• 한국세라믹학회지
• /
• 제13권1호
• /
• pp.30-34
• /
• 1976

In general the chemical composition of glass ceramics in Li2O-Al2O3-SiO2 system is similar to the composition of $\beta$-spodumene (Li2O-Al2O3-4SiO2). With the object to manufacture the glass ceramics which can be produced in the domestic pot the composition of glass was so settled at 1.0 Li2O.0.9Al2O3.6.0SiO2 in order to reduce the contents of Li2O, to prevent the corrosion of the pot and to decrease the cost of raw materials. 0.2 mole and 0.1 mole of the mixture of TiO2 and ZrO2 as nucleants were added to the basic composition of 1.0 Li2O-0.9Al2O3-6.0SiO2. Each sample was divided into two kinds with a TiO2/ZrO2 ratio of 2 to 1 and the other with a TiO2/ZrO2 ratio fo 1 to 1. Thermal expansion coefficient, the most important property of glass ceramics, was tested. The softening point and the melting point of the samples were observed by the use of a heating microscope. The results obtained were as follows. The manufacturing of glass ceramics seems to be possible in the industrial plant using the domestic pot. 1) The composition of the glass which can be melted in the domestic pot process was near 1.0 Li2O.0.9Al2O3.6.0SiO2. 2) The temperature range of crystal creation and crystal growth was between 850-94$0^{\circ}C$, and 5 hours holding the samples at the temperature range was enough to crystallize them. The major crystal was $\beta$-spdumene and there existed petalite partialy. 3) The thermal expansion coefficient fo the crystallized glass was negative. 4) The deforming point of the crystallized glass was 1435$^{\circ}C$.

• 한국세라믹학회지
• /
• 제38권10호
• /
• pp.936-941
• /
• 2001

5.31 mol% ${Y_2}{O_3}$-4.45 mo1% ${Nb_2}{O_5}$-90.31 mo1% $ZrO_2$에 ${Al_2}{O_3}$를 첨가한 복합체를 제조하여 알루미나 입도가 복합체의 균열 전파 저항성에 미치는 영향을 조사하였다. $ZrO_2/{Al_2}{O_3}$ 복합체에서는 R-cuve 거동이 관찰되었으며 0.2, $2.8{\mu}m$ ${Al_2}{O_3}$가 20 vol%가 첨가된 복합체의 인성값은 각각 7.9, $8.8MPam^{1/2}$이었다. 파괴인성값의 차이는 ${Al_2}{O_3}$ 입도 크기에 의존하는 $ZrO_2/{Al_2}{O_3}$ 복합체 내의 정방정 $ZrO_2$의 결정립 크기 차이에 의한 것으로 추정된다.

• 한국재료학회지
• /
• 제2권3호
• /
• pp.172-179
• /
• 1992

$Al_2O_3/ZrO_2$복합분말에 상릉분말을 침가하여 상압소결법으로 $Al_2O_3/ZrO_2$복합체를 제조한 후, 밀도, 강도, 경도 및 파괴인성등의 물성을 측정하였으며 미세구조 및 파괴단면도 관찰하였다. 상용분말의 침가량이 중량비로 50%이하인 경우에는 평균 꺽임 강도가 640 MPa정도로 거의 변화가 없었으며, 50%이상 첨가된 경우에는 강도가 저하되었는데, 이는 미세조직과 관계가 있는 것으로 생각된다. 또한 파괴인성(4.3-5.3 $Mpam^{1/2}$)값은 상용분말 첨가량에 비례하여 증가하였다. 파괴단면 관찰결과 파괴원인으로는 가공에서 생기는 표면 결함, $ZrO_2$ agglomeration에 의한 crack-like void 및 $Al_2O_3/ZrO_2$ nano복합체 분말과 상용분말간의 소결성 차이에서 생기는 계면 분리등이 관찰되었는데, nano 복합 분말만을 사용한 소결체에서는 가공에 의한 표면 결함만이 파괴원으로 작용하였다. 또한, 파괴형태는 주로 transgranular fracture이었다

• 대한의용생체공학회:학술대회논문집
• /
• 대한의용생체공학회 1995년도 추계학술대회
• /
• pp.131-133
• /
• 1995

• 전자공학회논문지 IE
• /
• 제49권2호
• /
• pp.1-8
• /
• 2012

단사정 구조의 순수 $ZrO_2$ 또는 5.35wt%의 $Y_2O_3$를 첨가한 정방정 구조의 $Y_2O_3(Y-TZP)$를 $Al_2O_3$에 첨가하여 그 기계적 특성 및 열충격 저항성을 연구하였다. $ZrO_2(m)$와 Y-TZP의 첨가량이 커짐에 따라 $Al_2O_3$의 소결 밀도가 증가하였다. 또한 Y-TZP의 첨가량이 증가함에 따라 비커스 경도도 증가하였고 첨가량 20wt%에서 최고값을 나타내었다. 시편의 경도는 소결 밀도에 의존함을 알 수 있었다. $ZrO_2(m)$나 Y-TZP 첨가량의 증가는 파괴인성을 향상시키는 결과를 얻을 수 있었다. 이러한 결과로 $Al_2O_3$의 경도는 $ZrO_2$의 transformation toughening 뿐 아니라 미세균열 강화에서도 얻어짐을 알 수 있었다. 단사정 구조의 순수 $ZrO_2$의 첨가는 $Al_2O_3-ZrO_2$의 열 충격 저항성을 향상시켰다. 결정입도는 $ZrO_2$의 첨가량이 증가함에 따라 커진다.

• 한국전기전자재료학회논문지
• /
• 제27권11호
• /
• pp.712-717
• /
• 2014

Glass ceramic has a high mechanical strength and low sintering temperature. So, it can be used as a thick film substrate or a high strength insulator. A series of glass ceramic samples based on MgO-$Al_2O_3-SiO_2-ZrO_2$ (MASZ) were prepared by melting at $1,600^{\circ}C$, roll-quenching and heat treatment at various temperatures from $900^{\circ}C$ to $1,400^{\circ}C$. Dependent on the heat treatment temperature used, glass ceramics with different crystal phases were obtained. Their nucleation behavior, microstructure and mechanical properties were investigated with differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), and Vicker's hardness testing machine. With increasing the heat treatment temperature of MASZ samples, their hardness and toughness initially increase and then reach the maximum points at $1,300^{\circ}C$, and begin to decrease at above this temperature, which is likely to be due to the softening of glass ceramics. As the content of $ZrO_2$ in MAS glass ceramics increases from 7.0 wt.% to 13 wt.%, Vicker's hardness and fracture toughness increase from $853Kg/mm^2$ to $878Kg/mm^2$ and $1.6MPa{\cdot}m^{1/2}$ to $2.4MPa{\cdot}m^{1/2}$ respectively, which seems to be related with the nucleation of elongated phases like fiber.

• Journal of Advanced Marine Engineering and Technology
• /
• 제33권2호
• /
• pp.322-329
• /
• 2009

Machinability of LAM(Laser Assisted Machining) has been studied for ceramics such as $Al_2O_3$, $Si_3_N4$ and $ZrO_2$ by $CO_2$ laser. It was possible to remove ceramics by PCBN tool because material became softening and deterioration by local laser beam irradiation. The advantage of LAM is the ability to produce larger material removal rates and tool life. But, for cutting of $Al_2O_3$ and $ZrO_2$, stage of laser power control was needed owing to thermal shock with high temperature of workpiece by laser power. And when $Si_3N_4$ was machined by LAM, $N_2$ gas spouted from surface of one cause of high temperature. Characteristics of LAM were analyzed using pyrometer, dynamometer, SEM and EDS to measure temperature of workpiece surface, cutting force, variation of machining surface and structure of lattice respectively. As the result of this study, it was found that machinability of LAM for ceramics in $CO_2$ laser and mechanism of LAM was different according to the kind of ceramics because of properties of materials.

• 한국재료학회지
• /
• 제15권7호
• /
• pp.453-457
• /
• 2005

Piezoelectric properties of $Pb(Mn_{1/3}Nb_{2/3})O_3-PbZrO_3-PbTiO_3$ ceramics were investigated with $Al_2O_3$ content $(0.0-1.0 wt\%)$. The constituent phases, microstructure, electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants were analyzed. Diffraction peaks for (002) and (200) planes were identified by X-ray diffractometer for all the specimens doped with $Al_2O_3$, indicating the MPB (morphotropic phase boundary) composition of tetragonal structures. The highest sintered density of $7.8 g/cm^3$ was obtained for $0.2wt\%\;Al_2O_3-doped$ specimen. Grain size increased by doping $Al_2O_3$ up to $0.3 wt\%$, and it decreased by more doping. Electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants increased by doping $Al_2O_3$ up to $0.2wt\%$, and it decreased by more doping. This might result from the formation of oxygen vacancies due to defects in $O^{2-}$ ion sites and the substitution of $Al^{3+}$ ions.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2005년도 춘계학술발표대회 및 제8회 신소재 심포지엄 논문개요집
• /
• pp.106-106
• /
• 2005

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2001년도 춘계학술대회 발표논문집
• /
• pp.40-46
• /
• 2001

A1₂TiO/sub 5/ 세라믹스의 열적 안정성은 MgO와 고온 arc용융노에서 MgAl₂O₄ spinel과 같은 고용체를 이루고, SiO₂, ZrO₂와 α-Al₂O₃등의 첨가제로 입자크기와 미세 균열을 감소시킴으로서 증가시킨다. A1₂TiO/sub 5/ 세라믹스의 낮은 열팽창 특성은 상이한 열팽창으로 hysteresis 곡선을 나타내며 이 현상은 미세균열의 opening과 closing으로 설명된다. 이들의 열팽창 곡선, 소성온도에 EK른 관계를 dilatometer로 연구하였다.