• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2002년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.85-87
• /
• 2002

The $(Ba_xBi_{0.6-x}Sr_{0.4})TiO_3$[x=0.1, 0.2, 0.3] ceramics were prepared by conventional mixed oxide method The structural properties of the $(Ba_xBi_{0.6-x}Sr_{0.4})TiO_3$[x=0.1, 0.2, 0.3] ceramics with the sintering temperature($1200^{\circ}C,\;1250^{\circ}C,\;1300^{\circ}C$) were investigated by XRD, SEM, EDS. Increasing the sintering temperature, the intensity of the $Ba_{0.5}Sr_{0.5}TiO_3$ (100), (110), (111), (200), (310) peaks and $SrBi_4Ti_4O_{15}$ (319), (040) peaks were increased. The gram of the $(Bi_{0.2}Ba_{0.4}Sr_{0.4})TiO_3$ ceramics sintered at $1250^{\circ}C$ were fine and uniform. Increasing the sintering temperature. the average gram size of the $(Bi_{0.2}Ba_{0.4}Sr_{0.4})TiO_3$ ceramics were decreased. The density of $(Bi_{0.1}Ba_{0.5}Sr_{0.4})TiO_3$ ceramics sintered at $1250^{\circ}C$ was 5.4524 [$g/cm^2$].

• 멤브레인
• /
• 제22권1호
• /
• pp.8-15
• /
• 2012

다공성 $La_{0.6}Sr_{0.4}Ti_{0.3}Fe_{0.7}O_{3-{\delta}}$로 코팅된 $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 관형 분리막은 압출성형 및 dip coating 방법으로 제조 되었다. 코팅된 관형 분리막의 특성은 X-선 회절분석기(XRD)와 전자 주사 현미경(SEM)을 이용하여 분석하였으며, 분석결과 $2{\mu}m$의 다공성 코팅 층을 갖는 페롭스카이트 구조임을 알 수 있었다. 산소투과량 분석은 $750{\sim}950^{\circ}C$ 범위에서 공급측과 투과 측을 대기 중 공기와 진공으로 하여 수행되었다. 다공성의 $La_{0.6}Sr_{0.4}Ti_{0.3}Fe_{0.7}O_{3-{\delta}}$로 코팅된 $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 관형 분리막의 산소투과량은 $950^{\circ}C$에서 $3.2mL/min{\cdot}cm^2$로 코팅되지 않은 분리막보다 높게 나타났으며, 11일 동안의 장기 안정성 실험결과 코팅 층에 의해 안정성이 증가됨을 알 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}Sr_{0.4}TiO_{3}(BST)$ films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}Sr_{x}TiO_{3}$ (x = 0.1 - 0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}Sr_{0.3}TiO_{3}$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.

• 한국전기전자재료학회논문지
• /
• 제15권11호
• /
• pp.933-938
• /
• 2002

(Ba,Sr)TiO$_{4}$ (BST) thin films on Pt/Ti/SiO$_{2}$/Si substrates were deposited by a sol-gel method and the etch characteristics of BST thin films have been investigated as a function of gas mixing ratio. The maximum etch rate of the BST films was 440 $AA$/min under such conditions as: CF$_{4}$(CF$_{4}$＋Ar) of 0.2, RF-power of 700 W, DC-bias voltage of -200 V, pressure of 15 mTorr and substrate temperature of 30 $^{circ}C$. The selectivities of BST to Pt, SiO$_{2}$ and PR were 0.38, 0.25 and 0.09, respectively. In the XPS (X-ray photoelectron spectroscopy) analysis, Barium (Ba) and Strontium (Sr) component in BST thin films formed low volatile compounds such as BaFx, SrFx, which are forms by the chemical reaction with F atoms and is removed by Ar ion bombardment. Titanium (Ti) is removed by chemical reaction such as TiF with ease. The result of secondary ion mass spectrometry (SIMS) analysis confirmed the existence of the BaFx, SrFK, TiFx.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제48권6호
• /
• pp.410-415
• /
• 1999

$Ba_{1-x}Sr_xTiO_3$ thin films with various ratio of Sr (X = 0.4, 0.5, 0.6) were grown $Pt/TiN/SiO_2/Si$ subastrate by RF magnetron sputtering deposition. As, Ag, and Cu films were deposited on $Ba_{1-x}Sr_xTiO_3$ thin films as top electrodes by using a thermal evaporator. The electrical properties of $Ba_{1-x}Sr_xTiO_3$ thin films for various compositions were characterized and the physical properties at interface between $Ba_{1-x}Sr_xTiO_3$ thin films and top electrodes were evaluated in terms of the work function difference. At x =0.5, the degradation of capacitance is lower to the other compositions. As negative biasapplied, the specimen with Cu top electrode has board saturation region and low leakage current since work function of Cu is bigger than other electrodes.$ Ba_{0.5}Sr_{0.5}TiO_3$ thin films with Cu top electrode, the dielectric constant was measured to the value of 354 at 1 kHz and the leakage current was obtained to the value of $5.26\times10^{-6}A/cm2$ at the forward bias of 2 V.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권5호
• /
• pp.265-269
• /
• 2000

$(Ba, Sr)TiO_3$thin films were etched with a magnetically enhanced inductively coupled plasma (MEICP) at different CF4/Ar gas mixing ratios. Experimental was done by varying the etching parameters such as rf power, dc bias and chamber pressure. The maximum etch rate of the BST films was $1800{AA}/min$ under $CF_4/(CF_4+Ar)$ of 0.1, 600 W/350 V and 5 mTorr. The selectivity of BST to Pt and PR was 0.6, 0.7, respectively. X-ray photoelectron spectroscopy (XPS) results show that surface reaction between Ba, Sr, Ti and C, F radicals occurs during the (Ba, Sr)TiO3 etching. To analyze the composition of surface residue after the etching, films etched with different CF_4/Ar$ gas mixing ratio were investigated using XPS and secondary ion mass spectroscopy (SIMS).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 반도체 재료 센서 박막재료 전자세라믹스
• /
• pp.18-21
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_3$ thin films doped by Bi from 5 to 20 mol% on a $Pt/Ti/SiO_2/Si$ substrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin film showed the lowest value of $5.13{\times}10^{-7}\;A/cm^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films were 333, 0.0095, and 31.1%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}$S $r_{0.4}$Ti $O_3$(BST) films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}$S $r_{x}$Ti $O_3$(x=0.1-0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}$S $r_{0.3}$Ti $O_3$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.00 nm.m.m.m.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 센서 박막재료 반도체재료 기술교육
• /
• pp.16-19
• /
• 2002

(Ba,Sr)TiO3(BST) thin film is an attractive material for the application in high-density dynamic random access memories (DRAMs) because of the high relative dielectric constant and small variation in dielectric properties with frequency. In this study, (Ba0.6,Sr0.4)TiO3 thin films on Pt/Ti/SiO2/Si substrates were deposited by a sol-gel method and the CF4/Ar inductively coupled plasma (ICP) etching behavior of BST thin films had been investigatedby varying the process parameters such as chamber pressure, ICP power, and substrate bias voltage. To analysis the composition of surface residue following etching BST films etched with different Ar/CF4 gas mixing ratio were investigated using x-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometer (SIMS).

• 한국전기전자재료학회논문지
• /
• 제17권8호
• /
• pp.852-858
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_{3}$thin films doped by Bi from 5 to 20 mol% on a Pt/Ti/$SiO_2$/Sisubstrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_{3}$ thin film showed the lowest value of 5.13$\times 10^{-7} A/{cm}^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_{3}$thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}Tio_{3}$ thin films were 333, 0.0095, and 31.1%, respectively.