• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1885-1887
• /
• 1999

본 연구에서는 $BaTiO_3$를 기본조성으로하는 반도성 세라믹스인 PTC 써미스터에 $Nb_2O_5$을 미량 첨가하여 미세구조 및 PTCR의 전기적 특성에 대해서 연구하였다. 또한 복소 임피던스 측정을 통하여 $Nb_2O_5$ 첨가에 따른 grain, grain boundary 저항변화에 대해서도 고찰하였다. $(Ba_{0.9}Sr_{0.05}Ca_{0.05})TiO_3-0.01SiO_2-0.001MnCO_3$를 기본조성으로 하여 $Nb_2O_5$ 첨가량을 $0.15{\sim}0.2mol%$까지 변화시켰으며 소결조건은 소결온도 $1350^{\circ}C$, 2h 유지하였으며 냉각속도는 $100^{\circ}C/h$로 하였다 첨가된 Nb의 양이 증가할수록 grain의 크기는 점차로 작아졌으며 상온저항과 peak 저항이 함께 증가하였다. 0.15mol% 첨가된 시편의 경우 상온저항은 $19[\Omega]$이었으며 peak 저항은 $5{\times}10^6[{\Omega}]$정도가 되었다.

• Journal of Surface Science and Engineering
• /
• v.35 no.6
• /
• pp.383-390
• /
• 2002

To investigate behaviors of Ti and O elements and microstructures of anodic titanium oxide films, the films were prepared by anodizing pure titanium in $H_2$S $O_4$, $H_3$P $O_4$, and $H_2O$$_2$ mixed solution at 180V. The microstructures and chemical states of the elements were analyzed using SEM, X-ray mapping, AFM, XRD, XPS (depth profile). The films formed on a titanium substrate showed porous layers which were composed of pore and wall, And with increasing anodizing time a hexagonal shape of cell structures were dominant and solace roughness increased. From the XRD result the structure of the Ti $O_2$ layer was anatase type of crystal on the whole. In the XPS spectra it was found that Ti and O were chemically binded in forms of Ti $O_2$, TiOH, $Ti_2$ $O_3$ at Ti 2p, and Ti $O_2$, $Ti_2$ $O_3$, $P_2$ $O_{5}$, S $O_4^{2-}$ at O ls respectively. Concentration of Ti $O_2$ decreased as the depth increased from the surface of the oxide film towards the substrate, but to the contrary concentrations of TiOH and $Ti_2$ $O_3$ increased.d.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.4
• /
• pp.445-450
• /
• 1999

Molecular dynamics (MD) simulation of non-rigid H-Y zeolite framework are performed at 298.15 and 5.0 K. Usual bond stretching, bond angle bending, torsional rotational, and non-bonded Lennard-Jones and electrostatic interactions are considered as intraframework interaction potentials. Calculated atomic parameters are in good agreement with the experiment, which indicates the successful reproduction of the framework structure and its motion. Both calculated bond lengths and bond angles are also in good agreement with the experiment except generally for a little longer bond lengths and a little smaller T-O-H bond angles. The calculated overall site occupation of HI keeps the order O(2) > O(3) > O(4) > O(t) at 298.15 K, which is very different from the experimental prediction, O(l) > O(3) > O(2) at 5 K. Calculated IR spectra of the H-Y zeolite framework show that most of the main peaks of the O-H bonds are in the broad region 3700-5000 cm-1 and that the O-T stretching bands appeared in 0-2000 cm-1 and at 2700 cm-1

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.40 no.11
• /
• pp.1556-1561
• /
• 2011

The purpose of this study was to investigate antioxidant enzyme activity and vitamin E concentrationin in Sprague-Dawley rat after being fed various extracts of Hizikia fusiforme. There were six experimental groups: control group (C), H. fusiforme ethanol extract group (EtOH), H. fusiforme dichloromethane fraction group ($CH_2Cl_2$), H. fusiforme ethylacetate fraction group (EtOAc), H. fusiforme butanol fraction group (n-BuOH), H. fusiforme water fraction group ($H_2O$). H. fusiforme extracts (400 mg/kg B.W) were orally administrated to the rats every day for 4 weeks. The activities of superoxide dismutase (SOD), catalase, glutathione peroxidase (GSH-Px), and concentrations of malondialdehyde (MDA) and vitamin E in the liver and blood were measured. The activity of SOD in the liver was significantly higher in the $CH_2Cl_2$ and $H_2O$ groups (p<0.05) than in the control and other extract groups. The SOD activity in serum increased significantly in all H. fusiforme groups (p<0.05) compared to the control group and it was also significantly higher in the EtOH and $H_2O$ groups (p<0.05) than in other extract groups. The serum catalase activity increased significantly in the n-BuOH group (p<0.05) compared to the control and other extract groups. The plasma MDA concentration decreased significantly in the n-BuOH and $H_2O$ group (p<0.05) compared to the control group. Serum concentration of ${\alpha}$-tocopherol showed no significant differences in most of the experimental groups, but it was significantly higher in the EtOAc group (p<0.05). The ${\alpha}$-tocopherol concentrations in the liver showed a significant increase in the $CH_2Cl_2$ and $H_2O$ groups (p<0.05) compared to the control and other extract groups. The liver ${\gamma}$-tocopherol concentrations in H. fusiforme extract groups showed a tendency to increase compared to the control group and it was significantly higher in the $H_2O$ group (p<0.05) than in other extract groups. These results suggest that supplementation of water extracts of H. fusiforme extract could be effective in improving the antioxidant system.

• Journal of Surface Science and Engineering
• /
• v.50 no.4
• /
• pp.296-300
• /
• 2017

NiO nanofibers with Au nanoparticles were synthesized by sol-gel and electrospinning techniques, in which the reduction process by ultraviolet exposure is included for the growth of Au nanoparticles in the electrospinning solution. FE-SEM(Field Emission Scanning Electron Microscopy), TEM(Transmission Electron Microscopy) revealed that the synthesized nanofibers had the diameter of approximately 200 nm. X-ray diffraction showed the successful formation of Au-decorated NiO nanofibers. Gas sensing tests of Au-decorated NiO nanofibers were performed using reducing gases of CO, and $C_6H_6$, $C_7H_8$, $C_2H_5OH$. Compared to as-synthesized NiO nanofibers, the response of Au-loaded NiO nanofibers to CO gas was found to be about 3.4 times increased. On the other hand, the response increases were only 1.1-1.3 times for $C_6H_6$, $C_7H_8$, and $C_2H_5OH$.

• Analytical Science and Technology
• /
• v.28 no.3
• /
• pp.182-186
• /
• 2015

In this study, the porous CuO/MnO₂ catalyst was prepared through the co-precipitation process from an aqueous solution of potassium permanganate (KMnO₄), manganese(II) acetate (Mn(CH₃COO)₂·4H₂O) and copper(II) acetate (Cu(CH₃COO)₂·H₂O). The phase change in MnO₂ was analyzed according to the reaction molar ratio of KMnO₄ to Mn(CH₃COO)₂. The reaction mole ratio of KMnO₄ to Mn(CH₃COO)₂·4H₂O was varied at 0.3:1, 0.6:1, and 1:1. The aqueous solution of Cu(CH₃COO)₂ was injected into a mixed solution of KMnO₄ and Mn(CH₃COO)₂ to 10~75 wt% relative to MnO₂. The Cu ion co-precipitates as CuO with MnO₂ in a highly dispersed state on MnO₂. The physicochemical property of the prepared CuO/MnO₂ was analyzed by using the TGA, DSC, XRD, SEM, and BET. The different phase types of MnO₂ were prepared according to the reaction mole ratio of KMnO₄ to Mn(CH₃COO)₂·4H₂O. The results confirmed that the porous CuO/MnO₂ catalyst with γ-phase MnO₂ was produced in the reaction mole ratio of KMnO₄ to Mn(CH₃COO)₂ as 0.6:1 at room temperature.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.424-429
• /
• 2009

The effects of $Na_2O$, $SiO_2$ and $H_2O$ contents of the synthetic mixtures prepared from water glass on the crystallinity and crystallite size of sodalite were studied. The composition of the synthetic mixtures described by $x\;Na_2O{\cdot}y\;SiO_2{\cdot}Al_2O_3{\cdot}z\;H_2O$ was varied within x=2.5~7.5, y=1.4~3.0, z=140~400. The hydrothermal reaction was carried out at $140^{\circ}C$ for 2 days. High content of $Na_2O$ resulted in the high crystallinity and small crystallite of sodalite. The $SiO_2/Al_2O_3$ molar ratios of around 2 were suitable for the synthesis of sodalite, and produced zeolite species were varied by the $H_2O$ content. Sodalite was mainly obtained with a high crystallinity from the synthetic mixtures with $SiO_2/Al_2O_3$ molar ratio of around 2 and high content of $Na_2O$. The high content of sodium ions caused a decrease in the particle sizes because of their role of structure directing agent.

• Biomolecules & Therapeutics
• /
• v.4 no.4
• /
• pp.402-407
• /
• 1996

Effects of oxidative stress on the induction of apoptosis and the activity of antioxidant enzymes were investigated in HL-60 cells using $H_2O$$_2$and cisplatin which generate oxygen species in the cell. Various concentrations of oxidants were treated to cells and at different incubation time, cells were harvested for assays. Cell viability, morphology by propidium iodide staining and DNA fragmentation by agarose gel electrophoresis were observed to determine whether they induce apoptosis. The activity of antioxidant enzymes such as superoxide dismutase and catalase was also measured to evaluate the cellular response to the oxidative damage. The results are as follows: $H_2O$$_2$ induced apoptosis at 10 $\mu$M after 6h incubation, while it took 12h for cisplatin. Both oxidants induced the superoxide dismutase activity at a tolerable low concentration. However, at a concentration which causes apoptotic cell death, the enzyme level was dropped markedly at first and then recovered to the normal level after which it declined again, probably due to cell death. On the other hand, changes in the activity of catalase were not significant at most concentrations except the statistically significant decrease at 24h after 10 $\mu$M-$H_2O$$_2$treatment. In this study, $H_2O$$_2$- and cisplatintreated cells showed similar results in apoptotic response and enzyme activities, suggesting that anticancer activity of cisplatin may be related, at least in part, to the production of oxygen free radicals.

• Journal of the Korean Magnetics Society
• /
• v.10 no.1
• /
• pp.37-41
• /
• 2000

We investigated the magnetoresistance effect and the exchange coupling of antiferromagnetic Fe$_2$O$_3$ spin-valve film. The X-ray diffractions of the spin-valve films having a different thickness of a $\alpha$-Fe$_2$O$_3$ were measured. The exchange coupling field (H$_{ex}$) between Fe$_2$O$_3$ and pinned NiFe layer was increased from 13.5 Oe to 84.5 Oe, as the thickness of Fe$_2$O$_3$ increased from 400 $\AA$ to 800 $\AA$. The surface roughness of $\alpha$-Fe$_2$O$_3$spin-valves increased with the increase of $\alpha$-Fe$_2$O$_3$thickness. Therefore, the increase of H$_{ex}$ will be due to the increase of the interface roughness. The MR ratios as a function of Fe$_2$O$_3$ thickness was not changed. And H$_{ex}$ increased by the increment of magnetostatic coupling between Fe$_2$O$_3$ and NiFe (pinned-layer) due to the increment of interface roughness. H$_{ex}$ depends on the surface roughness, but the magnetoresistance ratio doesn't doesn't.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.635-639
• /
• 1991

Monolithic gels in the ZrO2-SiO2 system containing up to 30 mol% ZrO2 were prepared from the mixed solutions of Zr(O.nC3H7)4 and partially prehydrolyzed Si(OC2H5)4 (Tetraethyl orthosilicate) by the sol-gel method. The effect of parameters such as the hydrolysis temperature, the amount of water and HCl on the hydrolysis condensation process was investigated and the obtained gels were studied by the IR spectra and TG-DTA. The results showed that the gelation time becomes shorter with increasing content of HCl, H2O and gelation temperature, and that the polymerization was more easily completed with the higher water volume causing the elimination of unreacted organic groups.