The microwave dielectric materials of the BaO-Nd$_2$O$_3$-TiO$_2$and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system were synthesized by conventional ceramic processing and sintered 1220 to 140$0^{\circ}C$ for 2 hours respectively. Their crystallization and dielectric properties were examined. In the BaO-Nd$_2$O$_3$-TiO$_2$ and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system. Nd$_2$Ti$_2$O$_{7}$ and (Sm, Nd)$_2$Ti$_2$O$_{7}$ were observed as a second phase respectively. The maximum relative dielectric constant were 79,99 for the BaO-Nd$_2$O$_3$-TiO$_2$system and 105.07 for the BaO-(Sm,Nd)$_2$O$_3$-TiO$_2$system and their Q-value were over 2000 at 3GHz.GHz.

• 한국세라믹학회지
• /
• 제35권8호
• /
• pp.775-782
• /
• 1998

This experiment is third study concerning BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} (Ln=Sm, Nd, Pr, La..) system which is known to show a high dielectric constant and Q value in microwave dielectric materials. The process of cry-stallization and the microwave dielectric properties of the specimens sintered at 1220-140$0^{\circ}C$ for 2 hr was investigated in the BaO-(Na,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} as well as BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system. The single phase BaPr2Ti5O14 and Ba(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}Ti5O14 was finally formed from the Pr2Ti2O7 (Nd, Pr)2Ti2O7 as a secondary phase in the BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} and BaO-(Nd, {{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system respectively The dielectric constant of the specimens sint-ered at 1280~131$0^{\circ}C$ showed the maximum value as 105(BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system) and 88 (BaO-(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system) and the Q values of them showed higher value than 1800 which are due to the maximum den-sity. However the dielectric properties of the specimens sintered at higher temperature than 131$0^{\circ}C$ were reduced due to the increases of pore which were resulted from the sudden grain growth.

• ETRI Journal
• /
• 제18권1호
• /
• pp.15-27
• /
• 1996

The effects of $Nd_2O_3$ and $TiO_2$ addition on the microstructures and microwave dielectic properties of $BaO-Nd_2O_3-TiO_2$ system were investigated. $BaNd_2Ti_4O_{12}$ or $BaNd_2Ti_{5}O_{14}$ phases were observed for compositions based on BaO/$Nd_2O_3$ = 1 ratio. The compositions deviated from $BaO/Nd_2O_3=1$ ratio were composed of major phases of $BaNd_2Ti_4O_{12}$ or $BaNd_2Ti_5O_{14}$, and the compound of $Nd_2O_3$ and $TiO_2(Nd_2Ti_2O_7)$ or that of BaO and $TiO_2(BaTi_4O_9)$. The microstructure of ceramic with $BaO{\cdot}Nd_2O_3{\cdot}4TiO_2$ composition varied from spherical grains to needlelike grains with increasing sintering temperature. With increasing $Nd_2O_3$, the optimum sintering temperature with maximum density increased, and the dielectric constant(${\varepsilon}_r$) and quality factor(Q) decreased due to the formation of secondary phases. With increasing $TiO_2$, the optimum sintering temperature and the dielectric constant decreased with increased Q value. And the temperature coefficient of resonant frequency, ${\tau}_f$ shifted toward positive direction. The dielectric ceramics with $BaO/Nd_2O_3=1$ showed Q values of above 2000 and dielectric constants of above 80 at 3GHz.

• 한국세라믹학회지
• /
• 제31권9호
• /
• pp.995-1004
• /
• 1994

Phase relation and microwave dielectric properties of the system BaO.(Nd1-xSmx)2O3.TiO2 (n=4, 5) were studied. With n=5 (1 : 1 : 5), Ba2Ti9O20 and TiO2 formed in case of X$\leq$0.7, and Ba2Ti9O20 and Sm2Ti2O7 formed at X=1.0 as the second phases dispersed in fine-grained orthorhombic matrix phase. With n=4 (1 : 1 : 4). on the contrary, only fine grains of an ortho-rhombic phase were observed irrespective of Nd/Sm ratio. The compositions of these two stable orthorombic phases having distinct lattic constants even with the same Nd/Sm ratio were estimated as 4BaO.5(Nd1-xSmx)2O3.18TiO2 and BaO.(Nd1-xSmx)2O3.4TiO2 with n=5 and n=4 in the system BaO.(Nd1-xSmx)2O3.TiO2, respectively. Consequently the composition BaO.(Nd1-xSmx)2O3.5TiO2 lies in the compatible triangle of 4BaO.5(Nd1-xSmx)2O3.18TiO2 and the second phases mentioned above. The microwave dielectric properties (~4 GHz) of BaO.(Nd1-xSmx)2O3.5TiO2 can be controlled effectively by adjusting Sm content : with increasing X from 0 to 0.7, both dielectric constant and the temperature coefficient of resonant frequency decreased monotonically from 82 to 65 and from 91 (ppm/$^{\circ}C$) to -19(ppm/$^{\circ}C$), respectively, while unloaded Q(Qo) remained constant at about 2,600.

• 한국재료학회지
• /
• 제8권7호
• /
• pp.659-663
• /
• 1998

BaO.$Nd_{2}O_{3}$.$4TiO_{2}$세라믹스에서 Bi 치환위치 및 Bi 치환 량에 따른 상, 미세구조, 마이크로파 유전특성 등을 조사하였다. BaO.$Nd_{2}O_{3}$.$4TiO_{2}$ 세라믹스의 Nd 치환되어 $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$고용체 (0$\leq$x$\leq$0.2)를 형성하였다. $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$에서 Bi 치환 량이 x=0에서 x=0.2까지 증가됨에 따라 입자크기가 계속 증가하였으며, 유전상수는 84에서 108까지 계속 증가하였고, 공진 주파수의 온도계수는 $44 ppm^{\circ}C$에서 $-30ppm^{\circ}C$로 계속 감소하였다. $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$조성에서 Bi 치환 량이 x=0.04에서 0.08사이일 때 가장 양호한 마이크로파 유전특성이 얻어졌으며 이 때의 유전상수 (${\varepsilon}_r$)는 89~92, Q, f는 5855-6091 GHz, 그리고 공진 주파수의 온도계수 (${\tau}_f$)는 -7.7-7.5 ppm/$^{\circ}C$이었다.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1311-1318
• /
• 1996

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 추계학술대회 논문집 학회본부
• /
• pp.320-323
• /
• 1997

The microwave dielectric properties of X Ba0-$0.15(Nd_{0.87}Bi_{0.13})_2O_3$-(0.85-X) $TiO_2$ ($X=0.13{\sim}0.17$) and 0.16Ba0-$0.15(Bi_xNd_{1-x})_2O_3-0.69TiO_2$ ($X=0.10{\sim}0.16$) ceramics were investigated. Dielectric constant, quality factor and temperature coefficient of resonant frequency of 0.16Ba0-$0.15(Nd_{0.87}Bi_{0.13})_2O_3-0.69TiO_2$ ceramics sintered at $1320^{\circ}C$ for 2 hours were 89.2, 1920(at 4GHz) and 5.2ppm/$^{\circ}C$, respectively.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 춘계총회 및 연구발표회 초록집
• /
• pp.115.2-115
• /
• 2003

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.136-144
• /
• 1999

텅스템브론즈형 고주파 유전체의 $BaORe_2O_3TiO_2$(BLT)와 $BaO(Nd({0.77}Y_{0.23})_2O_34TiO_2(B(NY)T)$의 결정구조를 Rietveld 정밀화법으로 분석하였다. 양이온은 X-선 데이터로부터, 산소이온은 중성자 데이터로부터 정밀화한 'combined법'에 의해 가장 신뢰성이 높은 결정구조분석 결과를 얻었다. Mateeva 등이 처음 제시한 결정구조의 결정학적 모순점을 해결하였다. BaORe2O34TiO2(Re=La, Nd, Y) 유전체는 $3\times2$개의 페롭스카이트 블록과 이 블록사이에 형성된 4개의 pentagon-channel로 이뤄진다. Ti-O6팔면체는 tilted 및 변형된 구조를 갖고 있고, 이에 의해 같은 z-층에 있는 Ba 및 Re 이온의 변위되어 초격자(c$\approx$ 7.6$\AA$)를 형성된다. Re 이온반경이 작은 B(NY)T의 Ti-O6 팔면체가 tilting 및 변형이 큰 것으로 나타났다. 유전상수 $\varepsilon_{\gamma}$과 온도계수 $au_\varepsilon$은 BLT의 경우 각각 $109.5, -180 ppm/^{\circ}C$였고, B(NY)T 경우 $76, +40ppm/^{\circ}C$이었다. Re 이온 크기가 작은 시료의 $\tau$$\varepsilon$이 +값을 나타내었다. 복합 페롭스카이트에서 관찰되는 $\tau_\varepsilon$과 팔면체 tilting과의 관계를 본 텅스텐 브론즈 구조재료에서 고찰하였다.

• 마이크로전자및패키징학회지
• /
• 제10권1호
• /
• pp.57-63
• /
• 2003

$BaO-Nd_2O_3-TiO_2$계 유전체 세라믹스에 lithium borosilicate계 유리를 첨가하여 저온소결특성과 마이크로파 유전특성을 조사하였다. 유리 프릿을 10∼l3 wt%의 범위로 첨가함으로서 순수한 $BaO-Nd_2O_3-TiO_2$계 세라믹스의 소결온도($1300^{\circ}C$)보다 현저히 낮은 850∼$900^{\circ}C$의 온도범위에서 상대밀도 97%이상의 소결체를 얻을 수 있었다. 10 wt%의 유리 프릿을 첨가함으로서 85$0^{\circ}C$의 소성온도에서 유전율($\epsilon_r$)54 및 품질계수($Q{\times}f$)2400 GHz그리고 공진주파수의 온도계수($\tau_f$)는 $+8ppm/^{\circ}C$으로서 우수한 유전 특성을 가지는 소결체를 얻을 수 있었다.