• Journal of the Korean Ceramic Society
• /
• v.36 no.5
• /
• pp.465-470
• /
• 1999

Sensing properties of $\alpha$-Fe2O3 thin film to reducing gases such as CHx and CO were systematically examined after deposition on Al2O3 substrate by PECVD(Plasma Enhanced Chemical Vapor Deposition)technique. Microstructure of deposited $\alpha$-Fe2O3 thin film showed the porous island structure. This specimen was annealed at 450, 550, $650^{\circ}C$ to enhance the gas sensing properties and investigated in terms of CO and C4H10 concentration from 500ppm to 3,000 ppm at operating temperature of 35$0^{\circ}C$ The gas sensitivity(%) to C4H10 measured at the operating temperature of 35$0^{\circ}C$ was 98.24 (highest sensitivity) 69.51 to CO and 2% to CH4 respectviely.

• Korean Journal of Metals and Materials
• /
• v.47 no.6
• /
• pp.378-382
• /
• 2009

We investigated the effects of deposition conditions on the fabrication of $Fe_{3}O_{4}$ thin films using a reactive DC magnetron sputtering at room temperature. The structural, electrical, and magnetic properties of Fe oxide films dependence on the film thickness, oxygen flow rate, and the substrate crystallinity were also studied. We have successfully fabricated $Fe_{3}O_{4}$ film with thickness of about 10 nm under optimal reactive sputtering conditions. The saturation magnetization, resistivity, and Verwey transition of the $Fe_{3}O_{4}$ film were298 emu/cc, $4.0{\times}10^{-2}{\Omega}cm$, and 125 K, respectively.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1997.06a
• /
• pp.79-85
• /
• 1997

Fe$_2$O$_3$ thin films were prepared on $Al_2$O$_3$ substrate by PECVD(Plasma-Enhanced Chemical Vapor Deposition) process. The phase transformation of iron oxide film was determined as the substrate temperature and reduction-oxidation process. $\alpha$-Fe$_2$O$_3$ was stable in deposition temperature ranges of 80~15$0^{\circ}C$. Fe$_3$O$_4$ phase was obtained by the reduction process of $\alpha$-Fe$_2$O$_3$ phase in H$_2$ ambient. Fe$_3$O$_4$ phase was transformed into a ${\gamma}$-Fe$_2$O$_3$ thin film under controlled oxidation conditions at 280~30$0^{\circ}C$.

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.5
• /
• pp.189-193
• /
• 2004

Pure and Sn or Pt doped $\alpha-Fe_2O_3$ thin films were prepared on $Al_2O_3$ substrates by RF-magnetron sputtering method and the sensitivities were compared. It was found that pure $\alpha-Fe_2O_3$ thin films did not exhibit much selectivity in CO and $i-C_4H_{10}$ gases while it showed the high sensitivity in proportion to the gas concentration of $C_2H_{5}OH$ gas. Pt-doped $\alpha-Fe_2O_3$ showed to be alike sensing properties as pure $\alpha-Fe_2O_3$ thin film in $C_2H_{5}OH$ gas. However, Sn-doped $\alpha-Fe_2O_3$ thin films exhibited the excellent sensitivity and selectivity in Hz gas. After microstructure modification by plasma etching on pure $\alpha-Fe_2O_3$ thin films, the gas sensing characteristics were dramatically changed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.3
• /
• pp.229-233
• /
• 2019

Pure $BiFeO_3$ (BFO) and (Eu, V) co-doped $Bi_{0.9}Eu_{0.1}Fe_{0.975}V_{0.025}O_{3+{\delta}}$ (BEFVO) thin films were deposited on $Pt(111)/Ti/SiO_2/Si(100)$ substrates by chemical solution deposition. The effects of co-doping were observed by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy (SEM). The electrical properties of the BEFVO thin film were improved as compared to those of the pure BFO thin film. The remnant polarization ($2P_r$) of the BEFVO thin film was approximately $26{\mu}C/cm^2$ at a maximum electric field of 1,190 kV/cm with a frequency of 1 kHz. The leakage current density of the co-doped BEFVO thin film ($4.81{\times}10^{-5}A/cm^2$ at 100 kV/cm) was two orders of magnitude lower than of that of the pure BFO thin film.

• Korean Journal of Materials Research
• /
• v.11 no.1
• /
• pp.39-43
• /
• 2001

Nanocrystalline Fe-Sm-O thin films were prepared by RF magnetron reactive sputtering method in $Ar+O_2$mixed atmosphere with the $O_2$content of 5%. The compositions of the thin films were changed by changing the number of $Sm_2O_3$ chips. The best soft magnetic properties of the thin film with the composition of $Fe_{83.4}Sm_{3.4}O_{13.2}$ were saturation flux density of 18 kG, coercivity of 0.82 Oe and effective permeability about 2,600 at 0.5~100 MHz, respectively. The electrical resistivity of Fe-Sm-O thin films was increased with increasing the amount of Sm and O elements which combined each other, the electrical resistivity of$Fe_{83.4}Sm_{3.4}O_{13.2}$ thin film was $130{\mu}{\Omega}cm$. In case of the small amount of Sm and O elements, the microstructures of Fe-Sm-O thin films showed a precipitated phase of $Sm_2O_3$ on the ${\alpha}-Fe$ phase. With the increase of the amount of Sm and O elements, the microstructures of the Fe- Sm-O thin films were changed into a mixed structure of ${\alpha}-Fe$ crystal-phase and Sm-oxide amorphous phase. The Fe-Sm-O thin films with Fe content in the range of 72~94 at% exhibited the quality factor (Q = $\mu$′/$\mu$") of 7~75 up to 50 MHz.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.60-60
• /
• 2011

Giant magnetoresistance (GMR), tunneling magnetoresistance (TMR), and magnetic random-access memory (MRAM) are currently active research areas in spintronics. The high magnetoresistance and the high spin polarization (P) of electrons in the ferromagnetic electrodes of tunnel junction or intermediate layers are required. Magnetite, Fe3O4, is predicted to possess as half-metallic nature, P ~ 100% spin polarization, and has a high Curie temperature (TC~850 K). Experiments demonstrated that the P~($80{\pm}5$)%, ~($60{\pm}5$)%, and ~40-55% for epitaxial (111), (110) and (001)-oriented Fe3O4 thin films, respectively. Epitaxial Fe3O4 films may enable us to investigate the effects of half metals on the spin transport without grain-boundary scattering.In addition, it has been reported that the Verwey transition (TV, a first order metal-insulator transition) of 120 K in bulk Fe3O4 is strongly affected by many parameters such as stoichiometry and stress, etc. Here we report that the growth modes, magnetism and transport properties of Fe3O4 thin films were strongly dependent on the oxygen pressure during film growth. The average roughness decreases from 1.021 to 0.263 nm for the oxygen pressure increase from $2.3{\times}10-7$ to $8.2{\times}10^{-6}$ Torr, respectively. The 120 K Verwey transition in Fe3O4 was disappeared for the sample grown under high oxygen pressure.

• Korean Journal of Materials Research
• /
• v.10 no.11
• /
• pp.755-759
• /
• 2000

The influence of $O_2$partial presure on saturation magnetization, coercivity and effective permeability(0.5~100MHz) of as-deposited Fe-Sm-O thin films, which were fabricated by RF magnetron reactive sputtering method, were investigated. The nanocrystalline Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film fabricated at $O_2$partial pressure of 5% exhibits the best magnetic softness with saturation magnetization of 18kG, coercivity of 0.82 Oe and effective permeability about 2,600 at 0.5~100MHz. $\alpha$-Fe grain size is decreased with increasing $O_2$partial pressure. In case of $O_2$partial pressure of 10%, it is observed that FeO compound is formed and soft magnetic properties are decreased. The electrical resistivity of Fe-Sm-O thin films were increased with increasing $O_2$partial pressure, the electrical resistivity of Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film with the best soft magnetic properties was 130 $\mu$$\Omega$cm. Therefore, It is assumed that the good soft magnetic properties of Fe(sub)83.4Sm(sub)3.4O(sub)13.2 thin film results from high electrical resistivity and decreasing $\alpha$-Fe grain size due to precipitation of Sm-Oxide phase.

• Journal of Magnetics
• /
• v.7 no.2
• /
• pp.51-54
• /
• 2002

The crystallization of amorphous Ba-ferrite/sapphire(001) thin films was studied in real-time synchrotron x-ray scattering experiments. In the sputter-grown amorphous films, we found the existence of epitaxial $Fe_3O_4$ interfacial crystallites (50-${\AA}$-thick), well aligned $[0.03^circ$full-width at half-maximum (FWHM)] to the sapphire [001] direction. The amorphous precursor was crystallized to epitaxial Ba-ferrite and \alpha-Fe_2O_3$grains in two steps; i) the nucleation of crystalline \alpha-Fe_2O_3$ phase started at $300^circ{C}$ together with the transformation of the $Fe_3O_4$ crystallites to the \alpha-Fe_2O_3$ crystallites, ii) the nucleation of Ba-ferrite phase occurred at temperature above $600^circ{C}$. In the crystallized films irrespective of the film thickness, the crystal domain size of the \alpha-Fe_2O_3$grains was about 250 ${\AA}$ in the film plane, similar to that of the Ba-ferrite grains.

• Journal of Sensor Science and Technology
• /
• v.8 no.2
• /
• pp.171-176
• /
• 1999

${\gamma}-Fe_2O_3$ thin films on $Al_2O_3$ substrate were prepared by the oxidation of $Fe_3O_4$ thin films processed by PECVD(Plasma-Enhanced Chemical Vapor Deposition) technique. The phase transformation of ${\gamma}-Fe_2O_3$ thin films was mainly controlled by the substrate temperature and oxidation process of $Fe_3O_4$ phase. $Fe_3O_4$ phase was obtained at the deposition temperature of $200{\sim}300^{\circ}C$. $Fe_3O_4$ phase could be transformed into ${\gamma}-Fe_2O_3$ phase under controlled oxidation at $280{\sim}300^{\circ}C$. $Fe_3O_4$ and ${\gamma}-Fe_2O_3$ obtained by oxidation of $Fe_3O_4$ phase had the same spinel structure and were coexisted. The oxidized ${\gamma}-Fe_2O_3$ thin film on $Al_2O_3$ substrate showed a porous island structure.