• Korean Journal of Crystallography
• /
• v.6 no.2
• /
• pp.111-117
• /
• 1995

TiO2 thin films were prepared on a (100)silicon wafer using a chemical vapor deposition(CVD) method. The deposition experiments were performed using the TTIP in the deposition temperature ransing from 200 content. The deposition rate of TiO2 was increased with the substrate temperature and the oxygen content. The thickness of the deposited thin film and the compositional analysis of this thin films with theoxygen content were measured using Ellipsometry, SEM and ESCA, respectively. The deposited thin film was composed of a bilayer, external TiO2 and internal Ti. Carbon as a residual impurity was found to remain when zero sccm O2 was purged into a reaction chamber and the composition of the deposited thin film was found to change Ti into TiO in a deeper layer. However, when 600sccm O2 was supplied to a reaction chamber, it has been found to reside less carbon content than without O2. Finally, in the condition of 1200sccm O2, no impurity level of carbon was observed and a deeper layer consisted of the Ti composite, even though the deposited surface was composed of TiO2.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.1
• /
• pp.19-24
• /
• 2007

The effects of $B_2O_3-SiO_2-R(R;CaO,\;BaO,\;ZnO,\;Bi_2O_3)$ borosilicate glass system on the sintering behavior and microwave dielectric properties of ceramic/glass composites were investigated as functions of modifier, glass addition ($30{\sim}50\;vol%$) and sintering temperature ($500{\sim}900^{\circ}C$ for 2 hrs). The addition of 50 and 45 vol% glass ensured successful sintering below $900^{\circ}C$. Sintering characteristics of the composites were well described in terms of modifier. Borosilicate glass enhanced the reaction with $Al_{2}O_{3}$ to form pores, second phases and liquid phases, which was responsible to component of modifier. Dielectric constant (${\varepsilon}_{r},\;Q{\times}f_{o}$) and temperature coefficient of resonant frequency (${\tau}_{f}$) of the composite with 50 and 45 vol% glass contents($B_{2}O_{3}:SiO_{2}:R=25:10:65$) demonstrated A-CaBS(7.8, 2,560 GHz, -81ppm/$^{\circ}C$), A-BaBs(5.8, 3.130 GHz, -64 ppm/$^{\circ}C$), A-ZnBS(5.7, 17,800 GHz, -21 ppm/$^{\circ}C$), A-BiBs(45 vol% glass in total)(8.3, 2,700 GHz, -45 ppm/$^{\circ}C$) which is applicable to substrate requiring an low dielectric properties.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.593-602
• /
• 1991

Al2O3 and NiO-doped Al2O3 powders were prepared from the ethanol solution of Al (NO3)3$.$9H2O and Ni(NO3)2$.$6H2O by spray pylolysis method using two-fluid nozzle. As a result of spraying test with 0.3 mol/{{{{ iota }} concentration starting solution, mean droplet sizes varied with 8.99∼9.69$\mu\textrm{m}$ and those standard deviation were 4.57∼5.12. As-prepared powders which were synthesized at 1000$^{\circ}C$ have spherical shape, sizes of 0.1∼3.0$\mu\textrm{m}$ and specific surface area of 22.34∼24.20㎡/g. Most powders consisted of {{{{ gamma }}-Al2O3 phase and transforned into ${\alpha}$-A;2O3 phase by calcination at 1100$^{\circ}C$ for 1 hr. NiO-doped Al2O3 sintered bodies had better sinterability than those of pure Al2O3 and 0.3 wt% NiO-doped Al2O3 had near theoretical density and dense microstructure.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.859-866
• /
• 2003

When calcium sulfoaluminate-based expansive cement was hydrated, ettringite and monosulfate were mainly formed. The crack of hardened cement was prevented by compensating drying shrinkage due to formation of the above hydrates. In order to study the hydration properties of calcium sulfoaluminate-based expanding cement, 3CaOㆍ3Al$_2$O$_3$ㆍCaSO$_4$(C$_4$A$_3$S) was prepared by chemical synthesis, and then the hydration of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.$2H_2O$-C$_3$A system_was characterized. Good $C_4$A$_3$S phase was prepared at $1300^{\circ}C$ by chemical synthesis, and the main hydration product of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.2$H_2O$ system was ettringite. In the case of hydration $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$ㆍ 2$H_2O$-C$_3$A system, ettringite was formed in the early period and it was transformed into monosulfate while consumed gypsum.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.1
• /
• pp.25-32
• /
• 2009

The glass-ceramics composed of coal bottom ash produced from a thermal power plant, $Na_{2}O$ and $Li_{2}O$ as a flux agent and $TiO_2$ as a nucleation agent were fabricated and its microstructures were analyzed. The nepheline was a major crystal phase in the glass-ceramics fabricated and its amount increased with $TiO_2$ addition. The glass-ceramics without $TiO_2$ addition had the thick surface crystals induced by a surface-crystallization mechanism and no crystal in the interior matrix. The surface crystallization, however, was restrained and the interior matrix was completely crystallized showing dendrite shape spread with fine particles < $1{\mu}m$ when added with $TiO_2$ above 4 wt%. For the glass-ceramics containing 6 wt% $TiO_2$, the $5{\mu}m$-long dendrite crystal; were interlocked each other which could suppress the crack propagation effectively at the external loading applied.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.3 s.36
• /
• pp.259-265
• /
• 2005

Characteristics of electroplated Ni films and $Ni-Al_2O_3$ composite films, such as yield strength, fracture elongation, and $Al_2O_3$ content, were evaluated as a function of electroplating current density. $Al_2O_3$ content was $11.48\~11.64\;vol\%$ for $Ni-Al_2O_3$ composite films electroplated at $5\~20\;mA/cm^2$, and decreased to $8.41\;vol\%$ at $30\;mA/cm^2$ $Ni-Al_2O_3$ possessed yield strengths higher than those of Ni films. Especially, $Ni-Al_2O_3$ fabricated at $5\;mA/cm^2$ exhibited $50\%$ improved yield strength. Fracture elongations of Ni and $Ni-Al_2O_3$ decreased with increasing the electroplating current density. $Ni-Al_2O_3$ electroplated at $5\;mA/cm^2$ exhibited more uniform dispersion of $Al_2O_3$ and higher yield strength and larger fracture elongation than the composite films processed at other current densities.

• Journal of Environmental Science International
• /
• v.6 no.2
• /
• pp.125-131
• /
• 1997

The mechanism of stomatal closing in response to $O_2$ was indirectly investigated by using $H_2O_2$ which is the intermediate product of $O_2$ metabolites. Stomata in epidermal strips close in response to $H_2O_2$. The effect of $H_2O_2$ on stomatal closing was dependent on the concentration of $H_2O_2$. 10 ppm $H_2O_2$ showed a clear effect on stomatal closing and 1000 ppm $H_2O_2$ induced complete stomatal closing after the treatment of 3 hours. Stomatal closing by $H_2O_2$ in intact leaf was also observed by measuring the diffusion resistance with porometer. It was found that the stomatal closing by $H_2O_2$ was not mediated by $Ca^{2+}$, and that was a different result observed in stomatal closing by water stress. Reversely, $Ca^{2+}$ showed a great inhibition on stomatal closing. The leakage of K+ in epidermal strips was doubled in response to $H_2O_2$ when it was campared to the control. 10 ppm $H_2O_2$ decreased photosynthetic activity. Fv/Fm representing the activity of Photosystem II was reduced about 4 % in 10 ppm $H_2O_2$ and 8 % in 100 ppm $H_2O_2$ In the treatment of 1.5 hour. However, stomatal closing by 10 ppm $H_2O_2$ was reduced about 56 %. According1y, it can be suggested that stomatal closing by $H_2O_2$ is related with the decrease of photosynthetic activity, but it was chiefly induced by the change of the membrane permeability. Key words Commelina communis, stomatal closing, $H_2O_2$, $Ca^{2+}$, photosynthesis.

• New & Renewable Energy
• /
• v.3 no.1 s.9
• /
• pp.54-59
• /
• 2007

A sintering aid, $B_{2}O_{3}$ have been included into a $LiAlO_{2}$ electrolyte support by a tape casting method in order to reinforce mechanical strength of the support for molten carbonate fuel cells [MCFCs). Starting idea originates from the low melting point of $B_{2}O_{3}$ ($450^{\circ}C$), which can provide the low temperature consolidation of ceramic materials. The mechanical properties and the microstructure changes of the $B_{2}O_{3}$-included electrolyte support were examined by scanning electron microscope, mercury porosimetry, X-ray powder diffraction [XRD], high temperature differential scanning calorimeter and three-point bending strength measurement. The mechanical strength was clearly improved by addition of $B_{2}O_{3}$. The increase of mechanical strength results from the neck growth of a new $LiAlO_{2}$ phase between $LiAlO_{2}$ particles by the liquid phase sintering. Average pore size and porosity of the electrolyte support reinforced by addition of the sintering aid, $B_{2}O_{3}$, was $0.24{\mu}m$ and 59%, respectively which were suitable microstructure of a matrix for an application of MCFCs.

• Journal of Korean Society for Atmospheric Environment
• /
• v.6 no.1
• /
• pp.31-42
• /
• 1990

In order to suggest an efficient catalyst systems for NOx reduction of flue gases from industrial boilers, $TiO_2$ supported $WO_3-V_2O_5, V_2O_5$ and $WS_2$ catalysts were tested for the performances of NOx reduction at high reactin temperature range (250-500$^\circ$C) using a simulated flue gas system. It was found that while the proposed $WO_3/TiO_2$ and $WO_3-V_2O_5/TiO_2$ catalysts showed a significant high NOx reduction efficiency at about 350-400$^\circ$C, the conventional commercial catalyst of $V_2O_5/TiO_2$ showed a significant drop in NOx reduction efficiency due to the excessive $NH_3$ oxidation. From the measurement of surface acidities of those catalysts, it was found that the acidity are well correlated with the activities of NOx reduction. The reason of high activity of $WO_3$ series catalysts at high reaction temperature seems due to the low value of surface excess oxygen compared with that of $V_2O_5/TiO_2$ seems equivalent to the acid site of that catalyst.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.5
• /
• pp.213-217
• /
• 2011

The nonlinear electrical properties and degradation behavior against an impulse-current of 400 A in the ZnO-$Pr_6O_{11}$-CoO-$Cr_2O_3$-$Y_2O_3$-$Er_2O_3$ (ZPCCYE) varistors were investigated with different $Y_2O_3/Er_2O_3$ ratios. The $Y_2O_3/Er_2O_3$ mole ratio has a significant effect on nonlinear electrical properties and impulse degradation behavior of the ZPCCYE varistors. The varistors added with $Y_2O_3/Er_2O_3$ = 0.5/0.5 exhibited the best nonlinear properties with 39 in nonlinear coefficient (${\alpha}$) and the best clamp characteristics, in which the clamping voltage ratio (K) was in the range of K = 1.62-2.18 at an impulse-current of 1-50 A. The varistors added with $Y_2O_3/Er_2O_3$ = 0.25/0.5 exhibited the best electrical stability, with $%{\Delta}E_{1mA/cm^2}$=-5.6%, $%{\Delta}{\alpha}$ = 6.7%, and $%{\Delta}J_L$ = -14.6% against an impulse-current of 400 A. On the contrary, the varistors added with $Y_2O_3/Er_2O_3$ = 0.5/0.5 were destroyed applying an impulse-current of 400 A.