• Proceedings of the KWS Conference
• /
• 2000.10a
• /
• pp.256-259
• /
• 2000

High viscosity mixing powder is a very useful material for laser cladding. This material has a high viscosity so that it can be sticked to substrate. Therefore, Laser cladding can be performed on a curved or slope surface. Laser cladding can be easily performed with the material instead of wire that is difficult to be manufactured in some case. In this experiment, it was used a high viscosity mixing powder which consists of a high temperature flux and a bronze powder. And AC2B alloy material was used as a substrate. Flux prevents the clad layer from being oxidized and increases bonding property between substrate and cladding material. It makes possible to laser cladding at low level energy.

• Journal of Welding and Joining
• /
• v.28 no.1
• /
• pp.66-71
• /
• 2010

With large specific strength and outstanding corrosion resistance and erosion resistance in sea water, titanium and titanium alloy are widely used in heat exchanger production. In particular, pure titanium demonstrates outstanding molding performance and may be considered optimal for production of heat exchanger. Since titanium is very vulnerable to oxidation and embrittlement during welding, processes with less heat input are widely used, and laser welding is widely applied by considering production performance and shield etc in atmosphere. So far, 1st report and 2nd report compared and analyzed embrittlement degrees by bead colors of weldment through oxygen and nitrogen quantitative analysis and hardness measurement, and evaluated welding performance and mechanical properties of butt welding. This study evaluated field applicability of lap welding to heat exchange plate of LPG re-liquefaction device for ships through tensile stress test, hardness test and internal pressure test etc after deducing optimal weding condition and applying to actual heat exchange plate. In bead overlap area, the experiment produced sound welds with no porosity or defect by increasing and decreasing laser power, and tensile-shear test results indicated virtually the same tension and yield strength as base metal. As a result of measuring hardness at lateral cross section and bead overlap zone of actual heat exchanger welds, hardness difference within 20Hv was produced at base metal, HAZ and weldment, and as a result of pneumatic and hydraulic pressure test, no leakage occurred.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.3 no.2
• /
• pp.23-31
• /
• 1997

The results of high speed photography, acoustic emission detection and plasma UV radiation intensity measurement during CO2 laser welding of stainless steel 304 are presented. Video images with high spatial and temporal resolution allowed to observe the melt dynamics and keyhole evolution. The existence of a high speed melt flow which originated from the part of weld pool and flowed along the sides wall of keyhole was confirmed by the slag motion on the weld pool. the characteristic frequencies of flow instability and keyhole fluctuations at different welding speed were measured and compared with the results of Fourier analyses of temporal acoustic emission (AE) and light emission (LE) spectra. The experimental results were compared with the newly developed numerical model of keyhole dynamics. (The model is based on the assumption that the propagation of front part of keyhole into material is due to the melt ejection driven by laser induced surface evaporation.) The calculations predict that a high speed melt flow is induced at the front part of keyhole when the sample travel speed exceeds several 10mm/s. The numerical analysis also shows the hump formation on the front keyhole wall surface. Experimentally observed melt behavior and transformation of the AE and LE spectra with variation of welding speed are qualitatively in good agreement with the model predictions.

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 1998.11a
• /
• pp.0-0
• /
• 1998

-Part I- As market needs become more various, the production of smaller quantities of a wider variety of products becomes increasingly important. In addition, in order to meet demands for more efficient production, long-term unmanned factory operation is prevailing at a remarkable pace. Within this context, laser machines are gaining increasing popularity for use in applications such as cutting and welding metallic and ceramic materials. FANUC supplies four models of $CO_2$ laser oscillators with laser power ranging from 1.5㎾ to 6㎾ on an OEM basis to machine tool builders. However, FANUC has been requested to produce laser oscillators that allow more compact and lower-cost laser machines to be built. To meet such demands, FANUC has developed six models of Slab type YAG laser oscillators with output power ranging from 150W to 2㎾. These oscillators are designed mainly fur cutting and welding sheet metals. The oscillator has an exceptionally superior laser beam quality compared to conventional YAG laser oscillators, thus providing significantly improved machining capability. In addition, the laser beam of the oscillator can be efficiently transmitted through quartz optical fibers, enabling laser machines to be simplified and made more compact. This paper introduces the features of FANUC’s developed Slab type YAG laser oscillators and their applications. - Part II - All-solid-state lasers employing laser diodes (LD) as a source of pumping solid-state laser feature high efficiency, compactness, and high reliability. Thus, they are expected to provide a new generation of processing tools in various fields, especially in automobile and aircraft industries where great hopes are being placed on laser welding technology for steel plates and aluminum materials for which a significant growth in demand is expected. Also, in power plants, it is hoped that reliability and safety will be improved by using the laser welding technology. As in the above, the advent of high-power all-solid-state lasers may not only bring a great technological innovation to existing industry, but also create new industry. This is the background for this project, which has set its sights on the development of high-power, all-solid-state lasers with an average output of over 10㎾, an oscillation efficiency of over 20%, and a laser head volume of below 0.05㎥. FANUC Ltd. is responsible for the research and development of slab type lasers, and TOSHIBA Corp. far rod type lasers. By pumping slab type Nd: YAG crystal and by using quasi-continuous wave (QCW) type LD stacks, FANUC has already obtained an average output power of 1.7㎾, an optical conversion efficiency of 42%, and an electro-optical conversion efficiency of 16%. These conversion efficiencies are the best results the world has ever seen in the field of high-power all-solid-state lasers. TOSHIBA Corp. has also obtained an output power of 1.2㎾, an optical conversion efficiency of 30％, and an electro-optical conversion efficiency of 12%, by pumping the rod type Nd: YAG crystal by continuous wave (CW) type LD stacks. The laser power achieved by TOSHIBA Corp. is also a new world record in the field of rod type all-solid-state lasers. This report provides details of the above results and some information on future development plans.

• Proceedings of the KWS Conference
• /
• 1994.05a
• /
• pp.148-151
• /
• 1994

• Journal of Welding and Joining
• /
• v.25 no.3
• /
• pp.51-56
• /
• 2007

A $CO_2$ laser overlay was conducted by using a Fe-based powder on the AC2B aluminum substrate. Cracks and intermetallic compounds (IMC) were observed inconsistently along the interface between the overlay and post-molten layer. A scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) detected some Fe-rich IMC ($Fe_3Al$, FeAl) as well as the brittle Al-rich IMC ($Fe_2Al_5,\;FeAl_3$). Micro vickers hardness proved the formation of Al-rich IMC ($FeAl_3$) along the interface by showing HV0.1 $800{\sim}900$. Furthermore, nano indentation was successfully applied to investigate the behavior of IMC more precisely than the micro vickers hardness.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.639-643
• /
• 2002

The main purpose of this study was to investigate the formation mechanisms of imperfections such as irregular humps, outer cavity and inner cavity in the laser fusion zone of diamond saw blade. Laser beam welding was conducted to join two parts of blade; mild steel shank and Fe-Co-Ni sintered tip. The variables were beam power and travel speed. The microstructure and elements distributions of specimens were analyzed with SEM, AES, EPMA and so on. It was found that these imperfections were responded to heat input. Irregular humps were reduced in 10.4∼17.6kJ/m heat input range. However there were no clear evidences, which could explain the relations between humps formation and heat input. The number of outer cavity and inner cavity decreased as heat input was increased. Considering both possible defects formations mechanisms, it could be thought that outer cavity was caused by insufficient refill of keyhole, which was from rapid solidification of molten metal and fast molten metal flow to the rear keyhole wall at low heat input. More inner cavities were found near the interface of the fusion zone and sintered segment and in the bottom of the fusion zone. Inner cavity was mainly formed in the upper fusion zone at high heat input whereas was in the bottom at low heat input. Inner cavity was from trapping of coarsened preexist pores in the sintered tip and metal vapor due to rapid solidification of molten metal before the bubbles escaped.

• Laser Solutions
• /
• v.16 no.3
• /
• pp.1-10
• /
• 2013

In this study, Al-Si coated boron steel(1.2 mm) were laser welded by $CO_2$ laser and hot-stamping was applied to the laser joints. Tensile properties and microstructures of the joints were investigated before and after hot-stamping. Tensile and yield strengths of the as welded specimen similar with base metal and fracture occurred base metal of boron steel. Although, in case of heat treated specimen, fracture occurred fusion zone that Al segregated zone near the bond line. These could be explained by the existence of ferrite, in the Al segregated zone near the bond line and base metal of boron steel. Before hot-stamping, hardness of base metal is lower than fusion zone and heat affected zone in spite of exist Al segregation zone($Fe_3$(Al,Si)). So fracture occurred base metal. Although, after hot-stamping, microstructure of base metal and welds zone transformed to martensite and bainite except in Al segregation zone near the bond line that $Fe_3$(Al,Si) transformed to a-ferrite. So fracture occurred Al segregation zone near the bond line.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.42-42
• /
• 2010

알루미늄 합금은 질량 대비 강도가 우수하고 내식성 및 저온 특성이 양호하여 구조재로서 널리 사용되고 있다. 또한 그 사용 추세가 점점 증가 하고 있으며 알루미늄 합금의 용접을 위해 현재까지 다양한 용접 공정이 적용되었다. 일반적으로 GMAW, GTAW 등의 아크 용접과 박판의 경우 저항 점용접, 그 외의 $CO_2$ laser, Nd:YAG laser와 같은 고밀도 에너지 용접 공정에 의한 연구 결과들이 많이 발표 되었다. 하지만 알루미늄 합금의 특성 상 용접부에 기공과 균열과 같은 결함들이 각 공정에서 많이 발생하며 이러한 결함을 감소시키기 위한 용접기술에 관해 많은 연구가 진행되고 있다. 본 연구에서는 GMAW, Plasma-GMAW 공정을 적용하여 알루미늄 합금의 용접특성을 비교하였다. 알루미늄 합금 Al 5052, Al 6061 4mm 두께 모재에 대해 BOP(Bead On Plate) 용접실험을 실시하였으며 생산성 측면에서 각 공정에 따라 완전 용입 시 최대 용접 속도를 측정하여 비교하였다. 용접 품질 측면에서는 비드 표면 및 단면을 검사하고 인장시험을 수행하였으며, 용접 기공과 균열을 X-ray 촬영을 통해 비교하였다. 또한 고속카메라 촬영을 통해 용접 중 플라즈마로 인한 산화막 제거 효과를 확인하고 각 공정별 용접 시작부의 아크 안정성을 평가하였다. 인장시험 결과 모든 모드에서 모재에서 파단됨을 확인 하였고, Plasma-GMAW 공정의 경우 플라즈마의 예열효과로 인하여 GMAW 보다 완전용입 기준 용접속도가 빨랐으며, 청정작용도 우수한 것으로 확인되었다.

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.71-74
• /
• 2000

자기 구속 균열 시험법인 Tapered 시편 균열 시험법을 이용하여 Al-Mg 합금의 CW $CO_2$ 레이저 용접시 Mg 함량 변화에 따른 고온균열감수성 변화를 조사하였다. Mg 함량 1.9wt.%에서 최대균열감수성을 나타내고 있으며 이보다 Mg 함량이 증가하거나 감소하면 고온균열 감수성이 감소한다. 용접금속 결정립 크기 또한 고온균열감수성과 관련이 있으며 Mg 함량이 증가할수록 결정립이 미세화되며, 1.9wt.%Mg 이상에서 결정립이 미세화될수륵 고온균열 감수성 이 감소한다.