• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.309-315
• /
• 1982

$FeAl_2O_4$ was formed from the starting material of $Fe_2O_3$ and $Al_2O_3$ by controlling the oxygen partial pressure using $H_2-CO_2$ gas mixture, over the temperature range of 800~120$0^{\circ}C$. The formation mechanism of $FeAl_2O_4$ was found to be a second order chemical reaction, and the activation energy of formation was observed as 39.97 kcal/mole. Vaporization behavior of $FeAl_2O_4$ under $CO_2$ atmosphere was observed over the temperature range of 800~120$0^{\circ}C$. $FeAl_2O_4$ was vaporized by a second order chemical reaction and the activation energy was found to be 21.8kcal/mole. Electrical conductivity of $FeAl_2O_4$ was also measured.

• Journal of the Korean Magnetics Society
• /
• v.8 no.1
• /
• pp.27-33
• /
• 1998

We have investigated tunneling magnetoresistance (TMR) properties of Fe/$Al_2O_3$/Co magnetic trilayer junctions sputtered on single-crystal Si (001) substrates. $Al_2O_3$ layers with thicknesses of 50~200 $\AA$ were deposited directly on the bottom ferromagnetic layer by a reactive rf sputtering. For comparsion, we prepared Pt/$Al_2O_3$/Pt tunnel junctions whose current-voltage (I-V) characteristics measured at 300 K indicated that reactively sputtered $Al_2O_3$ is a particularly good material for thin insulating barriers and allows us to form pinhole-free tunnel barriers. The magnetic tunnel junctions exhibit changes of tunnel resistance of about 0.1% at 300 K with an applied magnetic field and it was found that most junctions with Co as a top electrode have rather good I-V and TMR characteristics compared to those with Fe as a electrode. These results were discussed in relation to interfacial on the basis of those for Pt/$Al_2O_3$/Pt.

• Journal of Welding and Joining
• /
• v.14 no.1
• /
• pp.92-98
• /
• 1996

Al-Fe alloy layers on heated steel sheet were made by Al powder spray for 30 minutes at $700^{\circ}C$, $800^{\circ}C$ and $1000^{\circ}C$, respectively. As a results, for alloy layers formed at $700^{\circ}C$ and $800^{\circ}C$, main phases were brittle phase $FeAl_3 and Fe_2Al_5$, hardnesses were very high (Hv 700~800), corrosion resistances were good and surfaces were smooth, but wear resistances were bad. For alloy layer formed at $1000^{\circ}C$, main phase was ductile phase $Fe_3Al$, hardness was low (Hv 300~400), corrosion and wear resistances were excellent, but surface was rough. Therefore, alloy layers that formed at $700^{\circ}C$ and $800^{\circ}C$ were heat treated at $1000^{\circ}C$ for 10 minutes for the purpose of smooth surface and excellent wear resistance in this study. It was investigated that brittle phase $FeAl_3 and Fe_2Al_5$ of alloy layers fromed by Al powder spray at $700^{\circ}C$ and $800^{\circ}C$ turn into ductile phase $Fe_3Al$ by heat treated at $1000^{\circ}C$ for 10 minutes without changing smooth surface. It was concluded that the alloy layers formed by Al powder spray on heated steel sheet at $700^{\circ}C$ and $800^{\circ}C$ for 30 minutes and heat treated at $1000^{\circ}C$ for 10 minutes were excellent on wear and smooth surface.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.4
• /
• pp.281-288
• /
• 2000

To understand the effect of Fe on the oxidation behavior of TiAl alloys, TiAl-(2, 4, 6at% )Fe were oxidized at 800 and 90$0^{\circ}C$ in air. The oxidation resistance of TiAl-Fe alloys increased with increasing an iron content. The scales formed consisted of an outer $TiO_2$ layer, an intermediate $A1_2$$O_3$ layer, and an inner mixed ($TiO_2$+$A1_2$$O_3$) layer, being similar to other common TiAl alloys. But, the scales formed on TiAl-Fe alloys were generally thin compared to those formed on pure TiAl, and contained dissolved iron. Below the oxide scale, an oxygen affected zone was formed. This beneficial effects of Fe on increasing the oxidation resistance and scale adherence of TiAl alloys were attributed to the refinement of oxide grains, increased scale adherence and the enhanced alumina-forming tendency.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.144-148
• /
• 1999

The relationship between oxidation and sliding wear behavior of Fe-28 at%. Al alloys with B2 ordered structure has been investigated. Sliding wear tests of the alloys have been carried out under various environmental conditions using a pin-on-disk wear tester. The wear rate of the ordered alloys in an oxygen atmoshpere was found to be much lower than in an oxygen atmosphere showed that Fe2O oxides formed on the wearing surface. The oxide layer prevented direct contact of the two mating materials and therefore improved wear resistance of the Fe-Al intermetallic alloy. It was found that the surface Al2O3 oxide layer which provides good oxidation resistance and improved mechanical properties broke down easily and didnot function properly as an oxidation barrier.

• Korean Journal of Materials Research
• /
• v.16 no.2
• /
• pp.137-143
• /
• 2006

The effects of Cu and Fe additions on the thermal stability, microstructure and mechanical properties of $Al_{85}-Ni_{8.5}-Mm_{6.5},\;Al_{84}-Ni_{8.5}-Mm_{6.5}Cu_1,\;Al_{84}-Ni_{8.5}-M_{m6.5}Fe_1$ alloys, manufactured by gas atomization, degassing and hot-extrusion were investigated. Gas atomization, with a wide super-cooled liquid region, allowed the alloy powders to exhibit varying microstructure depending primarily on the powder size and composition. Al hotextruded alloys consisted of homogeneously-distributed fine-grained fcc-Al matrix and intermetallic compounds. A substitution of 1 at.% Al by Cu increased the thermal stability of the amorphous phase and produced alloy microstructure with smaller fcc-Al grains. On the other hand, the same substitution of 1 at.% Al by Fe decreased the stability of the amorphous phase and produced larger fcc-Al grains. The formation of intermetallic compounds such as $Al_3Ni,\;Al_{11}Ce_3\;and\;Al_{11}La_3$ was suppressed by the addition of Cu or Fe. Among the three alloys examined, the highest Vickers hardness and compressive strength were obtained for $Al_{84}-Ni_{8.5}-M_{m6.5}Cu_1$ alloy, and related to the finest fcc-Al grain size attained from increased thermal stability with Cu addition.

• Journal of the Korean Ceramic Society
• /
• v.39 no.8
• /
• pp.769-774
• /
• 2002

The powder mixture in which Fe-Ni alloy particles of 20 nm were homogeneously dispersed on $Al_2O_3$ particle surfaces was prepared by hydrogen reduction of $Al_2O_3$ and metal oxide powders. $Al_2O_3$/Fe-Ni nanocomposites fabricated by pressureless sintering were only composed of $Al_2O_3$ and ${gamma}$-Fe-Ni phases and achieved over 98% of the theoretical density at the sintering temperature above $1350^{\circ}C$. The highest strength and toughness of the composites were 574 MPa and 3.9 MP$a{\cdot}m1/2$, respectively. These values were about 20% higher than these of monolithic $Al_2O_3$ sintered at the same conditions. Nanocomposites showed ferromagnetic properties and coercive force was increased with decrease of the average particle size of dispersions.

• Journal of Magnetics
• /
• v.10 no.3
• /
• pp.99-102
• /
• 2005

Modification in exchange bias of a NiFe/FeMn/NiFe trilayer, on introduction of a nonmagnetic Al layer at the top FeMn/NiFe interface, is investigated in multilayers prepared by rf magnetron sputtering. The introduction of Al layer leads to vanishing of bias of the top NiFe layer. But the bias for the bottom NiFe layer increases steadily with increasing Al layer thickness and attains bias (230 Oe) which is greater than that of the trilayer without the Al layer (150 Oe). When the top NiFe layer thickness is varied, exchange bias has highest value at 12 nm thickness for 1 nm thicknes of Al layer. Ion beam etching of the top NiFe layer also leads to an enhancement in bias for the bottom NiFe layer.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.522-527
• /
• 2004

Nano sized FeAl intermetallic particles were successfully synthesized by plasma arc discharge pro-cess. The synthesized powders shouted core-shell structures with the particle size of 10-20 nm. The core was metallic FeAl and shell was composed of amorphous $AI_{2}O_{3}\;and\;a\;little\;amount\;of\;metallic\;Fe_{3}O_{4}.$ Because of the difference of Fe and Al vapor pressure during synthesis, the Al contents in the nanoparticles depended on the Al contents of master alloy.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.3
• /
• pp.149-154
• /
• 2009

Dense $5Cu_{0.6}Fe_{0.4}-Al_2O_3$ composite was consolidated from mechanically synthesized powders by pulsed current activated sintering method within 1 min. $5Cu_{0.6}Fe_{0.4}-Al_2O_3$ powder was synthesized from 3CuO and 2FeAI using the high energy ball milling. Dense $5Cu_{0.6}Fe_{0.4}-Al_2O_3$ with relative density of up to 95% was produced under simultaneous application of a 80 MPa pressure and the pulsed current. Mechanical properties and grain size of the composite were investigated.