• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.277-281
• /
• 2003

Effects of $CaF_2$ addition as a filler on the high frequency dielectric properties and sintering of CaO-$Al_2O_3-SiO_2-B_2O_3$(CASB) and ZnO-MgO-$B_2O_3-SiO_2$(ZMBS) glass composites were investigated. The optimal glass composition in the CASB system was 33.0CaO-$17.0Al_2O_3-35.0SiO_2-15.0B_O_3$(in wt%). The corresponding dielectric properties were k=8.1 and $Q{\times}fo$=1,200GHz. The sintering temperature was $800{\mu}m$. In case of 2MBS system, 25.0ZnO-25.0MgO-20.0$B_2O_3-30.0SiO_2$(in wt%) glass showed k=6.8 and $Q{\times}fo$=5,200GHz when it was sintered at $750^{\circ}C$. The maximum amount of $CaF_2$ in the CASB and 2MBS glass system without any detrimental effect on the sintering was 25.0 v/o and 15.0 v/o, respectively. The addition of $CaF_2$ in the glass systems improved the high frequency dielectric properties. In case of CASB+$CaF_2$ composite, k was 7.1 and $Q{\times}fo$ was 2,300GHz. And in case of 2MBS+$CaF_2$ composite, k was 5.9 and $Q{\times}fo$ was 8,100GHz. $CaF_2$ addition also reduced sintering temperature. Effects of $CaF_2$ on the dielectric and sintering properties was analyzed in terms of viscosity and crystallization behavior changes due to the interaction between $CaF_2$ and the glass systems.

• 한국세라믹학회지
• /
• 제37권12호
• /
• pp.1178-1186
• /
• 2000

타일의 내마모성과 내산성을 향상시키기 위해 결정화유리가 최근에 새로운 유약 재료로서 소개되고 있다. 신 유약의 연구에 사용된 조성은 $Ca_2$ZrSi$_4$O$_{12}$ 상에 근접하는 CaO-ZrO$_2$-SiO$_2$계의 유리조성의 분말로, 마이크로파 가열 (2.45 GHz)에 의해서 900-120$0^{\circ}C$의 0-20분간 소성되어 평가되었다. 그 결과, 100$0^{\circ}C$ 이상에서 소성한 시편은 내부 결정화를 나타내었으며, 결정상은 미세(5$mu extrm{m}$)한 크기를 갖는 $Ca_2$ZrSi$_4$O$_{12}$가 주 결정상이며, $Ca_2$ZrSi$_4$O$_{12}$, CaSiO$_3$, SiO$_2$의 세 상이 나타났다. 소결체의 미세구조는 사용한 유리분말의 입도의 영향을 받았다. 미세분말 (<38$\mu\textrm{m}$)을 이용한 소결체의 조직이 조세분말 (45-150$\mu\textrm{m}$)의 경우보다 수축율면에서 높았으며 낮은 기공도를 갖는 미세구조를 가졌다. 마이크로파에 의한 유리분말의 소성은 1000-120$0^{\circ}C$ 구간에서 10분 이내 결정화가 완료되는 급속 가열 공정이었으며 CaO-ZrO$_2$-SiO$_2$계 결정화 유리 제조에 균일한 체적가열을 할 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제23권4호
• /
• pp.323-326
• /
• 2010

$(Zn_{1-x}Ca_x)_2SiO_4$:Mn phosphors doped with Ca were synthesized by solid state reaction method. $(Zn_{1-x}Ca_x)_2SiO_4$:Mn phosphors showed XRD patterns of Willemite structure. Also, $CaSiO_3$ structure and new peak near 610 nm in $(Zn_{1-x}Ca_x)_2SiO_4$:Mn with increasing value of x were observed from XRD and PL. The new peak near 610 nm in $(Zn_{1-x}Ca_x)_2SiO_4$:Mn with doping Ca was attributed to formation of $CaSiO_3$.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.410-416
• /
• 1999

The reactivity of three kinds of spinels which CaO-Al2O3-SiO2 slag was investigated in terms of mineral phases and microstructures. New crystal products were not formed by reaction of 12CaO.7Al2O3 in the slag with spinels and free MgO components was preferenctially dissolved into slag for MgO-rich spinel and stoichiometric spinel. Meanwhile mineral phase was changed from 12CaO.7Al2O3 to CaO.Al2O3 to CaO.2Al2O3 finally to CaO.6Al2O3 having high melting point for Al2O3 -rich spinel. The Fe-oxide component of the slag was taken up by only stoichiometric spinel grains within the spinel clinker and the trapped amount of Fe-oxide was independent of MgO content of MgO in spinel clinker the more th resistance to slag corrosion but the less resistance to slag penetration.

• 한국세라믹학회지
• /
• 제31권6호
• /
• pp.629-636
• /
• 1994

The ferrimagnetic glass-ceramics in the system Fe2O3-CaO-SiO2 for hyperthermia were investigated. Glasses could be prepared up to the content of 40 wt% of Fe2O3 and below the weight ratio of 1.0 of CaO/SiO2. The maximum saturation magnetization and the maximum coercive force were 29.85 emu/g and 340.1 Oe respectively, for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. And for a glass 40Fe2O3.30CaO.30SiO2 composition the maximum saturation magnetization and the maximum coercive force were 18.47 emu/g and 374.4 Oe heat-treated at 1,00$0^{\circ}C$ and 90$0^{\circ}C$ for 8 hours respectively. The maximum hysteresis loss was 1,726.3 cal/g for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. It was found that the ferrimagnetic Fe2O3.CaO.SiO2 glass-ceramics was little injurious to human body as results of biocompatibility test and biotoxicity test.

• Korean Chemical Engineering Research
• /
• 제60권4호
• /
• pp.594-605
• /
• 2022

마이크로웨이브 소성로를 이용하여 굴 패각을 소성하여 CaO 제조하였다. 제조된 CaO를 수화 반응시켜서 Ca(OH)₂를 분석하였다. 합성한 Ca(OH)₂를 주성분으로하여 외부용 수성 도료 배합하였다. 굴 패각(325 mesh, 43 ㎛)은 (a) 950 ℃/1 시간와 (b) 1,150 ℃/1 시간 동안 탈탄산화반응을 시켜 CaO를 제조하였다. (a)의 소성 조건에서는 CaO 56.7 wt%이고 (b)의 소성 조건에서는 CaO 100 wt%였다. 굴 패각의 소성에 의한 CaO를 석회석의 경우와 비교하기 위하여 석회석(25~30 mm)을 950 ℃/1 시간 동안 탈탄산화 반응시켜서 CaO를 제조하였으며, XRD 분석 결과 CaO 100 wt%로 분석 되었다. 굴 패각의 소성 조건인 (b) 1,150 ℃, 1시간으로 CaO를 제조하여 수화 반응을 통하여 Ca(OH)₂를 합성하였다. 제조된 CaO의 수화 조건은 (a) CaO : H₂O(100 g : 200 g)과 (b) CaO : H₂O(100 g : 400 g)로 수화 반응성을 실시하였다. 수화 반응 결과, 저 반응성으로 확인 되었다. 100 wt%의 Ca(OH)₂를 합성하였다. 특히 (a)의 수화 조건에서 합성한 Ca(OH)₂는 판상형으로 분석되었다. 굴 패각으로 합성한 Ca(OH)₂를 주성분으로 외부용 수성 도료를 배합하였다. 외부용 수성 도료 표준 규격(KS M 6010)의 15개 항목에 대하여 분석하였을 때 냉동안정성을 제외한 다른 모든 기준에 적합한 것을 확인하였다.

• 자원리싸이클링
• /
• 제20권3호
• /
• pp.55-61
• /
• 2011

금속급 실리콘(MG-Si)을 태양전지용 실리콘(SOG-Si)으로 정제하기 위한 경제적인 프로세스를 구축하기 위하여 1823 K에서 CaO-$SiO_2$ 계 슬래그에 의한 붕소의 제거에 대하여 조사하였다. 본 연구에서 CaO-$SiO_2$와 $CaCO_3-SiO_2$ 슬래그의 염기도(%CaO/$%SiO_2$) 증가에 따라 B의 제거율은 각각 63%와 73%까지 증가하였다. 그러나 Ar 가스에 의한 슬래그와 실리콘의 교반 시간의 영향은 나타나지 않았다. 그리고 CaO-$SiO_2$ 계 슬래그에 $Na_2CO_3$를 첨가하였으나 그 영향은 크지 않았다. $CaCO_3-SiO_2$ 슬래그(염기도=1.2)에 의해 3회 처리한 결과 B의 농도는 1.03 ppm까지 감소하였다.

• Korean Chemical Engineering Research
• /
• 제57권6호
• /
• pp.812-825
• /
• 2019

국내에서 채광되는 백운석(dolomite, $CaMg(CO_3)_2$)을 회분식 형태의 마이크로웨이브 소성로($950^{\circ}C/60min$)에 의해 소성하여 경소백운석($CaO{\cdot}MgO$)을 제조하였다. 국내에서 산출된 두 개의 백운석 시료를 대상으로 경소백운석($CaO{\cdot}MgO$) 제조 후 수화 특성을 규명한 결과 반응성이 다름을 규명하였다. 경소백운석($CaO{\cdot}MgO$)의 수화 특성의 반응성을 이용하여 강산성 양이온 교환수지와 반응 시켜서 MgO를 분리하는 조건을 실시하였다. 분리 실험 조건은 경소백운석($CaO{\cdot}MgO$)과 $R-SO_3H$ (1:12 mass %)로 칼슘이온 흡착($Ca-(R-SO_3)_2$)하여 MgO를 분리하였다. 분리 후 MgO의 함량은 94 mass % 이상으로 분리되었다. 분리된 MgO를 $950^{\circ}C$, 60 min 동안 열처리 후 MgO의 순도는 96 mass %로 나타났다. 그리고칼슘 이온이 흡착된강산성 양이온교환수지($Ca-(R-SO_3)_2$)와 NaOH, $CO_2$ gas 반응에 의해서 98 mass %의 $CaCO_3$를 합성하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.195-195
• /
• 2008

CAS계 유리에 $CaCO_3-Al_2O_3$ 혼합물 및 화합물을 10, 30 wt% 첨가하여 저온 소걸 및 마이크로파 유전 특성을 고찰하였다. CAS계 유리의 연화온도는 $841^{\circ}C$ 이며, CAS계 유리에 $CaCO_3$ 와 30 wt%의 $CaCO_3-Al_2O_3$ 혼합물을 melting되며, 10 wt%의 $CaCO_3$, $Al_2O_3$, $1CaCO_3-1Al_2O_3$ 혼합물 및 $CaAl_2O_4$ 화합물를 10 wt% 첨가하였을 때 $900^{\circ}C$ 이하에서 소걸이 가능하였다. 복합체의 XRD 상 분석 결과, CaCO3를 첨가하였을 때에는 모든 조성이 비정질을 나타내었고, $Al_2O_3$와 $1CaCO_3-1Al_2O_3$ 혼합물은 $Al_2O_3$ 결정상이 생성되었고, $CaAl_2O_4$ 화합물은 $CaAl_2Si_2O_8$의 hexagonal와 anorthite 결정상이 생성되었다. 따라서 CAS-10 (A, C-A, CA) 복합체는 $900^{\circ}C$에서 각각 유전율 ($\varepsilon_r$) 6.4, 6.9, 5.15 와 품질계수 ($Q^*f$) 2,400, 1,500, 3,000의 마이크로파 유전 특성을 나타내어 LTCC 기판 재료로 사용이 가능하며, 특히 $CaAl_2O_4$ 화합물을 사용하였을 때 가장 우수한 유전 특성을 나타내는 것을 확인하였다.

• 자원리싸이클링
• /
• 제15권4호
• /
• pp.27-35
• /
• 2006

본 연구에서는 명반석 $[K_{2}SO_{4}{\cdot}Al_{2}(SO_{4})_{3}{\cdot}4Al(OH)_{3}]$을 고로수쇄슬래그의 활성화제로서 활용하기 위하여 하소 명반석과 고로수쇄슬래그의 수화반응 특성을 연구하였다. $650{\circ}C$에서 하소시킨 명반석은 $KAl(SO_{4})_{2}$와 $Al_{2}O_{3}$로 구성되어 있으며 하소 명반석-소석회-석고 계에서 하소 명반석은 소석회 및 석고와 $2KAl(SO_{4})_{2}+2Al_{2}O_{3}+13Ca(OH)_{2}+5CaSO_{4}{\cdot}2H_{2}O+73H_{2}O{\rightarrow}3(3CaO{\cdot}Al_{2}O_{3}{\cdot}3CaSO_{4}{\cdot}32H_{2}O)+2KOH$와 같이 반응하여 ettringite($3CaO{\cdot}Al_{2}O_{3}{\cdot}3CaSO_{4}{\cdot}32H_{2}O)$를 형성한다. 하소 명반석-고로수쇄슬래그 계에서는 하소 명반석에서 용해된 황산이온($SO_{4}^{2-}$)이 소석회와 반응하여 석고를 형성시키고, 석고는 다시 고로수쇄슬래그와 반응하여 ettringite를 형성시키면서 슬래그의 수화반응을 촉진시키기 때문에 하소 명반석을 고로수쇄슬래그의 활성화제로 사용할 수 있다.