• 한국전기전자재료학회논문지
• /
• 제17권11호
• /
• pp.1178-1185
• /
• 2004

In the atmosphere of $N_2$ gas, BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ polycrystal was grown by floating zone technique using BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ ceramics as a feed and SrTi $O_3$(1l0) single cystal as a seed. The dielectric constant and loss at 10 kHz, 100 kHz, and 1 MHz for the as-grown sample were measured as a function of temperature in the temperature range between -10$0^{\circ}C$ and 150 $^{\circ}C$ to find a dielectric peak with frequency dispersion at Curie point. The hysteresis loop showed that the grown sample had very small polarization which was 0-0.01 $\mu$C/$\textrm{cm}^2$ for the applied dc-electric fields from -7 kV/cm to +7 kV/cm. However, the normal hysteresis loop was appeared after oxygen annealing. The electric-field dependence of the dielectric constant for both the as-grown and the post-annealed samples was studied by measuring the dielectric constants as a function of the biased-electric fields and their tunability was figured out from it at room temperature(27 $^{\circ}C$) and cryotemperature( -73$^{\circ}C$). Tunability for the as-grown sample was 51 % and the figure of merit 20.4 at 10kHz with the biased electric-field of 12 kV/cm. The tunability for the grown sample may be increased up to 80 % if the electric field of 25 kV/cm is applied. Tunability for the post-annealed sample was 41 % and the figure of merit 10.3 at 10 kHz with the biased electric-field of 12 kV /cm. Post-annealing improved the crystallinity of the as-grown sample but decreased its tunability.ability.

• 한국세라믹학회지
• /
• 제41권10호
• /
• pp.771-776
• /
• 2004

Zr을 $8\%$ 첨가한 BZT 세라믹스를 종결정과 소재봉으로 사용하여 floating zone technique법으로 $Ba(Zr_{0.08}Ti_{0.92})O_3$ 다결정을 성장하였다. 열처리 효과를 알아보기 위하여 성장한 결정의 일부를 떼어내어 $1,200^{\circ}C$에서 10시간동안 산소 분위기에서 열처리하였다. $-100^{\circ}C$에서 $+150^{\circ}C$ 온도 영역에서 유전상수 및 유전손실을 10kHz, 100kHz, 그리고 1 MHz에서 측정하여 성장 결정의 유전특성을 알아보았다. 상온($27^{\circ}C$)과 저온($-73^{\circ}C$)에서 직류전장(-15kV/cm$\le$E$\le$15kV/cm)을 인가하면서 유전상수의 변화를 10kHz와 100kHz에서 측정함으로써 유전상수의 전장의존성을 알아보았다. 산소 열처리는 상온에서 10kHz의 튜너빌리티를 $47.5\%$에서 $51\%$로, 그리고 성능지수를 39.6에서 46.4로 향상시키었다. 바이어스 직류전장을 15kV/cm 이상 인가하면 성능지수가 46.4 이상으로 향상될 수 있으므로 이 물질이 마이크로파 전장 조절 소자에 응용될 수 있는 가능성이 있다.