• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.859-866
• /
• 2003

When calcium sulfoaluminate-based expansive cement was hydrated, ettringite and monosulfate were mainly formed. The crack of hardened cement was prevented by compensating drying shrinkage due to formation of the above hydrates. In order to study the hydration properties of calcium sulfoaluminate-based expanding cement, 3CaOㆍ3Al$_2$O$_3$ㆍCaSO$_4$(C$_4$A$_3$S) was prepared by chemical synthesis, and then the hydration of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.$2H_2O$-C$_3$A system_was characterized. Good $C_4$A$_3$S phase was prepared at $1300^{\circ}C$ by chemical synthesis, and the main hydration product of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.2$H_2O$ system was ettringite. In the case of hydration $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$ㆍ 2$H_2O$-C$_3$A system, ettringite was formed in the early period and it was transformed into monosulfate while consumed gypsum.

• Journal of the Korean Ceramic Society
• /
• v.37 no.5
• /
• pp.459-465
• /
• 2000

3CaO.3Al2O3.CaSO4(C4A3)clinker was prepared by solid state reaction and then its hydration property was investigated. C4A3 clinker was fired at various temperatures in the range of 700~135$0^{\circ}C$. The hydration of it was studied by XRD, DSC, Solid-state 27Al MAS NMR and SEM. According to the results, the Ca4A3 clinker was produced by reacting calcium aluminates with CaSO4 and Al2O3 and C4A3 was formed as a main phase after calcining at 120$0^{\circ}C$. The hydration products were mainly calcium monosulfoaluminate hydrate and Al(OH)3, and they were produced after 2hrs of hydration. However the hydration rate was about 74% at 3days.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.17-22
• /
• 2004

The microwave dielectric properties of $CaZrO_3$ ceramics with addition of $CaTiO_3$ were studied. The effect of glass addition on the low-temperature sintering and microwave dielectric properties of $CaZrO_3-CaTiO_3$ ceramics were also evaluated to develop the materials for functional substrates of low-temperature co-fired ceramics. When $10-20 wt\%$ of lithium borosilicate glass was added, the sintering temperature of the $CaZrO_3-CaTiO_3$ ceramics decreased from $1450^{\circ}C$ to below $900^{\circ}C$. As the $T_f$ of glass frits and $CaZrO_3$ are slightly negative and that of $CaTiO_3$ is significantly positive, zero $T_f$ could be realized by mixing an appropriate amount of $CaTiO_3$ with $CaZrO_3$. The $CaZrO_3-CaTiO_3$ ceramics sintered at $875^{\circ}C$ with $15wt\%$ glass frits showed the relative density of $98\%$, permittivity of 23, quality factor of 2500 GHz, and temperature coefficient of resonant frequency of $ -3 ppm/^{\circ}C$.

• Journal of Applied Biological Chemistry
• /
• v.43 no.1
• /
• pp.5-11
• /
• 2000

Three cDNA clones encoding rice calmodulin (CaM) isoforms (OsCaM-1, OsCaM-2, and OsCaM-3) were isolated from a rice cDNA library constructed from suspension-cultured rice cells treated with fungal elicitor. The coding regions of OsCaM-1 and O.sCaM-2 were 89% homologous at DNA Ievel, whereas the 5' and 3' untranslated regions were highly divergent. The polypeptides encoded by OsCaM-1 and OsCaM-2 was identical except two conservative substitution at position 8 and 75. The coding region of OsCaM-3 was consist of a typical conserved CaM domain and an additional C-terminal extension. The amino acid sequence of conserved CaM domain of OsCaM-3 shared only 86% identity with that OsCaM-1. The OsCaM-3 cDNA is belongs to a novel group of calmodulin gene due to its C-terminal extension of 38 amino acids, a large number of which are positively charged. The extension also contains a C-terminal CaaX-box prenylation site (CVlL). Genomic Southern analysis revealed at least six copies of CaM or CaM-related genes, suggesting that calmodulin may be represented by a small multigene family in the rice geneme. Expression of OsCaM gene was examined through Northern blot analysis. Transcript level of OsCaM-3 was increased by treatment with a fungal elicitor, whereas the OsCaM-1 and OsCaM-2 genes did not respond to the fungal elicitor. The expression of OsCaM-3 gene was remarkable inhibited in the rice cells treated with cyclosporine A, calcinurin inhibitor.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.349-352
• /
• 2005

In this work, effects of limestone powder on hydration of $C_3A-CaSO_4\cdot2H_2O$ system was discussed based on the XRD Quantitative analysis, and the possibility of Delayed Ettringite Formation was also discussed. The early hydration of $C_{3}A$ was delayed by addition of $CaCO_{3}$ powder. The delay effect was enhanced by increasing of $CaCO_{3}$ content and finer powder of $CaCO_{3}$ addition. After consumption of $CaSO_4\cdot2H_2O$, the reaction of $CaCO_{3}$ is started. Delayed Ettringite Formation would take place because monosulfoaluminate is not stable in presence of $CaCO_{3}$. In order to prevent the delayed ettringite formation in $C_3A-CaSO_4\cdot2H_2O-CaCo_3$ system, the reduction of monosulfoaluminate formation is important. Therefore, by increasing the amount of $CaCO_{3}$ addition and finer $CaCO_{3}$ powder addition, the delayed ettringite formation can be prevented.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1417-1422
• /
• 1994

Effect of MgO, CaSO4, and CaF2 addition on the formation of clinker minerals in portland cement have been investigated by measuring the amounts of free-CaO and C3S in the fired specimens and analyzing the Mg and S concentration in C3S and C2S. It was found that CaSO4 inhibited C3S formation but MgO addition offset this effect of CaSO4. MgO addition also enhanced the mineralizing effect of CaSO4+CaF2, resulting in the acceleration of C3S formation. It was suggested that Mg might inhibit the formation of sulphate compounds rim around C2S and thus C2S+CaOlongrightarrowC3S reaction was facilitated.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.1
• /
• pp.11-21
• /
• 2004

Crystallization of CaC $O_3$ from the solutions of various degrees of supersaturation was carried out by a spontaneous precipitation method. The solution was kept at $25^{\circ}C$ and pH 6.9∼8.8. The solution compositions were varied in two ways: (1) The total carbonate, [C $O_3$]$_{Τ}$, to total calcium. [Ca]$_{Τ}$, ratios vary as ; [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ >1. [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$=1, and [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$<1. (2) The total calcium concentration, [Ca]$_{Τ}$, held at 0.02 mo1/d $m^3$, 0.2 mo1/d $m^3$, and 0.4 mo1/d $m^3$. We found that the CaC $O_3$ phase crystallized from the solutions of [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ $\geq$ 1 was mostly calcite with less than 1% of vaterite, while the CaC $O_3$ crystals precipitated from low carbonate concentration toward calcium concentration, [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ < 1, were dominated by vaterite crystals. It appears that the polymorph of CaC $O_3$ precipitate was mainly controlled not by the calcium concentration but by the carbonate concentration during the spontaneous precipitation. Also, we found that the surface roughness of vaterite increased with decreasing carbonate concentration from 0.8 or 0.5 of [C $O_3$]$_{Τ}$/[Ca]$_{Τ}$ ratios and the surface area of vaterite increased from 5.64∼7.34 $\mu\textrm{m}$ to 8.39∼10.3 $\mu\textrm{m}$.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.24-30
• /
• 2003

A formation and conversion of AFm phases decisively play role in the hydration, hardening and corrosion processes of various cement. In this study, the conversion of Alumino-Ferrite Monohydrates(AFm) phases under the addition of $CaCO_3,;CaCl_2;and;CaSO_4{cdot}2H_2O$was investigated by the XRD quantitative analysis. The thypical AFm phases are $M_S(monosulfoaluminate),;M_C(monocarboaluminate);and;M_{Cl}(monochloroaluminate and also Called Friedel's salts)$in this cementitious system, The conversion reaction were not occurred in $M_C-CaCO_3,;M_{Cl}-CaCO_3$ and $M_{Cl}-CaCl_2$system. However, in $M_S-CaCO_3$ system, ettringite and $monocarboaluminate(M_C)$ were formed. In $M_S-CaCl_2;system;M_S$ was transformed to Friedel's $salts(M_{Cl})$ and ettringite was formed. In the case of $CaSO_4{cdot}2H_2O$ addition, all AFm $phases(M_S,;M_C;and;M_{Cl})$ were transformed to ettringite. The order of stabilization of AFm phases under $CaCO_3,;CaCl_2;and;CaSO_4{cdot}2H_2O$ was as follows : $M_S< M_C

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.81-86
• /
• 2003

Microwave dielectric properties have been investigated in the$(1-x)CaTiO_3-xYAlO_3$ (x=0.1~1.0) solid solution system. The mixtures of $CaTiO_3$ and $YalO_3$using solid state method were sintered at various temperatures. Their dielectric constants and related temperature coefficients were strongly depend on the composition of the solid solution. The optimum properties were recorded as for ${\varepsilon}_r=47,$ $Q{\times}f_0$=35000 and ${\tau}_f=+11ppm/^{\circ}C$ without sintering agent. Even at $1200^{\circ}C$ full densification has been achieved with addition of $CaB_2O_4$ in the $0.75CaTiO_3-0.25YalO_3$ composition. The sample of $0.3 wt%-CaB_2O_4$ added $ 0.75CaTiO_3-0.25YalO_3$ sintered at $1300^{\circ}C$ for 3 h showed optimum microwave dielectric properties of ${\varepsilon}_r=47$, $Q{\time}f_0=37000$ and ${\tau}_f=+17ppm/^{\circ}C$, which demonstrates the promising candidates for microwave dielectric materials covering 5~7 GHz range.

• Journal of the Korean Chemical Society
• /
• v.53 no.3
• /
• pp.272-278
• /
• 2009

The optimized structures and vibrational frequencies for $Ca^+-(CO)_n$ and $Ca^+-(CO_2)_n$ (n=1,2) complexes were calculated with MP2 and B3LYP methods employing 6-311++G(2d,p) basis sets. Also the binding energies were investigated for all complexes to compare the stabilities. For $Ca^+-(CO)_n$ C-bonded complexes are more stable than O-bonded complexes. Two stable conformations, linear and $C_{2v}$ form, are possible for $Ca^+-(CO)_2$ complexes and the $C_{2v}$ form is more stable than the linear form. $Ca^+-(CO_2)_2$ also has two possible conformations and linear form has slightly lower energy than $C_{2v}$ form.