• 폴리머
• /
• 제24권4호
• /
• pp.477-487
• /
• 2000

Poly(L-lactic acid) (PLLA)/poly($\beta$-hydroxynonanoate) (PHN) 블렌드의 흔화도와 결정화거동을 연구하기 위해 여러 중량 흔합비의 시료를 제조하였다. DSC, XRD 및 편광현미경을 이용하여 PLLA/PHN 블렌드의 열적 성질 및 특성을 연구하였다. PLLA와 PHN은 무정형 영역에서 부분적인 상용성을 가졌으며 PLLA의 결정화도는 PHN이 첨가됨으로 인하여 증가되었다. 그리고 PHN이 첨가됨으로써 PLLA의 T$_{g}$, T$_{c}$, T$_{m}$ 의 이동이 있었다. 편광현미경 분석을 통하여 PLLA 구정의 수는 PHN이 증가할수록 증가하는 것을 알 수 있었다. 이로부터 PHN은 PLLA에 대하여 기핵제의 역할이 있음이 관찰되었다.

• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.315-322
• /
• 1989

Li2O-Al2O3-SiO2 system glasses contained P2O5, TiO2 and ZrO2as the nucleating agents were melted and formed. The glass was subsequently heated first to nucleate and then to grow the crystals. At constant nucleating agent content the base glass compositions were varied and the influences of these variations on the crystallization behaviour were investigated. The study was made by measurement of thermal expansion coefficient, differential thermal analysis, X-ray diffraction analysis, scanning electron microscope observation and transmission measurement of crystallized glass specimen in visible region. It was shown that the content of crystalline phase decreased with increasing SiO2 content as well as decresing Li2O in the base glass compositions. As the result of X-ray diffrection analysis, the major crystal was $\beta$-quartz solid solution. The degree of crystallinity which was calculated using the noncrystalline scattering methods increased in S-shape with increasing heat treatment time. This change was similar to that in thermal expansion coefficient. The transmissions of 5mm thick samples were 80-90% in visible ray region.

• 한국세라믹학회지
• /
• 제32권4호
• /
• pp.507-515
• /
• 1995

The monolithic dry gels of the Li2O-Al2O3-TiO2-SiO2 system were prepared by the sol-gel technique using metal alkoxides as starting materials to obtain monolithic glass-ceramics at low temperature without melting. Activation energy for the crystal growth of the gel with 6.05% TiO2, nucleating ageng, for the preparation of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was 101.14kcal/mol. As a result of the analysis of DTA & XRD, it was confirmed that the crytallization of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was the most efficient when 6.05% TiO2, nucleating agent, was added. $\beta$-eucryptite solid solution crystals and $\beta$-spodumene solid solution crystals were detected in the sample heat treated above 85$0^{\circ}C$. The sintered gel heat treated at 85$0^{\circ}C$ had the specific surface area of 185$m^2$/g, the pore volume of 0.19cc/g and the average pore radius of 20.8$\AA$. This shows that the sintered gel is also comparatively porous material. In temperature range of 25~85$0^{\circ}C$ thermal expansion coefficient of the specimen which was crystallized for 10hrs at 85$0^{\circ}C$ was 6.7$\times$10-7/$^{\circ}C$, which indicated that the crystallized specimen was turned out to be the glass-ceramic with low thermal expansion.

• 한국세라믹학회지
• /
• 제48권1호
• /
• pp.80-85
• /
• 2011

The crystallization behavior and microstructural change of the glass-ceramics were analyzed as a function of concentration and etching time of the HF solution in order to enhance the degree of crystallinity induced by heterogeneous nucleation of glass of bottom ash containing 15 wt% $Li_2O$. The nucleation site seemed to be generated where the Si ion was eluted. The main crystal phases in the glass-ceramics fabricated in this study were $\beta$-spodumene and $Li_2SiO_3$. The specimens etched with HF of 0.5 vol% within 0~60 seconds showed increased crystalline peak intensities in XRD pattern with etching time compared to no-etched one. Also the crystal size and crystal occupancy in the glass matrix observed by SEM were increased with etching time. For the glass-ceramics etched with 1.0 and 2.0 vol% HF solution, the etching time over 10 s was not effective to increase the crystallinity. From this study, it was found that the glass-ceramics with the higher crystallinity could be obtained by HF-etching followed by heat treatment process, even though the nucleating agent or 2-stages thermal treatment process were not used.