• 한국군사과학기술학회지
• /
• 제21권6호
• /
• pp.760-766
• /
• 2018

The present study investigates the effect of PMMA and BN content on microstructure, mechanical and dielectric properties of silicon nitride($Si_3N_4$) ceramics in $Y_2O_3-Al_2O_3$ additive system. The total additive content was fixed at 8 wt.% and the amount of PMMA varies from 0 to 40 wt.% and BN varies from 0 to 36 wt.%, respectively. The crystalline phases of the samples were determined by X-ray diffraction analysis. All the sintered sample shows complete transformation of ${\alpha}$ to ${\beta}-Si_3N_4$ during the sintering process indicated that the phase transformation was unaffected by the PMMA or BN content. However, the microstructure shows that the residual porosity increased with increasing PMMA and BN content. In addition, the flexural strength and the dielectric constant decrease with addition of PMMA and BN due to the residual porosity. This article provides empirical study of design parameters for $Si_3N_4$-based radome materials.

• 한국산학기술학회논문지
• /
• 제11권6호
• /
• pp.1943-1948
• /
• 2010

평균 입도의 크기가 ${\sim}1.7\;{\mu}m$와 ${\sim}30\;nm$인 두 종류의 탄화규소 분말을 7 wt% $Y_2O_3$, 2 wt% $Al_2O_3$, 1 wt% MgO를 소결 첨가제로 사용하여 $1800^{\circ}C$에서 1 시간동안 Ar 분위기에서 압력을 가하여 고온가압소결을 하였다. 고온 가압소결한 시편은 $1950^{\circ}C$에서 6 시간동안 Ar 분위기에서 40 MPa의 압력을 가하여 고온 단조 하였다. 두 시편 모두 고온가압소결 후의 미세구조는 등방형 모양의 결정립을 나타내었으며, 고온 단조 후에 결정립 성장이 나타났다. 평균 입도의 크기가 작은 탄화규소 분말로 소결한 시편의 결정립의 크기가 고온 단조 후에도 더 작은 결정립을 나타내었다. 고온 단조 후의 압력축과 평행한 방향과 수직한 방향의 미세구조는 비슷하였다. 탄화규소의 $\beta$에서 $\alpha$로의 상변태가 활발하게 발생하지 않아 집합조직의 발달은 발견되지 않았다. 평균 입도의 크기가 큰 탄화규소 분말로 제작된 시편의 파괴인성 (${\sim}3.9\;MPa{\cdot}m^{1/2}$), 경도 (~ 25.2 GPa), 굽힘강도가 (480 MPa) 평균 입도의 크기가 작은 탄화규소로 제작된 시편보다 높게 나타났다.

• 한국세라믹학회지
• /
• 제48권2호
• /
• pp.127-133
• /
• 2011

Non-Alkali multicomponent $La_2O_3-Al_2O_3-SiO_2$ glasses has been designed and analyzed on the basis of a mixture design experiment with constraints. Fitted models for thermal expansion coefficient, glass transition temperature, Young's modulus, Shear modulus and density are as follows: ${\alpha}(/^{\circ}C)=8.41{\times}10^{-8}x_1+5.72{\times}10^{-7}x_2+2.13{\times}10^{-7}x_3+1.09{\times}10^{-7}x_4+1.10{\times}10^{-7}x_5+1.15{\times}10^{-7}x_6+2.72{\times}10^{-8}x_7+2.41{\times}10^{-7}x_8-1.08{\times}10^{-8}x_1x_2+4.28{\times}10^{-8}x_3x_7-2.02{\times}10^{-8}x_3x_8-1.60{\times}10^{-8}x_4x_5-2.71{\times}10^{-9}x_4x_8-2.19{\times}10^{-8}x_5x_6-3.89{\times}10^{-8}x_5x_7$ $T_g(^{\circ}C)=7.36x_1+15.35x_2+20.14x_3+8.97x_4+13.85x_5+4.22x_6+28.21x_7-1.44x_8-0.84x_2x_3-0.45x_2x_5-1.64x_2x_7+0.93x_3x_8-1.04x_5x_8-0.48x_6x_8$ $E(GPa)=2.04x_1+14.26x_2-1.22x_3-0.80x_4-2.26x_5-1.67x_6-1.27x_7+3.63x_8-0.24x_1x_2-0.07x_2x_8+0.14x_3x_6-0.68x_3x_8+0.29x_4x_5+1.28x_5x_8$ $G(GPa)=0.35x_1+1.78x_2+1.35x_3+1.87x_4+9.72x_5+29.16x_6-0.99x_7+3.60x_8-0.48x_1x_6-0.50x_2x_5+0.08x_3x_7-0.66x_3x_8+0.94x_5x_8$ ${\rho}(g/cm^3)=0.09x_1+0.51x_2-4.94{\times}10^{-3}x_3-0.03x_4+0.45x_5-0.07x_6-0.10x_7+0.07x_8-9.60{\times}10^{-3}x_1x_2-8.20{\times}10^{-3}x_1x_5+2.17{\times}10^{-3}x_3x_7-0.03x_3x_8+0.05x_5x_8$ The optimal glass composition similar to the thermal expansion coefficient of Si based on these fitted models is $65.53SiO_2{\cdot}25.00Al_2O_3{\cdot}5.00La_2O_3{\cdot}2.07ZrO_2{\cdot}0.70MgO{\cdot}1.70SrO$.

• 분석과학
• /
• 제9권3호
• /
• pp.302-309
• /
• 1996

Fe-5.7%Al-1.1%Cr-0.5%Si 및 여기에 0.12wt.%C가 함유된 합금의 최종 열처리를 $800^{\circ}C$에서 가열 후 수냉 또는 노냉함으로써 냉각방법에 의한 제진특성의 변화를 조사한 결과, 수냉은 이 합금의 제진특성을 현저히 악화시켰다. 그 원인을 미세조직 및 우선방위 특성과 관련시켜 조사하여 다음과 같은 결과를 얻었다. 열처리 후의 냉각방법에 의해 결정립 크기 및 잔류응력은 거의 무시할 정도로 변화가 없었으며, 이로부터 이들은 제진특성과 직접적인 상관이 없다고 판단되었다. 그러나 이 합금의 집합조직 형성은 수냉의 경우(200) 및 노냉의 경우(110)가 우세하게 형성되어, 이 현상을 이 합금의 자화용이축 <100>과 관련시켜 수냉시의 제진특성 악화를 해석할 수가 있었다. 즉 수냉에 의해 $180^{\circ}$ 자구벽이 $90^{\circ}$ 자구벽에 비해 많이 형성되어 제진에 결정적 역할을 하는 $90^{\circ}$ 자구벽이 적어져 그 제진특성이 악화된 것이다.

• 한국해양공학회지
• /
• 제25권6호
• /
• pp.97-104
• /
• 2011

Modified C95600 bronze contains Fe component of 0.7 weight percentage besides Cu-7Al-2.5Si composition. The shape of centrifugal cast is a circular pipe with thick wall. Specimens machined from the centrifugal cast were quenched in oil after isothermal holding at a given heat treatment temperature in the range of $700{\sim}900^{\circ}C$. Mechanical properties and structural morphology are depended on the quenching heat treatment temperature regardless of isothermal holding time. Tensile strength or Brinell hardness is increased with increasing heat treatment temperature. The microstructure caused by quenching contains mixing phases of ${\alpha}+{\beta}'+FeSi+{\kappa}$ which martensite of ${\beta}'$ phase has been transformed from ${\beta}$ phase. Effect of isothermal holding temperature on mechanical properties in case of quenching heat treatment attributes to the change of volume fraction of ${\beta}'$ on the structural morphology. Mechanical characteristics of specimen, initially quenched from $850^{\circ}C$, and then tempered at $500^{\circ}C$, does not show an obvious softening indication, because disappearance of ${\beta}'$ during tempering process can be compensated by precipitation of brittle phase ${\gamma}$.

• Korean Membrane Journal
• /
• 제8권1호
• /
• pp.21-30
• /
• 2006

A faujasite NaY zeolite membrane was prepared on a tubular ${\alpha}-Al_2O_3$ support by the secondary growth process, and effects of permeation test conditions on the $CO_2/N_2$ separation were investigated. A NaY zeolite membrane with good $CO_2/N_2$ separation was successfully synthesized by using the hydrothermal solution ($Al_2O_3:SiO_2:Na_2O:H_2O$ = 1:6:14:840 in a molar base): at a permeation temperature of $30^{\circ}C$, its $CO_2$ permeance and $CO_2/N_2$ separation factor were $2.5{\times}10^{-7}mol/m^2secPa$ and 34, respectively. The $CO_2$ and $N_2$ permeations were highly dependent on permeation test conditions (feed composition, feeding rate, feed pressure, He sweeping rate and permeation temperature). The results indicated that (i) $CO_2$ and $N_2$ permeations through NaY zeolite membrane are governed by surface and micropore diffusions, respectively, (ii) the preparation of NaY zeolite membrane with a large permeating area is one of the most difficult hurdles for its real applications, and (iii) the retardation of $N_2$ permeation is an effective key to improve $CO_2/N_2$ separation factor in NaY zeolite membrane.

• KSBB Journal
• /
• 제16권3호
• /
• pp.295-301
• /
• 2001

Thiobacillus ferrooxid,$\alpha$ns와 pyrite 광석을 연마하여 resin에 고정한 시편을 대상으로 침출 시간에 따른 표면의 특성 변화를 EPMA 및 SEM-EDS를 이용하여 이미지와 원소구성비율에 따라 살펴보았다. 침출이 진행됨에 따라 표면의 철성분은 전체적으로 증가한 반면 원소황은 감소하는 경향을 나타냈다. 고배율에 익한 SEM 이미지에서 침출이 진행됨에 따라 도덧모양의 생성물이 침출 13일 경과 시점에 서 나타나 23일 경과 후까지 자라났으나 30일 경과 시점 에서는 표면전체에 새로운 층 생성된 결과로 나타났다. SEM 이미지 상에서 spot과 배경 지접의 원소 구성비를 EDS에 의하여 분석한 후 비교한 결과 초기에는 원소 구성비의 차이가 큰 값을 보이나 침출이 증가함에 따라 좌이가 나 지 않으며 이는 칩풀이 진행됨에 따라 pyrite 표면변이 접차 생성불이 칩착 되는 것으로 볼 수 있었다.

• 한국재료학회지
• /
• 제19권6호
• /
• pp.305-312
• /
• 2009

The effects of Quenching and Partitioning (Q&P) and Annealed Martensite (AM) heat treatment on the microstructure and tensile properties were investigated for 0.24C-0.5Si-1.5Mn-1Al steels. The Q&P steels were annealed at a single phase ($\gamma$) or a dual phase (${\gamma}+{\alpha}$), followed by quenching to a temperature between $M_s$ and $M_f$. Then, enriching carbon was conducted to stabilize the austenite through the partitioning, followed by water quenching. The AM steels were intercritically annealed at a dual phase (${\gamma}+{\alpha}$) temperature and austempered at $M_s$ and $M_s{\pm}50^{\circ}C$, followed by cooling in oil quenching. The dual phase Q&P steels showed lower tensile strength and yieldyield strength than those of the single phase Q&P steels, and tThe elongation for the dual phase Q&P steel was partitioning 100s higher than that of that for the single phase Q&P steels as the partitioning time was less than 100s up to partitioning 100s. For AM steels, the tensile/yield strength decreased and the total elongation increased as the austempering temperature increased. The stability of the retained austenite controlled the elongation for Q&P steels and the volume fraction of the retained austenite controlled the elongation for AM steels.

• 자원리싸이클링
• /
• 제2권2호
• /
• pp.27-38
• /
• 1993

본 연구에서는 제철소에서 발생하는 전로 dust를 사용하여 심강법(분급)에 의한 철산화물을 분리하여 고순도의 철분말을 회수하였으며, 아래와 같은 결론을 얻었다. 가. 전로 dust의 물성 1) 재항의 1제강, 2제강 C/F(Clarifier) dust, 광장의 E/C(Evaporation coolar), dust, 중국강철공사(C.S.C) OM(Clarifier underflow) dust 금철분이 63~72%로 높고, Metal Fe 가 21~50% 함유되어 있으며, 기타 산화물로는 CaO, MgO, Al$_{2}O_{3}$, SiO$_{2}$ 등이 있다. 2) 재항의 1제강, 2제강 C/F dust, 광양의 E/C, E/P dust, 중국강철공사(C.S.C), OM(clarifier underflow) dust 입자의 형상은 청입이 주로 구형으로 응고된 모양이었으며, 일반적으로는 출립의 외각부는 magnetite, hematite 등으로 산화가 진해되어 있다. 3) 전로 dust 들에 대한 X-ray 회절분석결과, 재항의 1제강, 2제강, C/F dust, 광양의 E/C, E/P dust는 ${\alpha}$-Fe, FeO(wusute)가 중성분으로 존재하며 그 밖에 FE$_{3}O_{4}$9magnetite), Fe$_{2}O_{3}$ CaO가 소량으로 존재하고 있었으며, 중국강철공사(C.S.D) OM(underflow) dust는 ${\alpha}$-Fe, ${\alpha}Fe_{2}O_{3}$, graphite가 주성분으로 존재하며, 그 밖에 $Fe_{3}O_{4}$, Fe$_{2}O_{3}$, ZnO이 소량으로 존재하고 있었다. 4) 순수한 순철분말과 전로 dust를 구성하고 있는 순철은 마광에 따른 입자의 분쇄보다는 마광시 구형의 입자가 소성변형으로 인해 flake형상으로 변하여 체질입도분석시 입도의 증가를 초래하였으며, 반면 철산화물은 마광에 따른 입자의 미세화가 발생함을 볼 수 있었다. 나. 철분구 외수 실험 1) 광양의 dust를 40분간 마광하여 심강(분급)실험을 행했을 때 Fe 99.17% 품위 철분말을 37.8% 회수할 수 있었다. 2) 재항의 C/F dust를 40분간 마광하여 심강(분급)실험을 행했을 때 Fe 98.38% 품위의 철분말을 44.42% 회수할 수 있었다. 3) 70 gauss 자석을 사용하여 자력선별을 행했을 때 +65-200 mesh 사이에서 Fe 품위 98% 이상의 철분말을 회수 할 수 있으나 회수율(14%)이 낮다.

• 한국자기학회지
• /
• 제14권3호
• /
• pp.99-104
• /
• 2004

자기 터널 접합(Magnetic Tunnel Junction, MTJ)의 플라즈마 산화시간과 열처리 온도에 따른 자기저항(Tunneling Magnetoresistance, TMR) 온도의존특성을 연구하였다. 플라즈마 산화시간을 30$_{s}$ 70$_{s}$ 까지 10$_{s}$ 간격으로 변화시켜 측정한 결과, 산화시간 50초에서 상온에서 25.3%의 가장 높은 TMR 비를 얻었다. 스핀 분극도 $P_{0}$ 스핀파 지수(spin wave parameter) $\alpha$를 구한 결과, 산화시간 50$_{s}$ 에서 40.3%의 가장 높은 스핀 분극도와 가장 낮은 온도 의존 특성인 (10$\pm$4.742)${\times}$$10^{-6}$ $K^{－1.5}$스핀파 지수(spin wave parameter) $\alpha$값을 얻었다. 그리고 온도별 열처리 결과 175$^{\circ}C$에서 TMR비가 25.3%에서 27.5%까지 증가하였으며 스핀파 지수는 (10$\pm$0.719)${\times}$$10^{-6}$ K $^{－1.5}$ 까지 감소하여 온도의존도가 감소하였다.