• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.3
• /
• pp.228-232
• /
• 2006

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25\;wt\%\;CaCO_3$ and $0.2\;wt\%\;Li_{2}CO_3$ as sintering aids were manufactured according to the variation of poling field. The specimens could be sintered at $930\;^{\circ}C$. The piezoelectric properties were investigated according to the poling field. The maximum properties showed at the field of 6.5 kV/mm, which had kt of 0.49, Qmt of 1816, and $d_{33}$ of 81.4 pC/N.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.176-177
• /
• 2005

In this paper, in order to develop low temperature sintering $PbTiO_3$-system piezoelectric ceramics for thickness-vibration-mode piezoelectric transformer, $Pb_{0.76}Ca_{0.24}[(Mn_{1/3}Sb_{2/3})_{0.04}Ti_{0.96}]O_3$ ceramics using $0.25wt%CaCO_3$ and 0.2wt%$Li_2CO_3$ as sintering aids were manufactured according to the variation of poling field. Specimens could be sintered at the sintering temperature of $930^{\circ}C$. The piezoelectric properties increased according to the increase of poling field and showed the maximum values (kt=0.49, Qmt=1816, and $d_{33}$=81.4pC/N) under 6.5kV/mm.

• KEPCO Journal on Electric Power and Energy
• /
• v.2 no.2
• /
• pp.285-291
• /
• 2016

In chemical-looping combustion, pure oxygen is transferred to fuel by solid particles called as oxygen carrier. Chemical-looping combustion process usually utilizes a circulating fluidized-bed process for fuel combustion and regeneration of the reduced oxygen carrier. The performance of an oxygen carrier varies with the active metal oxide and the raw support materials used. In this work, spraydried Mn-based oxygen carriers were prepared with different raw support materials and their physical properties and oxygen transfer performance were investigated to determine that the raw support materials used are suitable for spray-dried manganese oxide oxygen carrier. Oxygen carriers composed of 70 wt% $Mn_3O_4$ and 30 wt% support were produced using spray dryer. Two different types of $Al_2O_3$, ${\gamma}-Al_2O_3$ and ${\alpha}-Al_2O_3$, and $MgAl_2O_4$ were applied as starting raw support materials. The oxygen carrier prepared from ${\gamma}-Al_2O_3$ showed high mechanical strength stronger than commercial fluidization catalytic cracking catalyst at calcination temperatures below $1100^{\circ}C$, while the ones prepared from ${\alpha}-Al_2O_3$ and $MgAl_2O_4$ required higher calcination temperatures. Oxygen transfer capacity of the oxygen carrier prepared from ${\gamma}-Al_2O_3$ was less than 3 wt%. In comparison, oxygen carriers prepared from ${\alpha}-Al_2O_3$ and $MgAl_2O_4$ showed higher oxygen transfer capacity, around 3.4 and 4.4 wt%, respectively. Among the prepared Mn-based oxygen carriers, the one made from $MgAl_2O_4$ showed superior oxygen transfer performance in the chemical-looping combustion of $CH_4$, $H_2$, and CO. However, it required a high calcination temperature of $1400^{\circ}C$ to obtain strong mechnical strength. Therefore, further study to develop new support compositions is required to lower the calcination temperature without decline in the oxygen transfer performance.

• Applied Biological Chemistry
• /
• v.24 no.2
• /
• pp.105-111
• /
• 1981

Growth responses of Brevibadterium ammoniagenes BA 17-2, which had been obtained by the treatment of several mutagens in our previous report, were investigated to select the preliminary optimal concentrations of phosphate, $Mg^{++}$, $Mn^{++}$ and thiamine for the production of 5'-XMP aminase. In this experiment it was shown that the concentration of phosphate in the medium has an important effect on the growth of microorganism. Using the medium containing 0.2% of $MgSO_4{\cdot}7H_2O$, 3mg/l of $MnSO_4{\cdot}H_2O$and $1\;mg/l$ of thiamine-HCl, the maximum cell mass was obtained at the concentration of 0.4% of $KH_2PO_4$ and $K_2HPO_4$, respectively. Above the concentration of these phosphates, cell growth was inhibited as the phosphate concentration increased to 1%, but the inhibition was overcome by the addition of 1% of $MgSO_4{\cdot}7H_2O$ and 3mg/l of thiamine-HCl. The 5'-XMP aminase activity was also influenced by the concentration of phosphate, $Mg^{++}$, $Mn^{++}$, and thiamine. In addition, the optimal culture pH and temperature for the enzyme activity were found to be 6.8 and $32^{\circ}C$, respectively.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.623-626
• /
• 1995

High coercivity thin $Fe_{3}O_{4}$ and ${\gamma}-Fe_{2}O_{3}$ films were deposited on Si substrate under well controlled $O_{2}$ partial pressure by dcreactive magnetron sputtering. The coercivity of as-deposited maggnetite films is below 640 Oe. After cxidizing at $360^{\circ}C$ for 10 minutes, the films transform to maghemite ${\gamma}-Fe_{2}O_{3}$ completely, and the coercivity increases greatly to 2100~4120 Oe, depending on modification of not with minor addition of Co or/and Mn. The orign of coercivity enhancement is attributed mainly to magnetic anisotropy arisen from interfacial stress. The addition of 5 at% Co and 5 at% Mn greatly enhances coercivity and squareness ratio. These films are potential for ultra-high density recording applications.

• Resources Recycling
• /
• v.8 no.3
• /
• pp.9-17
• /
• 1999

The study investrgated the properti es of lh$\xi$ dust~ from felToalloy manufacture, The chemical composition, composItron material, particle size and shapes of the bulk dust, sized dust and magnetically separated dust were llivestigated. As the result, we s suppose that the dust from HLgh Carbon Fenomauganesc Manufacturing Process is not sufficient as soource material of Mn because of the low Mn conteut (13.5%) aud complicated composition material The dust from Bag Filter of AOD Process is m mainly made up of $0.2~2\mu\textrm{m}$ $Mn_3O_4$ (Hausmatmite) particle in spherical shape and the Mn content is 63.1%. The dust from Cooler of AOD Process is mainly made up of coarse $Ca(OH)_2$ Mn, $Fe_yO_2$ $SiO_2$ and fine $Mn_3O_1$.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.2
• /
• pp.355-359
• /
• 2010

A $Li[Co_{1/3}Ni_{1/3}Mn_{1/3}]O_2$ cathode was modified by applying a $ZrF_x$ coating. The surface-modified cathodes were characterized by XRD, SEM, EDS, TEM techniques. XRD patterns of $ZrF_x$-coated $Li[Co_{1/3}Ni_{1/3}Mn_{1/3}]O_2$ revealed that the coating did not affect the crystal structure of the parent powder. SEM and TEM images showed that $ZrF_x$ nano-particles were formed as a coating layer, and EDS data confirmed that $ZrF_x$ distributed uniformly on the surface the powder. Capacity retention of coated samples at high C rates was superior to that of pristine sample. However, as the coating concentration increases beyond the optimum concentration, the rate capability was deteriorated. Whereas, as the increase of coating concentration to 2.0 wt %, the cyclic performances of the electrodes under the severe conditions (high cut-off voltage, 4.8 V, and high measurement temperature, $55^{\circ}C$) were improved considerably.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.134-137
• /
• 2004

새로운 리튬 2차전지용 양극활물질인 Li[NiMnCo]O2를 간단히 합성할 수 있는 방법과 Si의 doping에 의해 그 특성을 향상하였다. 원하는 당량비의 Li, Ni, Co, Mn의 nitrate를 고순도의 에탄올에 용해하고 여기에 Si의 원료물질로서 poly(methyl phenyl siloxane)을 원하는 양(전체 전이금속 이온의 $2{\sim}10\;mol%$)만큼 첨가한 후 약 30분 정도 교반하였다. 이 용액을 약 $70{\sim}80^{\circ}C$ 정도의 온도에서 고점도의 진흙 상태가 될 정도로 가열하고 $450{\sim}500^{\circ}C$의 온도에서 약 5시간 정도 열처리 하여 유기물이 없는 상태의 전구체를 제조하였다. 이 전구체를 분말형태로 분쇄하고 $600{\sim}650^{\circ}C$ 정도의 온도에서 3시간, $900{\sim}950^{\circ}C$ 정도의 온도에서 5시간 연속적으로 열처리 하여 최종 활물질을 제조하였다. 이렇게 제조된 활물질은 175mAh/g 정도의 높은 비용량을 나타내었으며 4.5V 충전 조건에도 우수한 수명특성을 나타내었다. Si이 doping되지 않은 활물질에 비해 Si이 doping된 물질은 율특성, 수명특성에서 보다 우수한 특성을 나타내었는데 이것은 층상구조 활물질의 격자상수 증가와 impedance 증가 억제에 기인한 것으로 분석되었다.

• Journal of the Korean Chemical Society
• /
• v.44 no.4
• /
• pp.322-327
• /
• 2000

A new absorption spectrometric method for the determination of the Cr$_2O_7^{2-}$ ionin acidic media has been developed. The new method is based on the oxidation-reduction reaction of the HCr$O_4^-$ ion with H$_2$O$_2$forming a deep blue CrO(O$_2$) $_2$ andis coupled with a technique of flow injection analysis(FIA). The new method provides a linear calibration curve which accurately follows the Beer's law over a wide range of the analytical concentrations(2.0 ${\times}$ $10^{-6}$M~8.0 ${\times}$ $10^{-3}$M) of K$_2$Cr$_2$O$_2$. The sensitivity of the new method is approximately two times greater than the current method and the effects of the interfering substances such as V, Co, Ni, Fe, and Mn are almost negligible except Cu.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.287-292
• /
• 1982

Nonohmic properties of ZnO ceramics with various small amounts of additives were studied in relation to experimental methods, additive contant and sintaring temperature. The kinds of additives used to following chemicals were basic additives ($0.5Bi_2O_3$, $0.3BaCO_3$, $0.5MnCO_3$, $0.5Cr_2O_3$, $0.1KNO_3$), $TiO_2$ and $Al(OH)_3$. Expecially, this study has focused on the effectsof $TiO_2$ and $Al(OH)_3$ in ZnO ceramics with the basic additives. SEM studies indicated that the addition of TiO2 promoted grain growth but retarded grain growth with the addition of $Al(OH)_3$. Also, in the case of calcination of ZnO with $TiO_2$ and ZnO with $Al(OH)_3$ previously, grain size of ZnO with $TiO_2$ was larger and that of ZnO with Al(OH)3 was smaller in comparison to the case with out calcination. From the viewpoint of nonohmic exponent and nonohimic resistance, electrical characteristics of ZnO, $TiO_2$ and the basic additives was more effective than that of ZnO, $Al(OH)_3$ and the basic additives. Nonohmic exponent and nonohmic resistance of ZnO, $TiO_2$ and the basic additives was 11-13 and 40-65 respectively.