• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.416-422
• /
• 1989

The particle size of synthesized SiC powders was decreased with increasing carbon content when the mixture of carbon and silica was carbonized at 1, 45$0^{\circ}C$ after hydrolysis of the mixture with the ranges of 3.1 to 3.5 in the mole ratio of Carbon/Alkoxide. The reacted fraction of $\beta$-SiC nearly had nothing to do with the mole ratio of Carbon/Alkoxide. When the reaction was made by adding 0.5wt% additives in the composition of 3.1 in the mole ratio of carbon/alkoxide, the additives decreased the yield of $\beta$-SiC and its sequence was Ba2O3>B>Fe>Al>Al2O3>Si. The effect of additives promoted the transformation of $\beta$-SiC to $\alpha$-SiC form and shwoed the increasing tendency of lattice constant. The two colors of $\beta$-SiC powder came out : one was the black grey with addition of Al, Al2O3 and B the other the light grey with addition of Fe, B2O3 and Si.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.9
• /
• pp.510-515
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta-SiC-TiB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of Al_2O_3+Y_2O_34. The result of phase analysis of composites by XRD revealed $\alpha-SIC(6H)\;TiB_2,\; and YAG(Al5Y3O12) crystal phase. The relative density and the mechanical properties of composites were increased with increasing $Al_2O_3+Y_2O_34 contents because YAG of reaction between $Al_2O_3\; and\; Y_2O_3$ was increased. The Flexural strength showed the highest value of 432.5MPa for composites added with 12wt% $Al_2O_3+Y_2O_34 additives at room temperature. Owing to crack deflection crack bridging phase transition and TAG of fracture toughness mechanism the fracture toughness showed 7.1MPa.m1/2 for composites added with 12wt% $Al_2O_3+Y_2O_34 additives at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest of $6.0\times10-4\Omega.cm\; and\; 3.1\times10-3/^{\circ}C4 respectively for composite added with 12wt% \Omega additives at room temperature. The electrical resistivity of the composites was all positive temperature coefficient resistance (PTCR) in the temperature range of $25^{\circ}C\; to\; 700^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.36 no.11
• /
• pp.1217-1227
• /
• 1999

• Journal of the Korean Electrochemical Society
• /
• v.25 no.4
• /
• pp.191-200
• /
• 2022

Na-β"-Al₂O₃ has been widely employed as a solid electrolyte for high-temperature sodium (Na) beta-alumina batteries (NBBs) thanks to its superb thermal stability and high ionic conductivity. Recently, a vapor phase conversion (VPC) method has been newly introduced to fabricate thin Na-β"-Al₂O₃ electrolytes by converting α-Al₂O₃ into β"-Al₂O₃ in α-Al₂O₃/yttria-stabilized zirconia (YSZ) composites under Na⁺ and O^2- dual percolation environments. One of the main challenges that need to be figured out is lowered conductivity due to the large volume fraction of the non-Na⁺-conducting YSZ. In this study, the effect of lithia addition in the β"-Al₂O₃ phase on the grain size and ionic conductivity of Na-β"-Al₂O₃/YSZ solid electrolytes have been investigated in order to enhance the conductivity of the electrolyte. The amount of pre-added lithia (Li₂O) precursor as a phase stabilizer was varied at 0, 1, 2, 3, and 4 mol% against that of Al₂O₃. It turns out that ionic conductivity increases even with 1 mol% lithia addition and reaches 67 mS cm^-1 at 350 ℃ of its maximum with 3 mol%, which is two times higher than that of the undoped composite.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.479-481
• /
• 2000

The effect of $Al_{2}O_{3}+Y_{2}O_{3}$ additives on fracture toughness of $\beta-SiC-TiB_2$ composites by hot-pressed sintering were investigated. The f$\beta-SiC-TiB_2$ ceramic composites were hot-presse sintered and annealed by adding 16, 20, 24wt% $Al_{2}O_{3}+Y_{2}O_{3}$(6 : 4wt%) powder as a liquid forming additives at low temperature($1800^{\circ}C$) for 4h. In this microstructures, the relative density is over 95.88% of the theoretical density and the porosity increased with increasing $Al_{2}O_{3}+Y_{2}O_{3}$ contents because of the increasing tendency of pore formation. The fracture toughness showed the highest of $5.88MPa{\cdot}m^{1/2}$ for composites added with 20wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. The electrical resistivity showed the lowest of $5.22{\times}10^{-4}\Omega{\cdot}cm$ for composite added with 20wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature and is all positive temperature coefficient resistance (PTCR) against temperature up to $700^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.28 no.3
• /
• pp.142-147
• /
• 2018

${\beta}-Tricalcium$ phosphate (TCP) was added to $Al_2O_3$ to make a biomaterial with good mechanical properties. Using a TCP powder synthesized by a polymer complexation method, $Al_2O_3$ composites containing 30 wt% TCP were fabricated and characterized for densification, phase, microstructure, strength, and fracture toughness. With optimizing the powder preparation conditions, a high densification of 97 % was obtained by sintering at $1350^{\circ}C$ for 2 h. No reaction between the two components occurred and there was no transition to ${\alpha}-TCP$. TCP grains with a size of $2-4{\mu}m$ were well surrounded by $Al_2O_3$ grains with a size of $1{\mu}m$ or less. Strength 61(Brazilian) or 187(3-p MOR) MPa, and fracture toughness 1.7 (notched beam) or 2.5 (indentation) $MPa{\cdot}m^{1/2}$ were obtained, which are large improvements over the strength of $TCP/Al_2O_3$ composites and toughness of TCP and hydroxyapatite in previous studies.

• Journal of the Korean Ceramic Society
• /
• v.38 no.8
• /
• pp.749-754
• /
• 2001

마이크로파 추출 및 하소 공정을 통하여 카올린으로부터 베타 알루미나 전구체 및 베타 알루미나 분말을 합성하였다. 황산 알루미늄 및 가성소다의 혼합 용액을 교반되는 에탄올 용액 중에 적하시켜서 $Al_2$(SO$_4$)$_3$.17$H_2O$ 및 $Na_2$SO$_4$.10$H_2O$의 균일한 침전물을 얻었다. $\beta$- 및 $\beta$\"-Al$_2$O$_3$상으로 구성된 베타 알루미나를 얻기 위하여 재래식 및 마이크로파 하소법으로 주어진 온도에서 약 2h 동안 침전물 시료를 하소하였다. 재래식 하소된 시료에 비하여 마이크로파 하소된 시료는 $\beta$\"-Al$_2$O$_3$상이 상대적으로 많이 존재하였다. 또한, 재래식 하소된 시료와 마이크로파 하소된 시료의 미세구조는 매우 상이하였다. 매우 상이하였다.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1634-1636
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta$-SiC-$TiB_2$ electroconductive ceramic composites were investigated as function of the liquid forming additives of $Al_{2}O_{3}+Y_{2}O_3$ and the annealing method. Phase analysis of composites by XRD revealed $\alpha$-SiC(6H), $TiB_2$, and YAG($Al_{5}Y_{3}O_{12}$). In pressureless annealing method, the relative density and the mechanical properties of composites were increased with increasing $Al_{2}O_{3}+Y_{2}O_3$ contents because YAG of reaction between $Al_{2}O_3$ and $Y_{2}O_3$ was increased. But In pressured annealing method, reaction between $Al_{2}O_3$ and $Y_{2}O_3$ formed YAG but the relative density decreased with increasing $Al_{2}O_{3}+Y_{2}O_3$ contents. The electrical resistivity of the composites was all positive temperature coefficient resistance (PTCR) in the temperature range of 25$^{\circ}C$ to 700$^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.15-18
• /
• 2001

The composites were fabricated 61 vol% $\beta$-SiC and $39vol%TiB_2$ powders with the liquid forming additives of 8, 12, 16wt% $Al_2O_3+Y_2O_3$ by hot pressing at $1730^{\circ}C$ and subsequent pressed annealing and pressureless annealing at $1750^{\circ}C$ for 4 hours to form YAG. The result of phase analysis of composites by XRD revealed $\alpha$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density of composites were increased with increasing $Al_2O_3+Y_2O_3$ contents. The fracture toughness showed the highest value of $7.77MPa{\cdot}m^{1/2}$ for composites added with 12wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest of $7.3{\times}10^{-4}{\Omega}{\cdot}cm$ and $3.8{\times}10^{-3}/^{\circ}C$, respectively, for composite added with 12wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $25^{\circ}C$ to $700^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.2
• /
• pp.127-135
• /
• 1992

It has been reported that natural petalite showed a low negative thermal coefficient and wide coefficient and wide coexisting region with liquid phase in Li2O-Al2O3-SiO2 system. Therefore, we investigated variation of microstructure and thermal and mechanical properties when the amount of SiO2 content in petalite compound and MgO addition to it compound were changed. As SiO2 content exceeded 80 wt%, crystal phases of $\beta$-cristobalite and $\beta$-spondumene solid solution were formed. Generally, the densification and bending strength were increased by the addition of MgO, but the positive thermal coefficient was found in the case of MgO 10 wt% addition because of second phase and glassy phase.