• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.3 no.4
• /
• pp.88-94
• /
• 2004

High manganese steel was maintained stability of Non-Magnetics performance. Fatigue tests were carried out under constant stress amplitude, using a non-magnetic high manganese steel. The fatigue crack growth mechanism of the high manganese steel was clarified from results such as observation of crack growth path and fracture surface. The result of getting this study was shown as following: 1) Remarkably ${\Delta}Kth$ of the high manganese steel is big with about 3 times of the general steel product. 2) In the low ${\Delta}K$ value region, da/dN is dependent on Kmax, and in the high ${\Delta}K$ value region, it is dependent on ${\Delta}Keff$. The reason of this behavior is crack closure due to fracture surface roughness and fretting oxide. 3) It seems to ease the stress concentration of crack tip crack growth behavior in the ${\Delta}Kth$ vicinity by the generation of the secondary crack.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.10
• /
• pp.49-55
• /
• 2000

This study describes the fatigue characteristics for Al2024 alloy, which is aircraft structure material. For this work, the plane-strain fracture toughness test, the plane-stress fracture toughness test and the crack growth rates test were conducted under the standard testing method. Test equipment is a computer-controlled closed-loop fatigue testing machine. The data of each test result is very important to aircraft structure reliability estimation, life prediction, design analysis, endurance analysis and damage tolerance analysis. In addition, the fatigue crack growth threshold($\DeltaKth$) value decreased as the stress ratio increased. Also, $\DeltaKth$ decreased as the thickness increased in LT, TL directions.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2003.10a
• /
• pp.106-111
• /
• 2003

This study made an experiment On fatigue crack propagation da/dn, stress intensity factor range ${\Delta}K$ respectively in room temperature and in low temperature. And we got the following characteristics from fatigue crack growth test carried Out in the environment of room temperature and law temperature at $25^{\circ}C$, $-60^{\circ}C$, $-80^{\circ}C$, and $-100^{\circ}C$ in the range of stress ratio of 0.3 by means of opening made displacement. The threshold stress intensity factor range ${\Delta}Kth$ in the early stage of fatigue crack growth (Mode I) and stress intensity factor range ${\Delta}K$ in the stable of fatigue crack growth (Made II) was decreased in proportion to descend temperature. It assumed that the fatigue resistance characteristics and fracture strength at law temperature and high temperature is considerable higher than that of room temperature in the early stage and stable of fatigue crack growth region.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.05a
• /
• pp.167-172
• /
• 2002

In this study, CT specimens were prepared from spring steel(SUP9) processed shot peening which was room temperature, high temperature experiment. And ire got the following characteristics from fatigue crack growth test carried out in the environment of room, and high temperature at $25^{\circ}C,\;100^{\circ}C,\;150^{\circ}C$ and $180^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. The threshold stress intensity factor range ${\Delta}Kth$ in the early stage of fatigue crack growth (Region I) and stress intensity (actor range ${\Delta}K$ in the stable of fatigue crack growth (Region II) was decreased in proportion to descend temperature. It assumed that the fatigue resistance characteristics and fracture strength at high temperature is considerable higher than that of room temperature in the early stage and stable of fatigue crack growth region.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.224-225
• /
• 2005

The lightness of components required on marine and shipbuilding industry is requiring high strength of components. In particular, fatigue failure phenomena, which happen in metal, bring on danger in human life and property. Therefore, antifatigue failure technology takes an important part of current industries. In this study, it was investigated about endurance and fatigue crack propagation rate of according to stress ratio of SMAW commonly using for welding structures in present. Fatigue crack propagation rate(da/dN) of low load(R=0.1) was lower than of high load(R=0.6) for piping weld. And in stage I, ${\Delta}$Kth, the threshold stress intensity factor of the weld under heavy load is higher than under small load. Fatigue life shows more improvement in the weld of stress ratio R=0.l than in the weld of stress ratio R=0.6.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.6 no.3
• /
• pp.198-207
• /
• 1998

To determine the effect of temperature and microstructure on the fatigue crack propagation behavior in Ti-3Al-2.5V alloy, experimental investigations have been carried out with the specimens of different temperatures and different volume fractions of prime $\alpha$-phase. The temperatures employed were room temperature, 20$0^{\circ}C$, 30$0^{\circ}C$ and 40$0^{\circ}C$ under the same frequency of 20Hz. To obtain the different volume fractions of the primary $\alpha$-phase, specimens were solution-treated at $\alpha$+$\beta$ and above the $\beta$ region. From the experimental results, following conclusions were obtained. (1) ΔKth was observed to increase with the less volume fraction of the primary $\alpha$-phase. (2) As the temperature increased. (3) Microstructures having more primary $\alpha$-phase showed higher strength at the high temperatures.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.6 no.2
• /
• pp.34-40
• /
• 2007

Antifatigue failure technology take an important part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore, this paper the effect of compressive residual stress and corrosion of spring steel(SAE 5155)by shot-peening on fatigue crack growth characteristics in stress ratio(R=0.05)was investigated with considering fracture mechanics. By using the methods mentioned above, We arrived at the following conclusions. The fatigue crack growth rate(da/dN) of the shot-peening material was lower than that of the un-peening material. And in stage I, ${\Delta}Kth$, the threshold stress intensity factor, of the shot-peen processed material is high in critical parts unlike the un-peening material. Also m, fatigue crack growth exponent and number of cycle of the shot-peening material was higher than that of the un-peening material. That is concluded from effect of da/dN. Finally fracture of shot-peening material and un-peening material was identified and discussed in this study.

• Journal of Industrial Technology
• /
• v.6
• /
• pp.33-38
• /
• 1986

The aim of this study is to find out the relationships between the microstructures of SM45C(AISI1045) steel and fatigue crack propagation behaviour. Three microstructures such as (i) as received (fully annealed). (ii) water quenched and tempered, and (iii) oil quenched and tempered were used for fundamental mechanical testing and fatigue crack proagation test. The microstructures of (ii) and (iii) showed superior in tensile strength to (i). Resistance against fatigue crack propagation was higher in structure (i), while tensile properties were better in structures (ii) and (iii). It is believed due to that the enhancement of roughness of fracture surface obsered in structure (i) increases ${\Delta}Kth$ and lowers fatigue crack growth rate. However it does not necessarily mean the quenched and tempered structures (ii) and (iii) are undesirable for the engineering component because fatigue limit in low cycle test appears usually higher in the microstructures of higher strength.