• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.4
• /
• pp.266-278
• /
• 1995

The high strain-rate dynamic plastic behavior of Fe-X%Mn alloys was investigated. The strain rate did not have an effect when tested under quasi-static strain rates($2{\times}10^{-3}/sec$ and $2{\times}10^{-1}/sec$). However, the true stress increased at all strain levels when the strain rate increased to $6{\times}10^3/sec$. Based on the experimental results, an constitution equation to calculate the dynamic strength for strain rates over $10^4/sec$ was determined. The Fe-5%Mn alloy containing athermal ${\alpha}^{\prime}$ martensite initially did not show work hardening. The work hardening increased with Mn content showing a maximum at 20% Mn. The high work hardening of Fe-20%Mn and Fe-30%Mn alloys appears to be closely related not only to the initial amounts of ${\varepsilon}$ martensite but to the strain induced transformation (${\gamma}{\rightarrow}{\varepsilon}$ and ${\varepsilon}{\rightarrow}{\alpha}^{\prime}$) occurring during each stages of deformation.

• Journal of Korea Foundry Society
• /
• v.23 no.3
• /
• pp.153-157
• /
• 2003

본 논문은 레오캐스팅용 AZ91 합금 슬러리를 제조하는 새로운 방법에 관한 것이다. 그 원리는 AZ91 합금 액상에서 Mn의 용해도차에 의해 생성되는 $Al_8(Mn,Fe)_5$ 정출물을 ${\alpha}-Mg$ 초정 생성을 위한 불균일 핵생성 자리로 사용하고자 하는 것이다. 제조된 슬러리의 미세조직 분석결과 $Al_8(Mn,Fe)_5$ 정출물이 ${\alpha}-Mg$ 내에 위치하고 있어, 이로부터 정출물이 효과적으로 불균일 핵생성 자리로 작용하고 있음을 알 수 있었다. 또한 Mn 함량의 증가는 $Al_8(Mn,Fe)_5$ 정출물 수를 증가시켜 고상분율이 일정할 때 슬러리 내 ${\alpha}-Mg$ 고상의 크기를 감소시키고 구형도를 향상시킨다. 이외에도 냉각속도 및 유지시간이 슬러리 미세조직에 미치는 영향에 대해서도 보고하였다.

• The Korean Journal of Mycology
• /
• v.21 no.1
• /
• pp.23-27
• /
• 1993

Ion effects on $11{\alpha}-hydroxylation$ of progesterone and $5{\alpha}-reduction\;of\;11{\alpha}-hydroxyprogesterone$ by Rhizopus nigricans were investigated. Metal ions such as $Cu^{2+},\;Cd^{2+},\;Co^{2+},\;Mn^{2+},\;Zn^{2+},\;Fe^{2+},\;Mg^{2+},\;Fe^{3+}\;and\;Na^+$ reduced the $11{\alpha}-hydroxylation$ activity, while $K^+$ stimulated the same reaction. Enzyme activity for the $5{\alpha}-reduction$ of $11{\alpha}-hydroxyprogesterone$ was increased in the presence of $Fe^{2+},\;Mn^{2+},\;Mg^{2+},\;Co^{2+},\;Zn^{2+},\;Fe^{3+},\;K^+\;and\;Na^+$, whereas it was decreased in the presence of $Cd^{2+}\;and\;Cu^{2+}$. Potassium ion of $10^{-3}\;M\;$ of concentration was found to be effective for the promotion of $11{\alpha}-hydroxylation$. On the other hand, cadmium ion of $10^{-4}\;M$ was proved to suppress the $5{\alpha}-reduction$ reaction. Progesterone is reported to be transformed into $11{\alpha}-hydroxyprogesterone$ which, in turn, is converted further into $11{\alpha}-hydroxy-allopregnane-3$, 20-dione by R. nigricans. From this point of view, the highest yield of $11{\alpha}-hydroxyprogesterone$ could be obtained when potassium ion of $10^{-3}\;M$ was given initially followed by addition of cadmium ion of $10^{-4}\;M$ to limit conversion of 11{\alpha}-hydroxyprogesterone into $11{\alpha}-hydroxy-allopregnane-\;3$, 20-dione.

• Korean Journal of Materials Research
• /
• v.9 no.9
• /
• pp.937-942
• /
• 1999

Fe계 합금의 적층결함에너지를 감소시키는 것으로 알려진 Mn이 Fe-20Cr-1C-Si 경면처리 합금의 변형유기 상변태거동과 상온 및 고온 마모저항성에 미치는 영향에 대하여 조사하였다. 15ksi의 접촉응력에 대하여 0~25wt.% Mn을 첨가한 시편은 모두 상온에서 마모손실량이 적은 우수한 마모저항성을 보였는데 Mn 첨가량이 5wt.% 이하인 시편의 경우 마모표면에서 ${\gamma}$$\longrightarrow$$\alpha$\`변형유기 상변태가 발생한 반면 15wt.% 이상 Mn을 첨가한 시편에서는 ${\gamma}$$\longrightarrow$$\varepsilon$변형유기 상변태가 발생하는 것으로 나타났다. 25$0^{\circ}C$까지 고온 마모시험결과 ${\gamma}$$\longrightarrow$$\alpha$\`변형유기 상변태가 발생한 5wt.% 이하 Mn 첨가시편은 Mn 첨가량이 증가할수록 마모손실량이 증가하는 것으로 보아 Mn 첨가는 ${\gamma}$$\longrightarrow$$\alpha$\`변형유기 상변태에 있어서 고온 마모저항성을 저하시키는 것으로 생각되며 이는 Mn이 ${\gamma}$$\longrightarrow$$\alpha$\`변형유기 상변태의 M(sub)d 온도를 감소시키기 때문으로 생각된다. 반면에 ${\gamma}$$\longrightarrow$$\varepsilon$변형유기 상변태가 일어난 15wt.% 이상 Mn 첨가 시편의 경우 Mn 첨가량 증가에 따른 고온 마모손실량의 차이가 없는 것으로 보아 ${\gamma}$$\longrightarrow$$\varepsilon$변형유기 상변태는 ${\gamma}$$\longrightarrow$$\alpha$\`변형유기 상변태에 비해 온도의 존성이 적은 것으로 생각된다.

• Journal of Power System Engineering
• /
• v.8 no.4
• /
• pp.31-37
• /
• 2004

The damping capacity and strength of Fe-2Al-26Mn alloys have been studied for the development of new materials with high strength and damping capacity. Particularly, the effect of ${\alpha}'\;and\;{\varepsilon}$ martensite phase, which constitutes the microstructure of cold rolled Fe-Al-Mn alloys, has been investigated in terms of the strength and damping capacity of the alloys. The damping capacity rises with increasing the degree of cold rolling and reveals the maximum value at 25% reduction. The damping capacity is strongly affected by the volume fraction of ${\varepsilon}$ martensite, while the other phases, such as ${\alpha}'$ martensite and austenite phase, actually exhibit little effect on damping capacity. Considering that tensile strength increases and elongation decreases with increasing the volume fraction of ${\alpha}'$ martensite, it is proved that tensile strength is mainly affected by the amount of ${\alpha}'$ martensite.

• Journal of Korea Foundry Society
• /
• v.33 no.2
• /
• pp.55-62
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-4wt%Mg-0.9wt%Si system alloy has been studied. According to the analysis of cooling curve for Al-4wt%Mg-0.9wt%Si-0.3wt%Fe-0.3/0.5wt%Mn alloy, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}-Al_5FeSi$ phases crystallized above eutectic temperature of $Mg_2Si$. Therefore, these phases affected both the fluidity and shrinkage behaviors of the alloy during solidification. As Fe and Mn contents of Al-4wt%Mg-0.9wt%Si system alloy increased from 0.1 wt% to 0.4 wt% and from 0.3 wt% to 0.5 wt% respectively, the fluidity of the alloy decreased by 26% and 33%. When Fe content of the alloy increased from 0.1 wt% to 0.4 wt%, 23% decrease of macro shrinkage and 19% increase of micro shrinkage appeared. Similarly, Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, 11% decrease of macro shrinkage and 14% increase of micro shrinkage appeared. Judging from the castability of the alloy, Al-4wt%Mg-0.9wt%Si alloy with low content of Fe and Mn, 0.1 wt% Fe and 0.3 wt% Mn, is recommendable.

• Journal of the Korean Magnetics Society
• /
• v.12 no.1
• /
• pp.24-29
• /
• 2002

It was observed that exchange bias field was increased with smooth surface and better ${\gamma}$-FeMn formation. Sputtering conditions were varied for the control of the surface roughness and ${\gamma}$-FeMn formation. From the results of Cu deposition as underlayer, it was found that ${\gamma}$-FeMn formation was closely related with the thickness of underlayer. After heat treatment, exchange bias field was increased over three times. This improvement was likely that the crystallites of ${\gamma}$-FeMn were well formed. In Co/Cu/Co/FeMn spin valve structure, magnetoresistance was increased over 1.4 times through the heat treatment. This was due to the disappearance of Co/Cu intermixed dead layer and removal of defect, and this was examined by AES analysis.

• Resources Recycling
• /
• v.11 no.6
• /
• pp.31-37
• /
• 2002

Microstructure of aluminum alloys produced by the different mixing ratio of secondary ingot made by aluminum UBC (used beverage can) and virgin aluminum was investigated. The phase transitions of casted ingot by heat treatment were also studied. The alloys were melted at the electric resistance furnace, then casted using ceramic filter. Homogenization heat treatment was conducted at $615^{\circ}C$ for 10hrs to control cast microstructure. There were several kinds of phases, in as-cast condition, such as $\alpha$($Al_{12}$ $((Fe,Mn)_3$Si), $\beta$($Al_{6}$ (Fe,Mn)), and fine $Mg_2$Si phases. Especially, the amount of $\beta$-phase which was harmful in forming process was large. The $\beta$-Phase formed was transformed to u-phase by heat treatment. The fine $Mg_2$Si in the aluminum matix was also transformed to $\alpha$-phase by this heat treatment. Impurities filtered during casting process were identified as intermetallic compounds of Fe, Cu, Si.

• Journal of Power System Engineering
• /
• v.11 no.1
• /
• pp.115-120
• /
• 2007

The effect of grain size on the damping capacity of Fe-26Mn-2Al alloy studied in this paper has been investigated after changing the microstructure by cold rolling and changing grain size. Micro structures in Fe-26Mn-2Al at room temperature consist of a large quantity of austenite and a small quantity of ${\varepsilon}\;and\;{\alpha}'$ martensite. And ${\varepsilon}\;and\;{\alpha}'$ martensite was increased by increasing the degree of cold rolling. The content of deformation induced martensite was increased with increasing the degree of cold rolling. Damping capacity was linearly increased with increasing ${\varepsilon}$ martensite content, which suggests that stacking faults and ${\varepsilon}$ martensite variant boundaries are the principle damping sources. With increasing the grain size in Fe-26Mn-2Al alloy, the damping capacity was increased due to increasing the volume fraction of ${\varepsilon}$ martensite by decrement in stability of austenite phase. With decreasing the grain size, the content of deformation induced martensite was decreased and the damping capacity was decreased.

• Journal of Magnetics
• /
• v.19 no.1
• /
• pp.55-58
• /
• 2014

We have synthesized ferromagnetic ${\tau}$-phase $Mn_{54}Al_{46}/{\alpha}$-phase $Fe_{65}Co_{35}$ composite by annealing a mixture of paramagnetic ${\varepsilon}$-phase $Mn_{54}Al_{46}$ and ferromagnetic ${\alpha}$-phase $Fe_{65}Co_{35}$ particles at $650^{\circ}C$. The volume fraction ($f_h$) of hard ${\tau}$-phase $Mn_{54}Al_{46}$ of the composite was varied from 0 to 1. During the annealing, magnetic phase transformation occurred from paramagnetic ${\varepsilon}$-phase to ferromagnetic ${\tau}$-phase $Mn_{54}Al_{46}$. The magnetization and coercivity of the composite monotonically decreased and increased, respectively, as the $f_h$ increased. These results are in good agreement with our proposed composition dependent coercivity and modified magnetization equations.