Etching Characteristics of Gold Thin Films using Inductively Coupled CF4/CI2/Ar Plasma (CF4/CI2/Ar유도 결합 플라즈마에 의한 gold 박막의 식각특성)

  • 김창일;장윤성;김동표;장의구
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.16 no.7
    • /
    • pp.564-568
    • /
    • 2003
  • The etching of Au thin films have been performed in an inductively coupled CF$_4$/Cl$_2$/Ar plasma. The etch rates were measured as CF$_4$ contents added from 0 to 30 % to Cl$_2$/Ar plasma, of which gas mixing ratio was fixed at 20%. Other parameters were fixed at an rf power of 700 W, a dc bias voltage of 150 V, a chamber pressure of 15 mTorr, and a substrate temperature of 3$0^{\circ}C$. The highest etch rate of the Au thin film was 3700 $\AA$m/min at a 10% additive CF$_4$ into Cl$_2$/Ar plasma. The surface reaction of the etched Au thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. XPS analysis indicated that Au reacted with Cl and formed Au-Cl, which is hard to remove on the surface because of its high melting point. The etching products could be sputtered by Ar ion bombardment.

Etching Characteristics of $SrBi_2Ta_2O_9$ Thin Film with adding $Cl_2$ into $CF_4/Ar$ plasma ($CF_4/Ar$ 플라즈마 내 $Cl_2$첨가에 의한 $SrBi_2Ta_2O_9$ 박막의 식각 특성)

  • Kim, Dong-Pyo;Kim, Chang-Il;Lee, Won-Jae;Yu, Byung-Gon;Kim, Tae-Hyung;Chang, Eui-Goo
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • /
    • pp.67-70
    • /
    • 2001
  • $SrBi_2Ta_2O_9$ thin films were etched at high-density $Cl_2/CF_4/Ar$ in inductively coupled plasma system. The chemical reactions on the etched surface were studied with x-ray photoelectron spectroscopy and secondary ion mass spectrometry. The etching of SBT thin films in $Cl_2/CF_4/Ar$ were chemically assisted reactive ion etching. The maximum etch rate was 1060 Am /min in $Cl_2$(20)/CF_4(20)/Ar(80). The small addition of $Cl_2$ into $CF_4$(20)/Ar(80) plasma will decrease the fluorine radicals and the increase CI radical. The etch profile of SBT thin films in $Cl_2/CF_4/Ar$ plasma is steeper than in $CF_4$/Ar plasma.Ā저會Ā저ﶖ⨀⡌ឫഀĀ᐀會Ā᐀㡆ﶖ⨀쁌ឫഀĀ᐀會Ā᐀遆ﶖ⨀郞ග堂瀀ꀏ會Āﶖ⨀〲岒ऀĀ᐀會Ā᐀䁇ﶖ⨀젲岒Ā㰀會Ā㰀顇ﶖ⨀끩Ā㈀會Ā㈀ﶖ⨀䡪Ā᐀會Ā᐀䡈ﶖ⨀Ā᐀會Ā᐀ꁈﶖ⨀硫Ā저會Ā저ﶖ⨀샟ගကĀ저會Ā저偉ﶖ⨀栰岒ఀĀ저會Ā저ꡉﶖ⨀1岒Ā저會Ā저Jﶖ⨀惝ග؀Ā؀會Ā؀塊ﶖ⨀ග㼀Ā切會Ā切끊ﶖ⨀⣟ගఀĀ搀會Ā搀ࡋﶖ⨀큭킢Ā저會Ā저

  • PDF

Recovery of Etching Damage of Etched PZT Thin Film by Inductively Coupled Plasma (유도결합 플라즈마에 의해 식각된 PZT 박막의 식각 Damage 개선)

  • 강명구;김경태;김창일
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.14 no.7
    • /
    • pp.551-556
    • /
    • 2001
  • In this work, the recovery of etching damage in the etched PZT thin film with $O_2$ annealing has been studied. The PZT thin films were etched as a function of Cl$_2$/Ar and additive CF$_4$ into Cl$_2$(80%) /Ar(20%). the etch rates of PZT thin films were 1600$\AA$/min at Cl$_2$(80%)/Ar(20%) and 1970 $\AA$/min at 30% additive Cf$_4$ into Cl$_2$(80%)/Ar(20%). In order to recover the characteristics of etched PZT thin films, the etched PZT thin films were annealed in $O_2$ atmosphere at various temperatures. From the hysteresis curves, ferroelectrical properties are improved by $O_2$ annealing process. The improvement of ferroelectric behavior is consistent with the increase of the (100) and (200) PZT phase revealed by x-ray diffraction (XRD). From x-ray photoelectron spectroscopy (XPS) analysis, intensities of Pb-O, Zr-O and Ti-O peak increase and the chemical residue peak is reduced by $O_2$ annealing. From the atomic force microscopy (AFM) images. it shows that the surface morphology of re-annealed PZT thin films after etching is improved.

  • PDF