• Journal of the Korean Ceramic Society
• /
• v.30 no.9
• /
• pp.695-700
• /
• 1993

In this study, we prepared Pb-Ti stock solution by sol-gel processing and deposited PbTiO3 thin film on a Pt coated SiO2/Si wafer by spin coating using the stock solution. We used lead acetate trihydrate and titanium isopropoxide. The stock solution was partially hydrolized and finally a 0.25M coating solution was prepared. We achieved spin coating at 4000rpm for 30 seconds and heated the thin film at 375$^{\circ}C$ for 5 minutes and at $600^{\circ}C$ for 5 minutes successively, first and second heating state. And the thin film was finally sintered at 90$0^{\circ}C$ for 1 hour in the air. The upper electrode of the thin film was made by gold sputtering and was cricle shape with radius 0.4mm. Measured dielectric constant, dissipation factor and phase transition temperature(Cuire Temp.) were about 275, 0.02 and 521$^{\circ}C$ respectively. To observe ferroelectric characteristics we calculated Pr(remnant polarization) and Ec(coercive field) byhysteresis curve. Ec was 72kV/cm and Pr was 11.46$\mu$C/$\textrm{cm}^2$.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.391-402
• /
• 1999

Characteristics of composite electrolytes which were prepared by coating a thin film of YSZ (yttria sta-bilized zirconia : (ZrO2)0.92 (Y2O3)0.08) on YDC (yttria doped ceria : Ce0.8Y0.2O1.9) with mixed conductivity have been investigated in order to develop the low-temperature solid oxide fuel cell. The thickness (t) of spin-coated YSZ thin films after the heat-treatment at 600$^{\circ}C$ was increased proportionally to the sol con-centrations (C) while the decrease in its thickness with the spin rate ($\omega$) could be expressed in the e-quation of ln t=9.49-0.53 ln $\omega$(0.99mol//s sol conc.) When the sol concentration and the spin rate being less than 0.99 mol/l and higher than 1000 rpm respectively reliable YSZ/YDC composite electrolytes could be obtained by multi-coating although several micro-cracks were observed in singly coated YSZ film surfaces. The dense YSZ film with a 1$\mu\textrm{m}$ thickness was prepared by coating of 0.99 mol/l YSZ sol five-times at 2000 rpm followed by heat-treatment at 1400$^{\circ}C$ for 2h, The adhesion between YSZ film and YDC substrate was found to be very good. The open circuit voltages of H2/O2 single cell with YSZ/YDC composite electrolytes were 0.79∼0.82 V at 800$^{\circ}C$ and 0.75∼0.77V at 900$^{\circ}C$ The open circuit voltage was inversely proportioned to the thickness ratio of YSZ thin film (1$\mu\textrm{m}$) to YDC substrate(0.28-2.22 mm)

• Journal of Korean Society of Water and Wastewater
• /
• v.13 no.3
• /
• pp.101-106
• /
• 1999

This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.

• Journal of Powder Materials
• /
• v.7 no.2
• /
• pp.63-70
• /
• 2000

Thermal spray coating process has proven to be effective at producing hard, dense, wear resistance coatings on the relatively mild substrates. Among several spraying techniques, HVOF (High Velocity Oxygen Fuel) and plasma coating processes, which are preferentially used for the wear resistance application such as capstans, have been applied in this study. The effects of pre-treatment, it-process and post-treatment parameters on the wear and mechanical properties of WC+12%Co, Cr3C2 and Al2O3 powder coatings have been investigated and correlated with the microstructures. The results indicated that the carbide coating was more preferable to the oxide coatings and the post-treatments consisting of vacuum annealing and sealing on carbide coatings led to significant improvements in wear resistance, adhesive strength and coating phase stabilization over the other processing techniques in this application.

• Resources Recycling
• /
• v.26 no.6
• /
• pp.97-101
• /
• 2017

Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open pores which are penetrable pores are necessary for industrial applications such as in high temperature filters and as support for catalysts. In this study, Fe foam with greater than 90% porosity and 2-mm pore size was successfully fabricated using a slurry coating process and the pore properties were characterized. The Fe and $Fe_2O_3$ powder mixing ratios were controlled to produce Fe foam samples with different pore sizes and porosity. First, the slurry was prepared through the uniform mixing of powders, distilled water, and polyvinyl alcohol(PVA). The amount of slurry coated with the PU foam increased with increasing $Fe_2O_3$ mixing powder ratio, but the shrinkage and porosity of the Fe foams decreased, respectively, with increasing $Fe_2O_3$ mixing powder ratio.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.653-657
• /
• 2012

In this study, a molybdenum disilicide ($MoSi_2$) coating process was investigated by hydrogen reduction and Si-pack cementation. At first, the metallic Mo coating was carried out by hydrogen reduction of $MoO_3$ powder at $750^{\circ}C$ for various holding times (1, 2, 3 h) in hydrogen atmosphere. A $4.3{\mu}m$ thick metallic molybdenum thin film was formed at 3 h. $MoSi_2$ was obtained by Si-pack cementation on molybdenum thin film through hydrogen reduction processing. It was carried out using $Si:Al_2O_3:NH_4Cl=5:92:3$ (wt%) packs at $900^{\circ}C$ for various holding times (30, 60, 90 min) in Ar atmosphere. When the holding time was 90 min, a $MoSi_2$ layer was coated successfully and a $15.4{\mu}m$ thickness was observed.

• Journal of Surface Science and Engineering
• /
• v.52 no.6
• /
• pp.350-356
• /
• 2019

In this study, the effect of mechanical polishing of carbon steel on the tribological properties of manganese phosphate coating on carbon steel has investigated. The microstructure, surface morphology and chemical composition were analyzed by SEM, EDS, and XRD. The surface roughness test was carried out in order to calculate Rvk value by 3D laser microscopy. Also, the tribology property of manganese phosphate coating was tested by ball-on disk. In the results of EDS analysis, coating layer consists of elements such in Mn, P, Fe, and O. XRD showed that (Mn,Fe)₅H₂(PO₄)₄·4H₂O in manganese phosphate coating layer was formed by the chemical reaction between manganese phosphate and elements in carbon steel. As the mechanical polishing degree increased, the friction coefficient was reduced. The rougher the mechanical polishing degree, the better corrosion resistance was obtained.

• 한국초전도학회:학술대회논문집
• /
• v.13
• /
• pp.71-71
• /
• 2003

• Korean Chemical Engineering Research
• /
• v.46 no.2
• /
• pp.274-278
• /
• 2008

Hard coating solutions were prepared from glycidoxypropyl trimethoxysilane (GPTMS) and methacryloxypropyl trimethoxysilane (MPTMS) precursors with different molar ratios of 10:0, 9:1, 7:3, 5:5, 3:7, and 0:10, respectively, by the sol-gel method. The polycarbonate (PC) sheets were spin-coated, and cured at $130^{\circ}C$ for 3 h. The effect of the GPTMS:MPTMS molar ratios of the mixture was investigated on the properties of coating films. The highest pencil hardness and adhesion to PC sheets of coating films were found for solution with GPTMS:MPTMS molar ratio of 5:5. Also, the pencil hardness of coating films was increased with increasing the $H_2O$ content in the coating solutions.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.538-544
• /
• 1998

The spallation of a thermal barrier coating layer depends on the formation of brittle spinels. thermal expansion mismatch between ceramic and metal. the phase transformation of a ceramic layer and residual stress of coating layer. In this work. the formation mechanism of oxide scale formed by oxidation treatment at 90$0^{\circ}C$ was investigated in order to verify oxidation behavior at the interface between E-beam coated $Zr0_2$-7wt.% $Y_20_3$ and plasma sprayed CoNiCrAIY. Some elements distributed in the bond coating layer were selectively oxidized after oxidation. At the initial time of oxidation. AI-depletion zone and $\alpha$-$Al_O_3$,O, were formed at the bond coating layer by the AI-outward diffusion. After layer grew until critical thickness. spinels. $Cr_20$, and $C0_2CrO_4$ by outward diffusion of Co. Cr, Ni were formed. It was found that the formation of spinels may be related to the spallation of $Zr0_2$-7wt.% $Y_20_3$ during isothermal oxidation.