• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.552-560
• /
• 1994

A composite of TiB2-Al2O3 system was successfully prepared from a mixture of TiO2, B2O3, and Al by self-propagating high temperature synthesis (SHS) with a novel characteristic, utilizing the internal oxidation heat of aluminium metal of the mixture, instead of by a conventional technique, externally heating a mixture of Ti, B and Al2O3. From a mixture with B/Ti molar ratio of =2.0, pure two phases of TiB2 and $\alpha$-Al2O3 with good crystallinity and small, uniform sizes were formed. However, when the B/Ti molar ratio of the mixture goes to a value less than 2.0, in addition to the above main minerals, a small smounts of metastable phases such as TiB and Ti3B4 were formed. It was found that about 60%, the optimum green density of compacts gave their highest reaction rate and temperature during SHS process. TiB2-Al2O3 system composite with B/Ti molar ratio of =2.0 could be pressurelessly sintered even at 190$0^{\circ}C$ under Ar gas flows without any addition of sintering aids, showing their good properties such as 91.2% in relative density, 2750 kgf/$\textrm{mm}^2$ in Vickers hardness and 2620 kgf/$\textrm{cm}^2$ in flexural strength.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.153-158
• /
• 2002

$Al_2O_3$ composites powders with 1∼11 wt% $TiO_2$ were prepared by wet method and sintered at 1350$^{\circ}C$, 1450$^{\circ}C$ for 2h. Mechanical properties and microstructural evolution were investigated in this study. $Al_2O_3$-3 wt% $TiO_2$ composite were high bulk density of 2.37 g/$cm^3$ and low apparent porosity of 6.3%. The composites containing of 3 wt% $TiO_2$ showed moderately high bending strength of 68.9 MPa and the young's modulus of 35.5 MPa. The composites with increasing $TiO_2$ contents exhibit reduced thermal expansion coefficient due to the formation of $Al_2TiO_5$ phase.

• Journal of Powder Materials
• /
• v.11 no.3
• /
• pp.247-252
• /
• 2004

Recently, it has been found that mechanical alloying (MA) facilitates the nanocomposites formation of metal-metal oxide systems through solid-state reduction during ball milling. In this work, we studied the MA effect of Fe$_{3}$O$_{4}$-M (M = Al, Ti) systems, where pure metals are used as reducing agents. It is found that composite powders in which $Al_{2}$O$_{3}$ and TiO$_{2}$ are dispersed in $\alpha$-Fe matrix with nano-sized grains are obtained by mechanical alloying of Fe$_{3}$O$_{4}$ with Al and Ti for 25 and 75 hours, respectively. It is suggested that the large negative heat associated with the chemical reduction of magnetite by aluminum is responsible for the shorter MA time for composite powder formation in Fe$_{3}$O$_{4}$-Al system. X-ray diffraction results show that the reduction of magnetite by Al and Ti if a relatively simple reaction, involving one intermediate phase of FeAl$_{2}$O$_{4}$ or Fe$_{3}$Ti$_{3}$O$_{10}$. The average grain size of $\alpha$-Fe in Fe-TiO$_{2}$ composite powders is in the range of 30 nm. From magnetic measurement, we can also obtain indirect information about the details of the solid-state reduction process during MA.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.412-417
• /
• 2001

본 연구는 습식법으로 수산화 알루미늄과 티타니아를 출발물질로 하여 $Al_2$O$_3$-TiO$_2$복합분체를 제조하였으며, 2 mol의 Al(OH)$_3$분말에 대하여 TiO$_2$분말량을 1, 3, 5, 7, 9, 11 wt%로 첨가하여 $Al_2$O$_3$-TiO$_2$복합분체의 특성을 조사하였다. 제조된 $Al_2$O$_3$-TiO$_2$계 복합분체는 $700^{\circ}C$~140$0^{\circ}C$까지 하소하여 XRD 분석을 한 결과 100$0^{\circ}C$까지는 TiO$_2$(rutile)상과 η-Al$_2$O$_3$상이 공존하다가 110$0^{\circ}C$부터 130$0^{\circ}C$까지는 η-Al$_2$O$_3$에서 $\alpha$-Al$_2$O$_3$로의 상전이가 일어나서 $\alpha$-Al$_2$O$_3$상과 TiO$_2$(rutile)상이 나타났으며 하소온도 140$0^{\circ}C$, TiO$_2$첨가량이 5 wt%일 때부터 $Al_2$TiO$_{5}$가 생성되기 시작하였다. TiO$_2$첨가량에 따른 비표면적값은 첨가량이 7 wt%까지는 감소하였으나 그 이상 첨가시 증가하였다. 입도분석 결과 평균입경은 15.74~23.21$mu extrm{m}$로서 TiO$_2$첨가량이 3 wt%일 때 가장 작은 값을 가졌으며 TiO$_2$첨가량은 5 wt% 이상부터 점차 감소하였다.

• Korean Journal of Metals and Materials
• /
• v.49 no.12
• /
• pp.1001-1004
• /
• 2011

The formation of TiC and $Al_2O_3$ particles based on the self-combustion reaction of the $Al-TiO_2-C-CuO$ system in an Al alloy melt was investigated. With an adequate amount of CuO in the system, a spontaneous reaction occurred within the Al alloy melt at $850^{\circ}C$ and thereafter was self-maintained, producing an Al matrix composite reinforced with thermodynamically stable TiC and $Al_2O_3$ particles. TiC and $Al_2O_3$ particles contributed to a considerable increase in the strength and stiffness, demonstrating the feasibility of this method as a practical application for structural parts.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1147-1155
• /
• 1996

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.11a
• /
• pp.133-133
• /
• 2001

• Journal of Welding and Joining
• /
• v.10 no.4
• /
• pp.213-221
• /
• 1992

Al$_{2}$O$_{3}$ ceramic coating layer by gas flame spraying was very porous, therefore it could not have wear and corrosion resistance at all. To get a dense and strong coating layer, a method to infiltrate an alloy into the pores of $Al_{2}$O$_{3}$ ceramic coating was investigated. Cu-Ti alloys, which had good wettability and reactivity with $Al_{2}$O$_{3}$ ceramic, were examined for infiltration. Infiltration of the alloys was performed in vacuum at 1100.deg.C. The melt of Cu-50 at % Ti alloy was well penetrated through the porous $Al_{2}$O$_{3}$ coating and tightly sealed the pores, unbounded area and microcracks in the coating. The alloy melt in the pores reacted with $Al_{2}$O$_{3}$ ceramic to produce a suboxide phase, Cu$_{2}$Ti$_{4}$O. This composite layer which was composed of $Al_{2}$O$_{3}$ and Cu$_{2}$Ti$_{4}$O phase had good microstructure and wear and corrosion resistance. Additionally, microstructures at interfaces between coating layers were greatly improved owing to the effect of vacuum heat treating.