Ga_2O_3$, and then single phase of GaN. The reaction time for full conversion $(t_c)$ decreased as the temperature increased. There were two-types of rapid reaction processes with the reaction temperature in the initial stage of nitridation at below $t_c$, and a relatively slow processes followed over $t_c$ does not depends on temperatures. The nitridation process was found to be limited by the rate of an interfacial reaction with the reaction order n value of 1 at $800^{\circ}C$ and by the diffusion-limited reaction with the n of 2 at above $1000^{\circ}C$, respectively, at below $t_c$. The activation energy for the reaction was calculated to be 1.84 eV in the temperature of below $830^{\circ}C$, and decreased to 0.38 eV above $830^{\circ}C$. From the comparative analysis of data, it strongly suggest the rate-controlling step changed from chemical reaction to mass transport above $830^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.147-147
• /
• 2011

High crystalline nonpolar a-plane (11-20) nitride light emitting diodes (LEDs) have been fabricated on r-plane (1-102) sapphire substrates by metalorganic chemical-vapor deposition (MOCVD). The multi-quantum wells (MQWs) active region is consists of 4 periods the nonpolar a-plane InGaN/GaN(a-InGaN/GaN) on a high quality a-plane GaN (a-GaN) template grown by using the multibuffer layer technique. The full widths at half maximum (FWHMs) of x-ray rocking curve (XRC) obtained from phiscan of the specimen that was grown up to nonpolar a-plane GaN LED layers with double crystal x-ray diffraction. The FWHM values were decreased down to 477 arc sec for $0^{\circ}$ and 505 arc sec for $-90^{\circ}$, respectively. After fabricating a conventional lateral LED chip which size was $300{\times}600{\mu}m^2$, we measured the optical output power by on-wafer measurements. N-electrode was made with Cr/Au contact, and ITO on p-GaN was formed with Ohmic contact using Ni/Au followed by inductively coupled plasma etching for mesa isolation. The optical output power of 1.08 mW was obtained at drive current of 20 mA with the peak emission wavelength of 502 nm.

• Korean Journal of Materials Research
• /
• v.28 no.4
• /
• pp.208-213
• /
• 2018

Epitaxial ($11{\bar{2}}0$) a-plane GaN films were grown on a ($1{\bar{1}}02$) R-plane sapphire substrate with photoresist (PR) masks using metal organic chemical vapor deposition (MOCVD). The PR mask with striped patterns was prepared using an ex-situ lithography process, whereas carbonization and heat treatment of the PR mask were carried out using an in-situ MOCVD. The heat treatment of the PR mask was continuously conducted in ambient $H_2/NH_3$ mixture gas at $1140^{\circ}C$ after carbonization by the pyrolysis in ambient $H_2$ at $1100^{\circ}C$. As the time of the heat treatment progressed, the striped patterns of the carbonized PR mask shrank. The heat treatment of the carbonized PR mask facilitated epitaxial lateral overgrowth (ELO) of a-plane GaN films without carbon contamination on the R-plane sapphire substrate. Thhe surface morphology of a-plane GaN films was investigated by scanning electron microscopy and atomic force microscopy. The structural characteristics of a-plane GaN films on an R-plane sapphire substrate were evaluated by ${\omega}-2{\theta}$ high-resolution X-ray diffraction. The a-plane GaN films were characterized by X-ray photoelectron spectroscopy (XPS) to determine carbon contamination from carbonized PR masks in the GaN film bulk. After $Ar^+$ ion etching, XPS spectra indicated that carbon contamination exists only in the surface region. Finally, the heat treatment of carbonized PR masks was used to grow high-quality a-plane GaN films without carbon contamination. This approach showed the promising potential of the ELO process by using a PR mask.