• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.130-136
• /
• 2005

The effects of additional Mg content, the size and volume fraction of reinforcement phase on the mechanical properties of ceramic particle reinforced aluminium matrix composites fabricated by pressureless metal infiltration process were investigated. The hardness of $SiC_p/AC8A$ composites increased gradually with an increase in the additive Mg content, while the bending strength of $SiC_p/AC8A$ composites increased with an increase in additive Mg content up to 5%. However, this decreased when the level of additive Mg content was greater than 5% due to the formation of coarse precipitates by excessive Mg reaction and an increase in the porosity level. The hardness and strength of the composites increased with decreasing the size of SiC particle. It was found that the composites with smaller particles enhanced the interfacial bonding than those with bigger particles from fractography of the composites. The hardness of $Al_2O_{3p}/AC8A$ composites increased gradually with an increase in the volume fraction, however, the bending strength of $Al_2O_{3p}/AC8A$ composites decreased when the volume fraction of alumina particle was greater than 40% owing to the high porosity level.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.103-107
• /
• 2003

Aluminum-based $Al/Al_2O_3$ composites were fabricated by a powder-in sheath rolling method. A stainless steel tube with outer diameter of 12 mm and wall thickness of 1 mm was used as a sheath. A mixture of aluminum powder and $Al_2O_3$ particles of which volume content was varied from 5 to 20%, was filled in the tube by tap filling and then rolled by 75% reduction in thickness at ambient temperature. The rolled specimen was then sintered at 56$0^{\circ}C$ for 0.5 h. The mixture of Al powders and $Al_2O_3$ particles was successfully consolidated by the sheath rolling. The $Al/Al_2O_3$ composite fabricated by the sheath rolling showed a recrystallized structure, while unreinforced Al powder compact fabricated by the same procedure showed a deformed structure. The unreinforced Al powder compact was characterized by a deformation (rolling) texture of which main component is {112}<111>, while the $Al/Al_2O_3$ composite showed a mixed texture oi deformation and recrystallization. The sintering resulted in recrystallization in Al powder compact and grain growth in the composite.

• Korean Journal of Metals and Materials
• /
• v.49 no.7
• /
• pp.583-588
• /
• 2011

$Cd_xZn_{1-x}O$ thin films were grown on quartz substrates by using the sol-gel spin-coating method. The mole fraction, x, of the $Cd_xZn_{1-x}O$ thin films was controlled from 0 to 1 by changes in the content ratio of the cadmium acetate dehydrate [$Cd{(CH_3COO)}_2{\cdot}2H_2O$] and zinc acetate dehydrate [$Zn{(CH_3COO)}_2{\cdot}2H_2O$]. The effects of the mole fraction on the morphological, structural, and optical properties of the $Cd_xZn_{1-x}O$ thin films were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and UV-visible spectroscopy. The $Cd_xZn_{1-x}O$ thin films exhibited the polygonal surface morphology and their grain size was increased ranging from 42.1 to 63.9 nm with the increase in the mole fraction. It was observed that the absorption bandgap of the $Cd_xZn_{1-x}O$ thin films decreased from 3.25 to 2.16 eV as the mole fraction increased and the Urbach energy ($E_U$) values changed inversely to the optical bandgap of the $Cd_xZn_{1-x}O$ thin films.

• Solar Energy
• /
• v.15 no.3
• /
• pp.15-27
• /
• 1995

This study presents experimental and numerical results of the temperature characteristics, the heat transfer phenomema, and the heat storage quantity during the heat storage process with sodium phyrophosphate decahydrate($Na_4P_2O_7{\cdot}10H_2O$)-Phase Change Material(PCM) in a latent heat storage tank(cubic type). It was proved that heat transfer by conduction was dominant because PCM($Na_4P_2O_7{\cdot}10H_2O$) during heating processes was gel phase, not liquid phase The gap ratio(rate of air content) of PCM became smaller, the thermal capacity of PCM became larger, therefore the temperature distribution of PCM slowly increased than that of large gap ratio. There was maximum 15% difference between measured temperatures and calculated temperatures.

• Korean Journal of Materials Research
• /
• v.23 no.1
• /
• pp.67-71
• /
• 2013

Porous $Al_2O_3$ dispersed with nano-sized Cu was fabricated by freeze-drying process and solution chemistry method using Cu-nitrate. To prepare porous $Al_2O_3$, camphene was used as the sublimable vehicle. Camphene slurries with $Al_2O_3$ content of 10 vol% were prepared by milling at $50^{\circ}C$ with a small amount of oligomeric polyester dispersant. Freezing of the slurry was done in a Teflon cylinder attached to a copper bottom plate cooled to $-25^{\circ}C$ while unidirectionally controlling the growth direction of the camphene. Pores were subsequently generated by sublimation of the camphene during drying in air for 48 h. The green body was sintered in a furnace at $1400^{\circ}C$ for 1 h. Cu particles were dispersed in porous $Al_2O_3$ by calcination and hydrogen reduction of Cu-nitrate. The sintered samples showed large pores with sizes of about $150{\mu}m$; these pores were aligned parallel to the camphene growth direction. Also, the internal walls of the large pores had relatively small pores due to the traces of camphene left between the concentrated $Al_2O_3$ particles on the internal wall. EDS analysis revealed that the Cu particles were mainly dispersed on the surfaces of the large pores. These results strongly suggest that porous $Al_2O_3$ with Cu dispersion can be successfully fabricated by freeze-drying and solution chemistry routes.

• Journal of the Korean Ceramic Society
• /
• v.12 no.4
• /
• pp.3-8
• /
• 1975

Hydration processes of the rapid hardening cement clinkers, which were synthesized from domestic alunite for major alumina source, limestone, kaolin and fluorite, were investigated by means of x-ray diffraction analysis, thermal analysis and microscopic observation etc. The clinkers were composed mainly of alite, calcium fluroaluminate (C11A7.CaF2) minerals. While the hydratio processes of the clinkers are altered by concentration of SO3 in the paste, calcium aluminate hydrates such as C4AH13, CAH10 and calcium monosulfate hydrate (C3A.CaSO4.12H2O) are formed at first and then some of them are transformed into ettringite(C3A.3CaSO4.32H2O) within 30~60 min. when the concentration of SO3 in the paste are enough. However the formed ettringite are changed slowly into calcium monosulfate hydrate as the concentration of SO3 become lowered, and the paste is hardened with these close-packed minerals. When the content of SO3 in clinker is so enough, calcium sulfoaluminate hydrates are found without any addition of anhydrite or hemi-hydrite.

• Resources Recycling
• /
• v.11 no.4
• /
• pp.27-36
• /
• 2002

The clinker of which main component was calcium-chloroaluminate ($l1CaOㆍ7Al_2$$O_3$ㆍ$CaCl_2$), was synthesized with the bottom ash of municipal solid waste incinerator ash. The hydration mechanism and synthesis temperature of calcium-chloro-aluminate were investigated. The synthesized clinker was blended with a cement. It was substituted with 3～13 wt.% for clinker and $CaSO_4$ of ordinary portland cement. The compressive strength and the content of leached heavy metals of its mortar were measured. Calcium-chloroaluminate was synthesized above $800^{\circ}C$ and its main hydrate was ettringite ($3CaOㆍAl_2$$O_3$ㆍ$3CaSO_4$ㆍ$32H_2$O). The calcium-chloroaluminate was also synthesized above $800^{\circ}C$ with the bottom ash of which size fraction was below 30 mesh mainly. The compressive strength of the blended cement mortar was increased as the additive content of the clinker synthesized from the bottom ash was increased by 11 wt.%. The concentration of heavy metals leached from each mortar was satisfied with the value of the environmental standards and regulations.

• Korean Journal of Materials Research
• /
• v.17 no.9
• /
• pp.480-483
• /
• 2007

Hydroxyapatites were prepared by the different $SiO_2$ addition at $1450^{\circ}C$ for 2h. With the increase of $SiO_2$ addition, microstructure, bulk density, porosity, mechanical strength of $hydroxyapatite/{\beta}-TCP$ composite were investigated. When the sintered HAp contained 1 wt% $SiO_2$, the each properties of the HAp were increased. But the excess addition of $SiO_2$ content above 1wt% the each property were decreased. This results were due to the ${\beta}-TCP$ phase. The ${\beta}-TCP$ phase appeared at 3 wt% $SiO_2$ addition and the ${\beta}-TCP$ phase was enhanced by the $SiO_2$ increasing.

• Applied Chemistry for Engineering
• /
• v.8 no.6
• /
• pp.939-944
• /
• 1997

The films of zeolite X on the surface of metal sieve were prepared by continuous crystallization method. It is known that the growth of zeolite crystal on the surface of metal is mainly dependent on the surface composition of metal sieve. In the present work, the zeolite nuclei could be easily formed as Cr content on the metal surface was removed by acid treatment. In order to investigate the proedure growing of zeolite crystal by the continuous crystallization method, the composition of zeolite X($6.36Na_2O-Al_2O_3-5.3SiO_2-190.8H_2O$)was supplied every 12hour. Then the mechanism and inter-relationship between the metal surface and nucleation are investigated. The results show that as the content of silica increases in the gel mixture, the nuclei of zeoilite are easily formed on the metal surface. Also, it was confirmed that the particle of zeolite stuck on the metal surface continues the linear growth. The particles are combined by the reaction of polycondensation, and finally become the shape of crystal. The sample synthesized by the film type was confirmed as zeolite X by the analyses of SEM and XRD.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.38-42
• /
• 2004

A pilot-scale experiment for the treatment of red tide in the enclosure was done in sea area of Shandong Province, P. R. China on Aug. 25, 2002. With the method of strong dielectric barrier discharge in microgap, $O_2$in air and $H_2O$ in seawater are ionized and dissociated into large numbers of OHㆍradicals, and then dissolved into a part of seawater to form OHㆍsolution of high concentration. With OH' concentration of 0.68mg/L, the kill efficiencies of 29 kinds of red tide organisms such as Chaetoceros lorenzianus and so on reached 99.89%, in which the kill efficiencies of bacterium and vibrio were 100%, and that of Gonyaulax cysts and Prei. Cysts were up to 100%. At the same time, the content of chlorophyll-a was decreased into the lowest limit of test. DO saturation of seawater was greatly increased to 100% because the residual OHㆍradical was decomposed into $H_2O$ and $O_2$after 20 minutes, Therefore the treatment of red tide using OHㆍradicals is a kind of advanced oxidation technology, which realizes zero pollution, zero emission and zero residual in the process of the production of OHㆍradicals and the treatment of red tide.