• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.74.1-74.1
• /
• 2000

• 한국전기전자재료학회논문지
• /
• 제24권3호
• /
• pp.194-199
• /
• 2011

In this study, non-stoichiometric 1-x$[(K_{0.5}Na_{0.5})_{0.97}(Nb_{0.96}Sb_{0.04})O_3]$ + x $CeMnO_3$ + 0.8 mol%CuO + 0.2 wt% $Ag_2O$ (x=0, 0.005) ceramics were prepared by a conventional mixed oxide and carbonate method, their dielectric and piezoelectric properties were investigated with the variations of sintering temperature. As $CeMnO_3$ substitution incereased, the density, piezoelectric constant($d_{33}$) and dielectric constant($\varepsilon_r$) were increased and the mechanical quality factor(Qm) was decreased. At the sintering temperature of $1100^{\circ}C$, the density, electromechanical coupling factor($k_p$), dielectric constant($\varepsilon_r$) and piezoelectric constant($d_{33}$) of 0.5mol% $CeMnO_3$ specimen showed the optimun values of 4.475 $g/cm^2$, 0.437, 552 and 166 pC/N, respectively. However, the mechanical quality factor($Q_m$) showed the minimum value of 380.

• 한국자기학회지
• /
• 제2권3호
• /
• pp.222-227
• /
• 1992

소량의 $V_2O_5$ 첨가가 Mn-Zn 훼라이트의 치밀화, 미세조직 및 자기적 성질에 미치는 영향에 대하여 연구하였다. 최대밀도는 0.1 wt% $V_2O_5$ 첨가시 관측되며, $V_2O_5$ 첨가는 불균일입자성장을 억제하는 것으로 확인되었다. 초투자율은 0.1 wt% $V_2O_5$ 첨가시 최대값을 나타내었고, 손실은 0.03 wt% $V_2O_5$ 첨가시 최소값을 나타내었다. 소량의 $V_2O_5$ 는 Mn-Zn 훼라이트에 고용되지만, 일정량 이상이 되면 2차상을 형성하여 입계에 편석하였다.

• 청정기술
• /
• 제17권1호
• /
• pp.41-47
• /
• 2011

순수한 $MnO_2$ 산화물을 과망간산칼륨과 망간아세테이트를 사용하여 침전법으로 제조하였고 소성온도를 달리하여 CO 산화반응을 수행하였다. 촉매의 물리화학적 특성을 알아보기 위하여 XRD, $N_2$ 흡착, $H_2-TPR$, CO-TPD 등의 특성분석을 수행하였다. $MnO_2$-300 촉매는 9nm 크기 근처의 좁은 기공크기 분포로 존재하며 $181m^2/g$의 높은 비표면적을 보였다. XRD와 $H_2-TPR$ 분석으로 $MnO_2$ 촉매는 $Mn^{4+}$와 $Mn^{3+}$의 산화상태임을 확인하였다. CO-TPD 분석으로 소성온도가 높아질수록 탈착되는 $CO_2$의 양이 감소하는 것을 확인하였다. $MnO_2$ 촉매의 소성온도에 따른 최적 활성에서는 $300^{\circ}C$에서 소성한 촉매가 가장 좋은 활성을 나타냈으며, $200^{\circ}C$ 이하에서 100%의 CO 전환율을 보였다. 수분 존재하의 CO 산화반응은 활성점에 $H_2O$와 CO의 경쟁 흡착으로 촉매의 활성을 감소시켰으며 수분제거 시 활성이 건조조건과 동일하게 회복되었다.

• 한국세라믹학회지
• /
• 제46권2호
• /
• pp.219-223
• /
• 2009

Effects of MgO or $R_2O_3$(R:Dy, Ho, Yb) on the capacitance aging behavior of multilayer ceramic capacitors (MLCCs) based on $BaTiO_3$ dielectrics under DC electrical fields has been studied. At a DC field of 1 $V{/\mu}m$, the capacitance of MLCC specimens dropped immediately in a very short period (<10 s, the first stage) and then decreased continuously with time (the second stage). Mn doping significantly increased the aging rate in the second stage. The addition of MgO or $R_2O_3$ notably decreased the second stage aging rate of Mn-doped specimens. Yb doping gives rise to the lowest aging rate in the second stage, which is due to the larger population of defect dipoles associated with oxygen vacancies.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.746-748
• /
• 2002

The effect of $MnO_2$ addition in $0.05Pb(Sn_{0.5}Sb_{0.5})O_3-0.8PbZrO_3-0.15PbTiO_3$(0.05PSS-0.8PZ-0.15PT) ceramics on crystal structure and electrical properties were studied. The sintering temperature and time were $1230^{\circ}C{\sim}1270^{\circ}C$ and 2hr, respectively. Then crystal structure, dielectric and pyroelectric properties were investigated. All the poled specimens showed the lower dielectric constant and $tan{\delta}$ than the unpoled specimens. Dielectric constant at 1kHz of the 0.05PSS-0.8PZ-0.15PT(MnO2 0.3wt%) system specimen sintered at $1250^{\circ}C$ for 2hr were 270 and showed the lowest $tan{\delta}$ of 0.2% after poling of $2kV_{DC}/mm$ at $150^{\circ}C$ for 30 minutes. Pyroelectric coefficient was maximum value of $50nC/cm^2K$ and Curie temperature was $224^{\circ}C$.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.132.2-132.2
• /
• 2000

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.87.2-87.2
• /
• 2000

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.181.2-181
• /
• 2000

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2002년도 추계총회 및 연구발표회 초록집
• /
• pp.184.2-184
• /
• 2002