• Journal of the Korean Ceramic Society
• /
• v.40 no.6
• /
• pp.608-614
• /
• 2003

Well developed hydroxyapatite whiskers (length 5 ${\mu}{\textrm}{m}$, diameter 0.5 ${\mu}{\textrm}{m}$) have been synthesized by the hydrolysis reaction of $\alpha$-tricalcium phosphate ($\alpha$-Ca$_3$(PO$_4$)$_2$) under pH 9.1 at 9$0^{\circ}C$ for 6 h. The effect of reaction conditions (temperature, time, pH) on the conversion of $\alpha$-tricalcium phosphate to hydroxyapatite was examined. In addition, the hydroryapatite was characterized in terms of microstructure, composition and thermal stability using XRD, SEM, ICP, and TGA instruments.

• Carbon letters
• /
• v.8 no.2
• /
• pp.95-100
• /
• 2007

A series of activated carbons (ACs) were derived from sugarcane bagasse under two activation schemes: steam-pyrolysis at $600-800^{\circ}C$ and chemical activation with $H_3PO_4$ at $500^{\circ}C$. Some carbons were treated at 400, $600^{\circ}C$, or for 1-3 h, and/or in flowing air during pyrolysis of acid-impregnated mass. XRD profiles displayed two broad diffuse bands centered around $2{\theta}=23$ and $43^{\circ}$, currently associated with diffraction from the 002 and 100/101 set of planes in graphite, respectively. These correspond to the interlayer spacing, Lc, and microcrystallite lateral dimensions, La, of the turbostratic (fully disordered) graphene layers. Steam pyrolysis-activated carbons exhibit only the two mentioned broad bands with enhancement in number of layers, with temperature, and small decrease in microcrystallite diameter, La. XRD patterns of $H_3PO_4$-ACs display more developed and separated peaks in the early region with maxima at $2{\theta}=23$, 26 and $29^{\circ}$, possibly ascribed to fragmented microcrystallites (or partially organized structures). Diffraction within the $2{\theta}=43^{\circ}$ is still broad although depressed and diffuse, suggesting that the intragraphitic layers are less developed. Varying the conditions of chemical activation inflicts insignificant structural alterations. Circulating air during pyrolysis leads to enhancement of the basic graphitic structure with destruction and degradation in the lateral dimensions.

• The Korean Journal of Food And Nutrition
• /
• v.25 no.3
• /
• pp.677-684
• /
• 2012

A bacterium strain GS-2 isolated from the Korean traditional seasoning food, Chungkookjang and was determined to produce large amounts of ${\gamma}$-PGA with high productivity when provided with simple nutrients (L-glutamic acid 2.0%, glucose 1.0%, $NH_4Cl$ 0.5%, $KH_2PO_4$ 0.05%, $MgSO_4{\cdot}7H_2O$ 0.01%, pH 7.0). In this study, the culture medium for this strain was optimized for the production of ${\gamma}$-PGA. The Bacillus subtilis GS-2 required supplementation with L-glutamic acid and other nutrients for maximal production of ${\gamma}$-PGA. The optimal culture conditions for ${\gamma}$-PGA production were a 48 hr culture time, a temperature of $33^{\circ}C$ and initial pH of 6.5 by rotary shaking (220 rpm). A maximum ${\gamma}$-PGA production of 31.0 $g/{\ell}$ was obtained with L-glutamic acid (30 $g/{\ell}$), sucrose (the main carbon source, 30 $g/{\ell}$), $NH_4Cl$ (the main nitrogen source, 2.5 $g/{\ell}$), $KH_2PO_4$ (1.5 $g/{\ell}$) and $MgSO_4{\cdot}7H_2O$ (0.15 $g/{\ell}$) in the culture medium.

• Journal of Korean Society of Environmental Engineers
• /
• v.33 no.4
• /
• pp.231-236
• /
• 2011

The effects of magnesium and calcium ions on phosphorus removal by aluminium coagulation were investigated with various jar tests using settled raw sewage. Maximum TP (total phosphate) removal occurred at pH around 5~6 with aluminium coagulation, and it decreased above pH 6. TP and $H_nPO_4^{n-3}$ removal efficiencies, however, were kept above 95% at pH above 6 by adding the divalent metallic ions like magnesium or calcium ions on aluminium coagulation process. At molar ratio of Al/P ($Al^{3+}/H_nPO_4^{n-3}$) above 3, TP removal efficiency was as high as 80%, and residual TP less than 0.2 mg/L occurred at Al/P ratio above 6. TP removal efficiency was improved by adding magnesium or calcium ions and the optimum $Al^{3+}/Mg^{2+}$ and $Al^{3+}/Ca^{2+}$ ratios were about 2. The required dose of aluminium coagulant was reduced for equivalent amount of TP removal by adding magnesium or calcium ions, as a result sludge generation was also reduced.

• Korean Journal of Food Science and Technology
• /
• v.21 no.5
• /
• pp.619-623
• /
• 1989

The cultural condition of Pseudomonas mendocina for polysaccharide production was examined. The optimal medium contains following composition per liter of distilled water: Sucrose 23.75g, $(NH_4)_2SO_4$ 1.57g, Yeast extract 0.5g, $KH_2PO_4\;2.9g,\;MgSO_4.\;7H_2O\;1.0g,\;CaCO_3$ 2.5g. The optimum temperature and pH were $30^{\circ}C$ and 6.5. At the condition. Ps mendocina produced 5.98g/l of polysaccharide. The culture viscosity after 3 days was 191mPa.s at $70sec^{-1}$. The product yield $(Y_{p/s})$ and specific productivity $(Q_p)$ were 25.18% and 32.83mg/g-cell/h.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.46-52
• /
• 1991

The hydroxyapatite powders were prepared by the reaction of Ca(CH3COO)2$.$H2O and H3PO4 in aqueous solution. Effect of Ca/P mole ration and pH value on the powder characteristics were investigated. For phosphoric acid was dissociated to PO43- ion above pH 10, the preparation condition of hydroxyapatite by H3PO4 solution had this value. Dried powders were agglomerated each other. The mean agglomerate particle diameter was minimum when the condition was pH 11, Ca/P=1.75 and its specific surface area was 97㎡/g. All powders had poor crystallinity and small CO2. It prevented CaCO3 from using aspirator in preparation and maturing time. In most cases, hydroxyapatite was decomposed into ${\beta}$-TCP at more than 800$^{\circ}C$, into ${\alpha}$-TCP at 1200$^{\circ}C$. However non-decomposed hydroxyapatite was remained in Ca/P=1.85.

• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.179-184
• /
• 2002

Polymer electrolyte films consisting of poly (vinylidenefluoride-hexafluoro-propylene) (PVdF-HFP) $H_3PO_4$and a mixture of ethylene carbonate(EC), $\gamma$-butyrolactone(BL) and dimethylcarbonate (DMC) were examined in order to obtain the best compromise between high protonic conductivity, homogeniety and dimensional stability. Measurements of differential scanning calorimetry and ionic conductivity have been carried out for various compositions. The highest proton conductivity of 7.3 $\times$$10^{-3}Sm^{-1}$ at $30^{\circ}C$ were obtained for a film of 30(PVdF-HFP) + 50EC/DMC + 20H$_3$PO$_4$. From the thermal study, it has been found that the PVdF-HFP gels are stable up to $80^{\circ}C$, and the $H_3PO_4$ enhances the miscibility of the polymer and the solvent by interacting sensitively with polymer segments.

• Journal of the Korean Chemical Society
• /
• v.39 no.1
• /
• pp.1-6
• /
• 1995

The surface of a sapphire substrate used for hetero-epitaxy was chemically polished in a mixture of $H_3PO_4\;and\;H_2SO_4$ solution. The extent of etching for various crystal orientations was found to be dependent on the etching time at $315{\pm}2^{\circ}C$ and at the composition of $H_2SO_4 : H_3PO_4$=3 : 1. In addition, the etching rates of the substrates were investigated in the mixture of $H_2SO_4 : H_3PO_4$=3 : 1 by volume and in the temperature range of 280~320$^{\circ}C$. From the plot of log R against 1/T, the activation penergy ($(E_a)$) was found to be in the order of $({\bar1}012) > (10{\bar1}0) > (11{\bar2}0) > (0001)$ plane. After removing the surface layers of the sapphire with (0001), $({\bar1}012),\;(10{\bar1}0)\;and\;(11{\bar2}0)$ plane by a thickness of 64.6, 46.5, 16.2 and 5.1 ${\mu}m$, respectively, the morphology of the resulting surface was observed by SEM.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.747-749
• /
• 2002

Hydroxyapatite powders were prepared after heating at $1250^{\circ}C$ by the direct reaction using oyster shells and $H_3$$PO_4$. Properties of hydroxyapatite powders were investigated as XRF, XRD, DTA, FT-IR, SEM. Only hydroxyapatite was observed in XRD powders which was heated at $1250^{\circ}C$ for 2 hours and there was no remained CaO in that sample. And the results of FT-IR of sample was confirmed hydroxyapatite. Sample was agglomerated together, but needle shape morphology was observed in powders heated at $1250^{\circ}C$.

• Journal of the Korean Magnetic Resonance Society
• /
• v.17 no.1
• /
• pp.19-23
• /
• 2013

The temperature dependences of the NMR spectrum and the spin-lattice relaxation times in $KH_2PO_4$ were investigated via single-crystal NMR and MAS NMR. The stretched-exponential relaxation that occurred because of the distribution of correlation times was indicative of the degree of the distribution of the double-well potential on the hydrogen bond. The behaviors responsible for the strong temperature dependences of the $^1H$ and $^{31}P$ spin-lattice relaxation times in the rotating frame $T_{1{\rho}}$ in $KH_2PO_4$ are likely related to the reorientational motion of the hydrogen-bond geometry and the $PO_4$ tetrahedral distortion.