• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.4013-4018
• /
• 2014

A 0.45 $cm^2$ DSSC device with a glass/FTO/blocking layer/$TiO_2$/N719(dye)/electrolyte/50 nm-Pt/50 nm-Au/FTO/glass was prepared to examine the stability of the Au/Pt bilayered counter electrode (CE) with electrolyte and the energy conversion efficiency (ECE) of dye-sensitized solar cells (DSSCs). For comparison, a 100 nm-thick Pt only CE DSSC was also prepared using the same method. The photovoltaic properties, such as the short circuit current density ($J_{sc}$), open circuit voltage ($V_{oc}$), fill factor (FF), and ECE, were checked using a solar simulator and potentiostat with time after assembling the DSSC. The microstructure of the Au/Pt bilayer was examined by optical microscopy after 0~25 minutes. The ECE of the Pt only CE-employed DSSC was 4.60 %, which did not show time dependence. On the other hand, for the Au/Pt CE DSSC, the ECEs after 0, 5 and 15 minutes were 5.28 %, 3.64 % and 2.09 %, respectively. The corrosion areas of the Au/Pt CE determined by optical microscopy after 0, 5, and 25 minutes were 0, 21.92 and 34.06 %. These results confirmed that the ECE and catalytic activity of Au/Pt CE decreased drastically with time. Therefore, a Au/Pt CE-employed DSSC may be superior to the Pt only CE-employed one immediately after integration of the device, but it would degrade drastically with time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.375-375
• /
• 2009

For many large-scale applications of high-temperature superconducting materials, large critical current density($J_c$) in high applied magnetic fields are required. A number of methods have been reported to introduce artificial pinning centers(APCs) in $YBa_2Cu_3O_{7-\delta}$(YBCO) films for enhancement of their $J_c$. We report measurements of critical current in $YBa_2Cu_3O_{7-\delta}$ films deposited by PLD on $SrTiO_3$ substrates decorated with Au nanoparticles. Au nanoparticles were synthesized on STO substrates with self assembled monolayer. Microstructural analysis of the obtained YBCO films was performed by using cross-section transmission electron microscopy(TEM). Phase and textural analysis was done using X-ray diffraction. The surface morphology and surface roughness(Ra) of the layers was measured by atomic force microscopy(AFM).

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2019.10a
• /
• pp.214-214
• /
• 2019

• Journal of the Korean Ceramic Society
• /
• v.52 no.1
• /
• pp.77-82
• /
• 2015

The effect of the electrode type on the dielectric and piezoelectric properties of $Pb(Mg_{1/3}Nb_{2/3})O_3-PbZrO_3-PbTiO_3$ (PMN-PZT) single crystals was investigated in an effort to improve their properties for various piezoelectric applications. First, three different types of PMN-PZT single crystals [PMN-PZT-A (piezoelectrically soft type; dielectric constant ~ 10,000), PMN-PZT-B (piezoelectrically soft type; phase-transition temperature between the rhombohedral and tetragonal phases ($T_{RT}$) ~ $145^{\circ}C$), PMN-PZT-C (piezoelectrically hard type; high mechanical quality factor ($Q_m$) ~ 1,000)] were fabricated using the solid-state single crystal growth (SSCG) method. Then, four different types of electrodes [sputtered Au, sputtered Cr/Au, sputtered Ti/Au, and fired Ag] were formed on the single crystals, and their dielectric and piezoelectric properties were measured. The single crystals with a sputtered Ti/Au electrode showed the highest dielectric and piezoelectric constants but the lowest coercive electric field ($E_C$). The single crystals with a fired Ag electrode showed the lowest dielectric and piezoelectric constants but the highest coercive electric field ($E_C$). This dependence on the type of electrode was most significant in the piezoelectrically hard PMN-PZT-C single crystals. However, the effects of the electrode type on the phase transition temperatures ($T_C$, $T_{RT}$) and dielectric loss were negligible. These results clearly demonstrate that it is important to select an appropriate electrode so as to maximize the dielectric and piezoelectric properties of single crystals in each type of piezoelectric application.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2004.08a
• /
• pp.198-198
• /
• 2004

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.43-43
• /
• 2000

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.795-803
• /
• 1994

Ferroelectric BaTiO3 thin film was produced using BaTi-ethoxide sol. This sol was prepared from BaTi-ethoxide by a partial hydrolysis with ammonia as a basic catalyst and ethylene glycol as a chelating agent. BaTiO3 thin film was prepared from three continuous spin-coating layers of the sol on bare Si(100) wafer at 2500 rpm followed by pyrolysis at $700^{\circ}C$ for 30 min. After the heat treatment, the film was 0.200$\pm$0.010 ${\mu}{\textrm}{m}$ thick and its grain size was 0.059 ${\mu}{\textrm}{m}$. On the other hand, electrical properties were measured for BaTiO3 thin film separately prepared on Au-deposited silicon wafer. The dielectric constant and loss of the BaTiO3 thin film at room temperature was 150~160 and 0.04 respectively, which was measured at 10 kHz and oscillation level of 0.1 V. In the measurements of the dielectric properties at high temperatures, it was observed that the capacitance of the thin film increases steeply, while the dielectric loss reaches maximum around 1$25^{\circ}C$, which corresponds a phase transition from tetragonal to cubic BaTiO3.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.59 no.1
• /
• pp.130-133
• /
• 2010

Although many structures based on $SnO_2$ nanowires have been demonstrated, there is a limitation towards practical application due to the unwanted contact potential between the metal electrode and the $SnO_2$ nanowire. This is mostly due to the presence of the native oxide layer that acts as an insulator between the metal contact and the nanowire. In this study the contact properties between Ti/Au contacts and a single $SnO_2$ nanowire was compared to the electrical properties of a contact without the oxide layer. RIE(Reactive Ion Etching) is used to selectively remove the oxide layer from the contact area. The $SnO_2$ nanowires were synthesized by chemical vapor deposition (CVD) and dispersed on a $Si/Si_3N_4$ substrate. The Ti/Au (20nm/100nm) electrodes were formed bye-beam lithography, e-beam evaporation and a lift-off process.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.601-610
• /
• 2007

Statement of problem: The adhesion between titanium and ceramic is less optimal than conventional metal-ceramic bonding, due to reaction layer form on cast titanium surface during porcelain firing. Purpose: This study characterized the effect of titanium-ceramic adhesion after gold and TiN coating on cast and wrought titanium substrates. Material and method: Six groups of ASTM grade II commercially pure titanium and cast titanium specimens$(13mm{\times}13mm{\times}1mm)$ were prepared(n=8). The conventional Au-Pd-In alloy served as the control. All specimens were sandblasted with $110{\mu}m\;Al_2O_3$ particles and ultrasonically cleaned for 5min in deionized water and dried in air before porcelain firing. An ultra-low-fusing dental porcelain (Vita Titankeramik) was fused on titanium surfaces. Porcelain was debonded by a biaxial flexure test at a cross head speed of 0.25mm/min. The excellent titanium-ceramic adherence was exhibited by the presence of a dentin porcelain layer on the specimen surface after the biaxial flexure test. Area fraction of adherent porcelain (AFAP) was determined by SEM/EDS. Numerical results were statistically analyzed by one-way ANOVA and Student-Newman-Keuls test at ${\alpha}=0.05$. Results: The AFAP value of cast titanium was greatest in the group 2 with TiN coating, followed by group 1 with Au coating and the group 3 with $Al_2O_3$ sandblasting. Significant statistical difference was found between the group 1, 2 and the group 3 (p<.05). The AFAP value of wrought titanium was greatest in the group 5 with TiN coating, followed by the group 4 with Au coating and the group 6 with $Al_2O_3$ sandblasting. Conclusion: No significant difference was observed among the three groups (p>.05). The AFAP values of the cast titanium and the wrought titanium were similar. However the group treated with $Al_2O_3$ sandblasting showed significantly lower value (p<.05).

• Macromolecular Research
• /
• v.15 no.7
• /
• pp.693-696
• /
• 2007