• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.732-734
• /
• 2003

A solvothermal synthetic method to $BaTiO_3$ nanoparticle has been investigated in toluene solution with $BaTi(OR)_6$ as precursor. A precursor prepared from barium metal with toluene, isopropanol and titanium isopropoxide was used as a starting material. Weight ratio of precursor to solvent prepared in the mixture are 5/100, 10/100, 20/100 and 50/100wt%. At the weight ratio of 50/100wt%, $BaTiO_3$ butterfly twin crystalline(${\fallingdotseq}100nm$) was obtained after synthesis at $250^{\circ}C$ for 20hrs in an autoclave. X-ray diffraction and transmission electron microscopy showed that the product of 50/100wt% has crystallization. At 5/100, 10/100, and 20/100wt%, however, red colloidal solution was obtained after synthesis and crystalline phase of $BaTiO_3$ was not produced.

• Proceedings of the KIEE Conference
• /
• 2002.11a
• /
• pp.88-90
• /
• 2002

The $BaTi_4O_9$ ceramics with $Y_2O_3$(0.5wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD. The microwave dielectric properties also were investigated as a function of sintering temperature. According to the X-ray diffraction pattern of the $BaTi_4O_9$ ceramics with $Y_2O_3$(0.5wt%), the orthorhombic $BaTi_4O_9$ were appeared. In the case of $BaTi_4O_9+Y_2O_3$(0.5wt%) ceramics sintered $1400^{\circ}C$, dielectric constant. quality factor and temperature coefficient of resonant frequency were 41.3, 41,600, $+3.2ppm/^{\circ}C$, respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.171-171
• /
• 2003

공정기술의 향상으로 DRAM(dynamic random acess memory)의 고집적화가 이루어지고 있으며, 각 개별소자 및 셀 영역의 점유면적의 감소가 요구되어지고 있다. 따라서 기존에 사용하던 NO (Si$_3$N$_4$/SiO$_2$)박막보다 유전율이 높은 고유전물질에 대한 연구가 진행되고 있다. Ta$_2$O$_{5}$, $Y_2$O$_3$, HfO$_2$, ZrO$_2$,Nb$_2$O$_{5}$, BaTiO$_3$, SrTiO$_3$ 및 (BaSr)TiO등이 고유전물질로 연구되고 있는데 그 중 공정의 안정성, 누설전류의 우수성으로 인해 Ta$_2$O$_{5}$이 많이 연구되고 있다. 본 실험에서는 TiO$_2$가 8 mol%가 첨가된 Ta$_2$O$_{5}$의 열처리 온도에 따른 전기적, 유전특성을 살펴보려고 한다살펴보려고 한다

• Proceedings of the KIEE Conference
• /
• 1993.07b
• /
• pp.1116-1118
• /
• 1993

$({Ba}_{1-x}La_x)TiO_3,\;x=0{\sim}0.005$ specimens were fabricated by solid stste reaction method, and their PTC characteristics were examined. The gain growth is inhibited by La substitution, and it is confirmed that the specimens are crystallized at $900^{\circ}C$ from DTA analysis. The 0.003mol La substituded specimens show lowest resistivity and best PTC effects. Furthermore, the electrode sintered-specimens exhibite better PTC effects than no sintered-specimens.

• Journal of the Korean Chemical Society
• /
• v.37 no.7
• /
• pp.683-686
• /
• 1993

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.217-217
• /
• 2008

$BaTiO_3$는 perovskite 구조를 가지는 대표적인 강유전체 재료로서 MLCC (Multi Layer Ceramic Capacitor), PTC thermistor 등에 널리 사용되어지고 있으며, 그 특성을 향상시키기 위하여 많은 연구가 진행되고 있다. 현제 $BaTiO_3$ 분말 제조의 대표적인 합성법으로는 하소와 분쇄공정이 없는 수열합성법이 대표적이나, 나노 사이즈로 제작시 $BaTiO_3$는 마이크로 크기와 달리 입방정상으로 우세한 상태로 존재한다. 이는 제조과정 중의 hydroxyl defect의 영향과 나노 분말의 표면에너지 증가 때문이라고 보고된다. 따라서 본 연구는 이러한 문제점을 해결하기 위해 일반적인 세라믹 제조 방법인 고상반응법을 이용한 나노 사이즈의 $BaTiO_3$ 제조를 위한 최적의 공정 조건을 확립하기 위하여 본 연구를 진행하였다. 조성은 $BaTiO_3$와 반응온도를 낮추기 위한 anatase의 $TiO_2$를 사용하였고, $BaCO_3/TiO_2$ 의 조성비 (1. 1.01, 1.02, 1.03)를 제어하여 혼합한 후, 24h ball-mill 하여 하소 온도 ($860^{\circ}C{\sim}1000^{\circ}C$) 변화에 따른 입자 사이즈와 입도 분포를 측정하였다. 제조된 $BaTiO_3$분말의 결정 구조 분석을 위하여 XRD (X-ray diffraction) 분석을 수행 하였는데, 분석 결과로부터 제조된 분말들이 정방정 (tetragonal)의 perovskite구조를 갖고 있음을 확인하였다. 또한 분말의 미세구조 확인을 위하여 SEM (scanning electron microscope) 관찰을 수행하였는데, 나노 사이즈의 구형 분말을 얻을 수 있음을 확인할 수 있었다.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.201-204
• /
• 2009

$BaTiO_3/SrTiO_3$ and $PbTiO_3/PbZrO_3$ superlattice thin films were fabricated on $Pt/Ti/SiO_2/Si$ substrate by the pulsed laser deposition process. The morphologies and physical properties of deposited films were characterized by using X-ray diffractometer, HR-SEM, and Impedance Analyzer. XRD data and SEM images of the films indicate that each layer was well deposited alternatively in the superlattice structure. The dielectric constant of $BaTiO_3/SrTiO_3$ superlattice thin film was higher than that of individual $BaTiO_3$ or $SrTiO_3$ film. Same result was obtained in the $PbTiO_3/PbZrO_3$system. The dielectric constant of a superlattice film was getting higher as the number of layer is increased.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1960-1961
• /
• 2005

Ploycrystalline $Pb(Zr_{0.5},Ti_{0.5})O_3$ and $BaTiO_3$ powder were prepared by sol-gel process. The alumina substrate were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The Pb(Zr0.5, Ti0.5)O3/BaTiO3 multilayered thick films with laminating times were fabricated on alumina substrate by screening printing method. The obtained thick films were sintered at $800^{\circ}C$ with upper electrode of Ag paste for 1 hour, Structural properties of Pb(Zr0.5,Ti0.5)O3/BaTiO3 multilayered thick films were investigated. As a result of the Differential Thermal Analysis(DTA) of Pb(Zr0.5,Ti0.5)O3, exothermic peak was observed at around $650^{\circ}C$. The X-ray diffraction (XRD) patterns indicated that BaTiO3 and Pb(Zr0.5,Ti0.5)O3 phases and porosities were formed in the interface of Pb(Zr0.5,Ti0.5)O3 / EaTiO3 multilayered thick films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.32-32
• /
• 2008

Microstructure and positive temperature coefficient of resistivity (PTCR) characteristics of $0.9BaTiO_3-0.1(Bi_{0.5}Na_{0.5})TiO_3$ [BaBiNT] ceramics doped with $Nb_2O_5$ were investigated in order to develop the Pb-free high Curie temperature ($T_c$)(>$160^{\circ}C$) PTC thermistor. The BaBiNT ceramics showed a tetragonal perovskite structure, irrespective of the added amount of $Nb_2O_5$. They also have a homogeneous microstructure. The resistivity of BaBiNT ceramics was gradually decreased by doping $Nb_2O_5$, which might be due to $Nb^{+5}$ ions substituting for $Ti^{+4}$ sites. The PTCR characteristics of BaBiNT ceramics appeared when the amount of doped $Nb_2O_5$ exceeded 0.0025mol%. Moreover, the abrupt grain growth was observed for the 0.03mol% $Nb_2O_5$added BaBiNT ceramics. It showed an especially high $T_c$ of approximately $172^{\circ}C$ and good PTCR characteristics of a high $\rho_{max}/\rho_{min}$ ratio ($2.96\times10^3$), a high resistivity temperature factor (11.40/$^{\circ}C$) along with a relatively low resistivity ($3.5\times10^4\Omega{\cdot}cm$).

• Journal of the Korean Ceramic Society
• /
• v.40 no.4
• /
• pp.365-370
• /
• 2003

The phase development process of $Ba_2$ $Ti_{9}$ $O_{20}$ ceramics is not clearly known and frequently accompanies second phases which deteriorate dielectric properties. In synthesizing $Ba_2$ $Ti_{9}$ $O_{20}$ ceramics, in order to trace the reaction sequence during conventional solid-state reaction in BaO-Ti $O_2$ system, different barium sources of BaC0$_3$ and BaTi0$_3$ precursor were used as starting materials. From the analysis of XRD patterns, different secondary phases could be identified depending on the barium source used, which might mean that the equilibrium phases in BaO-Ti $O_2$ system are very difficult to be synthesized. Because the BaTi0$_3$ precursor provides short diffusion paths of ions, the system revealed less secondary phases during solid state reaction. In synthesizing BaO-xSm$_2$0$_3$-4.5Ti0$_2$ system using different barium sources, different secondary phases were developed also. Microstructure and dielectric properties were examined and discussed in terms of secondary phase development.