• Journal of the Korean Ceramic Society
• /
• v.33 no.8
• /
• pp.871-876
• /
• 1996

It is believed that fly ash could be suitable for preparing the sialon by carbothermal reduction method because the total amount of SiO2 and Al2O3 is above 80% and the unburned residual carbon is above 5% within the fly ash. The effects of reaction temperature (1350, 1400, 145$0^{\circ}C$) reaction time (1, 5, 10 hours) and the amount of carbon additions (C/SiO2=2, 3, 4 mole) on the $\beta$-sialon synthesis were obserbed, It was conformed that $\beta$-sialon (Z=2.15~2.18) was formed as major phase under all of the synthesis conditions and small amount of Si2ON2 SiC, AlN and Si3N4 was formed depending on the synthesis conditions. FeSix intermetal-lic compound was formed above 140$0^{\circ}C$ reaction temperature due to the large amount of iron oxides within the raw fly ash.

• Journal of Korea Foundry Society
• /
• v.28 no.4
• /
• pp.179-183
• /
• 2008

Mechanical properties of the spray-cast Al 6061 alloy with variation of Mg/Si addition were investigated. After spray-cast, hot extrusion was performed at $460^{\circ}C$ then followed ageing treatment to the T6 condition. SEM, EDX, and XRD were used to characterize a ${\beta}(Mg_{2}Si)$ precipitate. The amount of ${\beta}$ precipitate was calculated from the XRD measurements. Hardness, ultimate tensile strength and elongation were tested then compared with those of the Al 6061 alloys made by ingot metallurgy (I/M) and powder metallurgy (P/M). The ultimate tensile strength and elongation of the spray-cast Al 6061 alloy were 318MPa and 16.5%, respectively. These properties were improved in the 2.2 wt%Mg and 1.3wt%Si addition up to 349MPa of UTS and 12.5% of elongation, mainly due to increased amount of a fine supersaturated ${\beta}(Mg_{2}Si)$ precipitate.

• Journal of Korea Foundry Society
• /
• v.30 no.1
• /
• pp.34-45
• /
• 2010

The effects of alloy elements and cooling rate on the solidification path and the formation behavior of $\beta$ phase in Fe-containing Al-Si alloys were studied based on the thermodynamic analysis and the pertinent experiments. The thermodynamic calculation was systematically performed by using Thermo-Calc program. For the thermodynamic analysis in high alloy region of Al-Si-Fe ternary system, a thermodynamic database for Thermo-Calc was correctly updated and revised by the collected up-to-date references. For the thermodynamic-based prediction of various solidification paths in Fe-containing Al-Si system, liquidus projection of Al-Si-Fe ternary system, including isotherms, invariant, monovariant, bivariant reactions and equilibrium temperatures, was calculated and analyzed as functions of composition and temperature. The calculated results were compared to the experimental results using various casting specimens. In order to analyze various solidification sequences as functions of Si and Fe content, 4 representative alloy compositions, low Fe content in both low and high Si contents and high Fe content again in both low and high Si contents, were designed in this study. For better understanding of the influence of cooling rate on the formation behavior of $\beta$ phase, 4 alloys were solidified under furnace and rapidly cooled conditions. Cooling curves of solidified alloys were recorded by thermal analysis. Various important solidification events were evaluated using the first derivative-cooling curves. Microstructures of the casting samples were studied by the combined analysis of optical microscopy (OM) and scanning electron microscopy (SEM).

• Journal of the Korean Ceramic Society
• /
• v.29 no.3
• /
• pp.232-240
• /
• 1992

Densification behavior, microstructural evolution, and mechanical properties of hot-pressed specimens using $\beta$-SiC and $\alpha$-SiC powder with Al2O3 additive were studied. Beta-SiC powder was fully densified as 205$0^{\circ}C$, but $\alpha$-SiC powder was at 210$0^{\circ}C$. The maximum flexural strength and the fracture toughness of the specimen hot-pressed using $\beta$-SiC powder were 681 MPa and 6.7 MPa{{{{ SQRT {m } }}, and thosevalues of specimen hot-pressed using $\alpha$-SiC powder were 452 MPa and 4.7 MPa{{{{ SQRT {m } }}, respectively. The strength superiority of specimen hot-pressed using $\beta$-SiC powder was due to the finer grain size, and higher density. The higher toughness of specimen hot-pressed using $\beta$-SiC powder than $\alpha$-SiC powder than $\alpha$-SiC powder was due to the crack deflection mechanism arised from the difference of thermal expansion coefficient between $\alpha$ and $\beta$-SiC phases which were co-existed in the sintered body.

• Journal of the Korean Ceramic Society
• /
• v.46 no.5
• /
• pp.452-455
• /
• 2009

A cost-effective route to synthesize $\beta$-SiAlONs from Si mixtures by reaction bonding followed by post-sintering was investigated. Three different z values, 0.45, 0.92 and 1.87, in $Si_{6-z}Al_zO_zN_{8-z}$ without excess liquid phase were selected to elucidate the mechanism of SiAlON formation and densification. For RBSN (reaction-bonded silicon nitride) specimens prior to post-sintering, nitridation rates of more than 90% were achieved by multistep heating to $1400^{\circ}C$ in flowing 5%$H_2$/95%$N_2$; residual Si was not detected by XRD analysis. An increase in density was acquired with increasing z values in post-sintered specimens, and this tendency was explained by the presence of higher amounts of transient liquid phase at larger z values. Measured z values from the synthesized $\beta$-SiAlONs were similar to the values calculated for the starting compositions. Slight deviations in z values between measurements and calculations were rationalized by a reasonable application of the characteristics of the nitriding and post-sintering processes.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.473-480
• /
• 1997

$\beta-SiC$powder with or without the addition of 1-3 wt% of $\beta-SiC$ whiskers (seeds) was hot-pressed at $1850^{\circ}C$ for 1 h using $Al_2O_3$ and $Y_2O_3$ as sintering aids. The hot-pressed materials were subsequently annealed at $1950^{\circ}C$ to enhance grain growth. The introduction of $\beta-SiC$ whiskers into $\beta-SiC$ does not affect the microstructure as well as mechanical properties significantly because the whiskers are not viable in the presence of liquid phase during hot-pressing. The strengths and fracture toughnesses of the hot-pressed and subsequently 5 h-annealed materials with 1 wt% $\beta-SiC$ whiskers and without $\beta-SiC$ whiskers were 465 MPa and 5.8 MPaㆍ$m^{1/2}$, and 451 MPa and 5.5 MPaㆍ$m^{1/2}$, respectively.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.13-22
• /
• 2010

The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. $\beta$-SiC powder with 0, 2, 6, 10 wt% of $\alpha$-SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at $1700-1850^{\circ}C$ for 10 min. The heating rate, applied pressure and sintering atmosphere were kept at $100^{\circ}C/min$, 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to $1700^{\circ}C$ consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at $1750^{\circ}C$ and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of $\alpha$-SiC seeds into $\beta$-SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the $\alpha$-SiC seeds added in $\beta$-SiC, the rate of grain growth decreased with $\alpha$-SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.347-356
• /
• 1992

Various kaolin samples with different alumina content were prepared from calcined admixture of kaolin and ammonium sulfate by varying the treatment time in sulfuric acid. Samples were nitridated under N2 or N2-H2 atmosphere with changing the amount of added carbon, the reaction time and temperature. As the alumina content lowered, the size of kaolin particles decreased and the specific surface area increased. XRD analysis indicated that ${\alpha}$-quartz remained by decomposition of halloysite and meta-halloysite. Experimental results of nitridation behavior are summerized as follows; 1) Nitridation under N2 atmosphere. With the increase of C/SiO2 ratio and with the decrease of Al2O3 content, disappearance of XRD pattern peaks of mullite, ${\alpha}$-quartz and ${\alpha}$-Al2O3 were accelerated at 1300$^{\circ}C$. SiC was the main phase in the reaction product of acid-treated kaolin samples nitridated at 1300$^{\circ}C$ for 10 hours regardless of C/SiO2 ratio. But the XRD peak intensities of ${\beta}$-Si3N4, ${\beta}$-sialon and SiC did not show much difference when untreated raw kaolin was fired at the same condition. When the ratio of C/SiO2 was 3.5, ${\beta}$-sialon and ${\beta}$-Si3N4 existed in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 7 hours. Only ${\beta}$-sialon existed in the same sample fired at 1400$^{\circ}C$ for 10 hours. ${\beta}$-sialon was obtained from all of the acid-treated kaolin samples fired at 1400$^{\circ}C$ for 40 hours, but AlN and SiC remained in the untreated kaolin sample. Z value of the ${\beta}$-sialon obtained from the 22% alumina containing kaolin sample fired at 1400$^{\circ}C$ for 40 hours was about 1.3(XRD) and 1.5(EDS). 2) Nitridation under 80N2+2OH2 mixed gas atmosphere with the C/SiO2 ratio of 1 Mullite was not found, but ${\alpha}$-Si3N4, and ${\beta}$-sialon were present in the reaction product of about 22% alumina containing kaolin sample fired at 1300$^{\circ}C$ for 10 hours. When untreated kaolin sample was nitridated at the same condition, mullite remained. AlN and SiC were not found in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 5 hours. On the other hand, AlN and SiC remained in the product of untreated kaolin fired at the same condition.

• Journal of Korea Foundry Society
• /
• v.26 no.3
• /
• pp.123-128
• /
• 2006

Mechanical and thermal properties of spray-cast hypereutectic Al-20wt.%Si-xwt.%Fe alloys (x=0, 1, 3, 5) were investigated. After the spray-casting, hot extrusion was performed at $400^{\circ}C$. Intermetallic compound (${\beta}-Al_5FeSi$) and primary Si are observed in the spray-cast aluminum alloys. The size of primary Si and intermetallic compound of the spray-aluminum alloys became finer and more uniformly distributed than that of the permanent mold cast ones. Ultimate tensile strength of the spray-cast aluminum alloys increased by increasing Fe contents, but that of the permanent mold cast aluminum alloys decreased by increasing Fe contents possibly due to increased amount of coarse intermatallic compound. The coefficient of thermal expansion (CTEs) of the aluminum alloys became lower with finer primary Si and intermetallic compound, and this is attributed to the increased amount of interfacial area between the aluminum matrix and the phases of finer Si and intermetallic compound.

• Journal of the Korean Institute of Gas
• /
• v.19 no.5
• /
• pp.41-46
• /
• 2015

It is known that in aluminum 6061-T6, which is composed of $Mg_2Si$ and ${\beta}-Al_5FeSi$, void nucleation grows around ${\beta}-Al_5FeSi$ of Al606-T6. In this work, growth of voids was checked by scanning a 6061-T6 specimen with SEM observation. The effects of dislocation damping, coherency strain and voids on ultrasonic attenuation and nonlinearity parameters were experimentally measured. It was observed that a nonlinearity parameter increases until 75 percent of fatigue life and decreases after that. From the results, the authors inferred that dislocation damping and coherency damping increase nonlinearity parameters and void nucleation decreases them as ultrasonic scattering increases with void. The application of nonlinearity parameters in estimating degradation of materials with complex microstructures through fatigue process, therefore, should be carefully considered.