• 한국세라믹학회지
• /
• 제27권1호
• /
• pp.55-61
• /
• 1990

Effect of Al2O3 addition on the mechanical properties and microstructure of Ce-TZP were studied. 12, 14, 16Ce-TZP containing 0-40wt% Al2O3 were prepared by sintering at 155$0^{\circ}C$ for 2h. in air. Density, linear shrinkage, bending strength, Vickers hardness, microstructuer and the amount of stress induced phase transformation were examined. Vickers hardness increased linearly with increasing amounts of Al2O3. The amount of transformation and fracture toughness decreased linearly with increasing amount of Al2O3. Linear shrinkage and relative density decreased with increasing Al2O3 content in all composition of Ce-TZP. Grain growth of Ce-TZP was inhibited by Al2O3 dispersion and fracture mode of Ce-TZP/Al2O3 composites transformed from intergranular to transgranular fracture as the amount of Al2O3 increased. TEM observation revealed that Al2O3 particles were located mainly at grain boundaries of ZrO2.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.498-504
• /
• 2014

Particulate nitride composites have been fabricated by sintering the compacted powder of AlN and 5 - 64.3 mol% $Al_2O_3$, with a small addition of $Y_2O_3$ ($Y_2O_3$/AlN, 1 wt%), in 1-atm nitrogen gas at $1650-1900^{\circ}C$. The composites were characterized in terms of sintering behavior, phase relations, microstructure and thermal shock resistance. AlN, 27R AlN pseudopolytype, and alminium oxynitride (AlON, $5AlN{\cdot}9Al_2O_3$) were found to existin the sintered material. Regardless of batch composition, the AlN-$Al_2O_3$ powder compacts exhibited similar sintering behavior; however, the degree of shrinkage commonly increased with increasing $Al_2O_3$ content, consequently giving high sintered bulk density. By increasing the $Al_2O_3$ addition up to ${\geq}50 mol%$, the matrix phase in the sintered material was converted from AlN or 27R to AlON. Above $1850^{\circ}C$, a liquid phase was formed by the reaction of $Al_2O_3$ with AlN, aided by $Y_2O_3$ and mainly existed at the grain boundaries of AlON. Thermal shock resistance was superior in the sintered composite consisting of AlON with dispersed AlN or AlN matrix phase.

• 대한화학회지
• /
• 제46권4호
• /
• pp.336-345
• /
• 2002

본 연구에서는 조합화학을 이용하여 $CaO-Gd_2O_3-Al_2O_3$계에서 $Eu^{3+}$와 $Tb^{3+}$활성 적색 및 녹색 PDP용 형광체를 탐색하였으며 탐색된 형광체의 합성온도, 최적조성,발광 특성 등을 조사하였다. $CaO-Gd_2O_3-Al_2O_3$의 삼성분계의 형광특성 라이브러리를 작성하기 위하여 210개의 다른 조성을 가진 시료를 고분자 착체 중합법으로 합성하였다. 합성된 형광체 분말을 VUV PL로 측정하여 형광 특성 라이브러리를 작성하였고 발광특성이 잘 나타난 시료를 XPD를 이용하여 결정 구조를 확인하였다. 적색 형광체로서 탐색된 $Ca_{\alpha}$G$d_{0.95-\alpha-\beta}$$Al_\beta$$O_\delta$ : Eu(0.02< $\alpha+\beta$ <0.04)형광체는 색순도 면에서 상용형광체보다 개선된 특성을 보였으며 녹색 형광체로서 탐색된 $CaGdAl_3O_7$ : Tb, Ca$Al_{12}$$O_{19}$ : Tb, $Gd_4Al_2$$O_9$ : Tb, $Gd_3Al_5$$O_{12}$ : Tb 형광체 중에서 $CaGdAl_3O_7$ : Tb, Ca$Al_{12}$$O_{19}$ : Tb형광체는 상용 형광체에 비해 잔광시간이 짧은 특성을 보였다

• 동력기계공학회지
• /
• 제3권2호
• /
• pp.57-63
• /
• 1999

The fabrication of $Al_2O_3/Al$ composites by pressureless infiltration technique was made to investigate the effects of processing variables such as content of Mg, processing temperature and time on the infiltration behavior of molten Al and microstructure. When the pure Al was infiltrated into mixtures of Mg and $Al_2O_3$ powder, processing temperature required to spontaneous infiltration was decreased and critical processing temperature and Mg content were $700^{\circ}C$ and 3wt% respectively. The content of Mg was found the most powerful variable for infiltration of molten Al. The infiltration ratio increased with Mg content and processing temperature, however the $Al_2O_3/Al$ composites which were fabricated by high Mg content and processing temperature resulted in non uniform dispersion of $Al_2O_3$ particles by excessive interfacial reaction. XRD pattern indicated that $MgAl_2O_4$ and AIN was observed at the interface of $Al_2O_3$ particles and in the Al matrix as reaction products.

• 한국진공학회지
• /
• 제19권5호
• /
• pp.385-390
• /
• 2010

원자층 증착법(Atomic Layer Deposition, ALD)을 이용하여 ZnO 나노막대에 ZnO:Al과 $Al_2O_3$를 코팅하여 coaxial 형태의 나노선 구조를 제작하여 광학적 특성을 분석하였다. 반도체인 ZnO:Al을 코팅하는 경우 Al이 ZnO층에 확산되어 ZnO에 도핑이 되는 효과를, $Al_2O_3$를 코팅하는 경우 반도체-절연체 계면 상태가 존재함을 광전이 특성을 이용하여 확인하였다.

• 한국분말재료학회지
• /
• 제7권1호
• /
• pp.35-41
• /
• 2000

Al2O3$.$SiC particle was prepared was prepared by the self-propagting high temperature sYthesis(SHS) process from a mixture of SiO2, Al and C powders, The fabricated Al2O3$.$SiC particle was applied to 2024Al/(Al2O3$.$SiC)pcomposite as a reinforcement. Aluminum matix composites were fabricares by the powder extrusion method using the synthesized Al2O3$.$SiC particle and commercial 2024Al powder. Theoptimum preparation conditions for Al2O3$.$SiC partticle by SHS process were described. The influence of the Al2O3$.$SiC voiume fraction on the mechanical was composite was also discussed. Despite adiabatic temperature was about 2367K, SHs reaction was completed not by itself, but by using pre-heating. Mean particle size of final particle synthesized was 0.73 ${\mu}$m and most of the particle was smaller than 2${\mu}$m. Elastic modulus and tensile strength of the composite increased with increase the volume fraction of reinforcement but, tensile strength depreciated at 30 vol% of reinforcement.

• 한국세라믹학회지
• /
• 제34권5호
• /
• pp.483-490
• /
• 1997

Al2O3/metal composites were fabricated by oxidation and reaction of molten Al-alloy into two types of commercial Al2O3-SiO2 fibrous insulation board. The growth rate, composition and microstructure of these materials were described. An AlZnMg(7075) alloy was selected as a parent alloy. Mixed polycrystalline fiber and glass phase fiber were used as a filler. The growth surface of an alloy was covered with and without SiO2. SiO2 powder was employed as a surface dopant to aid initial oxidation of Al-alloy. Al-alloy, SiO2, fiber block and growth inhibitor CaSiO3 were packed sequentially in a alumina crucible and oxidized in air at temperature range 90$0^{\circ}C$ to 120$0^{\circ}C$. The growth rate of composite layer was calculated by measuring the mass increasement(g) per unit surface($\textrm{cm}^2$). XRD and optical microscope were used to investigate the composition and phase of composites. The composite grown at 120$0^{\circ}C$ and with SiO2 dopant showed rapid growth rate. The growth behavior differed a little depending on the types of fiber used. The composites consist of $\alpha$-Al2O3, Al, Si and pore. The composite grown at 100$0^{\circ}C$ exhibited better microstructure compared to that grown at 120$0^{\circ}C$.

• 센서학회지
• /
• 제1권1호
• /
• pp.93-100
• /
• 1992

이트리아 안정화(安定化) 지르코니아(92 mole% $ZrO_{2}$+8 mole% $Y_{2}O_{3}$)에 0.5 mole% $SiO_{2}$와 $0{\sim}2.0{\;}mole%{\;}Al_{2}O_{3}$가 첨가된 소결체의 소결성, 기계적 및 전기적 성질에 대하여 조사하였다. 소결밀도(燒結密度)는 0.5 mole% $Al_{2}O_{3}$가 첨가되었을 때 가장 높게 나타났으며 1.5 mole%이상 $Al_{2}O_{3}$가 첨가됨에 따라 감소하는 경향을 나타내었다. 비커스 경도(硬度)는 소결밀도(燒結密度)에 비례하여 나타났으며, 0.5 mole% $Al_{2}O_{3}$가 첨가되었을 때 가장 높은 전도성을 나타내었다. 일정한 산소분압(酸素分壓)에 따른 기전력 측정에서도 0.5 mole% $Al_{2}O_{3}$가 첨가되었을 매 가장 높았다. 제작된 산소(酸素)센서들의 응답특성(應答特性) 결과에서 $SiO_{2}$와 $Al_{2}O_{3}$가 각각 0.5 mole% 첨가된 센서의 응답특성이 가장 좋았다.

• Korean Chemical Engineering Research
• /
• 제46권4호
• /
• pp.806-812
• /
• 2008

귀금속촉매 존재하에서 암모니아 전환반응은 배가스내의 암모니아를 처리하는데 중요한 기술이다. 과잉용액 함침법을 이용하여 $Pt-Rh/Al_2O_3$, $Pt-Rh/TiO_2$, $Pt-Rh/ZrO_2$, $Pt-Pd/Al_2O_3$, $Pd-Rh/Al_2O_3$, $Pd-Rh/TiO_2$, $Pd-Rh/ZrO_2$, $Pt-Pd-Rh/Al_2O_3$, $Pd/Ga-Al_2O_3$, $Rh/Ga-Al_2O_3$, 그리고 $Ru/Ga-Al_2O_3$의 촉매를 제조하였다. 제조된 촉매는 1/4"의 반응기에 $10,000{\sim}50,000hr^{-1}$의 공간속도 조건하에서 촉매활성능 실험을 수행하였다. 암모니아의 초기농도는 2,000 ppm (나머지는 공기)으로 유지하였다. $T_{50}$는 암모니아 전환율이 50%일 때를 나타내는 온도를, $T_{90}$은 90%의 전환율일 때의 온도를 나타낸다. 알루미나를 담지체로 사용했을때의 $T_{50}$와 $T_{90}$은 다른 담체를 사용했을때의 $T_{50}$와 $T_{90}$보다 훨씬 낮았다. Pd-Rh촉매의 경우 $Al_2O_3$를 담체로 사용하였을 때 $ZrO_2$나 $TiO_2$보다 저온 활성이 우수하게 나타났다. 황산화물의 피독실험 결과 본 연구에서는 최종적으로 $Pt-Rh/Al_2O_3$ 촉매가 다른 촉매에 비하여 우수함을 보였다. 실험결과 Pt-Rh가 암모니아 전환공정에서 유용한 촉매라는 사실을 알 수 있다.

• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.106-112
• /
• 1995

In order to examine the effect of CuO and Al2O3 addition on the electrical conductivity of ZnO, both Al2O3 (0, 1, 2, 5, 10at.%) and CuO (1, 5at.%) were added to ZnO. Al2O3 addition (~2at.% Al) increased the total electrical conductivity of ZnO which was already decreased by CuO doping effect Above solid solubility of Al (~2at.%), ZnAl2O4 formed and the total electrical conductivity decreased due to the decrease of sintered density. Impedance measurements were used to know the reason and degree of contribution of three resistive elements, ZnO grain, ZnO/CuO, and ZnO/ZnO grain boundaries, to the total electrical conductivity changed.