• 한국세라믹학회지
• /
• 제23권4호
• /
• pp.11-16
• /
• 1986

$BaTiO_3$ ceramics powder was prepared by coprecipitation method either in oxalic acid solution or in potassium hydroxide solution. Thermal decomposition of coprecipitated $BaTiO(C_2O_4)_2$.$4H_2O$ powder in oxalic acid solution was investigated by means of Themogravimetry Differential Thermal Analysis and X-ray Diffraction Analysis. Low temperature decomposition of coprecipitated $BaTiO(C_2O_4)_2$.$4H_2O$ caused narrow particle size distribution whereas high temperature decomposition caused fairly wide particle size distribution by partial sintering. As the reaction time increased the average particle size of coprecipitated $BaTiO_3$ powder in KOH solution was increased. The most narrow paticle size distribution was obtained when the coprecipi-tates were ripened for 4hrs.

• 한국세라믹학회지
• /
• 제24권6호
• /
• pp.579-585
• /
• 1987

The effects of flux KCl and dopant Nb2O5 on the PTCR characteristics of BaTiO3 prepared by molten salt synthesis method have been investigated. As the amount of dopant Nb2O5 is over the solubility limit in BaTiO3, the room-temperature resistivity increases, and the PTCR effect and the grain size decrease. The variation of the amount of flux KCl slightly influences on the room-temperature resistivity, PTCR effect and grain size in Nb2O5 doped BaTiO3, but BaTiO3 ceramics prepared by the method of molten salt synthesis show larger PTCR effect than those of conventional calcining of mixed oxides.

• 한국세라믹학회지
• /
• 제38권11호
• /
• pp.1015-1022
• /
• 2001

본 연구에서는 용융염법에 의한 Ba-ferrite의 생성기구와 그 자기적특성에 대해 조사하였다. 출발원료 중 BaC $O_3$만이 용융염내에서 용해도를 가졌으며, 이는 용융염내에서는 Ba-ferrite의 생성이 용해된 $Ba^{2+}$가 F $e_2$ $O_3$나 $\delta$-FeOOH의 표면으로 확산하여 표면반응을 통해 일어나는 것으로 보인다. 한편, 출발물질($\delta$-FeOOH와 F $e_2$ $O_3$)에 따라 생성된 Ba-ferrite가 합성되는 온도는 더 낮은 온도에서 생성됨을 알 수 있었다.

• 한국반도체및디스플레이장비학회:학술대회논문집
• /
• 한국반도체및디스플레이장비학회 2004년도 춘계학술대회 발표 논문집
• /
• pp.234-239
• /
• 2004

본 연구에서는 마이크로파용 유전재료로서 널리 사용되고 있는 BNT($BaO-Nd_{2}O_{3}-TiO_{2}$)계 세라믹스를 기본조성으로 하고, 저융점의 phoshpate계 유리 프릿의 첨가를 통해 LTCC(Low Temperature Cofired Ceramic)에 적용 가능한 유전율을 가진 조성을 개발 하고자, $70P_{2}O_{5}-5B_{2}O_{3}-(25-x)BaO-xNa_{2}O$ 유리를 제조 및 특성을 평가하였다. 또한, BNT계 세라믹스에 glass frit을 5 - 15 wt% 범위에서 첨가하고, $800 - 950^{\circ}C$의 온도범위에서 소결하여 제조된 유리-세라믹 복합체의 소결특성 및 유전특성을 조사하였다.

• 한국재료학회지
• /
• 제24권4호
• /
• pp.207-213
• /
• 2014

Flexible $BaTiO_3$ films as dielectric materials for high energy density capacitors were deposited on polyethylene terephthalate (PET) substrates by r.f. magnetron sputtering. The growth behavior, microstructure and electrical properties of the flexible $BaTiO_3$ films were dependent on the sputtering pressure during sputtering. The RMS roughness and crystallite size of the $BaTiO_3$ increased with increasing sputtering pressure. All $BaTiO_3$ films had an amorphous structure, regardless of the sputtering pressures, due to the low PET substrate temperature. The composition of films showed an atomic ratio (Ba:Ti:O) of 0.9:1.1:3. The electrical properties of the $BaTiO_3$ films were affected by the microstructure and roughness. The $BaTiO_3$ films prepared at 100 mTorr exhibited a dielectric constant of ~80 at 1 kHz and a leakage current of $10^{-8}A$ at 400 kV/cm. Also, films showed polarization of $8{\mu}C/cm^2$ at 100 kV/cm and remnant polarization ($P_r$) of $2{\mu}C/cm^2$. This suggests that sputter deposited flexible $BaTiO_3$ films are a promising dielectric that can be used in high energy density capacitors owing to their high dielectric constant, low leakage current and stable preparation by sputtering.

• Journal of Magnetics
• /
• 제19권4호
• /
• pp.333-339
• /
• 2014

Single crystal growth of $BaFe_{12}O_{19}$ by the solid state crystal growth method was attempted. Seed crystals of ${\alpha}-Fe_2O_3$ were pressed into pellets of $BaFe_{12}O_{19}$ + 2 wt% $BaCO_3$ and heat-treated at temperatures between $1150^{\circ}C$ and $1250^{\circ}C$ for up to 100 hours. Instead of single crystal growth taking place on the seed crystal, BaO diffused into the seed crystal and reacted with it to form a polycrystalline reaction layer of $BaFe_{12}O_{19}$. The microstructure, chemical composition and structure of the reaction layer were studied using scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS), x-ray Diffraction (XRD) and micro-Raman scattering and confirmed to be that of $BaFe_{12}O_{19}$. XRD showed that the reaction layer shows a strong degree of orientation in the (h00)/(hk0) planes in the sample sintered at $1200^{\circ}C$. $BaFe_{12}O_{19}$ layers with a degree of orientation in the (hk0) planes could also be grown by heat-treating an ${\alpha}-Fe_2O_3$ seed crystal buried in $BaCO_3$ powder.

• 한국세라믹학회지
• /
• 제39권7호
• /
• pp.628-634
• /
• 2002

수열합성법에 의한 정방정 BaTiO$_3$ 분말의 생성속도 및 유전특성에 대해서 연구하였다. 초미립 BaTiO$_3$분말의 합성을 위한 출발물질로는 Ba(OH)$_2$. 8$H_2O$, TiO$_2$(anatase)가 사용되었으며, 광화제로써 KOH가 사용되었다. 수열합성은 20$0^{\circ}C$의 온도에서 1~168시간동안 이루어 졌으며, 정방정상으로의 상전이를 관찰하기 위하여 1100~130$0^{\circ}C$의 온도로 하소처리 하였다. 최적의 조건(20$0^{\circ}C$에서 168시간동안 수열합성 된 분말을 120$0^{\circ}C$에서 3시간 하소한 분말)에서 얻어진 분말은 0.5~0.7$mu extrm{m}$ 정도의 분말이었으며, 유전특성 평가결과 고유전율 재료로써 적합함을 알 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.335-338
• /
• 1998

The effect of glass flit addition on microwave dielectric properties of BaTiO$_3$-3TiO$_2$ ceramic was studied. Addition of glass frit to this system obtained sintered sample below sintering temperature 105$0^{\circ}C$. At BaTiO$_3$-3TiO$_2$+ g1ass frit 3wt% + BaWO$_4$6 wt%m, this ceramic showed excellent microwave properties of dielectric constant 34, Q$\times$f 8,100, temperature coefficient of resonant frequency 4 ppm/$^{\circ}C$ .

• Elastomers and Composites
• /
• 제50권1호
• /
• pp.7-12
• /
• 2015

The $BaCrO_4$ nanoparticles were synthesized from a 0.1 M $K_2CrO_4$ and 0.1 M $BaCO_3$ solution with stirring for 10 h. The product was washed several times with acetone and heated to $700^{\circ}C$ for 6 h. At that time, the color of mixture was a greenish yellow. The graphene/$BaCrO_4$ nanocomposites were prepared with graphene and $BaCrO_4$ nanoparticles by stirring in tetrahydrofuran and heated in an electric furnace at $700^{\circ}C$ for 2 h. The $BaCrO_4$ nanoparticles, graphene/$BaCrO_4$ and heated graphene/$BaCrO_4$ nanocomposites were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The graphene/$BaCrO_4$ nanocomposites and heated graphene/$BaCrO_4$ nanocomposites were evaluated as a photocatalyst and discussed about kinetics study for the degradation of organic dyes, such as methylene blue and rhodamine B under ultraviolet light irradiation at 254 nm.

• 한국세라믹학회지
• /
• 제35권12호
• /
• pp.1274-1279
• /
• 1998

The glass forming ability of the PbO-B2O3-TiO3-BaO system was investigated in relation to transitieon tem-peratures and the atomic ratio between constituents. Glass forming tendency was improved as the tem-peratures and the atomic ratio between constituents. Glass forming tendency was improved as the tem-perature differences between liquidus temperature and crystallization(or glass transition) temperature de-creased and the temperature difference between crystallization and glass transition temperature increases. The atomic ratio could be used as a criterion to deign glass systems. The interposition of B and Ba atoms between Pb and Ti atoms was one of important factors in glass formation.