• Korean Journal of Materials Research
• /
• v.33 no.8
• /
• pp.330-336
• /
• 2023

The effects of Ni²⁺ substitution for Mg²⁺-sites on the microwave dielectric properties of (Mg_1-xNi_x)(Ti_0.95(Mg_1/3Ta_2/3)_0.05)O₃ (0.01 ≤ x ≤ 0.05) (MNTMT) ceramics were investigated. MNTMT ceramics were prepared by conventional solid-state reaction. When the MgO / TiO₂ ratio was changed from 1.00 to 1.02, MgTi₂O₅ was detected as a secondary phase along with the MgTiO₃ main phase in the MNTMT specimens sintered at 1,400 ℃ for 4h. For the MNTMT specimens with MgO / TiO₂ = 1.07 sintered at 1,400 ℃ for 4h, a single phase of MgTiO₃ with an ilmenite structure was obtained from the entire range of compositions. The relative density of all the specimens sintered at 1,400 ℃ for 4h was higher than 95 %. The quality factor (Qf) of the sintered specimens depended strongly on the degree of covalency of the specimens, and the sintered specimens with x = 0.01 showed the maximum Qf value of 489,400 GHz. The dielectric constant (K) decreased with increasing Ni²⁺ content because Ni²⁺ had a lower dielectric polarizability (1.23ų) than Mg²⁺ (1.32ų). As Ni²⁺ content increased, the temperature coefficient of resonant frequency (TCF) improved, from -55.56 to -21.85 ppm/℃, due to the increase in tolerance factor (t) and the lower dielectric constant (K).