• Korean Journal of Materials Research
• /
• v.5 no.1
• /
• pp.140-148
• /
• 1995

Optical properties of $TiO_{2}$. Ag filrns and $TiO_{2}/Ag/TiO_{2}$ multilayer filrns with different thickness were predicted using the transfer matrix, and these results were compared with real transmittance curves of the sputterdeposited films. With the complex refractive indices, it was possible to predict transmittance characteristics which were close to real data for $TiO_{2}$ and Ag films. Due to the diffusion and agglomeration of Ag during $TiO_{2}$ deposition, optical properties of the sputterdeposited $TiO_{2}/Ag/TiO_{2}$ films were found to be very different from the transmittance curves predicted using the transfer matrix. Using deposition of 4nm-thick or 6nm-thick TI layers as a diffusion barrier, however, the transmittance curves of $TiO_{2}/Ti/Ag/Ti/TiO_{2}$ five-layer films became similar to ones predicted for $TiO_{2}/Ag/TiO_{2}$ threeiayer films.

• Applied Chemistry for Engineering
• /
• v.23 no.3
• /
• pp.293-296
• /
• 2012

Nanocomposites were fabricated as titanium dioxide ($TiO_2$) doped with nanometals (Au, Ag) by sonochemical reduction method and sol-gel method in order to investigate their antimicrobial activities. Then, the antimicrobial activity of the resulting samples was compared by the measurement of colony numbers survived on the agar plate incubated for 24 h after the loading E. coli on the solid-state media with the nanocomposites. The initial antimicrobial activity of the metal (Au, Ag)-doped $TiO_2$ was higher than that of the pristine $TiO_2$. Afterwards the nanocomposite samples were kept at $4^{\circ}C$ for a long time and the aged samples exhibited the different antimicrobial activity. With the elapse of aging times, Ag-doped $TiO_2$ with $TiO_2$ coating ($Ag-TiO_2$@$TiO_x$) exhibited the higher antimicrobial activity than those of $Ag-TiO_2$and $Au-TiO_2$. The $TiO_2$ coating on the $Ag-TiO_2$ may prevent the oxidation of Ag nanometals and stabilize colloidal nanocomposites.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.38-43
• /
• 2009

In this study, we investigated photocatalytic ability of plasma sprayed $TiO_2$ and Ag sputtering $TiO_2$(Ag-$TiO_2$) coatings. A sputtering processes were adopted to coat the surface of $TiO_2$ with Ag(99.99%). Ag was sputtered at 10mA, 450V for $1{\sim}11$ seconds. $TiO_2$ and Ag-$TiO_2$ coatings were heat-treated at 250, 300, 350, $400^{\circ}C$ for $0{\sim}240$seconds. Photoelectrical conductivity was measured by four-point probe, and photodegradation was calculated by UV-V is spectrometer. Microstructure observation of $TiO_2$ and Ag-$TiO_2$ coatings were investigated by SEM. Crystal structure of $TiO_2$ and Ag-$TiO_2$ coatings were investigated by XRD. Qualitative analyses of $TiO_2$ and Ag-$TiO_2$ coatings were conducted by EDX. When $TiO_2$ coatings were heat-treated at $350^{\circ}C$ for 30 sec, photoelectrical conductivity and photodegradation were best. And in XRD analysis result, (101)/(110) relative intensity ratio of $TiO_2$(rutile) was comparably changed with photoelectrical conductivity. When Ag-$TiO_2$ coatings were heat-treated at $350^{\circ}C$ for 30 [sec] after sputtering Ag for 7 sec, Photoelectrical conductivity and photodegradation are best. Surface of coatings in such condition has very small and uniform Ag particles.

• Elastomers and Composites
• /
• v.57 no.1
• /
• pp.1-8
• /
• 2022

In this study, the photo-deposition method was used to introduce Ag onto the surface of TiO₂ to synthesize an Ag-TiO₂ composite. The effects of the varying amounts of AgNO₃ precursor and annealing time periods on the Ag content in the composites, as well as their antibacterial characteristics under visible light conditions were studied. SEM analysis revealed the spherical morphology of the Ag-TiO₂ composite. Compared with TiO₂, the Ag particles were too small to be observed. An XPS analysis of the Ag-TiO₂ surface confirmed the Ag content and showed the peak intensities for elements such as Ag, Ti, O, C, and Si. The highest Ag content was observed when 33.3 wt.% of AgNO₃ and an annealing time of 6 h were employed; this was the optimum annealing time for Ti-Ag-O bonding, in that the lowest number of O bonds and the highest number of Ag bonds were confirmed by XPS analysis. Superior antibacterial properties against Bacillus and Escherichia coli, in addition to the widest inhibition zones were exhibited by the Ag-TiO₂ composite with an increased Ag content in a disk diffusion test, the bacterial reduction rate against Staphylococcus aureus and Escherichia coli being 99.9%.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.84-89
• /
• 2014

In this work, Ag-$TiO_2$ nanocomposites were prepared via the sonochemical deposition of Ag nanometals on $TiO_2$ nanoparticles. The size of deposited Ag nanometals was ranged in 1~3 nm and the number of Ag nanometals deposited on $TiO_2$ increased in proportion to the dosage amounts of Ag precursors. As-prepared Ag-$TiO_2$ was loaded on the sterilized agar plate together with an aliquot volume of diluted E-coli, followed by 30 min irradiation of the solar simulated light ($600{\sim}1800{\mu}w/cm^2$). Finally, the agar plate was incubated for 24 h at $37^{\circ}C$ and the number of survived colonies were counted. It was experimentally confirmed that Ag-$TiO_2$ exhibited the higher antimicrobial activity than that of pure $TiO_2$, based on measuring the colony number of control sample. The survived colony numbers on the agar plate decreased with the increase of dosage amounts of Ag-$TiO_2$ and the irradiated intensity of solar simulated light for 30 min before incubating. The increase of Ag nanometal doposition induced the progressive enhancement of antimicrobial activity, but rather reduced the photocatalytic activity of Ag-$TiO_2$ probably due to the excessive presence of Ag nanometals on $TiO_2$ matrix.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.9
• /
• pp.681-684
• /
• 2010

The $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ multilayered structure for the transparent electrodes in plasma display panel was designed by essential macleod program (EMP) and the multilayered film was deposited on a glass substrate by direct-current (DC)/radio-frequency (RF) magnetron sputtering system. During film deposition process, the Ag layer in $TiO_2$/Ag/$TiO_2$ structure became oxidized and the filter characteristic was degraded easily. In this study, ZnS layer was adopted as a diffusion blocking layer between $TiO_2$ and Ag to prevent the oxidation of Ag layer efficiently in $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ structure. Based on the AES depth profiling analysis, the Ag layer was effectively protected by the ZnS layer as compared with the $TiO_2$/Ag/$TiO_2$ multilayered films without ZnS as an antioxidant layer. The 3 times stacked $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ films have low sheet resistance of $1.22{\Omega}/{\square}$ and luminous transmittance was as high as 62% in the visible ranges.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.2
• /
• pp.63-67
• /
• 2015

$TiO_2/Ag/TiO_2$ trilayer films were deposited with radio frequency (RF) and direct current (DC) magnetron sputtering onto the glass substrate to consider the influence of Ag interlayer on the optical properties of the films. The thickness of $TiO_2$ films was kept at 24 nm, while the thickness of Ag interlayer was varied as 5, 10, 15, and 20 nm. As-deposited $TiO_2$ single layer films show the optical transmittance of 66.7% in the visible wave-length region and the optical reflectance of 16.5%, while the $TiO_2$ films with a 15 nm thick Ag interlayer show the enhanced optical transmittance of 80.2% and optical reflectance of 77.8%. The carrier concentration was also influenced by Ag interlayer. The highest carrier concentration of $1.01{\times}10^{23}cm^{-3}$ was observed for a 15 nm thick Ag interlayer in $TiO_2/Ag/TiO_2$ films. The observed result means that an optimized Ag interlayer in $TiO_2/Ag/TiO_2$ films enhanced the structural and optical properties of the films.

• Journal of the Korean Vacuum Society
• /
• v.5 no.2
• /
• pp.147-155
• /
• 1996

Optical properties of $TiO_2/M/Ag/M/TiO_2$ films have been changed with the diffusion barrier metal M. Optimum opticla properties of $TiO_2/M/Ag/M/TiO_2$ as the transparent heat mirror film, could be obtained with Ti among diffusion barrier metals of Ti, Cu, Zr and Al. $TiO_2/M/Ag/M/TiO_2$ film, which was fabricated by sputtering of 18 nm-thick $TiO_2$ and Ag, and 4nm-thick Ti, showed maximum transimittance of 89% at visible wavelength and infrared reflectance of 97% at wavelength of 3000 nm. Optical properties of this film was not degraded by Xenon-sunshine weather test for 240 hours. For specimens with barrier layers of Cu, Zr, and Al, degradation of optical properties by weather test was increased in a sequence of films with Cu, Zr, and Al barrier layers.

• Applied Chemistry for Engineering
• /
• v.34 no.1
• /
• pp.36-44
• /
• 2023

Core-shell TiO₂/Ag nanoparticles were synthesized by a modified sol-gel process and the reverse micelle method using acetoxime as a reducing agent in water/dodecylbenzenesulfonic acid (DDBA)/cyclohexane. The structure, shape, and size of the TiO₂/Ag nanoparticles were investigated using X-ray diffraction (XRD), UV-visible spectroscopy, scanning electron microscope (SEM), transmission electron microscope (TEM), and thermogravimetric analysis (TGA). The size of TiO₂/Ag nanoparticles could be controlled by changing the [water]/[DDBA] molar ratio values. The size and the polydispersity of TiO₂/Ag nanoparticles increased when the [water]/[DDBA] molar ratio rose. The resultant Ag nanoparticles over the anatase crystal TiO₂ nanoparticles exhibited a strong surface plasmon resonance (SPR) peak at about 430 nm. The SPR peak shifted to the red side with the increase in nanoparticle size. Conductive pastes with 70 wt% TiO₂/Ag nanoparticles were prepared, and the pastes were coated on the PET films using a screen-printing method. The printed paste films of the TiO₂/Ag nanoparticles demonstrated greater surface resistance than conventional Ag paste in the range of 405~630 μΩ/sq.

• Journal of the Korean GEO-environmental Society
• /
• v.17 no.2
• /
• pp.5-11
• /
• 2016

$MWCNT-TiO_2$ nano composites and $Ag-MWCNT-TiO_2$ nano composites were prepared from Multi-Walled Carbon NanoTube (MWCNT), titanium (IV) butoxide (TNB) solution and silver nitrate ($AgNO_3$) by the sol-gel method. The dispersion and structure of Ag in the synthesized composites was observed by Scanning Electron Microscopy (SEM) and Field Emission Transmission Electron Microscopy (FE-TEM). X-Ray Diffraction (XRD) patterns of the composites showed that the composites contained an anatase phase. The Energy Dispersive X-ray spectroscopy (EDX) showed the presence of C, O, Ti and Ag peaks. The $TiO_2$ particles were distributed uniformly in the MWCNT network, and Ag particles were virtually fixed on the surface of the tubes. Also decomposition of the methylene blue was investigated according to UV radiation times for study photocatalytic activity. $Ag-MWCNT-TiO_2$ nano composites show high photodegradation than $MWCNT-TiO_2$ nano composites. The results indicate that the high conductivity of Ag improved the photoactivity of the $MWCNT-TiO_2$ composite.