• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.505-512
• /
• 1998

In this study, two-layer thermal barrier coatings composed of plasma sprayed 0.3mm $ZrO_2(8wt% Y_2o_3)$ ceramic coating layer and O.lmm $NiCrAlCoY_20_3$ bond coating layer on AISI 316 were investigated microstructure of the coating, oxidation of the metallic bond coating and adhesive strength to evaluate the durability of coating layer after cyclic and isothermal test at 90$0^{\circ}C$. And quantitative phase analysis of $ZrO_2(8wt% Y_2o_3)$ ceramic coating was performed as a function of thermal exposure time using XRD technique. The results showed that the amount of m - 2rO, phase in the coating was slightly increased with increasing thermal exposure time at 90$0^{\circ}C$. The c/a ratio of t' - $ZrO_2$ in the as-sprayed coating was 1.0099 and slightly increased to 1.0115 after 100 hours heat treatment. It was believed that $Y_2O_3$ in high yttria tetragonaJ(t') was transformed to low yttria tetragonaJ(t) by $Y_2O_3$ diffusion with increasing thermal exposure time. The adhesive strength was gradually decreased as thermal exposure time increased. After the isothermal test, the failure predominantly occured in ceramic coating layer. On the other hand. the specimens after cyclic thermal test were mostly failed at bond coating/ceramic coating interface. The failure was oeeured by decreasing the bond strength between bond coating and oxide scale which were formed by oxidation of the metallic elements within bond coating and by thermal stress due to thermal expansion mismatches between the oxide scale and ceramic coating.

• Journal of Surface Science and Engineering
• /
• v.20 no.2
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.667-673
• /
• 1992

The alumina-zirconia composite powders of core particle ZrO2 coated with Al2O3 were prepared by the hydrolysis-deposition of the mixed aluminum salt solution of Al2(SO4)3-Al(NO3)3-Urea. The effects of hydrolysis reaction and coating parameters on characteristics of coated powders and composites were also investigated. The degree of coating could be estimated from the ratio of tetra-/mono-ZrO2 present at the room temperature after heat-treating coated powders at 120$0^{\circ}C$ and the result of TEM observations. When the content of ZrO2 in the dispersed coating system, the coating time, and the volume ratio of water/solution were 50 mg/g, 180 min, and 5, respectively the coating efficiency was maximum (the ratio of tetra-/mono-ZrO2 was 87/13). The relative densities of coated Al2O3-ZrO2 composites sintered at 1$650^{\circ}C$ for 4 hrs were about 91~98% and the maximum ratio of tetra-/mono-ZrO2 in Al2O3-20wt% ZrO2 composites was 62/38.

• Nuclear Engineering and Technology
• /
• v.55 no.5
• /
• pp.1855-1862
• /
• 2023

Graphite crucibles are used for melting uranium and its alloys in VIM furnace. Various coating materials namely Al₂O₃, ZrO₂, MgO etc. are applied on the inner surface of the crucibles using paint brush or thermal spray technique to mitigate U-C interaction. These leads to significant amount of carbon pick-up in uranium. In this study, the attempts are made to develop multilayer coatings comprising of SiC/Y₂O₃ and Mo/Y₂O₃ on graphite to study the feasibility of minimizing U-C interaction. The parameters are optimized to prepare SiC coating of about 70㎛ thickness using CVD technique on graphite coupons and subsequently Y₂O₃ coating of about 250㎛ thickness using plasma spray technique. Molybdenum and Y₂O₃ layers were deposited using plasma spray technique with 70㎛ and 250㎛ thickness, respectively. Interaction studies of the coated graphite with molten uranium at 1450℃ for 20 min revealed that Y₂O₃ coating with SiC interlayer provides physical barrier for uranium-graphite interaction, however, this led to the physical separation of coating layer. Y₂O₃ coating with Mo interlayer provided superior barrier effect showing no degradation and the coatings remained intact after interaction tests. Therefore, the Mo/Y₂O₃ coating was found to be a promising solution for minimizing carbon pick-up during uranium/uranium alloy melting.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.677-684
• /
• 1997

The effects of fluxes on MgO coating materials for tundish were investigated. As the number of charge in continuous casting was increased, the basicity of tundish slag was decreased due to the increase of silica formed by dissolution from rice hull. As a result, the wear of magnesia lining was increased. In aggregates of MgO coating materials, magnesioferrite was formed by the reaction between magnesia and ferric oxide formed by the oxidation of molten steel, while matrix parts of MgO coating materials were worn by CaO-Al2O3-SiO2 compounds. Silica in rice hull extracted to the molten slag reduced basicity of slag and formed forsterite in the result of its reaction with magnesia lining. Also, fayalite was formed from the reaction between silica and ferric oxide and it caused the increment of magnesia lining's wear. The wear of magnesia lining by flux of CaO-SiO2 was larger than that of Cao-Al2O3 and calcia in the flux increased the wear of magnesia lining through the formation of rankinite.

• Korean Journal of Materials Research
• /
• v.24 no.7
• /
• pp.357-362
• /
• 2014

Thermal barrier coatings(TBCs) are being applied in many industrial fields such as thermal power generation, aviation and seasonal fields. $ZrO_2-Y_2O_3$(8%) thermal spray coating powders are commercially used as thermal-barrier coating materials to protect against oxidation and corrosion of heat-resistant alloys at elevated temperatures. Currently, $ZrO_2-Y_2O_3$(8%) thermal-spray powder is made using the industrial co-precipitation process, which is very complex and requires a lot of time. In this study, orthorhombic $ZrO_2$ and $Y_2O_3$ powders were fabricated by mechanical mixing, which is more economical than the co-precipitation process. A tetragonal, yttria-stabilized zirconia(YSZ) coating-layer was produced by plasma spraying, using orthorhombic $ZrO_2-Y_2O_3$(8%) powder. Our experimental results indicate that $ZrO_2-Y_2O_3$(8%) mixed powder can be used economically in industry because it is no longer necessary to make this powder by liquid and gas-phase methods.

• Korean Journal of Materials Research
• /
• v.30 no.7
• /
• pp.359-368
• /
• 2020

This study is aimed at improving the plasma resistance of Al₂O₃ ceramics on which plasma resistant YAS(Y₂O₃-Al₂O₃-SiO₂) frit is melt-coated using a simple heat-treatment process. For this purpose, the results of phase analysis and microstructural observations of the prepared YAS frits and the coating layers on the Al₂O₃ ceramics according to the batch compositions are compared and discussed with regard to the results of plasma resistance test. The prepared YAS frits consist of crystalline or amorphous or co-existing crystalline and amorphous phases according to the batch compositions, depending on the role and content of each raw material. The prepared YAS frit is melt-coated on the densely sintered Al₂O₃ ceramics, resulting in a dense coating layer with a thickness of at least ~ 80 ㎛. The YAS coating layer consists of crystalline YAG(Y₃Al₅O₁₂), Y₂Si₂O₇, and Al₂O₃ phases, and YAS glass phase. Plasma resistance of YAS coated Al₂O₃ ceramics is strongly dependent on the content of the YAG(Y₃Al₅O₁₂) and Y₂Si₂O₇ crystalline phases in the coating layer, especially on the content of the YAG phase. Comparing the weight loss of YAS coating ceramics with values obtained for commercial Y₂O₃, Al₂O₃, and quartz ceramics, the plasma resistance of the YAS coating ceramics is 6 times higher than that of quartz, 2 times higher than that of Al₂O₃, and 50 % of the resistance of Y₂O₃.

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.428-433
• /
• 1999

An objective of this study is to compare the characteristics of coating layer of plasma sprayed fine $Al_2O_3$ and those of layer by commercial $Al_2O_3$(Metco 105). The microstructure of fine $Al_2O_3$ coating layer was denser compared with commercial $Al_2O_3$ coating layer. The surface roughness$(R_a)$ of the layer by the fine $Al_2$O$_3$ was lower compared with that of commercial $Al_2O_3$. Thickness of splat for fine $Al_2O_3$ was $1.4\mu\textrm{m}$ while the commercial $Al_2O_3$ was $3.53\mu\textrm{m}$. The main phase existing in coating layer was of $\gamma-Al_2O_3$ and the fraction of $\alpha-Al_2O_3$ in fine $Al_2O_3$ coating layer was 8.39% and that of commercial $Al_2O_3$ was 13.79%. Microhardness was no great difference between the fine and commercial $Al_2O_3$ but deviation of the fine $Al_2O_3$ coating layer was relatively large. Accordingly, the strength of splat of the coating was expected that fine $Al_2O_3$was lower than commercial $Al_2O_3$ powder.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.160-167
• /
• 2011

Plasma sprayed ceramic coatings inherently contain pores and usually also cracks. Post-treatment of the plasma sprayed coatings is a way to close the connected pores and cracks. In this study, post-sealing treatment in plasma sprayed $Al_2O_3$ coatings was employed to overcome the reduction of coating properties. $Al_2O_3$ plasma thermal spray coating was made on aluminum alloys plate, $CrO_3$ post coating and heat treatment at $550^{\circ}C$ was carried out in order for final $Cr_2O_3$ to be saturated through phase transformation. Chromia sealing began at the fine defect in coated microstructure, while larger pores were permeated later. The increase in concentration and treatment frequency of sealing solution resulted in the decrease of porosity of coating layer, while cracks occurred partially after the third treatment. After twice treatment of 10M $CrO_3$ solution, microhardness and breakdown voltage of $Al_2O_3$ coatings were found to increase by ${\fallingdotseq}$ 50% and ${\fallingdotseq}$ 390% respectively than without post-treatment.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1087-1093
• /
• 1999

Bioglass which is one of the surface active bionmaterials has a good biocompatibility but a poor mechanical strength, In the present work therefore two types of fluoride-containing bioglasses were coated on an alumina to improve mechanical strength. Crystallization of the coating layer and the hydroxyapatite formation on the bioactive glass coatings in tris-buffer solution were studied. When bioactive glass coated alumina was heat-treated Na2CaSi3O8 crystal was formed on the layer at lower temperature while wollastonite(CaSIO3) was obtained at higher temperature. Hydroxyapatite forming rate on the coating layer with Na2CaSi3O8 crystal was delayed with SiO2 contents in glass composition. However the hydroxyapatite was developed in 20minutes regardless SiO2 contents when the coating layer crystallized into wollastonite. More amount of P3+ ions were leached out of the coating layer with wollastonite than that with Na2CaSi3O8 crystal while Na+ and Ca2+ ions were leached out more easily from the Na2CaSi3O8 crystal containing coating layer.