• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.978-985
• /
• 2001

The amorphous alumina was obtained by flash calcination of Bayer gibbsite[$Al(OH)_3$aluminum trihydroxide]. Rehydration and pore characteristics of $r-A1_2O_3$ prepared from rehydrated amorphous alumina were investigated. Crystal phases of pseudo-boehmite and bayerite were changed when amorphous alumina was hydrated at various conditions such as time, the ratio of water/alumina and pH. Specific surface areas and pore volumes of $r- A1_{2O}_3$ were influenced by the reaction time, water/alumina and PH of rehydration. The total pore volume of $r-A1_{2O}_3$increases with increasing the reaction time and ratio of water/alumina. Especially, the pure pseudo-boehmite of single phase could be prepared, when amorphous alumina was hydrated in the range of pH 6.5-8.0 in water/alumina= 10 at $90^{\circ}C$ for 7hr. The $r-Al_{2O}_3$, obtained by calcination of the prepared pseudo-boehmite at $500^{\circ}C$ for 2hrs, is characterized by the specific surface area of $265m^2$/g, total pore volume of $0.75cm^3$/g.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.1
• /
• pp.214-222
• /
• 2018

Alane(aluminum trihydride, $AlH_3$) is a candidate material involving high energetic capacity for solid propellant or explosives. In this study aluminum trihydride-etherate ($AlH_3{\cdot}(C_2H_5)_2O$) was synthesized through a wet process, and solid alane was extracted by controlled crystallization. Alane crystals were grown during the crystallization step with phase conversion of aluminum trihydride-etherate to alane using an anti-solvent. Stable crystal forms were found by a 2 hour crystallization process at $85^{\circ}C$. Finally the extracted solid aluminium trihydride consisted mainly of ${\gamma}-type$ with $50-100{\mu}m$ in size.

• The Bulletin of The Korean Astronomical Society
• /
• v.42 no.1
• /
• pp.45.2-46
• /
• 2017

3C 84 (NGC 1275) is one of the most famous radio galaxies and a lot of VLBI observations have been conducted to date because of its brightness and proximity (z = 0.0176; 1 mas = 0.36 pc). The source is entering a significantly active phase with long-term increase in radio flux at cm wavelengths since 2005, and the increased activity at very-high-energy (VHE) gamma rays. In order to study properties of sub-pc-scale structure and the circumnuclear environment in 3C 84, we have conducted multi-epoch VLBI observations with the Korean VLBI Network (KVN) at 86 and 129 GHz, and monthly monitoring by the KVN and VERA Array (KaVA) at 43 GHz from 2015 August. Following the report in the previous KAS meeting (cf. 2016 KAS Autumn Annual Meeting, [구 GC-10]), we present further results mainly on the basis of twelve-epoch observations with KaVA at 43 GHz. Through the monthly monitoring with KaVA, we found that peak intensity of the pc-scale southern lobe (C3) was increased from $2.60\;Jy\;beam^{-1}$ in 2015 October to $9.80\;Jy\;beam^{-1}$ in 2016 June, corresponding to a flux increase of 3.7 times in eight months. We also detected change in direction of motion of C3 from transversal to outward with respect to C1, concurrently with the beginning of its flux increase in 2015 October. We consider that these phenomena are due to interaction of C3 with the ambient medium, and are related to the gamma-ray flare which has been detected with VHE gamma-ray telescopes such as MAGIC and VERITAS.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.17 no.3
• /
• pp.30-36
• /
• 2013

This paper presents a method to estimate a storage life for loss of stabilizer content as storage periods using accelerated life test data. The estimate of storage life based on deterministic accelerated life test and degradation data cannot describe a condition distribution and storage life distribution. Previously, the method to show the condition distribution and storage life distribution by using gamma process has been studied. But it has limitation because it is impossible to collect the deterioration data at initial production phase. The estimated storage life presented by this study shows the similar value to previous studies and the method can describe the condition distribution and storage life distribution. So, the estimation method studied in this paper can be used for a life cycle management about deterioration of propellant for propulsion unit or components of missile, too.

• Journal of the Korean Ceramic Society
• /
• v.30 no.12
• /
• pp.1045-1053
• /
• 1993

Alumina hydrates were prepared by the neutralization of AlCl3.6H2O solution with NH3 gas diluted with N2 gas. The values of pH in reaction solution influenced the formation of alumina hydrates minerals. Amorphous alumina hydrates, for example, were formed at ${\gamma}$-Al2O3longrightarrow$\delta$-Al2O3longrightarrow$\theta$-Al2O3longrightarrow$\alpha$-Al2O3. (2) Bayeritelongrightarrowamorphouslongrightarrow${\gamma}$-Al2O3longrightarrow$\delta$-Al2O3longrightarrowη-Al2O3longrightarrow$\theta$-Al2O3longrightarrow$\alpha$-Al2O3. On the other hand, the shape of alumina hydrates whichw ere prepared by the reacton of Al2(SO4)3.16H2O solution and NH3 gas was spherical, the progress of its phase transformation with increasing temperature was amorphouslongrightarrow${\gamma}$-Al2O3longrightarrow$\alpha$Al2O3 in sequence.

• Journal of Microbiology and Biotechnology
• /
• v.17 no.2
• /
• pp.348-358
• /
• 2007

Metallothionein, a cysteine-rich stress response protein that is naturally induced by a variety of immunologic stressors, has been shown to suppress autoimmune disorders through mechanisms not yet fully defined. In the present study, we examined the underlying mechanisms by which metallothionein might mediate such regulation of autoimmunity. $Na\ddot{i}ve\;CD4^+$ T cells from metallothionein-deficient mice differentiated to produce significantly less IL-10, $TGF-{\gamma}$, and repressor of GATA, but more $IFN-{\gamma}$ and T-bet, when compared with those from wild-type mice. The levels of IL-4 and GATA-3 production were not different between the two groups of mice. Conversely, treatment with exogenous metallothionein during the priming phase drove $na\ddot{i}ve$ wild-type $CD4^+\;T$ cells to differentiate into cells producing more IL-10 and $TGF-{\beta}$, but less $IFN-{\gamma}$ than untreated cells. Metallothionein-primed cells were hyporesponsive to restimulation, and suppressive to T cell proliferation in an IL-10-dependent manner. Lymphocytes from metallothionein-deficient mice displayed significantly elevated levels of AP-1 and JNK activities in response to stimulation compared with those from wild-type controls. Importantly, transgenic mice overexpressing metallothionein exhibited significantly reduced susceptibility to collagen-induced arthritis and enhanced IL-10 level in the serum, relative to their nontransgenic littermates. Taken together, these data suggest that metallothionein is able to promote the generation of IL-10-and $TGF-{\beta}$-producing type 1 regulatory T-like cells by downregulating JNK-dependent AP-1 activity. Thus, metallothionein may play an important role in the regulation of Th1-dependent autoimmune arthritis, and may represent both a potential target for therapeutic manipulation and a critical element in the diagnostic assessment of disease potential.

• Macromolecular Research
• /
• v.16 no.2
• /
• pp.139-148
• /
• 2008

Biodegradable and elastic poly(L-lactide-co-$\varepsilon$-caprolactone) (PLCL) was electrospun to prepare nanofibers, and N-isopropylacrylamide (NIPAAm) was then grafted onto their surfaces under aqueous conditions using $^{60}Co-{\gamma}$ irradiation. The graft yield increased with increasing irradiation dose from 5 to 10 kGy and the nanofibers showed a greater graft yield compared with the firms. SEM confirmed that the PLCL nanofibers maintained an interconnected pore structure after grafting with NIPAAm. However, overdoses of irradiation led to the excessive formation of homopolymer gels on the surface of thc PLCL nanofibers. The equilibrium swelling and deswelling ratio of the PNIPAAm-g-PLCL nanofibers (prepared with 10 kGy) was the highest among the samples, which was consistent with the graft yield results. The phase-separation characteristics of PNIPAAm in aqueous conditions conferred a unique temperature-responsive swelling behavior of PNIPAAm-g-PLCL nanofibers, showing the ability to absorb a large amount of water at < $32^{\circ}C$, and abrupt collapse when the temperature was increased to $40^{\circ}C$. In accordance with the temperature-dependent changes in swelling behavior, the release rate of indomethacin and FITC-BSA loaded in PNIPAAm-g-PLCL nanofibers by a diffusion-mediated process was regulated by the change in temperature. Both model drugs demonstrated greater release rate at $40^{\circ}C$ relative to that at $25^{\circ}C$. This approach of the temperature-controlled release of drugs from PNIPAAm-g-PLCL nanofibers using gamma-ray irradiation may be used to design drugs and protein delivery carriers in various biomedical applications.

• Nutritional Sciences
• /
• v.9 no.4
• /
• pp.323-329
• /
• 2006

To more accurately estimate vitamin A and vitamin E intake of Koreans, food composition databases of the tocopherol and carotenoid contents of Korean foods are needed. In this study, the tocopherol $(\alpha-,\;\gamma-,\;and\;\delta-)$ and carotenoid ($\alpha-carotene,\;\beta-carotene,\;\beta-ctyptoxanthin$, lutein, and zeaxanthin) contents of 12 Korean cooked combination foods commonly consumed by children in Kwangju, Republic of Korea, were determined using reversed-phase HPLC. All samples were obtained from 3 different households in Kwangju during summer, 2005. All cooked foods in this study had detectable quantities of $\alpha-tocopherol,\;\gamma-tocopherol$ except for shoegogimugook, and $\delta-tocopherol$ except for myulchibokkeum Doejigogibokkeum had the highest $\alpha-tocopherol$ content (0.64 mg/l00 g edible portion), and $\gamma-tocopherol\;and\;\delta-tocopherol$ contents of gimbab were the highest among the foods (1.01 and 0.26 mg/l00 g edible portion). $\beta-carotene$ was found in all food samples. Gimbab had the highest contents of $\alpha-carotene,\;\beta-carotene$, and lutein among Korean cooked combination foods (158.3, 266.6, and $375.4{\mu}g/100g$ edible portion). Miyukgook contained only $\beta-carotene$ ($2.5{\mu}g/100g$ edible portion). Considerable sample-to-sample variability in tocopherol and carotenoid compositions were observed in several Korean cooked combination foods included in this study. Some of these carotenoids $(\alpha-carotene,\;\beta-carotene,\;and\;\beta-cryptoxanthin)$ are vitamin A precursors. The findings of this study may be valuable for use in Korean databases as well as nutrient consumption research for vitamin A and vitamin E.

• Korean Journal of Metals and Materials
• /
• v.46 no.3
• /
• pp.125-130
• /
• 2008

Conventional plasma carburizing or nitriding for austenitic stainless steels results in a degradation of corrosion resistance. However, a low temperature plasma surface treatment can improve surface hardness without deteriorating the corrosion resistance. The 2-step low temperature plasma processes (the combined carburizing and post nitriding) offers the increase of both surface hardness and thickness of hardened layer and corrosion resistance than the individually processed low temperature nitriding and low temperature carburizing techniques. In the present paper, attempts have been made to investigate the influence of the introduction of Ar gas (0~20%) in nitriding atmosphere during low temperature plasma nitriding at $370^{\circ}C$ after low temperature plasma carburizing at $470^{\circ}C$. All treated specimens exhibited the increase of the surface hardness with increasing Ar level in the atmosphere and the surface hardness value reached up to 1050 HV0.1, greater than 750 $HV_{0.1}$ in the carburized state. The expanded austenite phase (${\gamma}_N$) was observed on the most of the treated surfaces. The thickness of the ${\gamma}_N$ layer reached about $7{\mu}m$ for the specimen treated in the nitriding atmosphere containing 20% Ar. In case of 10% Ar containing atmosphere, the corrosion resistance was significantly enhanced than untreated austenitic stainless steels, whilst 20% Ar level in the atmosphere caused to form CrN in the N-enriched layer (${\gamma}_N$), which led to the degradation of corrosion resistance compared with untreated austenitic stainless steels.

• The Journal of Korean Society for Radiation Therapy
• /
• v.26 no.1
• /
• pp.59-67
• /
• 2014

Purpose : This study aims to evaluate 3D dosimetric impact for MIP image and each phase image in stereotactic body radiotherapy (SBRT) for lung cancer using volumetric modulated arc therapy (VMAT). Materials and Methods : For each of 5 patients with non-small-cell pulmonary tumors, a respiration-correlated four-dimensional computed tomography (4DCT) study was performed. We obtain ten 3D CT images corresponding to phases of a breathing cycle. Treatment plans were generated using MIP CT image and each phases 3D CT. We performed the dose verification of the TPS with use of the Ion chamber and COMPASS. The dose distribution that were 3D reconstructed using MIP CT image compared with dose distribution on the corresponding phase of the 4D CT data. Results : Gamma evaluation was performed to evaluate the accuracy of dose delivery for MIP CT data and 4D CT data of 5 patients. The average percentage of points passing the gamma criteria of 2 mm/2% about 99%. The average Homogeneity Index difference between MIP and each 3D data of patient dose was 0.03~0.04. The average difference between PTV maximum dose was 3.30 cGy, The average different Spinal Coad dose was 3.30 cGy, The average of difference with $V_{20}$, $V_{10}$, $V_5$ of Lung was -0.04%~2.32%. The average Homogeneity Index difference between MIP and each phase 3d data of all patient was -0.03~0.03. The average PTV maximum dose difference was minimum for 10% phase and maximum for 70% phase. The average Spain cord maximum dose difference was minimum for 0% phase and maximum for 50% phase. The average difference of $V_{20}$, $V_{10}$, $V_5$ of Lung show bo certain trend. Conclusion : There is no tendency of dose difference between MIP with 3D CT data of each phase. But there are appreciable difference for specific phase. It is need to study about patient group which has similar tumor location and breathing motion. Then we compare with dose distribution for each phase 3D image data or MIP image data. we will determine appropriate image data for treatment plan.