• Korean Journal of Materials Research
• /
• v.10 no.11
• /
• pp.770-777
• /
• 2000

Microstructure and mechanical properties of the $Cu_6Sn_5$-dispersed 63Sn-37Pb solder alloy, for which $Cu_6Sn_5$ powders less than $1{\mu\textrm{m}}$ size were fabricated by mechanical alloying, were characterizde and compared with those of the Cu-dispersed solder alloy. Compared to the $Cu_6Sn_5$-dispersed solder alloy, large amount of $Cu_6Sn_5$ and fast growth of $Cu_6Sn_5$ were observed in the Cu-dispersed alloy. The $Cu_6Sn_5$-dispersed solder alloy exhibited lower yield strength, but higher ultimate tensile strength than those of the Cu-dispersed alloy. With dispersion of 1~9 vol% $Cu_6Sn_5$ and Cu, the yield strength increased from 23 MPa and to 40 MPa, respectively. The ultimate tensile strength increased from 34.7 MPa to 45.3 MPa and to 43.1 MPa with dispersion of 5 vol% $Cu_6Sn_5$ and Cu, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.3
• /
• pp.45-51
• /
• 2013

Thermal annealing tests were performed in an in-situ scanning electron microscope chamber at $130^{\circ}C$, $150^{\circ}C$, and $170^{\circ}C$ in order to investigate the effects of solder structure on the growth kinetics of intermetallic compound (IMC) in Cu/Sn-3.5Ag microbump. Cu/Sn-3.5Ag($6{\mu}m$) microbump with spreading solder structure showed $Cu_6Sn_5$ and $Cu_3Sn$ phase growths and then IMC phase transition stages with increasing annealing time. By the way, Cu/Sn-3.5Ag($4{\mu}m$) microbump without solder spreading, remaining solder was transformed to $Cu_6Sn_5$ right after bonding and had only a phase transition of $Cu_6Sn_5$ to $Cu_3Sn$ during annealing. Measured activation energies for the growth of the $Cu_3Sn$ phase during the annealing were 0.80 and 0.71eV for Cu/Sn-3.5Ag($6{\mu}m$) and Cu/Sn-3.5Ag($4{\mu}m$), respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.15-20
• /
• 2007

Growth kinetics of intermetallic compound (IMC) at various interface in Cu pillar bump during aging have been studied by thermal aging at 120, 150 and $165^{\circ}C$ for 300h. In result, $Cu_6Sn_5\;and\;Cu_3Sn$ were observed in the Cu pillar/SnPb interface and IMC growth followed parabolic law with increasing aging temperatures and time. Also, growth kinetics of IMC layer was faster for higher aging temperature with time. Kirkendall void formed at interface between Cu pillar and $Cu_3Sn$ as well as within the $Cu_3Sn$ layer and propagated with increasing time. $(Cu,Ni)_6Sn_5$ formed at interface between SnPb and Ni(P) after reflow and thickness change of $(Cu,Ni)_6Sn_5$ didn't observe with aging time. The apparent activation energies for growth of total $(Cu_6Sn_5+Cu_3Sn),\;Cu_6Sn_5\;and\;Cu_3Sn$ intermetallics from measurement of the IMC thickness with thermal aging temperature and time were 1.53, 1.84 and 0.81 eV, respectively.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.33-35
• /
• 2006

The interactions between Cu/Sn-Ag-(Cu) and Sn-Ag-(Cu)/Ni interfacial reactions were studied during isothermal aging at $150^{\circ}C$ for up to 1000h using Cu(ENIG)/Sn-3.5Ag-(0.7Cu)/Cu(ENIG) sandwich solder joints. A typical scallop-type Cu-Sn intermetallic compound (IMC) layer formed at the upper Sn-Ag/Cu interface after reflowing, whereas a $(Cu,Ni)_6Sn_5$ IMC layer was observed at the Sn-Ag/ENIG interface. The Cu in the $(Cu,Ni)_6Sn_5$ IMC layer formed on the Ni side was sourced from the dissolution of the opposite Cu metal pad or Cu-Sn IMC layer. When the dissolved Cu arrived at the interface of the Ni pad, the $(Cu,Ni)_6Sn_5$ IMC layer formed on the Ni interface, preventing the Ni pad from reacting with the solder. Although a long isothermal aging treatment was performed at $150^{\circ}C$, no Ni was detected in the Cu-Sn IMC layer formed on the Cu side. Compared to the single Sn-Ag/ENIG solder joint, the formation of the $(Cu,Ni)_6Sn_5$ IMC layer of the Cu/sn-Ag/ENIG sandwich joint effectively retarded the Ni consumption from the electroless Ni-P layer.

• Journal of Welding and Joining
• /
• v.20 no.1
• /
• pp.97-102
• /
• 2002

The growth kinetics of intermetallic compound layers formed between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad by solid stateisothermal aging were examined. The interfacial reaction between the eutectic Sn-3.5Ag solder and the Cu and Ni/Cu pad was investigated at 70, 120, 150, $170^{\circ}C$ for various times. The intermetallic compound layer was composed of two phase: $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the solder and $Cu_6Sn_5$(${\varepsilon}-phase$) adjacent to the copper and on solder/Ni pad the intermetallic compound layer was $Ni_3Sn_4$. Because the values of time exponent(n) have approximately 0.5, the layer growth of the intermetallic compound was mainly controlled by volume diffusion over the temperature range studied. The apparent activation energy for layer growth of total Cu-Sn($Cu_6Sn_5 + Cu_6Sn$), $Cu_6Sn_5$, $Cu_3Sn$ and $Ni_3Sn_4$ intermetallic compound were 64.82kJ/mol, 48.53kJ/mol, 89.06kJ/mol and 71.08kJ/mol, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.33-37
• /
• 2008

The effects of Cu and Sb on the microstructure and mechanical properties of Sn-Sb-Cu-Ni-Cd whitemetal were investigated. Any compound phase was not observed in the whitemetal with 0.05 wt% Cu, while as the Cu content was increased, star- or needle-like $Cu_6Sn_5$ phases were found. The tensile strength gradually increased with Cu up to 5 % and then remained almost constant with Cu content above 5 %, while the hardness continuously increased with Cu content because of the increased hard $Cu_6Sn_5$ phases. As the Sb content increased, SbSn cuboids were present as well as $Cu_6Sn_5$. The tensile steength and hardness continuously increased and the elongation decreased with Sb content.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.114-117
• /
• 2003

본 연구에서는 계산을 통해 나온 Sn-Ag-Cu 삼원계 공정점(Sn-3.7Ag-0.9Cu)을 바탕으로 그 근처의 응고경로가 다른 6가지 조성(Sn-4.6Ag-0.4Cu, Sn-4.9Ag-1.0Cu, Sn-3.9Ag-1.3Cu, Sn-2.2Ag-1.2Cu, Sn-2Ag-0.7Cu, Sn-2.7Ag-0.3Cu)에 대한 솔더합금의 미세조직을 관찰하였다. 응고경로는 $L\;\rightarrow\;L+Primary\;\rightarrow\;L+Primary+Secondary\;\rightarrow\;Ternary\;Eutectic+Primary+Secondary$로 되며 6가지 경우를 예상할 수 있다 솔더합금의 미세조직은 느린 냉각으로 인하여 빠른 냉각, 보통 냉각에 비해 상대적으로 커다란 $\beta-Sn$ dendrite를 보였고 $Ag_3Sn,\;Cu_6Sn_5$과는 다르게 $\beta-Sn$는 약 $30^{\circ}C$의 과냉(DSC분석)이 존재하게 되어 Sn-4.6Ag-0.4Cu의 경우에는 $Ag_3Sn$상이, Sn-2.2Ag-1.2Cu의 경우에는 $Cu_6Sn_5$가 과대성장을 하였다. 솔더의 기계적 특성을 살펴보고자 Cu 기판위에서 각 조성의 솔더볼을 솔더링한 후 다양한 냉각 속도를 적용하여 reflow 솔더링을 하고 솔더/기판 접합에 대한 전단 강도 시험을 실시했다. 냉각 속도가 빠를수록 $\beta-Sn$의 dendrite가 미세해져서 높은 전단 강도를 보였고 6가지 조성의 솔더볼중 공정조직 분율이 낮은 Sn-2Ag-0.7Cu 조성의 경우에서 낮은 전단 강도가 나타났다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.133-137
• /
• 2003

The effect of Bi additions to the eutectic Sn-3.5Ag solder alloy on the growth kinetics of the intermetallic compound (IMC) layers during solid-state aging of Sn-Ag-Bi/Cu solder joints has been Investigated. The Bi additions enhanced the growth rate of the total IMC layer comprising of $Cu_6Sn_5$ and $Cu_3Sn$ sublayers. This enhanced IMC growth rate was primarily due to the rapid increase In the growth rate of $Cu_6Sn_5$ sublayer. The growth rate of $Cu_3Sn$ sublayers was little influenced and appeared to be retarded by the Bi additions. The observed growth behavior of $Cu_6Sn_5$ and $Cu_3Sn$ sublayers could be understood if the interfacial reaction barrier at the $Cu_6Sn_5/solder$ interface were reduced by the segregation of Bi at the interface.

• Korean Journal of Materials Research
• /
• v.9 no.9
• /
• pp.926-931
• /
• 1999

The microstructure, wettability, shear strength and aging effect of Sn-3.5Ag/Cu and Alloy42 lead-frame solder joints were measured for comparison. In the case of Sn-3.5Ag/Cu, $Ag_3Sn and Cu_6Sn_5$ phases in the matrix Sn and $1~2\mu\textrm{m}$ thick $Cu_6Sn_5$ phase at the interface of solder/lead-frame were formed. In the case of Sn-3.5Agl Alloy42, only AgJSn phase of low density in the matrix Sn and $0.5~1.5\mu\textrm{m}$ thick $FeSn_2$, phase at the interface of solder/leadframe were formed. Comparing to Cu, Alloy42 showed wider area of spread and smaller contact angle, thus better wet­tability. But shear strength and ductility of Alloy 42 solder joints were only 33% and 75% of those of Cu, respectively After aging at $180^{\circ}C$ for 1 week, $\xi-Cu_3Sn$ layer on $\eta-Cu_6Sn_5$ layer was formed on Cu lead-frame, while coarsened cir­cular $Ag_3Sn$ phase in the matrix and thickened $FeSn_2$, at the interface were formed on Alloy42 lead- frame.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.59-59
• /
• 2002

Sn-Ag-Cu solder is known as most competitive in many kinds of Pb-free solders. In this study, effects of solderability with plated layers such as Cu, Cu/Sn, Cu/Ni and Cu/Ni/Au were investigated. Sn-3.5Ag-0.7Cu solder balls were reflowed in commercial reflow machine (peak temp. : 250℃ and conveyer speed : 0.6m/min). In wetting test, immersion speed was 5mm/sec., immersion time 5sec., immersion depth 4mm and temperature of solder bath was 250℃. Wettability of Sn-3.5Ag-0.7Cu on Cu, Cu/Sn (5㎛), Cu/Ni (5㎛), and Cu/Ni/Au (5㎛/500Å) layers was investigated. Cu/Ni/Au layer had the best wettability as zero cross time and equilibrium force, and the measured values were 0.93 sec and 7mN, respectively. Surface tension of Sn-3.5Ag-0.7Cu solder turmed out to be 0.52N/m. The thickness of IMC is reduced in the order of Cu, Cu/Sn, Cu/Mi and Cu/Ni/Au coated layer. Shear strength of Cu/Ni, Cu/Sn and Cu was around 560gf but Cu/Ni/Au was 370gf.