• Korean Journal of Materials Research
• /
• v.23 no.12
• /
• pp.672-679
• /
• 2013

$Fe_4[Fe(CN)_6]_3$ coated on a mica or $TiO_2$/mica surface as infrared reflective blue pigment was prepared by a hydrothermal method. $Fe_4[Fe(CN)_6]_3$, used as coloring agent, was uniformly coated on mica or $TiO_2$/mica under the optimized condition of a 1.2 : 1 weight ratio between iron(III) chloride hexahydrate and potassium ferrocyanidetrihydrate at the initial pH level of 4.5 at $70^{\circ}C$. The infrared (IR)-reflective pigments were characterized by SEM, Zeta-potenial, FT-IR, and UV-VIS NIR spectrophotometry. Especially the CIE color coordinate and total solar reflectance(TSR) properties of the pigments were investigated in relation to variation of the coating and coated substrate thicknesses. Isolation-heat paint was prepared with 20 wt% blue pigments fully dispersed in acryl-urethane resin and several additives to coat the film uniformly. The films were also measured with CIE color coordinate, TSR, and the surface temperature was recorded by an isolation-heat measuring system. The pigments and films of $Fe_4[Fe(CN)_6]_3$ coated on mica and $TiO_2$/mica showed high TSR values compared with the TSR value of $Fe_4[Fe(CN)_6]_3$ itself. According to the increase of TSR value, the property of isolation-heat is effective. To realize the optimal blue color, we applied the the pigment to $TiO_2$ coated mica(TM(b)) which has blueish interference color. The pigment of $Fe_4[Fe(CN)_6]_3$ coated on TM(b) shows a strong blue color compared with that of $Fe_4[Fe(CN)_6]_3$ coated on $TiO_2$/Mmca(TM(w)), which has a whitish interference color.

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.3
• /
• pp.316-322
• /
• 2006

The current study evaluated the technical feasibility of the application of $TiO_2$ photocatalysis for the removal of nocotine which has well known as a representative material of environmental tobacco smoke(ETS). Four different preliminary experiments were performed for the evaluation of nicotine removal using photocatalyst-coated construction materials. The photocatalytic removal of nicotine was investigated for five parameters: dry condition of coating tiles, type of coating sol, number of coatings, relative humidity(RH), and input concentrations. Prior to performing the parameter tests, adsorption of nicotine onto the current experimental system was surveyed. All the variables tested in the present study exhibited to influence the photocatalytic decomposition of Nicotine. A dry condition of high temperature and short dry period presented higher photocatalytic oxidation(PCO) efficiency compared to that of low temperature and long dry period. ST-KO3 sol showed higher decomposition efficiency than E-T Sol. The PCO efficiency increased as the number of coating increased. High humidity and low input concentrations exhibited higher PCO efficiency. Consequently, it is noted that the five parameters tested in the present study should be considered for the application of photocatalyst-coated construction materials in cleaning nicotine in ETS.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.40 no.9
• /
• pp.631-637
• /
• 2003

We have evaluated structural and electric, ferroelectric properties of PZT(30/70) thick film prepared by using 1,3-propanediol based sol-gel method on Pt/Ti/SiO$_2$/Si substrates. Rapid thermal annealing (RTA) is used to reduce the thermal stress and final furnace annealing is processed at $650^{\circ}C$. As the results of SEM analysis, we find that we get 350 nm in thickness for one coating and 1 $\mu$m for three times of coating. In the results of C-D analysis at 1 kHz, dielectric constant ($\varepsilon$$_{r}$) and dissipation factor were 886 and 0.03, respectively. C-V curve is shaped as a symmetrical butterfly. Leakage current density at 200 kV/cm is 1.23${\times}$10$^{-5}$ A/cm$^2$ and in the results of hysteresis loops measured at 150 kV/cm, the remnant polarization (P$_{r}$) and the coercive field (E$_{c}$) are 33.8 $\mu$C/cm$^2$ and 56.9 kV/cm, respectively. PZT(30/70) thick film exhibits relatively good ferroelectric, electric properties.s..

• Korean Journal of Materials Research
• /
• v.16 no.3
• /
• pp.145-150
• /
• 2006

Various colors of light emitting diodes(LED) and four-band white light sources are obtained using a violet LED and various phosphor films. $BaMg_2Al_{16}O_{27}:Eu\;(blue),\;SrGa_2S_4:Eu\;(green),\;and\;Eu(TTA)_3(PTA)$ (red) phosphors are dispersed in poly-vinyl-alcohol aqueous solutions, and phosphor films are prepared by coating the suspensions to PET film. The narrow band emission of $Eu(TTA)_3(PTA)$ phosphor has excellent red luminescent property for four-band white light excited by the violet LED.

• Journal of Surface Science and Engineering
• /
• v.49 no.3
• /
• pp.280-285
• /
• 2016

In this study, we investigated the influences of potassium fluoride(KF) addition on the surface characteristics of plasma electrolytic oxidation(PEO) coating produced on Al alloy. The PEO of marine grade Al alloy(5083 grade) was conducted in KOH 1g/L solution adding different concentrations of KF(0, 1 and 2 g/L) under a galvanostatic regime. With KF addition, unusual behavior was observed on the voltage-time characteristic curves, which can be characterized by the following process: (i) initial rapid increase in voltage (ii) a short plateau after 1st breakdown (iii) gradual increase in voltage (iv) intermittent fluctuation of voltage after 2nd breakdown. The SEM observation revealed irregular surface morphology with KF addition, as compared with one formed without KF addition, which had a reticulate structure. The XRD analysis detected the formation of aluminium hydroxide fluoride hydrate($H_{4.76}Al_2F_{3.24}O_{3.76}$) on surface grown by PEO process with KF. Particularly, at very early stage of the process (~ 120 s), thin film was formed having nanoporous structure, and F element was confirmed on surface by EDS analysis. The thickness and surface roughness of the coating increased with increasing KF concentration. As a result, KF addition was found to be less beneficial influences on PEO of marine grade Al alloy, and therefore needs further research to improve its capability.

• Journal of Power System Engineering
• /
• v.18 no.6
• /
• pp.58-63
• /
• 2014

This paper deals with the effects of counterpart materials on the wear behavior of thermally sprayed STS316 coatings. STS316 powders were flame-sprayed onto a carbon steel substrate. Dry sliding wear tests were performed using the applied loads of 15 N. AISI52100, $Al_2O_3$, $ZrO_2$ and $Si_3N_4$ balls were used as counterpart materials. Wear behavior of STS316 coatings against different counterpart materials were studied using a scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDS). The results show that the wear behavior of thermally sprayed STS316 coatings strongly depends on the type of counterpart material. Dominant wear mechanism was similar for all studied materials as failure of adhesion film except for Si3N4 used as counterpart material. In the case of Si3N4 used as counterpart material, dominant wear mechanism was abrasion.

• Journal of Surface Science and Engineering
• /
• v.28 no.6
• /
• pp.368-375
• /
• 1995

Thermal CVD method is in general used for the fabrication of TiC/$Al_2O_3$-coated carbide tools. The growth of TiC layer and the coating morphology depended on the chemical composition of the hard metal substrate on which the tool properties were strongly influenced. TiC-coated layer was grown by the diffusion of carbon from the substrate, whereas the growth of $Al_2O_3$ layer was unrelated to the composition of substrate. In the nitride hard coatings of Zr, Nb and Mo metals deposited on high speed steel substrate by magnetron sputtering, the reactivity of the metal elements was decreased with increasing group number in one period of the periodic system. The hard material films exhibited the highest adhesion with the chemical composition of stoichiometry or substoichiometry. The critical load as a measure of adhesion was evaluated using scratch tester. The CVD tools indicated the values of 80 and 40N in the coated layers with proper bonding to the substrate and with $\eta$ phase of 1$\mu\textrm{m}$ in the interface respectively, but the nitride films prepared by sputtering of PVD showed only the values between 10 and 20N.

• Journal of the Korean GEO-environmental Society
• /
• v.25 no.5
• /
• pp.29-37
• /
• 2024

This study aimed to investigate the changes in chemical components that occur when weak clay is mixed with steel slag modified with calcium oxide, and to understand the expression characteristics of compressive strength according to hydrophilicity and curing time. XRF testing, SEM imaging, vane shear strength and uniaxial compressive strength testing were conducted. Calcium (Ca) released from the steel slag increases the Ca content in clay by increasing the number of crystal particles and forming a coating layer known as calcium silicate hydrate (CaO-SiO₂-H₂O) through chemical reactions with SiO₂ and Al₂O₃ components. The weak clay stabilized with steel slag is classified into an initial inactive zone where strength relatively does not increase and an activation zone where strength increases over curing time. The vane shear strength of the initial inactive area was found to be 4.4 to 18.4 kN/m² in the state of the weight mixing ratio Rss 30% (steel slag 30% + clay 70%). In the case of the active area, the maximum uniaxial compressive strength increased to 431.8 kN/m² after 480 hours of curing time, which increased due to the apparent adhesion strength of clay through pozzolanic reaction. Therefore, considering the strength expression characteristics of stabilized mixed clay based on the mixing ratio (Rss) during the recycling of steel slag can enhance its practicality in civil engineering sites.

• Laser Solutions
• /
• v.3 no.2
• /
• pp.35-43
• /
• 2000

Laser direct patterning of the coated photoresit (PMER-NSG31B) layer was studied to make halftone dots on gravure printing roll. The selective laser hardening of photoresist by Ar-ion laser(wavelength : 333.6nm∼363.8nm) was controlled by the A/O modulator. The coating thickness in the range of 5㎛∼11㎛ could be obtained by using the up-down directional moving device along the vertically located roll. The width, thickness and hardness of the hardened lines formed under laser power of 200∼260㎽ and irradiation time of 4.4∼6.6$\mu$ sec/point were investigated after developing. The hardened width increased according to the increase of coating thickness. Though the hardened thickness was changed due to the effect of the developing solution, the hardened layer showed good resistance to the scratching of 2H pencil. Also, the hardened minimum line widths of 10㎛ could be obtained. The change of line width was also found after etching, and the minimum line widths of 6㎛ could be obtained. The hardened lines showed the good resistance to the etching solution. Finally, the experimental data could be applied to make gravure halftone dots using the developed imaging process, successfully.

• Corrosion Science and Technology
• /
• v.21 no.5
• /
• pp.340-347
• /
• 2022

In this research, mixed metal oxide (TiO₂, RuO₂) coating was applied to grade 1 titanium as a bipolar plate for polymer electrolyte membrane fuel cell (PEMFC). Electrochemical experiments were carried out in an aqueous solution of pH 3 (H₂SO₄ + 0.1 ppm HF, 80 ℃) determined by DoE. The air was bubbled to simulate a cathode environment. Potentiodynamic polarization test revealed that corrosion current densities of the titanium substrate and MMO-coated specimen were 0.180 µA/cm² and 4.381 µA/cm², respectively. There was no active peak. After potentiostatic experiment, current densities of the titanium substrate and the MMO-coated specimen were 0.19 µA/cm² and 1.05 µA/cm², respectively. As a result of observing the surface before and after the potentiostatic experiment, cracked dried clay structures were observed without corrosion damage. Both the titanium substrate and the MMO-coated specimen could not satisfy the interfacial contact resistance suggested by the DoE. Thus, further research is needed before they could be applied as bipolar plates.