A 4 nm layer of ZrOx (targeted x-2) was deposited on an interfacial layer(IL) of native oxide (SiO, t∼1.2 nm) surface on 200 mm Si wafers by a manufacturable atomic layer chemical vapor deposition technique at 30$0^{\circ}C$. Some as-deposited layers were subjected to a post-deposition, rapid thermal annealing at $700^{\circ}C$ for 5 min in flowing oxygen at atmospheric pressure. The experimental x-ray diffraction, x-ray photoelectron spectroscopy, high-resolution transmission electron microscopy, and high-resolution parallel electron energy loss spectroscopy results showed that a multiphase and heterogeneous structure evolved, which we call the Zr-O/IL/Si stack. The as-deposited Zr-O layer was amorphous $ZrO_2$-rich Zr silicate containing about 15% by volume of embedded $ZrO_2$ nanocrystals, which transformed to a glass nanoceramic (with over 90% by volume of predominantly tetragonal-$ZrO_2$(t-$ZrO_2$) and monoclinic-$ZrO_2$(m-$ZrO_2$) nanocrystals) upon annealing. The formation of disordered amorphous regions within some of the nanocrystals, as well as crystalline regions with defects, probably gave rise to lattice strains and deformations. The interfacial layer (IL) was partitioned into an upper Si $o_2$-rich Zr silicate and the lower $SiO_{x}$. The latter was sub-toichiometric and the average oxidation state increased from Si0.86$^{＋}$ in $SiO_{0.43}$ (as-deposited) to Si1.32$^{＋}$ in $SiO_{0.66}$ (annealed). This high oxygen deficiency in $SiO_{x}$ indicative of the low mobility of oxidizing specie in the Zr-O layer. The stacks were characterized for their dielectric properties in the Pt/{Zr-O/IL}/Si metal oxide-semiconductor capacitor(MOSCAP) configuration. The measured equivalent oxide thickness (EOT) was not consistent with the calculated EOT using a bilayer model of $ZrO_2$ and $SiO_2$, and the capacitance in accumulation (and therefore, EOT and kZr-O) was frequency dispersive, trends well documented in literature. This behavior is qualitatively explained in terms of the multi-layer nanostructure and nanochemistry that evolves.ves.ves.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• KIISE Transactions on Computing Practices
• /
• v.24 no.3
• /
• pp.129-137
• /
• 2018

NVMe(Non-Volatile Memory Express) SSD(Solid State Drive) is a high-performance storage that makes use of flash memory as a storage cell, PCIe as an interface and NVMe as a protocol on the interface. It supports multiple I/O queues which makes it feasible to process parallel-I/Os on multi-core environments and to provide higher bandwidth than SATA SSDs. Hence, NVMe SSD is considered as a next generation-storage for data-center and cloud computing system. However, in the virtualization system, the performance of NVMe SSD is not fully utilized due to the bottleneck of the software I/O stack. Especially, when it uses I/O stack of the hypervisor or the host operating system like Xen and KVM, I/O performance degrades seriously due to doubled-I/O stack between host and virtual machine. In this paper, we propose a new I/O engine, called Direct-AIO (Direct-Asynchronous I/O) engine, that can access NVMe SSD directly for I/O performance improvements on QEMU emulator. We develop our proposed I/O engine and analyze I/O performance differences between the existed I/O engine and Direct-AIO engine.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.341-344
• /
• 2004

The superconducting properties of $YBa_2Cu_3O_x$ with different content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as an additive in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and $BaPbO_3$ would be the main phase in the sample. Therefore, $BaPbO_3$ was chosen as the impurity additive for the comparative study. The single phase of $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Different contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the Phase analysis in the XRD patterns it was proved that there was no reaction between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as an impurity additive in $YBa_2Cu_3O_x$.

• Electrical & Electronic Materials
• /
• v.8 no.5
• /
• pp.594-600
• /
• 1995

Dielectric properties at microwave frequencies of ($Zr_{0.65}$, $Sn_{0.35}$) $Ti_{1.04}$ $O_{4.04}$ ceramics with additives, NiO as an agent to improve dielectric properties and $B_{2}$ $O_{3}$ as a firing agent were investigated. When 0.5 - 1.5 wt% of NiO is add, the grain growth is inhibited and the shape of the grain is uniformed, Dielectric constant(Fr) and bulk density are increased with raising amount of NiO at sintering temperature of 1330 - 1360.deg. C, but the temperature coefficient of resonant frquency(.epsilon.$_{r}$) decreased gradually as the NiO content increased. The value of Qx $f_{o}$ was increased as the amount of NiO was increased in the range of 0.5 to 1.0 wt% and the Qx $f_{o}$, was decreased slightly with raising sintering temperature. With NiO of 1.0 wt% and at sintering temperature of 1360.deg. C, this ceramics was found to have excellent microwave properties of .epsilon.$_{r}$=37.8, Qx $f_{o}$ = 48.600 and .tau.$_{f}$ = 7 ppm/.deg. C.C.. C.. C.C.. C.. C.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.12-15
• /
• 2004

There are two major approaches to obtain texture template for HTS coated conductor (CC) ---IBAD and RABiTS. CC's with IBAD template showed both longer and higher Ic results so far. IBAD for CC began with YSZ, the processing of which is very slow compared to other processings needed for the fabrication of CC. Because of this very slow processing speed, IBAD with other materials such as Gd$_2$Zr$_2$O$_{7}$(GZO) and MgO have been developed. The processings of IBAD-GZO and IBAD-MgO are known to be up to 3times and 100 times. respectively, as fast as the processing of IBAD-YSZ. IBAD-MgO is very attractive in that the processing is very fast. IBAD-MgO also needs additional buffer layer(s). Many materials are being investigated to be used as a buffer layer on top of the MgO. BaZrO$_3$ (BZO) is a good candidate as the buffer layer on top of the IBAD-MgO because it is chemically stable and does not react with YBCO at high temperatures. It also has good lattice match with MgO. The BZO film has been deposited on single crystal MgO, and YBCO film was deposited on BZO/MgO to investigate the possibility of using BZO as both the buffer and capping layer of the CC.C.

• Journal of the Korean Ceramic Society
• /
• v.28 no.9
• /
• pp.661-666
• /
• 1991

Microstructure, room temperature resistivity and temperature coefficient of resistance of BaTiO3 ceramics were studied by varying cooling rates and additives such as TiO2, SiO2 and Al2O3. The basic composition of the BaTiO3 ceramics was formed by adding 0.25 mol% Dy2O3 and 0.07 mol% MnO2 to the BaTiO3 composition. Unlike the additives of SiO2 and Al2O3, an addition of 2 mol% TiO2 to the basic composition was effective to control the grain size of the fired specimens. The room temperature resistivity and the temperature coefficient of resistance for the specimen of this particular compostion were measured as about 102 ohm.cm and 16.5%/$^{\circ}C$, respectively. The observed grain boundary phase of the sample with Al2O3 additive was BaTi3O7, while that of the samples with SiO2 additive was confirmed as BaTiSiO5.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.189-194
• /
• 1999

Crystallization of glasses in the system (Ca, Sr, Ba)$O-Al_2O_3-B_2O_3-SiO_2-TiO_2$ and dielectric properties of crystallized glasses were investigated. As increasing B2O3 content and decreasing SiO2 content in the glass, the major crystalline phase changed from $(Sr, Ba)_2TiSi_2O_8$ to (Ca, Sr, Ba)TiO3, the dielectric constant of crystallized glasses increased and the Temperature Coefficient of Capacitance (TCC) changed to negative. The dielectric constant and TCC was estimated for (Sr, Ba)2TiSi2O8 phase as 18 and -440 $ppm/^{\circ}C$, respectively and for (Ca, Sr, Ba)TiO3 phase as 307 and -1900 $ppm/^{\circ}C$, respectively. The dielectric properties of (Ca, Sr, Ba)TiO3 phase (in this study) were similar to those of (Ca, Ba) TiO_3 solid-solution^12)$, but $(Sr, Ba)_2TiSi_2O_8$ phase (in this study) and $Sr_2TiSi_2O_\;8^4$ showed the different properties.

• Korean Journal of Clinical Laboratory Science
• /
• v.38 no.2
• /
• pp.82-86
• /
• 2006

Leukemia arises in hematopoietic progenitor cells and is characterized by impaired or blocked differentiation, uncontrolled proliferation and resistance to apoptosis. Molecular mechanisms underlying cellular functions by $As_2O_3$, however, have been poorly investigated. The consensus of several reports is that $As_2O_3$ induces apoptosis in leukemia cells by activating genes for apoptosis. The present study aimed to investigate the effects of $As_2O_3$ on the cell cycle and its morphological change and a relationship between the caspase-3 and $As_2O_3$-induced apoptosis. Caspase-3 is involved in $As_2O_3$-induced apoptosis in K562 cells. In this study, to address whether $As_2O_3$-induced apoptosis is mediated by caspase-3 activity, the same samples were probed with a specific antibody. The pretreatment of $25{\mu}M$ Z-VAD-fmk, a specific inhibitor of caspase, decreased $As_2O_3$-induced cytotoxicity. And $As_2O_3$ significantly increased the percentages of the cells accumulated in the G2/M phase of the cell cycle in a time- and dose-dependent manner. Chromatin condensational changes were observed with Hoechst 33258 staining after treatment of $As_2O_3$. It was shown that $As_2O_3$-induced apoptosis is controlled through caspase-3 activation. These results may provide a useful rationale for CML treatment.

• Journal of the Korean Ceramic Society
• /
• v.27 no.3
• /
• pp.369-382
• /
• 1990

ZrO2-Toughened Alumina-Ceramics(ZTA) with Cr2O3 and HfO2 as addition were synthesized by assintering method for solid solution of Al2O3/Cr2O3 and ZrO2/HfO2, and were prepared by pressureless sintering at 1$600^{\circ}C$. The effects of Cr2O3 and HfO2 on the thermal and mechanical properties, the sintering mechanism, and the wearness between theory and experiment were investigated. Among three kinds of mechanisms such as stress-induced transformation, microcracking, and crack deflection it contributed to the ZTA system with a few exceptons according to composite. We show that wearness can be estimated sufficiently by HV and KIC through theory and experiment.