• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1079-1088
• /
• 1996

Discontinuous ${\gamma}$-LiAlO2 fibers for fiber-reinforcing MCFC matrixes have been produced by the sol-gel process using the centrifugal spinning apparatus of the Rotary type. Gel fibers could be obtained through spinning of stable LiAlO2 complex polymetric sols under the optimum spinning conditions (hollow-disc rotating velocity 9000 rpm sol feeding rate of 4ml/min flowing N2 temperature of 4$0^{\circ}C$ and flowing N2 pressure of 4 bar). It was found that defect free and densified ${\gamma}$-LiAlO2 fibers with the relative density of 98% and the mean diameter of 4.7${\mu}{\textrm}{m}$ were prepared when the spinned fibers were heat-treated to 100$0^{\circ}C$ on the specified heating schedule. in particular the mean diameter and length of fibers could be controlled by the pressure of flowing N2 and the chopping-sieving method respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_{2}$(0 ${\times}$ 0.14) oxides have been synthesized by hydrothermal treatment of $(Co_{x}Mn_{1-x})_{3}O_{4}$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}-NaMnO_{2}$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_{2}$, comparing to orthorhombic $LiMnO_2$.

• Electrical & Electronic Materials
• /
• v.14 no.12
• /
• pp.7-10
• /
• 2001

Orthorhombic type LiCo$_{x}$Mn$_{1-x}$ O$_2$(0$\leq$x$\leq$0.14) oxides have been synthesized by hydrothermal treatment of (Co$_{x}$Mn$_{1-x}$ )$_3$O$_4$precursors and LiOH aqueous solution at 17$0^{\circ}C$. As-synthesized powders showed well-ordered $\beta$-MaMnO$_2$structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic LiCo$_{0.1}$Mn$_{0.9}$O$_2$, comparing to orthorhombic LiMnO$_2$./TEX>.EX>.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_2$ (0 x 0.14) oxides have been synthesized by hydrothermal treatment of ($Co_{x}Mn_{1-x}$)$_3O_4$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}$-$NaMnO_2$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_2$, comparing to orthorhombic $LiMnO_2$.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.10
• /
• pp.1129-1135
• /
• 1999

Free energy perturbation and molecular dynamics simulations were carried out to investigate the relative binding affinities of [17] ketonand (1) toward alkali metal cations in methanol. The binding affinities of 1 toward the alkali metal cations were calculated to be in the order Li+ > Na+ > K+ > Rb+ > Cs+, whereas our recent theoretically predicted and experimentally observed binding affinities for [18]starand (2) were in the order K+ > Rb+ > Cs+ > Na+ > Li+. The extremely different affinities of 1 and 2 toward smaller cations, Li + and Na+ , were explained in terms of the differences in their ability to change the conformation to accommodate cations of different sizes. The carbonyl groups constituting the central cavity of 1 can reorganize to form a cavity with the optimal M+ -O distance, even for the smallest Li+, without imposing serious strain on 1. The highest affinity of 1 for Li+ was predominantly due to the highest Coulombic attraction between the smallest Li+ and the carbonyl oxygens of 1.

• Journal of Industrial Technology
• /
• v.43 no.1
• /
• pp.43-48
• /
• 2023

Spinel LiNi_0.5Mn_1.5O₄ (LNMO) has been considered as one of most promising cathode material, because of its low-cost and competitive energy density. However, 4.7V vs. Li/Li⁺ of high operating potential facilitates electrolyte degradation on cathode-electrolyte interface during charge-discharge process. In particular, commercial polyvinylidene fluoride (PVDF) is not sutaible for LNMO cathode binder because its weak van der waals force induces thick and non-uniform coverage on the cathode surface. In this review, we study high performance binders for LNMO cathode, which forms uniform coating layer to prevent direct contact between electrolyte and LNMO particle as well as modifying high quality cathode electrolyte interphase, improved cell performace.

• Journal of the Korean Ceramic Society
• /
• v.45 no.7
• /
• pp.423-429
• /
• 2008

Ceramic Fiber separator is the promising material for thermal battery system because it reduces the production cost and offers the potential to a new application compared to a pellet type electrolyte. The molten salt electrolytes for thermal battery were prepared by the impregnation of the commercial glass filters such as GF-A, C and F (Whatman, USA) with two types of molten-lithium salts, LiCl-KCl and LiK-LiBr-LiF. The wetting properties were evaluated by wetting balance test and wetting angle measurement. The wetting behaviors were strongly affected by the composition of the molten salts and the pore structure of the glass separators. The optimum wetting conditions for maximum loading and effective retention of the molten electrolyte were also studied.

• Transactions on Electrical and Electronic Materials
• /
• v.9 no.1
• /
• pp.20-23
• /
• 2008

Organic light-emitting diodes (OLEDs) are attractive because of possible application in display with low-operating voltage, low-power consumption, self-emission and capability of multicolor emission by the selection of emissive materials. To investigated the optical effects, we studied the electrical and optical characteristics due to thickness variation of electron injection materials LiF on organic light-emitting diodes in the ITO (indium-tin-oxide)/N,N'-diphenyl-N, N'-bis(3-methyphenyl)-1,1'-biphenyl-4,4'-diamine(TPD)/tris(8-hydroxyquinoline) aluminum $(Alq_3)/LiF$ layer/Al device. We maintained the thicknesses of TPD and $Alq_3$ layers at 40 nm and 60 nm, respectively. The deposition rates of TPD and $Alq_3$ were in the $1.5{\AA}/s$ under a base pressure of $5{\times}10^{-6}$ Torr. It was found that luminance and luminous efficiency of the device with 0.7 nm LiF layer improve 25 times and 7 times than the device without the LiF layer, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.286-286
• /
• 2007

Li이 첨가된 0.7(Ba,Sr)$TiO_3$-0.3MgO 후막 interdigital 커패시터를 연구하였다. Li이 첨가된 0.7(Ba,Sr)$TiO_3$-0.3MgO의 후막을 $Al_2O_3$ 기판 위에 형성하기 위하여 스크린 프린팅 방법을 이용하였다. $BaSrTiO_3$의 세라믹 물질은 높은 유전율(1MHz에서 500이상)과 낮은 유전 손실(1MHz에서 0.01)값을 가지고 있는 반면, $1350^{\circ}C$의 높은 온도에서 소결되는 단점이 있다. 따라서 본 연구에서는 $BaSrTiO_3$ 세라믹 물질의 유전특성을 향상시키고 $1350^{\circ}C$의 높은 소결온도를 낮추기 위해서, MgO(30wt%)와 Li(3wt%)을 $BaSrTiO_3$에 첨가하였다. 그리고 10um의 후막을 $Al_2O_3$ 기판 위에 스크린 프린팅 방법을 통해 형성한 후, 50um finger gap의 interdigital 커패시터를 Ag 전극을 이용하여 제작하였다. 샘플을 제작하기 전에, Frequency와 유전율의 상관관계를 알아보기 위해 3D simulator를 통해 시뮬레이션 하였고, 주파수와 온도별 유전 특성, 구조와 전암-전류에 대한 특성을 본 연구의 결과를 통해 토의 할 것이다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.7
• /
• pp.517-520
• /
• 2010

Lead-free $0.9(Na_{0.52}K_{0.48})NbO_3$ - $0.1LiTaO_3$ piezoelectric ceramics doped with $Ag_2O$ (0-4 mol%) have been prepared by the conventional mixed oxide method. The structural and electrical properties were analyzed in order to find its potential applications. The crystal structure of 1-4 mol% Ag doped $0.9(Na_{0.52}K_{0.48})NbO_3$-$0.1LiTaO_3$ lead free piezoelectric ceramics were investigated for several sintering temperatures ($1100^{\circ}C$) by the use of X-ray diffraction analysis. In order to analyze the effect of Ag dopants on the $0.9(Na_{0.52}K_{0.48})NbO_3$-$0.1LiTaO_3$ ceramic, the diffraction intensity ratio of the (002) to (200) planes were calculated from the X-ray diffraction patterns of the ceramic samples.