• E2M - 전기 전자와 첨단 소재
• /
• 제8권4호
• /
• pp.426-433
• /
• 1995

Effect of boron in GaAs have been investigated by photo induced current transient spectroscopy(PICTS). The starting material was undoped liquid encapsulated Czochralski(LEC) semi insulating GaAs and boron ion implantation at 150keV energy was conducted with dose of 10$\^$12/ and 10$\^$13/ions/cm$\^$2/. In ion implanted samples, the peaks related arsenic vacancy(V$\_$As/) were decreased but complex lattice defect was increased with annealing temperature. U band was observed at ion implanted(10$\^$13/ ions/cm$\^$2/) and thermally treated(550.deg. C) sample. More negative peak was detected after annealing at temperature between 600 and 700.deg. C. The measurement of dark current showed that the formation of B$\_$GA/-V$\_$As/, complex defect and complex lattice defect by ion implantation were a reasonable explanation for the decrease in dark current.

• 대한전자공학회논문지
• /
• 제26권12호
• /
• pp.1995-2000
• /
• 1989

The ion beam system of 20keV C-W (Cockroft Walton) type composed of the AuGe alloy LMIS(Liquid Metal Ion Source) has been designed and constructed. For the fabrication of the ohmic contact to the n-GaAs, the ion beam extracted from the AuGe alloy source was implanted into the n-GaAs, and it was measured by contact resistivity. The stable AuGe ion beam(2.5\ulcorner/cm\ulcorner was obtained at the extraction voltage of 14.5kV. The measurements of the contact resistivity were done by the TLM (Transmission Line Model) method and the specific contact resistivity was found to be 2.4x10**-5 \ulcornercm\ulcornerfor the implanted sample by the 1.9x10**20/cm**3 and the annealed sample at 30\ulcorner for 2 min.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2005년도 추계학술대회 논문집
• /
• pp.326-329
• /
• 2005

As a flexible method to fabricate sub-micrometer patterns, Focused Ion Beam (FIB) instrument and Self-Assembled Monolayer (SAM) resist are introduced in this work. FIB instrument is known to be a very precise processing machine that is able to fabricate micro-scale structures or patterns, and SAM is known as a good etch resistance resist material. If SAM is applied as a resist in FIB processing fur fabricating nano-scale patterns, there will be much benefit. For instance, low energy ion beam is only needed for machining SAM material selectively, since ultra thin SAM is very sensitive to $Ga^+$ ion beam irradiation. Also, minimized beam spot radius (sub-tens nanometer) can be applied to FIB processing. With the ultimate goal of optimizing nano-scale pattern fabrication process, interaction between SAM coated specimen and $Ga^+$ ion dose during FIB processing was observed. From the experimental results, adequate ion dose for machining SAM material was identified.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1246-1249
• /
• 1994

Thin amorphous film of $a-Se_{75}Ge_{25}$ acts as a positive resist in ion beam lithography. Previously, we reported the optical characteristics of amorphous $Se_{75}Ge_{25}$ thin film by the low-energy ion beam exposure and presented analytically calculated values such as ion range, ion concentration and ion transmission coefficient, etc. As the calculated results of analytical calculation, the energy loss per unit distance by $Ga^+$ ion is about $10^3[keV/{\mu}m]$ and nearly constant for all energy range. Especially, the projected range and struggling for 80 [KeV] $Ga^+$ ion energy are 0.0425[${\mu}m$] and 0.020[${\mu}m$], respectively. Hear, we present the results of Monte-Carlo computer simulation of Ga ion scattering, exposure and development in $a-Se_{75}Ge_{25}$ resist film for focused ion beam(FIB) lithography. Monte-Carlo method is based on the simulation of individual particles through their successive collisions with resist atoms. By the summation of the scattering events occurring in a large number N(N>10000) of simulated trajectories within the resist, the distribution for the range parameters is obtained. Also, the deposited energy density and the development pattern by a Gaussian or a rectangular ion beam exposure can be obtained.

• 한국진공학회지
• /
• 제1권1호
• /
• pp.121-125
• /
• 1992

Secondary Ion Mass Spectrometry (SIMS) is widely known as highly sensitive a surface analysis technique. Efforts for quantification have been hindered, however, by the presence of matrix effects. Here we describe a new technique for the quantitative analysis of AlxGa1-xAs. Instead of Al+, Ga+, As+ ions, CsX+ ions (X=Al, Ga, As) have been detected. Intensity of these molecular ions appears to be much less affected by matrix effects. We have successfully accomplished the compositional analysis with standard deviation better than 2 percent.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2009년도 춘계학술대회 논문집
• /
• pp.363-364
• /
• 2009

• 한국표면공학회지
• /
• 제32권2호
• /
• pp.83-92
• /
• 1999

GaN etching was performed using planar inductively coupled $Cl_2$-based plasmas and the effects of main process parameters on the characteristics of the plasmas and their relations to GaN etch rates were studied. Also, the GaN etch mechanism was investigated using a Langmuir probe and optical emission spectroscopy (OES) during the etching, and X-ray photoelectron spectroscopy (XPS) of the etched surfaces. The GaN etch rates increased with the increase of chlorine radical density and ion energy, and a vertical etch profile haying the etch rate close to 4000 $\AA$/min could be obtained. The addition of 10% Ar to $Cl_2$ gas increased the GaN etch rate and the addition of Ar (more than 20%) and HBr generally reduced the GaN etch rate. The GaN etch rate appeared to be more affected by the chemical reaction between Cl radicals and GaN compared to the physical sputtering itself under the sufficient ion bombardments to break GaN bonds.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권4호
• /
• pp.203-209
• /
• 2000

This paper proposes the improvement of the etch rate of GaN using a magnetized inductively coupled $CH_4/H_2/Ar$plasma. The gradient magnetic field with the axial direction is investigated using Gauss-meter and the ion current density is measured using double Langmuir probe. The applied magnetic field changes the ion current density profile in the radial direction, resulting in producing the higher density in the outer region than in the center. GaN dry etching process is carried out based on the measurements of the ion current density. The each rate of 2000 /min is achieved with $CH_4/H_2/Ar$ chemistries at 800 W input power, 250W rf bias power, 10 mTorr pressure and 100 gauss magnetic field.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권4호
• /
• pp.372-378
• /
• 1996

The phtoreflectance(PR) spectra of B ion implanted semi-insulating(SI) GaAs were studied. Ion implantation was performed by 150keV implantation energy and 1*10/aup 12/-10$^{15}$ ions/c $m^{2}$ doses. Electronic band structure was damaged by ion implantation with above 1*10$^{13}$ ions/c $m^{2}$ dose. When samples were annealed, " peak was observed at 30-40meV below band gap( $E_{g}$). It should be noted that this energy is close to the ionization energies of S $i_{As}$ , and GeAs in G $a_{As}$ which are also found as impurities in LEC GaAs, it is therefore possible that this feature is related to S $i_{As}$ , or G $e_{As}$ and B ions by implanted defect associated with them. From PR spectra of etched samples which is as-implanted by 1*10$^{14}$ and 1*10$^{15}$ ions/c $m^{2}$ dose, the depth of destroyed electronic band structure was from surface to 0.2.mu.m below surface.nic band structure was from surface to 0.2.mu.m below surface.

• 대한전자공학회논문지
• /
• 제26권6호
• /
• pp.63-70
• /
• 1989

액체금속이온원으로 부터 발생한 AuGe 이온빔을 GaAs기판에 주입시킨 후 이 시료의 표면성분과 구조를 AES(Auger electron spectroscopy), RHEED(reflection high energy electron diffraction), SEM(scanning electron microscopy) and EPMA(electron probe microanalysis)등으로 조사하였으며 AES depth profile 실험결과를 이체충돌에 의한 Monte Carlo simulation과 비교하였다. AuGe 이온이 주입된 시료를 AES, EPMA로 측정한 결과 As의 preferential스피터링이 나타났으며 300$^{circ}$C로 열처리하면 Ga과 outdiffusion되었다. 또한 측정한 Au와 Ge의 depth profile은 이체충돌에 의한 Monte Carlo simulation의 결과와 잘 일치하였다.