• Bulletin of the Korean Chemical Society
• /
• v.31 no.6
• /
• pp.1628-1632
• /
• 2010

Porous ${\eta}-Al_2O_3$ was synthesized by modified sol-gel method using ionic liquid as a templating material. The addition of ionic liquid assisted to increase the surface area of alumina. However, the acidity of aluminas prepared with ionic liquids was hardly affected regardless the change of its structural properties. Among the ionic liquids used in this study, 1-butyl-3-methylimidazolium hexafluorophosphate ([Bmim][$PF_6$]) was the most effective ionic liquid to produce porous ${\eta}-Al_2O_3$ particles. The catalytic performance of these aluminas has been investigated in dehydration of methanol to produce dimethyl ether. The alumina prepared with [Bmim][$PF_6$] outperformed the other aluminas except ${\eta}-Al_2O_3$ without modification in this reaction.

• Corrosion Science and Technology
• /
• v.6 no.5
• /
• pp.257-260
• /
• 2007

In order to further improve the corrosion resistance and wear resistance of the Ni-P coatings of electroless plating, electroless Ni-P/n-$Al_2O_3$ composite deposits were prepared by adding some nano $Al_2O_3$ Particles in Ni-P plating bath. The bath composition and proproties were studied in this paper. The orthogonal test was applied in order to get the new composite solution, taking the initial stable potential as evaluation standard and considering the elements correlation at the same time. The processing parameters have been optimized by single factor experiment in which the depositing speed was chosen as the evaluation standard. The results showed that the process is stable and the composite Ni-P/n-$Al_2O_3$ deposits werebright and smooth, whose hardness and corrosion resistance are much better than simple Ni-P coatings. Furthermore the surface appearance and structure of the composite Ni-P/n-$Al_2O_3$ coating were investigated by SEM and XRD method. It was proved that the coating surface is typical cystiform cells and its structure is amorphous. All test results ofcomposite coating showed that all various physical coating properties had been improved by adding nano-particles. The hardness of optimal coating is more than 600HV and increases to 1000HV after heat-treating, and its hardness is 20~50% higher than Ni-P coating. The rust points appeared in 200 hour by immersing the coating into the 10%HCl solution and the corrosive speed is $3{\times}10^{-3}mg/(cm^2{\cdot}h)$which was obtained after 300 hour. In the same condition Ni-P coating is $5.6{\times}10^{-3}mg/(cm^2{\cdot}h)$. The salt spray resistance of the layers can exceed 600h with the thickness $20{\mu}m$.

• The Korean Journal of Ceramics
• /
• v.2 no.3
• /
• pp.142-146
• /
• 1996

The molten carbonate fuel cell matrices, which are usually made of high surface, fine particle size ${\gamma}-LiAlO_2$ are reinforced with coarse particles of the same material and alumina fibers. An the effects of reinforcing materials on pore characteristics, sintering properties and mechanical properties of the matrices are examined.Among the matrices examined, the highest mechanical reinforcement has been achieved in the one containing 10 wt.% coarse particles and 20 wt.% alumina fibers.

• Journal of Powder Materials
• /
• v.7 no.4
• /
• pp.212-217
• /
• 2000

An optimum route to fabricate the $Al_2O_3/Cu$ nanocomposites with sound microstructure and improved mechanical properties was investigated. Microstructural investigations for the composites prepared using $Al_2O_3/Cu$-nitrate showed that fine Cu particles with average size of 150 nm were homogeneously distributed within the $Al_2O_3$ matrix grains and at the grain boundaries. Fracture strength of 953 MPa and toughness of 4.8 Mpa(equation omitted)m were measured for the composite. The strengthening and toughening of the composites are explained by the refinement of the microstructure and the crack bridging/deflection, respectively.

• Journal of the Korean Ceramic Society
• /
• v.52 no.4
• /
• pp.273-278
• /
• 2015

${\alpha}-Al_2O_3$ was synthesized by solvothermal synthesis using ${\alpha}-Al_2O_3$ seed, precursor of fine boehmite (Al(OOH)) or gibbsite ($Al(OH)_3$), and 1, 4-butanediol solvent. The seed content and precursor type were selected as variables in order to synthesize ${\alpha}-Al_2O_3$. The formation time of ${\alpha}-Al_2O_3$ was reduced and the size of the particles was decreased with addition of the seed. When the seed content was increased, the size of the synthesized ${\alpha}-Al_2O_3$ was reduced. Morphologies of the as-synthesized ${\alpha}-Al_2O_3$ with ${\alpha}-Al_2O_3$ seed were polyhedron-shaped, while the shape was plate-like or polyhedral without the seed, depending on the additives or the average particle size of the boehmite precursor. The aggregation of as-synthesized ${\alpha}-Al_2O_3$ from boehmite was smaller than that from gibbsite. As-synthesized ${\alpha}-Al_2O_3$, with 140 nm size, was obtained by using the seed and boehmite precursor.

• Korean Journal of Materials Research
• /
• v.21 no.11
• /
• pp.604-610
• /
• 2011

The effect of $BaF_2$ flux in $Y_3Al_5O_{12}:Ce^{3+}$(YAG:Ce) formation was investigated. Phase transformation of $Y_3Al_5O_{12}$(YAG) was characterized by using XRD, SEM, and TEM-EDS, and it was revealed that the sequential formation of the $Y_4Al_2O_9$(YAM), $YAlO_3$(YAP) and $Y_3Al_5O_{12}$(YAG) in the temperature range of 1000-1500$^{\circ}C$. Single phase of YAG was revealed from 1300$^{\circ}C$. In order to find out the effect of $BaF_2$ flux, three modeling experiments between starting materials (1.5$Al_2O_3$-2.5$Y_2O_3$, $Y_2O_3$-$BaF_2$, and $Al_2O_3$-$BaF_2$) were done. These modeling experiments showed that the nucleation process occurs via the dissolution-precipitation mechanism, whereas the grain growth process is controlled via the liquid-phase diffusion route. YAG:Ce phosphor particles prepared using a proposed technique exhibit a spherical shape, high crystallinity, and an emission intensity. According to the experimental results conducted in this investigation, 5% of $BaF_2$ was the best concentration for physical, chemical and optical properties of $Y_3Al_5O_{12}:Ce^{3+}$(YAG:Ce) that is approximately 10-15% greater than that of commercial phosphor powder.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.3
• /
• pp.208-219
• /
• 2004

To find a suitable oxygen carrier particle for a 50kW chemical-looping combustor, which was designed and installed to demonstrate continuous oxidation and reduction, three oxygen carrier particles(NiO/bentonite, $NiO/NiAl_2O_4$, $CoO_x/CoAl_2O_4$) were prepared. The reactivity and the attrition resistance of particles were measured and investigated by a thermo-gravimetrical analyzer and an attrition test apparatus respectively. From the viewpoints of oxygen transfer capacity, optimum reaction temperature(operating temperature range), reaction rate, carbon deposition rate, and attrition resistance, NiO/bentonite particle showed better performance than the other particles, therefore we selected NiO/bentonite particle as an optimum oxygen carrier particle.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• 연구논문집
• /
• s.22
• /
• pp.151-160
• /
• 1992

The wear resistance of electroless Ni-P-X(X A1203, Diamond) composite coating layers was studied by Taber abrasion test technique. The wear resistance of composite coating layers was particularly relied upon the codeposited content, particle size and distribution of particles, and heat treatment of coating layers, as well as the electroless nickel plating bath employed. In this study, we lay emphasis on the wear resistance of electroless composite coating layers containing A1203 particles(1.2~Im, 6.7hIm, 11.5lIm, 20l1m) or diamond particles (1.5jim, 5gm). From the result of composite coating A1203 and diamond particles, the wear resistance of composite coating layers is as follows.

• Journal of Powder Materials
• /
• v.9 no.3
• /
• pp.189-198
• /
• 2002

In this work, transient liquid phase (TLP) bonding of Ni-Cr heat resisted cast alloy (HP) was investigated. And also the behaviors of the solid particles distributed in the interlayer during TLP bonding were investigated. The MBF-60 and solid particles (Ni, Fe, and $Al_2O_3$ powders respectively) added MBF-60 which will be a liquid phase coexisting with solid particles at the bonding temperature were used as insert metal. The effective and sound bonding was possible by spark plasma sinter-bonding due to the differences of electric resistance between base metal and liquid insert layer which creates high temperature region. During the isothermal solidification, $Al_2O_3$ particles and solid particles of liquid phase sintered insert metal have shown no growth, while Ni and Fe particles grow rapidly. In this TLP bonding using the MBF-60 and distributed Fe, Ni particles as insert materials, the whole isothermal solidification process was dominated by the growth rate of the solid particles distributed in the interlayer.