• Journal of the Korean Vacuum Society
• /
• v.7 no.s1
• /
• pp.179-182
• /
• 1998

Boron carbide coating has some very attractive properties for nuclear and semiconductor industry. The potential of atmosheric plasma spray as manufacturing methods for $B_4C$ coating was discussed. In this work, the boron carbide coating with low porosity, high microhardness and good life of thermal shock resistance was deposited by the control of spraying distance. The relationship between the properties of $B_4C$ coatings and their spraying distance was studied.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.777-783
• /
• 2003

The mechanical properties of B$_4$C/Al composites normally depend on the species and quantity of reaction products between B$_4$C and Al and then the control of reaction products is necessary to make desirable composites for lightweight advanced or armor materials. TiB$_2$ is chemically inert with aluminum and has a lower contact angle (85$^{\circ}$ at 100$0^{\circ}C$) to liquid aluminum than B$_4$C. Thus, TiB$_2$ coating on B$_4$C may lower infiltration temperature of aluminum when the B$_4$C/Al composites is fabricated by infiltration process. In this study, the effects of TiB$_2$ on the microstructure and mechanical properties of the B$_4$C/Al composites have been investigated. TiB$_2$ coated B$_4$C powder was prepared using the sol-gel technique. It was found that the B$_4$C surface is homogeneously covered with TiB$_2$ having a particles size of 20-50 nm. While the B$_4$C/Al composites prepared by infiltration after TiB$_2$ coating had 17 wt% of unreacted Al, on the other hand, the B$_4$C/Al composites without coating included 14 wt% of Al. As a result, the composites infiltrated after the coating showed higher fracture toughness and lower hardness. This strongly suggests that TiB$_2$ not only lowers the infiltration temperature, but also inhibits the reaction between B$_4$C and Al.

• Corrosion Science and Technology
• /
• v.7 no.4
• /
• pp.233-236
• /
• 2008

Halide-activated pack cementation was utilized to deposit B-doped silicide coating. The pack powders were consisted of $3Wt.c/oNH_4Cl$, 7Wt.c/oSi, $90Wt.c/oAl_2O_3+TiB_2$. B-doped silicide coating was consisted of two layers, an outer layer of $NbSi_2$ and an inner layer of $Nb_5Si_3$. Isothermal oxidation resistance of B-doped silicide coating was tested at $1250^{\circ}C$ in static air. B-doped silicide coating had excellent oxidation resistance, because continuous $SiO_2$ scale which serves as obstacle of oxygen diffusion was formed after oxidation.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.4
• /
• pp.39-46
• /
• 2004

This experiment was carried out to study on the effect of surface coating on thermal insulation of farm structures to improve thermal resistance and reflective effect of solar radiation. Nine different types of experimental specimen were compared in the temperature variations of inside and outside; A, B, C, D. E and F types are box container and G, H and I types are drum container. The size of these containers is $1,500{\times}2,000{\times}2,500$ mm and ${\varphi}$ $280{\times}330$ mm, respectively. Specimen of 3-type box(A, B, C) is galvanized steel sheet of thickness 0.45 mm. D, E and F types are sandwich panel of the thickness 50 mm inserted with urethane, glass wool and polystyrene form, respectively. G, H and I types are paint pot using in general. The surface of A. D, E, F and I types didn't any treatment, B, C and G types were treated with thermal insulation coating on the outside surface(B, G) or the inside and outside surface(C). And H type was treated with water paint coating on the only outside surface. In general, the experimental results showed the following tendencies; In case of A, B and C types. it was found that the thermal insulation effect of types coated with thermal insulation coating was improved remarkably than that of no treatment. And the thermal insulation effect between steel sheet and sandwich panel type was nearly similar There was not a significant difference of thermal insulation effect between thermal insulation coating and water paint coating. In time of drum container filled with rough rice, The difference of heat transfer tendency and temperature variation among surface treatments was nearly similar that of box types of galvanized steel sheet. And there was time lag about 6 hours between the temperature of middle part of rice and that of inside or outside surface.

• Journal of Powder Materials
• /
• v.16 no.2
• /
• pp.110-114
• /
• 2009

Mechanical coating process was applied to form 89 %-hydrolyzed poly vinyl alcohol (PVA) onto boron carbide ($B_4C$) nanopowder using one step high energy ball mill method. The polymer layer coated on the surface of B4C was changed to glass-like phase. The average particle size of core/shell structured $B_4C$/PVA was about 50 nm. The core/shell structured $B_4C$/PVA was formed by dry milling. However, the hydrolyzed PVA of $98{\sim}99%$ with high glass transition temperature ($T_g$) was rarely coated on the powder. The $T_g$ of polymer materials was one of keys for guest polymer coating on to the host powder by solvent free milling.

• KSBB Journal
• /
• v.19 no.3
• /
• pp.221-225
• /
• 2004

Bacillus polyfermenticus SCD derived from Bacillus sp., which is commonly called as Bisroot$^{ⓡ}$. The goal of this study, is to Increase stability of Bacillus polyfermenticus SCD in low pH, high temperature and high glucose concentration via three layer coating. The viability of coated Bacillus polyfermenticus SCD increased to 30%, 20%, 14% in the condition of pH 2 4 6 than that of uncoated Bacillus polyfermenticus SCD at 37$^{\circ}C$ for 4 h. Final viability of the coated Bacillus polyfermenticus SCD in 80$^{\circ}C$ increased to 40% than that of uncoated Bacillus polyfermenticus SCD. In high glucose concentration coated Bacillus polyfermenticus SCD is more stable than uncoated about 50%. In conclusion, the three layer coated Bacillus polyfermenticus SCD is very stable for low pH, high temperature and high glucose concentration.

• Composites Research
• /
• v.33 no.5
• /
• pp.235-240
• /
• 2020

In this study, in order to improve the impact resistance of the B₄C tile-inserted B₄C_p/Al7075 hybrid composite, a control method of the B₄C/Al7075 interface was developed and the characteristics of the controlled interface were analyzed. B₂O₃, Ni, and Si were coated on the B₄C tile surface using additional thermal oxidation, electroless plating, and plasma spraying. The coated B₄C tile is inserted into the B₄C_p/Al7075 composite material using the liquid pressurization method. Interfacial energy, bonding strength, and impact resistance were measured to analyze the effect of the coating. All coatings enhanced interfacial energy, bonding strength, and impact resistance, and in particular, it was confirmed that the impact resistance increased by 86.8% when B₂O₃ coating was used. This study is significant in developing and analyzing a core surface treatment method that improves the performance of B₄C/Al series composites, which are attracting attention as next-generation lightweight amour and bulletproof materials.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.278-285
• /
• 2006

Coating mixtures of the resin B-H for the application to the desulfurization system of power plant were coated on carbon steels and cured at the temperature of $65^{\circ}C{\sim}80^{\circ}C$. After being contacted with 70wt% $H_2SO_4$ solution of $100^{\circ}C\;and\;120^{\circ}C$ for several hours, their composition, Vicker's hardness and microstructures by SEM were examined. Corrosion resistance of the coating mixtures to $H_2SO_4$ solution was related to the content of $SO_3$ in the coated specimens after corrosion test. The lower curing temperature and the shorter curing time the coated specimens went through, the higher corrosion resistance to acid they showed, but the more cracks were developed at higher temperature. It was realized that the corrosion resistance to sulfaric acid solution was increased on the condition of curing temperature above $65^{\circ}C$ and curing time above 12 hours at least.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.2
• /
• pp.60-67
• /
• 2011

Ternary B-C-N coatings were deposited on Si(100) wafer substrate from $B_4C$ target by RF magnetron sputtering technique in $Ar+N_2+CH_4$ gas mixture. In this work, the effect of reactant gas ratio, $CH_4/(N_2+CH_4)$ on the composition, kinds and amounts of bonding states comprising B-C-N coatings were investigated using two different bias power sources of continuous and unipolar DCs. In addition, the tribological properties of coatings were studied with the composition and bonding state of coating. It was found that the substrate bias power had an effect on chemical composition, and all of the obtained coatings were nearly amorphous. Main bonding states of coatings were revealed from FTIR analyses to be h-BN, C-C, C-N, and B-C. The amount of C-C bonging mainly increased with increase of the reactant gas ratio. From our studies, both C-C and h-BN bonding states improved the tribological properties but B-C one was found to be harmful on those. The best coating from tribological points of view was found to be $BC_{1.9}N_{2.3}$ composition.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.61 no.4
• /
• pp.585-589
• /
• 2012

The characteristics of interface layer and the effect of mole fraction of inlet gas mixture($B_2H_6/H_2/N_2/TiCl_4$) on the microstructure of Ti(B,N) films were studied by microwave plasma hot filament CVD process. Ti(B,N) films were deposited on a substrate(STD-61) to develop a high performance of resistance wear coating tool. Ti(B,N) films were obtained at a gas pressure of 1 torr, bias voltage of 300 V and substrate temperature of $480^{\circ}C$ in $B_2H_6/H_2/N_2/TiCl_4$gas system. It was found that TiN, $TiB_2$, TiB and hexagonal boron nitride(h-BN) phases exist in thin layer on the STD-61.