• E2M - 전기 전자와 첨단 소재
• /
• 제12권7호
• /
• pp.7-11
• /
• 1999

Fully sealed field emission display in size of 4.5 inch has been fabricated using single-wall carbon nanotubes-organic vehicle com-posite. The fabricated display were fully scalable at low temperature below 415$^{\circ}C$ and CNTs were vertically aligned using paste squeeze and surface rubbing techniques. The turn-on fields of 1V/${\mu}{\textrm}{m}$ and field emis-sion current of 1.5mA at 3V/${\mu}{\textrm}{m}$ (J=90${\mu}{\textrm}{m}$/$\textrm{cm}^2$)were observed. Brightness of 1800cd/$m^2$ at 3.7V/${\mu}{\textrm}{m}$ was observed on the entire area of 4.5-inch panel from the green phosphor-ITO glass. The fluctuation of the current was found to be about 7% over a 4.5-inch cath-ode area. This reliable result enables us to produce large area full-color flat panel dis-play in the near future. Carbon nanotubes (CNTs) have attracted much attention because of their unique elec-trical properties and their potential applica-tions [1, 2]. Large aspect ratio of CNTs together with high chemical stability. ther-mal conductivity, and high mechanical strength are advantageous for applications to the field emitter [3]. Several results have been reported on the field emissions from multi-walled nanotubes (MWNTs) and single-walled nanotubes (SWNTs) grown from arc discharge [4, 5]. De Heer et al. have reported the field emission from nan-otubes aligned by the suspension-filtering method. This approach is too difficult to be fully adopted in integration process. Recently, there have been efforts to make applications to field emission devices using nanotubes. Saito et al. demonstrated a car-bon nanotube-based lamp, which was oper-ated at high voltage (10KV) [8]. Aproto-type diode structure was tested by the size of 100mm $\times$ 10mm in vacuum chamber [9]. the difficulties arise from the arrangement of vertically aligned nanotubes after the growth. Recently vertically aligned carbon nanotubes have been synthesized using plasma-enhanced chemical vapor deposition(CVD) [6, 7]. Yet, control of a large area synthesis is still not easily accessible with such approaches. Here we report integra-tion processes of fully sealed 4.5-inch CNT-field emission displays (FEDs). Low turn-on voltage with high brightness, and stabili-ty clearly demonstrate the potential applica-bility of carbon nanotubes to full color dis-plays in near future. For flat panel display in a large area, car-bon nanotubes-based field emitters were fabricated by using nanotubes-organic vehi-cles. The purified SWNTs, which were syn-thesized by dc arc discharge, were dispersed in iso propyl alcohol, and then mixed with on organic binder. The paste of well-dis-persed carbon nanotubes was squeezed onto the metal-patterned sodalime glass throuhg the metal mesh of 20${\mu}{\textrm}{m}$ in size and subse-quently heat-treated in order to remove the organic binder. The insulating spacers in thickness of 200${\mu}{\textrm}{m}$ are inserted between the lower and upper glasses. The Y\ulcornerO\ulcornerS:Eu, ZnS:Cu, Al, and ZnS:Ag, Cl, phosphors are electrically deposited on the upper glass for red, green, and blue colors, respectively. The typical sizes of each phosphor are 2~3 micron. The assembled structure was sealed in an atmosphere of highly purified Ar gas by means of a glass frit. The display plate was evacuated down to the pressure level of 1$\times$10\ulcorner Torr. Three non-evaporable getters of Ti-Zr-V-Fe were activated during the final heat-exhausting procedure. Finally, the active area of 4.5-inch panel with fully sealed carbon nanotubes was pro-duced. Emission currents were character-ized by the DC-mode and pulse-modulating mode at the voltage up to 800 volts. The brightness of field emission was measured by the Luminance calorimeter (BM-7, Topcon).

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.65-65
• /
• 2018

갈바륨 도금강판은 알루미늄의 우수한 차폐 특성과 내열성, 열 반사성을 가지며 아연의 희생방식 특성을 겸비하여 동일 부착량의 용융 아연도금 및 알루미늄 도금강판에 비해 우수한 내식성을 나타낸다고 알려져 있다. 또한 이것은 표면이 미려하고 경제성이 높아 건자재 용도로 현재까지도 세계적으로 널리 이용되고 있다. 여기서 지칭하는 바륨 도금강판(galvalume steel)은 아연과 알루미늄 도금강판의 장점을 접목하기 위해 55 Al-43.4 Zn-1.6 Si (wt.%)로 구성되어 개발된 3원계 성분의 합금도금강판이다. 한편, 최근에는 강재의 내식성을 향상시키기 위한 다양한 연구 결과에 의해 Zn-Al-Mg의 3원계 합금도금강판도 개발되어 사용되고 있다. 이것은 기존의 아연도금 강판 보다 10배 정도의 우수한 내식성을 나타내는 것으로 보고되고 있다. 특히, 이것은 도금된 평판부의 내식성은 물론 절단된 도금 단면부의 내식성도 매우 우수하다고 알려져 있다. 그러나 상기한 갈바륨 도금강판의 경우에는 도금된 표면부에 비해 단면부의 내식성이 상대적으로 취약한 것으로 알려져 있다. 따라서 본 연구에서는 갈바륨 도금강판의 내식성을 종합적으로 향상시키기 위하여 이 갈바륨 도금강판 상에 PVD 스퍼터링법에 의해 Mg 코팅막의 제작을 시도하였다. 여기서 Mg 코팅막은 후처리 된 갈바륨 도금강판 상에 Ar 공정압력 2 및 20 mTorr 조건 중 1.5 및 $3{\mu}m$ 두께로 제작하였다. 또한 제작한 코팅막에 대해서는 모폴로지 관찰(SEM) 및 결정구조 분석(XRD)을 하였고, 분극측정, 염수분무 시험(SST) 및 복합부식 시험(CCT)에 의해 표면 및 단면부의 내식성평가를 수행하였다. 또한 여기서는 염수분무 및 복합부식 시험 후의 시험편도 채취 하여 표면 및 단면부위에 대한 원소조성 분석(EPMA)과 결정구조 분석(XRD)을 실시하였다. 이상의 실험 결과에 의하면, 본 실험에서 제작한 Mg 코팅막은 그 두께가 두꺼울수록 표면 Mg 결정립의 크기가 증가하였고, 그 부식속도가 증가하는 경향을 나타내었다. 또한 여기서는 공정압력이 높은 조건에서 제작한 막일수록 Mg(002)면 피크 강도가 감소하고 Mg(101)면 피크의 배향성이 증가하였다. 그때 그 막의 내식성은 향상되는 경향을 나타내었다. 그리고 종합적으로 염수분무 및 복합부식 시험 결과에 의하면 Mg이 코팅된 갈바륨 도금강판은 기존 갈바륨 도금강판 보다 내식성이 현저히 향상되었다. 특히, 단면부 내식성의 경우에는 기존 대비 5배 이상 향상되는 경향을 나타내었다. 여기서 단면부 내식특성 분석을 위한 EPMA 원소조성 분석 결과에 의거하면, 부식 초기에는 마그네슘의 부식생성물에 의해 단면부가 치밀하게 보호되고 있음을 확인할 수 있었다. 그 이후에는 부식이 지속적으로 진행됨에 따라 갈바륨 도금층에서 용출된 알루미늄 및 아연 성분이 마그네슘과 함께 치밀한 부식생성물을 형성하여 단면부를 차폐함에 따라 단면부의 내식성이 크게 향상된 것으로 생각된다. 이러한 부식생성물의 결정구조 분석 결과에 따르면, 염수분무와 복합부식 시험에서는 공통적으로 MgO, $Mg(OH)_2$ 이외에도 Simonkolleite상 등이 형성되었다. 또한 건-습 반복 부식시험인 복합부식시험 후에는 $Mg_5(CO_3)_4(OH)_24H_2O$(Hydromagnesite)상 등이 형성됨을 확인할 수 있었다. 즉, 본 실험에서 후처리된 갈바륨 도금강판 상에 제작한 마그네슘 코팅막의 경우에는 상기와 같은 다양한 부식반응에 의해 표면 및 단면부에 형성된 Mg계 부식생성물과 $Zn_5(OH)_8Cl_2H_2O$(Simonkolleite)상에 의해서 표면은 물론 단면부 내식성이 크게 향상된 것으로 사료된다.