• 한국재료학회지
• /
• 제23권6호
• /
• pp.304-308
• /
• 2013

The effect of a sputter deposition sequence of Cu, Zn, and Sn metal layers on the properties of $Cu_2ZnSnS_4$ (CZTS) was systematically studied for solar cell applications. The set of Cu/Sn/Zn/Cu multi metal films was deposited on a Mo/$SiO_2$/Si wafer using dc sputtering. CZTS films were prepared through a sulfurization process of the Cu/Sn/Zn/Cu metal layers at $500^{\circ}C$ in a $H_2S$ gas environment. $H_2S$ (0.1%) gas of 200 standard cubic centimeters per minute was supplied in the cold-wall sulfurization reactor. The metal film prepared by one-cycle deposition of Cu(360 nm)/Sn(400 nm)/Zn(400 nm)/Cu(440 nm) had a relatively rough surface due to a well-developed columnar structure growth. A dense and smooth metal surface was achieved for two- or three-cycle deposition of Cu/Sn/Zn/Cu, in which each metal layer thickness was decreased to 200 nm. Moreover, the three-cycle deposition sample showed the best CZTS kesterite structures after 5 hr sulfurization treatment. The two- and three-cycle Cu/Sn/Zn/Cu samples showed high-efficient photoluminescence (PL) spectra after a 3 hr sulfurization treatment, wheres the one-cycle sample yielded poor PL efficiency. The PL spectra of the three-cycle sample showed a broad peak in the range of 700-1000 nm, peaked at 870 nm (1.425 eV). This result is in good agreement with the reported bandgap energy of CZTS.

• Current Photovoltaic Research
• /
• 제4권1호
• /
• pp.16-20
• /
• 2016

$Cu_2ZnSnS_4$ (CZTS) thin films were fabricated by successive electrodeposition of layers of precursor elements followed by sulfurization of an electrodeposited Cu-Zn-Sn precursor. In order to improve quality of the CZTS films, we tried to optimize the deposition condition of absorber layers. In particular, I have conducted optimization experiments by changing the Cu-layer deposition time. The CZTS absorber layers were synthesized by different Cu-layer conditions ranging from 10 to 16 minutes. The sulfurization of Cu/Sn/Zn stacked metallic precursor thin films has been conducted in a graphite box using rapid thermal annealing (RTA). The structural, morphological, compositional, and optical properties of CZTS thin films were investigated using X-ray diffraction (XRD), Field emission scanning electron microscopy (FE-SEM), Raman spectroscopy, and X-ray Flourescenece Spectrometry (XRF). Especially, the CZTS TFSCs exhibits the best power conversion efficiency of 4.62% with $V_{oc}$ of 570 mV, $J_{sc}$ of $18.15mA/cm^2$ and FF of 45%. As the time of deposition of the Cu-layer to increasing, the properties were confirmed to be systematically changed. And we have been discussed in detail below.

• Current Photovoltaic Research
• /
• 제1권2호
• /
• pp.82-89
• /
• 2013

$Cu_2ZnSnS_4$ thin film have been fabricated by rapid thermal annealing of dc-sputtered metal precursor with Cu/ZnSn/Cu stack in sulfur ambient. A CZTS film with a good uniformity was formed at $560^{\circ}C$ in 6 min. $Cu_2SnS_3$ and $Cu_3SnS_4$ secondary phases were present at $540^{\circ}C$ and a trace amount of $Cu_2SnS_3$ secondary phase was present at $560^{\circ}C$. Single-phase large-grained CZTS film with rough surface was formed at $560^{\circ}C$. Solar cell with best efficiency of 4.7% ($V_{oc}=632mV$, $j_{sc}=15.8mA/cm^2$, FF = 47.13%) for an area of $0.44cm^2$ was obtained for the CZTS absorber grown at $560^{\circ}C$ for 6 min. The existence of second phase at lower-temperature annealing and rough surface at higher-temperature annealing caused the degradation of cell performance. Also poor back contact by void formation deteriorated cell performance. The fill factor was below 0.5; it should be increased by minimizing voids at the CZTS/Mo interface. Our results suggest that CZTS absorbers can be grown by rapid thermal annealing of metallic precursors in sulfur ambient for short process times ranging in minutes.

• Current Applied Physics
• /
• 제18권12호
• /
• pp.1571-1576
• /
• 2018

Recent study shows that the main reason for limiting CZTS device performance lies in the low open circuit voltage, and crucial factor that could affect the $V_{oc}$ is secondary phases like ZnS existing in absorber layer and its interfaces. In this work, the $Cu_2ZnSnS_4$ thin film solar cells were prepared by sputtering CuSn and CuZn alloy targets. Through tuning the Zn/Sn ratios of the CZTS thin films, the crystal structure, morphology, chemical composition and phase purity of CZTS thin films were characterized by X-Ray Diffraction (XRD), scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) and Raman spectroscopy. The statistics data show that the CZTS solar cell with a ratio of Zn/Sn = 1.2 have the best power convention efficiency of 5.07%. After HCl etching process, the CZTS thin film solar cell with the highest efficiency 5.41% was obtained, which demonstrated that CZTS film solar cells with high efficiency could be developed by sputtering CuSn and CuZn alloy targets.

• 한국재료학회지
• /
• 제23권1호
• /
• pp.7-12
• /
• 2013

The $Cu_2ZnSnS_4$ (CZTS) thin film solar cell is a candidate next generation thin film solar cell. For the application of an absorption layer in solar cells, CZTS thin films were deposited by pulsed laser deposition (PLD) at substrate temperature of $300^{\circ}C$ without post annealing process. Deposition time was carefully adjusted as the main experimental variable. Regardless of deposition time, single phase CZTS thin films are obtained with no existence of secondary phases. Irregularly-shaped grains are densely formed on the surface of CZTS thin films. With increasing deposition time, the grain size increases and the thickness of the CZTS thin films increases from 0.16 to $1{\mu}m$. The variation of the surface morphology and thickness of the CZTS thin films depends on the deposition time. The stoichiometry of all CZTS thin films shows a Cu-rich and S-poor state. Sn content gradually increases as deposition time increases. Secondary ion mass spectrometry was carried out to evaluate the elemental depth distribution in CZTS thin films. The optimal deposition time to grow CZTS thin films is 150 min. In this study, we show the effect of deposition time on the structural properties of CZTS thin film deposited on soda lime glass (SLG) substrate using PLD. We present a comprehensive evaluation of CZTS thin films.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.407.2-407.2
• /
• 2016

Cu2ZnSnS4 (CZTS) 박막은 낮은 가격과 유리한 특성을 가지므로서 차세대 박막 태양전지에서 이상적인 흡수층 물질 중 하나로 여겨지고 있다. 우리는 CZTS 박막 태양전지를 합성하는 데 있어서 Zn와 ZnS를 전구체에 사용하여 이에 따른 특성 차이를 연구하였다. 열처리 한 박막은 Zn와 ZnS를 사용하였을 때 특성 차이를 조사하기 위하여 여러 분석을 진행하였다. CZTS 박막의 미세구조와 조성 분포, 전기적 특성을 살펴보았다. Zn를 사용한 CZTS 박막은 큰 입자크기와 더 적은 영역에서 Zn가 집중되어 있는 층을 가진다. CZTS와 Mo 경계인 이 영역에 ZnS 2차상이 존재함을 의미하며 Zn 타겟을 사용하였을 때 더 낮은 Zn 조성을 가지는 것을 확인하였고 이는 결과적으로 접합 특성의 향상을 가져온다. 제작 된 CZTS 태양 전지 소자에서 이러한 이유로 Zn를 사용하였을 때 5.06%로 ZnS를 사용하였을 때에 비하여 더 높은 효율을 얻을 수 있었다.

• Current Photovoltaic Research
• /
• 제1권2호
• /
• pp.109-114
• /
• 2013

$Cu_2ZnSnS_4$ (CZTS) nanoparticles were synthesized by a solvothermal method using copper (II) acetate, zinc acetate, tin chloride, and sulfur in diethylenetriamine solvent. Binary sulfide particles such as CuS, ZnS, SnS, and $SnS_2$ were obtained at $180^{\circ}C$; single-phase CZTS nanoparticles were obtained at $280^{\circ}C$. CZTS nanoparticles with spherical shape and grain size of 40 to 60 nm were obtained at $280^{\circ}C$. In the middle of 180 and $280^{\circ}C$, CZTS and ZnS phases were found. The time variation of reaction at $280^{\circ}C$ revealed that an amorphous state formed first instead of binary phases and then the amorphous phase was converted to crystalline CZTS state; it is different reaction path way from conventional solid-state reaction path of which binary phases react to form CZTS. CZTS films deposited and annealed from single-phase nanoparticles showed porous microstructure and poor adhesion. This indicates that a combination of CZTS and other flux phase is necessary to have a dense film for device fabrication.

• 한국재료학회지
• /
• 제25권12호
• /
• pp.708-712
• /
• 2015

This study reports the effects of $H_2S$ gas concentration on the properties of $Cu_2ZnSnS_4(CZTS)$ thin films. Specifically, sulfurization process with low $H_2S$ concentrations of 0.05% and 0.1%, along with 5% $H_2S$ gas, was studied. CZTS films were directly synthesized on Mo/Si substrates by chemical bath deposition method using copper sulfate, zinc sulfate heptahydrate, tin chloride dihydrate, and sodium thiosulfate pentahydrate. Smooth CZTS films were grown on substrates at optimized chemical bath deposition condition. The CZTS films sulfurized at low $H_2S$ concentrations of 0.05 % and 0.1% showed very rough and porous film morphology, whereas the film sulfurized at 5% $H_2S$ yielded a very smooth and dense film morphology. The CZTS films were fully crystallized in kesterite crystal form when they were sulfurized at $500^{\circ}C$ for 1 h. The kesterite CZTS film showed a reasonably good room-temperature photoluminescence spectrum that peaked in a range of 1.4 eV to 1.5 eV, consistent with the optimal bandgap for CZTS solar cell applications.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.444.1-444.1
• /
• 2014

높은 광흡수 계수를 갖는 Cu(In,Ga)Se2(CIGS) 화합물 박막 소재는 고효율 태양전지 양산을 위해 가장 전도유망한 재료이나 상대적으로 매장량이 적은 In 및 Ga을 사용한다는 소재적 한계가 있다. Cu2ZnSnSe4(CZTSe) 혹은 Cu2ZnSnS4(CZTS)와 같은 Cu-Zn-Sn-Se계 화합물 반도체는 CIGS 내 희소원소인 In과 Ga이 범용원소인 Zn 및 Sn으로 대체된 소재로써 미래형 저가 태양전지 개발을 위해 활발히 연구되고 있는데, 그 화합물 조합에 따라 0.8eV부터 1.5eV까지의 에너지 밴드갭을 갖는 것으로 알려져 있다. 본 연구에서는 열분해법으로 CZTS 나노 입자를 합성하였다. 용매로 Oleylamine을 사용하였는데, $220^{\circ}C{\sim}340^{\circ}C$의 온도 범위에서 3시간 30분 동안 CZTS 나노입자를 합성하였고, $240^{\circ}C$에서 3시간~5시간까지 합성하였다. 헥산을 이용하여 원심분리기와 초음파세척기로 용매인 Oleylamine을 제거하였고, 진공오븐에서 건조된 CZTS 분말의 FE-SEM(Field Emission Scanning Electron Microscope), XRD(X-Ray Diffraction), EDS(Energy Dispersive Spectroscopy) 분석 등을 통해 합성온도에 따른 구조적, 화학적 조성 변화를 조사하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제45회 하계 정기학술대회 초록집
• /
• pp.321.1-321.1
• /
• 2013

높은 광흡수 계수를 갖는 Cu(In,Ga)Se2(CIGS) 화합물 박막 소재는 고효율 태양전지 양산을 위해 가장 전도유망한 재료이나 상대적으로 매장량이 적은 In 및 Ga을 사용한다는 소재적 한계가 있다. Cu2ZnSnSe4(CZTSe) 혹은 Cu2ZnSnS4(CZTS)와 같은 Cu-Zn-Sn-Se계 화합물 반도체는 CIGS 내 희소원소인 In과 Ga이 범용원소인 Zn 및 Sn으로 대체된 소재로써 미래형 저가 태양전지 개발을 위해 활발히 연구되고 있는데, 그 화합물 조합에 따라 0.8eV부터 1.5eV까지의 에너지 밴드갭을 갖는 것으로 알려져 있다. 본 연구에서는 열분해법으로 CZTS 나노 입자를 합성하였다. 용매로 Oleylamine을 사용하였는데, $260{\sim}340^{\circ}C$의 온도 범위에서 5시간 30분 동안 CZTS 나노입자를 합성하였고, $300^{\circ}C$에서 5시간 30분~9시간까지 합성하였다. 헥산을 이용하여 원심분리기와 초음파세척기로 용매인 Oleylamine을 제거하였고, 진공오븐에서 건조된 CZTS 분말의 FE-SEM (Field Emission Scanning Electron Microscope), XRD (X-Ray Diffraction), EDS (Energy Dispersive Spectroscopy) 분석 등을 통해 합성온도에 따른 구조적, 화학적 조성 변화를 조사하였다.